CN102416187A - Photo-catalyst air purifying liquid and preparation method thereof - Google Patents
Photo-catalyst air purifying liquid and preparation method thereof Download PDFInfo
- Publication number
- CN102416187A CN102416187A CN2011103248518A CN201110324851A CN102416187A CN 102416187 A CN102416187 A CN 102416187A CN 2011103248518 A CN2011103248518 A CN 2011103248518A CN 201110324851 A CN201110324851 A CN 201110324851A CN 102416187 A CN102416187 A CN 102416187A
- Authority
- CN
- China
- Prior art keywords
- parts
- air purifying
- purifying liquid
- nano
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a photo-catalyst air purifying liquid and a preparation method thereof, belonging to technical field of preparation of cleaning agents. The photo-catalyst air purifying liquid is prepared by mixing the following raw materials in parts by weight: 4-6 parts of nano-titanium dioxide, 1-3 parts of nano-silicon dioxide, 3-10 parts of melamine or sodium sulfate, 15-25 parts of polyethylene glycol and 50-70 parts of water, wherein the particle diameter of the nano-titanium dioxide is 5-10 nanometers; the water refers to distilled water; and the photo-catalyst air purifying liquid can be prepared by uniformly mixing the raw materials according to a certain proportion, emulsifying and dispersing. Compared with the prior art, the photo-catalyst air purifying liquid and the preparation method thereof have the advantages of reasonable mixing of raw materials, low preparation cost, convenience for using, good cleaning effect and the like; the air cleaning agent can be sprayed in rooms or coated on furniture, can naturally evaporate without leaving any trace; and the nano-silicon dioxide can play a role in sterilizing, resisting bacteria and decomposing harmful gases under the exciting action of weak ultraviolet irradiation.
Description
Technical field
The present invention relates to a kind of cleaning agent, specifically a kind ofly can be sprayed in the room or spread upon on the furniture, room air or furniture are carried out photocatalyst air purifying liquid of antibacterial, sterilization, cleaning and preparation method thereof.
Background technology
Research shows: nano titanium oxide, particle diameter have very strong adsorptivity between 5-25 nanometers, and it can be adsorbed onto its surface with harmful gass such as airborne benzene, formaldehyde, under the irradiation of uviol lamp, with its decomposition.
Summary of the invention
Technical assignment of the present invention is the deficiency to prior art; Provide a kind of and can be sprayed in the room or the volatilization of giving free rein to of the furniture surface in room, only need faint ultraviolet radiation just can excitation nano titanium dioxide generation cleaning, photocatalyst air purifying liquid of antibacterial, resolving harmful gas effect and preparation method thereof.
The technical solution adopted for the present invention to solve the technical problems is:
Photocatalyst air purifying liquid is that the raw materials mix by following parts by weight forms:
Nano titanium oxide: 4-6 part,
Nano silicon: 1-3 part,
Tripolycyanamide or sodium sulfate: 3-10 parts,
Polyethylene Glycol: 15-25 parts,
Water: 50-70 parts.
Also be added with silicon third in the above-mentioned mixed material: 2-4 part.
Also be added with acetic acid in the above-mentioned mixed material: 5-15 part.
The particle diameter of above-mentioned nano titanium oxide is between 5-10 nanometers.
Said water is distilled water, and the temperature of water is between 50-90 ℃.
The manufacture method of said photocatalyst air purifying liquid is that above-mentioned raw materials is mixed in proportion, and promptly can be made into said photocatalyst air purifying liquid through the emulsifying dispersion treatment.
Photocatalyst air purifying liquid of the present invention and preparation method thereof compared with prior art, the beneficial effect that is produced is:
1) the present invention has that material combination is reasonable, preparation cost is low; Characteristics such as easy to use, cleaning effect is good; Owing to adopted nano titanium oxide to make raw material, therefore, only need faint ultraviolet radiation just can excitation nano titanium dioxide generation antibacterial, the effect of resolving harmful gas.
2) the present invention can be sprayed in the room or spreads upon above the furniture, can volatilize naturally and leave no trace, only need faint ultraviolet radiation just can excitation nano titanium dioxide generation antibacterial, the effect of antibiotic, resolving harmful gas.And to the environment non-secondary pollution, to human non-toxic, have no side effect.
3) sterilizing rate of the present invention reaches more than 95%, and the harmful gas removing rate reaches more than 85%.
The specific embodiment
Explanation at length below below in conjunction with embodiment photocatalyst air purifying liquid of the present invention and preparation method thereof being done.
Embodiment 1:
Titanium dioxide with 5-10 nanometers: 5 parts, nano silicon: 2 parts, tripolycyanamide: 3 parts, 20 parts of Polyethylene Glycol, water: 70 parts of mix homogeneously, promptly can be made into said air cleaning liquid through the emulsifying dispersion treatment, can be used as eliminating smell agent and use.
Embodiment 2:
Titanium dioxide with 5-10 nanometers: 4 parts, nano silicon: 3 parts, sodium sulfate: 10 parts, 15 parts of Polyethylene Glycol, water: 68 parts of mix homogeneously, promptly can be made into said air cleaning liquid through the emulsifying dispersion treatment, can be used as eliminating smell agent and use.
Embodiment 3:
Titanium dioxide with 5-10 nanometers: 6 parts, nano silicon: 1 part, tripolycyanamide: 10 parts, 25 parts of Polyethylene Glycol, water: 58 parts of mix homogeneously, promptly can be made into said air cleaning liquid through the emulsifying dispersion treatment, can be used as eliminating smell agent and use.
Embodiment 4:
Titanium dioxide with 5-10 nanometers: 5 parts, nano silicon: 2 parts, sodium sulfate: 3 parts, Polyethylene Glycol: 25 parts, 65 parts of mix homogeneously of water, promptly can be made into said air cleaning liquid through the emulsifying dispersion treatment, can be used as eliminating smell agent and use.
Embodiment 5:
With the third 3 parts of mixing of 2 parts of 5 parts of titanium dioxide, the nano silicons of 5-10 nanometers, silicon as solute; 55 parts of mixing of water of 10 parts of 10 parts of tripolycyanamide, 15 parts of Polyethylene Glycol, acetic acid and 70 ℃ are as solvent, even with above-mentioned solute and solvent, promptly can be made into said air cleaning liquid through the emulsifying dispersion treatment, can be used as air purifying preparation and use.
Embodiment 6:
With the third 2 parts of mixing of 3 parts of 4 parts of titanium dioxide, the nano silicons of 5-10 nanometers, silicon as solute; 53 parts of mixing of water of 15 parts of 3 parts of tripolycyanamide, 20 parts of Polyethylene Glycol, acetic acid and 50 ℃ are as solvent, even with above-mentioned solute and solvent, promptly can be made into said air cleaning liquid through the emulsifying dispersion treatment, can be used as air purifying preparation and use.
Embodiment 7:
With the third 4 parts of mixing of 1 part of 6 parts of titanium dioxide, the nano silicon of 5-10 nanometers, silicon as solute; 54 parts of mixing of water of 25 parts of 10 parts of tripolycyanamide, Polyethylene Glycol and 90 ℃ are as solvent, even with above-mentioned solute and solvent, promptly can be made into said air cleaning liquid through the emulsifying dispersion treatment, can be used as the deacration cleanser and use.
Embodiment 8:
With the third 3 parts of mixing of 2 parts of 4 parts of titanium dioxide, the nano silicons of 5-10 nanometers, silicon as solute; With 5 parts of acetic acid, Polyethylene Glycol: 66 parts of mixing of water of 20 parts and 70 ℃ are as solvent, and above-mentioned solute and solvent is even, promptly can be made into said air cleaning liquid through the emulsifying dispersion treatment, can be used as the deacration cleanser and use.
Claims (8)
1. photocatalyst air purifying liquid is characterized in that, is that the raw materials mix by following parts by weight forms:
Nano titanium oxide: 4-6 part,
Nano silicon: 1-3 part,
Tripolycyanamide or sodium sulfate: 3-10 parts,
Polyethylene Glycol: 15-25 parts,
Water: 50-70 parts.
2. photocatalyst air purifying liquid according to claim 1 is characterized in that, also is added with silicon third in the mixed material: 2-4 part.
3. photocatalyst air purifying liquid according to claim 1 is characterized in that, also is added with acetic acid in the mixed material: 5-15 part.
4. photocatalyst air purifying liquid according to claim 1 is characterized in that the particle diameter of nano titanium oxide is between 5-10 nanometers.
5. photocatalyst air purifying liquid according to claim 1 is characterized in that, said water is distilled water.
6. photocatalyst air purifying liquid according to claim 1 is characterized in that the temperature of said water is between 50-90 ℃.
7. photocatalyst air purifying liquid according to claim 6 is characterized in that the temperature of said water is between 60-80 ℃.
8. the manufacture method of photocatalyst air purifying liquid according to claim 1 is characterized in that, is that above-mentioned raw materials is mixed in proportion, and promptly can be made into said photocatalyst air purifying liquid through the emulsifying dispersion treatment.