CN107433664A - 一种阻燃地板的生产工艺 - Google Patents
一种阻燃地板的生产工艺 Download PDFInfo
- Publication number
- CN107433664A CN107433664A CN201710836590.5A CN201710836590A CN107433664A CN 107433664 A CN107433664 A CN 107433664A CN 201710836590 A CN201710836590 A CN 201710836590A CN 107433664 A CN107433664 A CN 107433664A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- water
- proof
- production technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种阻燃地板的生产工艺,包括如下步骤:(1)在基板的表面涂覆一层阻燃面漆;(2)涂刷防水防腐除醛胶剂:所述防水防腐除醛胶剂,含有水性树脂、防腐防霉剂、防虫剂、防白蚁剂、除甲醛剂、成膜助剂、防冻剂和水,其中各组分的百分重量比含量分别为:水性树脂5‑90份、防腐防霉剂0.01‑30份、防虫剂0.01‑20份、防白蚁剂0.01‑15份、除甲醛剂0.01‑20份、成膜助剂0.01‑30份、防冻剂0.01‑15份、水5‑95份。
Description
技术领域
本发明涉及一种木地板生产工艺,属于木制品生产工艺技术领 域。
背景技术
作为一种装饰材料,地板越来越多地被人们用来装饰自己的家居 和工作场所,由于地板主要由易燃的木材构成,地板表面又普遍涂 有易燃的油漆,因而地板在使用过程中的安全问题也越来越被人们 所关注,现代地板虽然在耐磨性、防变形方面得到显著提高,但在 阻燃方面尚未有大的突破,因此如何提高地板的阻燃性能,保证地板 的使用安全,成为了业界亟待解决的课题。
发明内容
本发明的目的在于:提供一种阻燃地板及其生产工艺,本发明 不仅大大提高了阻燃效果,而且本发明的物理力学性能也非常优秀, 具有理想的使用效果。
本发明采用了如下技术方案:一种阻燃地板的生产工艺,包括如 下步骤:
(1)在基板的表面涂覆一层阻燃面漆;
(2)涂刷防水防腐除醛胶剂:所述防水防腐除醛胶剂,含有水性树 脂、防腐防霉剂、防虫剂、防白蚁剂、除甲醛剂、成膜助剂、防冻 剂和水,其中各组分的百分重量比含量分别为:水性树脂5-90份、 防腐防霉剂0.01-30份、防虫剂0.01-20份、防白蚁剂0.01-15 份、除甲醛剂0.01-20份、成膜助剂0.01-30份、防冻剂0.01-15 份、水5-95份。
进一步地,在基板的表面涂覆10~25g/cm2阻燃面漆,涂覆 阻燃面漆之后并进行紫外线固化,紫外线固化是通过紫外线照射阻 燃面漆表面,固化能量为200~250mj/cm2,固化时间为3~5 秒。
采用以上技术方案的有益效果是:
与现有技术相比,本发明采用多种涂层协同作用,使得本发明既 提高了阻燃效果,又保证了良好的力学性能。
本发明生产的阻燃地板,具有防水防腐除醛的功能。
具体实施方式
下面结合实施例对本发明做进一步说明:
实施例:
一种阻燃地板的生产工艺,包括如下步骤:
(1)在基板的表面涂覆一层阻燃面漆;
(2)涂刷防水防腐除醛胶剂:所述防水防腐除醛胶剂,含有水性树 脂、防腐防霉剂、防虫剂、防白蚁剂、除甲醛剂、成膜助剂、防冻 剂和水,其中各组分的百分重量比含量分别为:水性树脂5-90份、 防腐防霉剂0.01-30份、防虫剂0.01-20份、防白蚁剂0.01-15 份、除甲醛剂0.01-20份、成膜助剂0.01-30份、防冻剂0.01-15 份、水5-95份。
其中,在基板的表面涂覆10~25g/cm2阻燃面漆,涂覆阻燃 面漆之后并进行紫外线固化,紫外线固化是通过紫外线照射阻燃面 漆表面,固化能量为200~250mj/cm2,固化时间为3~5秒。
Claims (2)
1.一种阻燃地板的生产工艺,其特征在于:包括如下步骤:
(1)在基板的表面涂覆一层阻燃面漆;
(2)涂刷防水防腐除醛胶剂:所述防水防腐除醛胶剂,含有水性树脂、防腐防霉剂、防虫剂、防白蚁剂、除甲醛剂、成膜助剂、防冻剂和水,其中各组分的百分重量比含量分别为:水性树脂5-90份、防腐防霉剂0.01-30份、防虫剂0.01-20份、防白蚁剂0.01-15份、除甲醛剂0.01-20份、成膜助剂0.01-30份、防冻剂0.01-15份、水5-95份。
2.根据权利要求1所述的阻燃地板的生产工艺,其特征在于:在基板的表面涂覆10~25g/cm2阻燃面漆,涂覆阻燃面漆之后并进行紫外线固化,紫外线固化是通过紫外线照射阻燃面漆表面,固化能量为200~250mj/cm2,固化时间为3~5秒。