CN107418205A - 一种聚酰亚胺轴承保持器材料及制造方法 - Google Patents

一种聚酰亚胺轴承保持器材料及制造方法 Download PDF

Info

Publication number
CN107418205A
CN107418205A CN201710672607.8A CN201710672607A CN107418205A CN 107418205 A CN107418205 A CN 107418205A CN 201710672607 A CN201710672607 A CN 201710672607A CN 107418205 A CN107418205 A CN 107418205A
Authority
CN
China
Prior art keywords
parts
polyimides
bearing cage
thermosetting
nano
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710672607.8A
Other languages
English (en)
Inventor
宋文选
陈尧
周蓓蓓
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanjing Haiyin Communication Equipment Co Ltd
Original Assignee
Nanjing Haiyin Communication Equipment Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanjing Haiyin Communication Equipment Co Ltd filed Critical Nanjing Haiyin Communication Equipment Co Ltd
Priority to CN201710672607.8A priority Critical patent/CN107418205A/zh
Publication of CN107418205A publication Critical patent/CN107418205A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种聚酰亚胺轴承保持器材料及制造方法，将聚酰亚胺、二氧化钛、纳米碳、氮化钛、镍混合加入配料搅拌机中搅拌得到混合物；将所述混合物进行模型热固，即可得到轴承保持器，本发明的聚酰亚胺轴承保持器材料具有自润滑、高耐磨、耐高温、高硬度的特点。

Description

一种聚酰亚胺轴承保持器材料及制造方法
技术领域
本发明涉及一种聚酰亚胺轴承保持器材料生产技术，属于轴承技术领域。
背景技术
陶瓷轴承包括全陶瓷轴承和陶瓷球混合轴承，全陶瓷轴承是指套圈（包括保持器）和滚动体均为陶瓷材料，陶瓷球混合轴承则指套圈为轴承钢，仅滚动体为陶瓷材料。由于陶瓷球具有高硬度、高耐磨、低摩擦、低密度、耐腐蚀等优异特性，在确保轴承长寿命、高可靠工作方面优势明显。由于为了使得轴承使用寿命长，一般要求保持器的硬度要低于滚动体的硬度，而为了提高轴承耐磨性，一般是对陶瓷球进行研究，降低其摩擦系数，提高其耐磨性能，而对于与其紧密相关的保持器这方面的研究较少。
发明内容
发明目的：为了克服现有技术中存在的不足，本发明提供一种自润滑、高耐磨、高硬度的聚酰亚胺轴承保持器材料。
技术方案：为实现上述目的，本发明采用的技术方案为：
一种聚酰亚胺轴承保持器材料，包括以下重量份计的原料制成：聚酰亚胺80-90份，二氧化钛13-15份，纳米碳15-20份、氮化钛0.5-3份、镍0.5-3份。
优选的：聚酰亚胺85份，二氧化钛14份，纳米碳18份、氮化钛2份、镍1份。
一种制作聚酰亚胺轴承保持器材料的方法，将聚酰亚胺、二氧化钛、纳米碳、氮化钛、镍混合加入配料搅拌机中搅拌得到混合物；将所述混合物进行模型热固，即可得到轴承保持器。
优选的：热固的温度为10-500oC，热固时逐步温升，当温升到500oC，逐步降温，直至保持器降到室温。
优选的：热固的温度时间为0.1-5小时。
本发明相比现有技术，具有以下有益效果：
本发明采用聚酰亚胺作为基体制作轴承保持器，得到的轴承保持器耐高温，其摩擦系数低，增加二氧化钛、氮化钛进行改性，使得其强度增加，增加纳米碳使得其摩擦系数进一步降低，增加镍使得其导热性得到增加，耐高温更好，因此得到的保持器具有自润滑、高硬度、高耐磨性、耐高温。
具体实施方式
下面结合具体实施例，进一步阐明本发明，应理解这些实例仅用于说明本发明而不用于限制本发明的范围，在阅读了本发明之后，本领域技术人员对本发明的各种等价形式的修改均落于本申请所附权利要求所限定的范围。
实施例1
一种聚酰亚胺轴承保持器材料，包括以下重量份计的原料制成：聚酰亚胺80份，二氧化钛13份，纳米碳15份、氮化钛0.5份、镍0.5份。
一种制作聚酰亚胺轴承保持器材料的方法，将聚酰亚胺、二氧化钛、纳米碳、氮化钛、镍混合加入配料搅拌机中搅拌得到混合物；将所述混合物进行模型热固，热固的温度为10-500oC，热固时逐步温升，当温升到500oC，逐步降温，直至保持器降到室温。热固的温度时间为0.1-5小时。即可得到轴承保持器。
实施例2
本实施例与实施例1的区别在于：一种聚酰亚胺轴承保持器材料，包括以下重量份计的原料制成：聚酰亚胺90份，二氧化钛15份，纳米碳20份、氮化钛3份、镍3份。
实施例3
本实施例与实施例1、2的区别之处在于，一种聚酰亚胺轴承保持器材料，包括以下重量份计的原料制成：聚酰亚胺85份，二氧化钛14份，纳米碳18份、氮化钛2份、镍1份。
以上所述仅是本发明的优选实施方式，应当指出：对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (5)

1.一种聚酰亚胺轴承保持器材料，其特征在于：包括以下重量份计的原料制成：聚酰亚胺80-90份，二氧化钛13-15份，纳米碳15-20份、氮化钛0.5-3份、镍0.5-3份。
2.根据权利要求1所述聚酰亚胺轴承保持器材料，其特征在于：聚酰亚胺85份，二氧化钛14份，纳米碳18份、氮化钛2份、镍1份。
3.一种制作权利要求1-3的聚酰亚胺轴承保持器材料的方法，其特征在于：将聚酰亚胺、二氧化钛、纳米碳、氮化钛、镍混合加入配料搅拌机中搅拌得到混合物；将所述混合物进行模型热固，即可得到轴承保持器。
4.根据权利要求3所述方法，其特征在于：热固的温度为10-500oC，热固时逐步温升，当温升到500oC，逐步降温，直至保持器降到室温。
5.根据权利要求3所述方法，其特征在于：热固的温度时间为0.1-5小时。
CN201710672607.8A 2017-08-08 2017-08-08 一种聚酰亚胺轴承保持器材料及制造方法 Pending CN107418205A (zh)