CN107414018A - 一种可膨胀石墨醇基铸造涂料 - Google Patents
一种可膨胀石墨醇基铸造涂料 Download PDFInfo
- Publication number
- CN107414018A CN107414018A CN201710742974.0A CN201710742974A CN107414018A CN 107414018 A CN107414018 A CN 107414018A CN 201710742974 A CN201710742974 A CN 201710742974A CN 107414018 A CN107414018 A CN 107414018A
- Authority
- CN
- China
- Prior art keywords
- expansible graphite
- alcohol
- base foundry
- coating
- foundry coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
一种可膨胀石墨醇基铸造涂料,按重量份计的以下物质：镁砂粉11‑20、二氧化钛2‑3、十二烷基硫酸钠4‑7、可膨胀石墨30‑45、氢氧化铝2‑4、十六烷基三甲基氯化铵0.3‑0.5、荔枝叶10‑13、亚麻油1‑3、硬脂酰胺3‑5、六亚甲基四胺3‑6、乙醇12‑23；本发明成本低、节能环保，通过优化生产工艺流程和配方，制得的涂料具有耐高温、强度高、透气性佳等优点。
Description
技术领域
本发明涉及铸造涂料领域，具体涉及一种可膨胀石墨醇基铸造涂料。
背景技术
铸造涂料是指用来涂敷在型腔或砂芯表面，以改变其表面耐火度、化学稳定性、抗金属冲刷性、抗粘砂性等性能的铸造辅助材料，它是由多种性质不同的材料组成的分散系，其组成主要包括耐火材料、悬浮剂、载体、粘结剂及特殊添加剂等组成。作用于铸件时要求涂料有良好的工艺性能、工作性能、质量稳定性以及施涂重现性，一方面可以起到隔热，均衡温度，免除金属液的冲击腐蚀性的目的，另一方面可以防止铸件产品因局部冷却过快而造成的开裂、砂眼、白口铁形成等缺陷。铸造涂料种类繁多，大体可以分为两类：水基涂料和醇基涂料。其中醇基涂料在涂覆后经点燃既可固化，不需烘干，能缩短生产周期，简化工艺，减少烘干设备投资，是被铸造界广为使用的一种快干涂料，已广泛应用于钢、铁、有色铸件的生产中。
发明内容
本发明解决其技术问题所采用的技术方案是：一种可膨胀石墨醇基铸造涂料，其特征是，它由下列重量份的原料制成：镁砂粉11-20、二氧化钛2-3、十二烷基硫酸钠4-7、可膨胀石墨30-45、氢氧化铝2-4、十六烷基三甲基氯化铵0.3-0.5、荔枝叶10-13、亚麻油1-3、硬脂酰胺3-5、六亚甲基四胺3-6、乙醇12-23。
本发明的有益效果是：本发明成本低、节能环保，通过优化生产工艺流程和配方，制得的涂料具有耐高温、强度高、透气性佳等优点。
具体实施方式
具体实施例：一种可膨胀石墨醇基铸造涂料，其特征是，它由下列重量份的原料制成：镁砂粉11-20、二氧化钛2-3、十二烷基硫酸钠4-7、可膨胀石墨30-45、氢氧化铝2-4、十六烷基三甲基氯化铵0.3-0.5、荔枝叶10-13、亚麻油1-3、硬脂酰胺3-5、六亚甲基四胺3-6、乙醇12-23。
本发明的有益效果是：本发明成本低、节能环保，通过优化生产工艺流程和配方，制得的涂料具有耐高温、强度高、透气性佳等优点。
显然，上述实施例仅仅是为清楚地说明所作的举例，而并非对实施方式的限定。对于所属领域的普通技术人员来说，在上述说明的基础上还可以做出其它不同形式的变化或变动。这里无需也无法对所有的实施方式予以穷举。而由此所引伸出的显而易见的变化或变动仍处于本发明创造的保护范围之中。
Claims (1)
1.一种可膨胀石墨醇基铸造涂料，其特征是，它由下列重量份的原料制成：镁砂粉11-20、二氧化钛2-3、十二烷基硫酸钠4-7、可膨胀石墨30-45、氢氧化铝2-4、十六烷基三甲基氯化铵0.3-0.5、荔枝叶10-13、亚麻油1-3、硬脂酰胺3-5、六亚甲基四胺3-6、乙醇12-23。