CN107399130A - A kind of automobile using cabin decorative panel - Google Patents
A kind of automobile using cabin decorative panel Download PDFInfo
- Publication number
- CN107399130A CN107399130A CN201710594097.7A CN201710594097A CN107399130A CN 107399130 A CN107399130 A CN 107399130A CN 201710594097 A CN201710594097 A CN 201710594097A CN 107399130 A CN107399130 A CN 107399130A
- Authority
- CN
- China
- Prior art keywords
- layer
- weight
- parts
- resin
- nano
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of automobile using cabin decorative panel, including at least four-layer structure, wherein disinfection filtering purifying layer (2) is by polypropylene (PP) resin, polyethylene (PE) resin and inorganic nano bactericidal purifying solution is processed is made, the decorating material board can be used in the decoration material in automobile cabin, can be from improving air in purifying vehicle all the time, play a part of sterilization simultaneously, belong to nontoxic, it is colourless, it is tasteless, it is non-stimulated, it is corrosion-free, free of contamination green product, with except formaldehyde, antibiotic and sterilizing effect is good, stability is good, cost price is low.
Description
Technical field
The present invention relates to a kind of automobile using cabin decorative panel with air-cleaning function, belong to automobile green science and technology technology
Field, there is purification air and energy-saving environmental-protection function.
Background technology
In today's society, in-vehicle air pollution increasingly attracts people's attention, and it is normal to treat in-vehicle air pollution problem
Rule treatment effect is also not so good as people's will.Although various air pollutions can be adsorbed, decompose or converted to current Household Air Purifier
Thing, air cleanliness is effectively improved, but its application is broadly divided into family expenses, commercialization, industry, building;Vehicle air purifier
Because the installation inconvenience of its volume does not see more excellent market prospects.Although traditional vehicle air purifier is blown using air draught
Wind mode gathers gas filtration, but natural dissipation release is mixed most of gas in the air of pollution again, so circulation
Collection, filtering and release, in addition to the energy consumption for increasing machine and abrasion, what people were absorbed to is only reduction of pollution level
Air, even if prolonged purification of air again, it is also not possible to enjoy pure air.For those with high-pressure electrostatic absorption
Air purifier, due to being limited by high voltage power supply, it is impossible to use on automobile.
The pernicious gases such as formaldehyde are filled with new car or newly-decorated room simultaneously, because formaldehyde is colourless, had strongly
Smell, the irritative gas for having very big toxic action to human body, every a large amount of places for using adhesive, always have formaldehyde and release
Put.Existing automobile removes the method that formaldehyde products are a lot, either utilize activated carbon to carry out physical absorption, or liquid on the market
Dispel formaldehyde agent, the formaldehyde in the air that not only can not really degrade, the secondary of interior can be also caused because of the toxic side effect of chemicals
Pollution.The cabin decorative panel of automobile is an indispensable part in automotive trim, and it is located at the inside of car hold, primarily served
The decoration function of blank vehicle body is blocked, its shortcoming is exactly that function is single.
Therefore, at present, by using purifier come in-car air is purified can not meet it is current
Demand, a kind of new substitute products are needed badly to solve the problem.
The content of the invention
In view of this, it is an object of the invention to provide a kind of tool that can be filled a hole in the market, overcome existing procucts deficiency
There is the automobile using cabin decorative panel of air-cleaning function.
The present invention is as follows using technical scheme:
A kind of automobile using cabin decorative panel with air-cleaning function, including at least four-layer structure, respectively fire-retardant face
The bed of material (1), disinfection filtering purifying layer (2), hot melt adhesive film (3) and nonwoven layer (4), wherein filtration, purification layer (2) are positioned at fire-retardant
Between precoat (1) and hot melt adhesive film (3), nonwoven layer (4) is used as substrate, positioned at the bottom of hot melt adhesive film (3).
The disinfection filtering purifying layer (2) is sterilized net by polypropylene (PP) resin, polyethylene (PE) resin and inorganic nano
Change that solution is processed is made, its specific method is by parts by weight:50% polypropylene (PP), 50% polyethylene (PE) resin are mixed
Close, the inorganic nano bactericidal purifying solution for the 1.5%-3.0% for accounting for above-mentioned hybrid resin weight is poured into jointly with hybrid resin
In mixer, set temperature in blender jar and stir 15-20 minutes as 35-40 degrees Celsius, with 360-400 revs/min of speed,
Low temperature drying is so as to independent obtained bactericidal purifying masterbatch resin after taking-up;Above-mentioned bactericidal purifying masterbatch resin addition electret is melted
Spray (ECMB) equipment, through being produced on the non-woven meltblown lines of TANDEC, be produced into non-woven fabric fiber body, make 3-10mm
Disinfection filtering purifying layer 2 is made in thickness non-inductive windings filter core, and the thickness of disinfection filtering purifying layer 2 is 3-10mm.
Described inorganic nano bactericidal purifying solution uses following preparation method:It is by 33-35% parts by weight, concentration
38000ppm, the average grain diameter≤10nm Nano Silver aqueous solution with self-cleaning function, the N doping activity of 57-59% parts by weight
Nano-titanium dioxide powder, its purity >=99.5%, average grain diameter≤5nm, energy activated wavelength≤800nm, 2.5-4.5% weight
Measure the AGS-WB purification additives of part and nitrogenous active carbon nanoparticles, the particle diameter≤15nm of 3.5-5.5% parts by weight are stirred
It is mixed.
The decorating material board can be used in the decoration material in automobile cabin, can be improved from all the time in purifying vehicle
Air, while play a part of sterilization, belong to nontoxic, colourless, tasteless and nonirritant, corrosion-free, free of contamination green production
Product, have except formaldehyde, antibiotic and sterilizing effect is good, stability is good, cost price is low.
Brief description of the drawings
Fig. 1 is the automobile using cabin decorative panel embodiment 1 of the present invention;
Fig. 2 is the automobile using cabin decorative panel embodiment 2 of the present invention.
Reference:1- inflaming retarding fabric layers, 2- disinfection filtering purifying layers, 3- hot melt adhesive films, 4- nonwoven layers, 5- breathe freely
Waterproof layer.
Embodiment
Below in conjunction with the accompanying drawing in the embodiment of the present invention, the technical scheme in the embodiment of the present invention is carried out clear, complete
Site preparation describes, it is clear that described embodiment is only part of the embodiment of the present invention, rather than whole embodiments.It is based on
Embodiment in the present invention, those of ordinary skill in the art are obtained all other under the premise of creative work is not made
Embodiment, belong to the scope of protection of the invention.
It is described in detail below by way of specific embodiment and with reference to accompanying drawing to the production method in the present invention and device,
But these embodiments are only the purpose illustrated, it is no intended to carry out any restriction to the scope of the present invention.
Embodiment 1:
Referring to Fig. 1, Fig. 1 is the structural representation of the automobile using cabin decorative panel of the present invention.It includes at least four-layer structure,
Including inflaming retarding fabric layer 1, disinfection filtering purifying layer 2, hot melt adhesive film 3 and nonwoven layer 4, wherein filtration, purification layer 2 is positioned at fire-retardant
Between precoat 1 and hot melt adhesive film 3, nonwoven layer 4 is used as substrate, positioned at the bottom of hot melt adhesive film 3.The ornament materials is rolling
Material, used with facilitating storage to transport and processing.
The core of the present invention is the manufacturing of disinfection filtering purifying layer 2, and the disinfection filtering purifying layer 2 is by polypropylene
(PP) resin, polyethylene (PE) resin and inorganic nano bactericidal purifying solution is processed is made, its specific method is by parts by weight:
50% polypropylene (PP), 50% polyethylene (PE) resin are mixed, and will account for the 1.5%-3.0%'s of above-mentioned hybrid resin weight
Inorganic nano bactericidal purifying solution is poured into mixer jointly with hybrid resin, and it is Celsius as 35-40 to set temperature in blender jar
Spend, stir 15-20 minutes with 360-400 revs/min of speed, low temperature drying is so as to independent obtained bactericidal purifying tree after taking-up
Fat master batch;Above-mentioned bactericidal purifying masterbatch resin is added into electretization melt-blown (ECMB) equipment, through being given birth in the non-woven melt-blowns of TANDEC
Produced in producing line, be produced into non-woven fabric fiber body, made 3-10mm thickness non-inductive windings filter cores and disinfection filtering purifying layer is made
2, the thickness of disinfection filtering purifying layer 2 is 3-10mm.
Described inorganic nano bactericidal purifying solution uses following preparation method:It is by 33-35% parts by weight, concentration
38000ppm, the average grain diameter≤10nm Nano Silver aqueous solution with self-cleaning function, the N doping activity of 57-59% parts by weight
Nano-titanium dioxide powder, its purity >=99.5%, average grain diameter≤5nm, energy activated wavelength≤800nm N doping activity
Nano-titanium dioxide powder, 2.5-4.5% parts by weight AGS-WB (nanometre Ag antibacterial aqueous coating) purification additives and
Nitrogenous active carbon nanoparticles, the particle diameter≤15nm of 3.5-5.5% parts by weight are stirred and are mixed.Wherein using particle diameter 10nm,
Solid content (Ag) 30000ppm, effective antimicrobial component 90ppm, abrasion resistance > 10000 times nano-silver water solution.Wherein nitrogen is mixed
Miscellaneous nano-titanium dioxide powder is anatase titanium dioxide, and its nitrogen doped changes the molecular structure of titanium dioxide, improves titanium dioxide
The performance of titanium, make titanium dioxide excites wave band, and visible region is expanded to from ultraviolet region, as long as under daylight and light being light wave
Less than 800nm, without ultraviolet light, can just there is excitation to it, and performance greatly strengthens.Car can quickly and efficiently be decomposed
The gas harmful to human body and environment such as interior formaldehyde, benzene, ammonia, organic volatile, improves antibacterial deodorizing ability.
Described inorganic nano bactericidal purifying solution can be also made of following preparation method:By by the dense of 33% parts by weight
Spend for 12000ppm, average grain diameter≤10nm nano-silver water solution, 58% parts by weight N doping active nano titanic oxide
The AGS-WB purifications of powder (purity >=99.5%, average grain diameter≤5nm, energy activated wavelength≤800nm), 6.4% parts by weight
Its main content of additive, 1% parts by weight reaches 59.5% active nano palladium oxide powder, the NRT- of 1.2% parts by weight
P20000 active nanos anion powder and 0.4% parts by weight content 99.9%, average grain diameter 14nm nano active graphene
Powder be thoroughly mixed being made.Experiment proves that disinfection filtering purifying layer 2 made of the method is with more beneficial
Filter sterilization effect.
Embodiment 2:
Referring to Fig. 2, Fig. 2 is the structural representation of the automobile using cabin decorative panel of the present invention.It includes at least five-layer structure,
Including inflaming retarding fabric layer 1, disinfection filtering purifying layer 2, hot melt adhesive film 3 and nonwoven layer 4, in addition to breathable water repellant layer 5, fire-retardant face
The bed of material 1 and breathable water repellant layer 5 abut combination to play a part of fire-retardant and waterproof, and wherein filtration, purification layer 2 is located at air permeable waterproof
Between layer 5 and hot melt adhesive film 3, nonwoven layer 4 is used as substrate, positioned at the bottom of hot melt adhesive film 3.The ornament materials is rolling simultaneously
Material, used with facilitating storage to transport and processing.
It is same as Example 1, the disinfection filtering purifying layer 2 by polypropylene (PP) resin, polyethylene (PE) resin and
Inorganic nano bactericidal purifying solution is processed to be made, and its specific method is by parts by weight:50% polypropylene (PP), 50% poly- second
Alkene (PE) resin is mixed, will account for above-mentioned hybrid resin weight 1.5%-3.0% inorganic nano bactericidal purifying solution with
Hybrid resin is poured into mixer jointly, set in blender jar temperature as 35-40 degrees Celsius, with 360-400 revs/min
Speed stirs 15-20 minutes, and low temperature drying is so as to independent obtained bactericidal purifying masterbatch resin after taking-up;By above-mentioned bactericidal purifying tree
Fat master batch adds electretization melt-blown (ECMB) equipment, through being produced on the non-woven meltblown lines of TANDEC, is produced into on-woven
Fibres body, make 3-10mm thickness non-inductive windings filter cores and disinfection filtering purifying layer 2, the thickness of disinfection filtering purifying layer 2 is made
For 3-10mm.Described inorganic nano bactericidal purifying solution can be also made of following preparation method:By by 33% parts by weight
Concentration is 12000ppm, average grain diameter≤10nm nano-silver water solution, the N doping active nano titanium dioxide of 58% parts by weight
Titanium valve body (purity >=99.5%, average grain diameter≤5nm, energy activated wavelength≤800nm), the AGS-WB of 6.4% parts by weight are net
Change additive, 1% parts by weight its main contents reach 59.5% active nano palladium oxide powder, the NRT- of 1.2% parts by weight
P20000 active nanos anion powder and 0.4% parts by weight content 99.9%, average grain diameter 14nm nano active graphene
Powder be thoroughly mixed being made.
Although giving detailed description and explanation to the embodiment of the present invention above, it should be noted that
We can carry out various equivalent changes and modification to above-mentioned embodiment according to the conception of the present invention, and its caused function is made
, all should be within protection scope of the present invention during with the spirit still covered without departing from specification and accompanying drawing.It is described above, be only
Presently preferred embodiments of the present invention, it is not intended to limit the invention, every technical spirit according to the present invention is to above example institute
Any trickle amendment, equivalent substitution and the improvement made, should be included within the protection domain of technical solution of the present invention.
Claims (1)
1. a kind of automobile using cabin decorative panel, there is five-layer structure, including inflaming retarding fabric layer (1), disinfection filtering purifying layer (2),
Hot melt adhesive film (3) and nonwoven layer (4), in addition to breathable water repellant layer (5), inflaming retarding fabric layer (1) and breathable water repellant layer (5) abut
Combination to play a part of fire-retardant and waterproof, wherein filtration, purification layer (2) be located at breathable water repellant layer (5) and hot melt adhesive film (3) it
Between, nonwoven layer (4) is used as substrate, positioned at the bottom of hot melt adhesive film (3), it is characterised in that
The disinfection filtering purifying layer (2) is molten by polypropylene (PP) resin, polyethylene (PE) resin and inorganic nano bactericidal purifying
Liquid is processed to be made, and its specific method is by parts by weight:50% polypropylene (PP), 50% polyethylene (PE) resin are mixed,
The inorganic nano bactericidal purifying solution for the 1.5%-3.0% for accounting for above-mentioned hybrid resin weight and hybrid resin are poured into stirring jointly
In machine, set temperature in blender jar and stir 15-20 minutes as 35-40 degrees Celsius, with 360-400 revs/min of speed, take out
Low temperature drying is so as to independent obtained bactericidal purifying masterbatch resin afterwards;Above-mentioned bactericidal purifying masterbatch resin is added into electretization melt-blown to set
It is standby, through being produced on non-woven meltblown line, be produced into non-woven fabric fiber body, make 3-10mm thickness non-inductive windings filter core i.e.
Disinfection filtering purifying layer (2) is made, the thickness of disinfection filtering purifying layer (2) is 3-10mm;
Described inorganic nano bactericidal purifying solution uses following preparation method:It is by the concentration by 33% parts by weight
12000ppm, average grain diameter≤10nm nano-silver water solution, the N doping active nano titanic oxide powder of 58% parts by weight
The AGS-WB purification additions of (purity >=99.5%, average grain diameter≤5nm, energy activated wavelength≤800nm), 6.4% parts by weight
Agent, 1% parts by weight its main contents reach 59.5% active nano palladium oxide powder, the NRT-P20000 of 1.2% parts by weight lives
Property nano-negative ion powder and 0.4% parts by weight content 99.9%, average grain diameter 14nm nano active graphene powder carry out
It is thoroughly mixed and is made.