CN107399130B - A kind of automobile cabin decorative panel - Google Patents

A kind of automobile cabin decorative panel Download PDF

Info

Publication number
CN107399130B
CN107399130B CN201710594097.7A CN201710594097A CN107399130B CN 107399130 B CN107399130 B CN 107399130B CN 201710594097 A CN201710594097 A CN 201710594097A CN 107399130 B CN107399130 B CN 107399130B
Authority
CN
China
Prior art keywords
layer
weight
parts
resin
nano
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201710594097.7A
Other languages
Chinese (zh)
Other versions
CN107399130A (en
Inventor
唐棣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
For our testing and Certification Co., Zhejiang
Original Assignee
For Our Testing And Certification Co Zhejiang
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by For Our Testing And Certification Co Zhejiang filed Critical For Our Testing And Certification Co Zhejiang
Priority to CN201710594097.7A priority Critical patent/CN107399130B/en
Priority to CN201510586632.5A priority patent/CN105034466B/en
Publication of CN107399130A publication Critical patent/CN107399130A/en
Application granted granted Critical
Publication of CN107399130B publication Critical patent/CN107399130B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a kind of automobile cabin decorative panels, including at least four-layer structure, wherein disinfection filtering purifying layer (2) is by polypropylene (PP) resin, polyethylene (PE) resin and inorganic nano bactericidal purifying solution is processed is made, the decorating material board can be used in the decoration material in automobile cabin, it can be from improving purification in-vehicle air all the time, play the role of sterilization simultaneously, belong to nontoxic, it is colourless, it is tasteless, it is non-stimulated, it is corrosion-free, free of contamination green product, with except formaldehyde, antibiotic and sterilizing effect is good, stability is good, cost price is low.

Description

A kind of automobile cabin decorative panel
Technical field
The present invention relates to a kind of automobile cabin decorative panel with air-cleaning function, belongs to automobile green science and technology technology Field has purification air and energy-saving environmental-protection function.
Background technique
In today's society, in-vehicle air pollution increasingly attracts people's attention, and it is normal to treat in-vehicle air pollution problem Rule treatment effect is also not so good as people's will.Although various air pollutions can be adsorbed, decompose or be converted to current Household Air Purifier Object effectively improves air cleanliness, but its application range is broadly divided into household, commercialization, industry, building;Vehicle air purifier Because more preferably market prospects are not seen in the installation inconvenience of its volume.Although traditional vehicle air purifier is blown using air draught Wind mode acquires gas filtration, but natural dissipation release is mixed most of gas in the air of pollution again, is so recycled Acquisition, filtering and release, other than the energy consumption and abrasion that increase machine, what people were absorbed into is only reduction of pollution level Air, even if prolonged air cleaning again, it is also not possible to enjoy pure air.For those with high-pressure electrostatic absorption Air purifier is not utilized on automobile due to being limited by high voltage power supply.
Be filled with the pernicious gases such as formaldehyde in new car or newly-decorated room simultaneously, due to formaldehyde be it is colourless, have it is strong Smell, the irritative gas for having very big toxic action to human body, all a large amount of places using adhesive, always have formaldehyde and release It puts.On the market existing automobile except formaldehyde products it is very much, either using active carbon progress physical absorption method or liquid It dispels formaldehyde agent, the formaldehyde in the air that not only can not really degrade can also cause indoor secondary because of the toxic side effect of chemicals Pollution.The cabin decorative panel of automobile is indispensable a part in automobile interior decoration, is located at the inside of car hold, primarily serves The decoration function of blank vehicle body is blocked, disadvantage is exactly to have a single function.
Therefore, at present, by using purification device come to in-vehicle air carry out purification be no longer satisfied it is current Demand needs the new substitute products of one kind to solve the problems, such as this.
Summary of the invention
In view of this, can fill a hole in the market the purpose of the present invention is to provide a kind of, overcome the insufficient tool of existing procucts There is the automobile cabin decorative panel of air-cleaning function.
The present invention is as follows using technical solution:
A kind of automobile cabin decorative panel with air-cleaning function, including at least four-layer structure, respectively fire-retardant face The bed of material (1), disinfection filtering purifying layer (2), hot melt adhesive film (3) and nonwoven layer (4), wherein filtration, purification layer (2) is located at fire-retardant Between precoat (1) and hot melt adhesive film (3), nonwoven layer (4) is used as substrate, is located at the bottom of hot melt adhesive film (3).
The disinfection filtering purifying layer (2) is sterilized net by polypropylene (PP) resin, polyethylene (PE) resin and inorganic nano Change that solution is processed is made, specific method is by parts by weight: 50% polypropylene (PP), 50% polyethylene (PE) resin mix It closes, the inorganic nano bactericidal purifying solution for accounting for the 1.5%-3.0% of above-mentioned hybrid resin weight is poured into jointly with hybrid resin In blender, sets temperature in blender jar and is stirred 15-20 minutes as 35-40 degrees Celsius, with 360-400 revs/min of speed, Low temperature drying is after taking-up to independent obtained bactericidal purifying masterbatch resin;Above-mentioned bactericidal purifying masterbatch resin addition electret is melted It sprays (ECMB) equipment, through producing on the non-woven meltblown line of TANDEC, is produced into non-woven fabric fiber body, is made into 3-10mm Disinfection filtering purifying layer 2 is made in thickness non-inductive windings filter core, disinfection filtering purifying layer 2 with a thickness of 3-10mm.
The inorganic nano bactericidal purifying solution uses following preparation method: by 33-35% parts by weight, concentration for The N doping activity of the nano silver aqueous solution of 38000ppm, average grain diameter≤10nm with self-cleaning function, 57-59% parts by weight Nano-titanium dioxide powder, purity >=99.5%, average grain diameter≤5nm, energy activated wavelength≤800nm, 2.5-4.5% weight Nitrogenous active carbon nanoparticles, the partial size≤15nm of the AGS-WB purification additive and 3.5-5.5% parts by weight of measuring part are stirred It is mixed.
The decorating material board can be used in the decoration material in automobile cabin, can be improved in purifying vehicle from all the time Air, while playing the role of sterilization, belong to nontoxic, colourless, tasteless and nonirritant, corrosion-free, free of contamination environmentally protective production Product have except formaldehyde, antibiotic and sterilizing effect is good, stability is good, cost price is low.
Detailed description of the invention
Fig. 1 is automobile cabin decorative panel embodiment 1 of the invention;
Fig. 2 is automobile cabin decorative panel embodiment 2 of the invention.
Appended drawing reference: 1- inflaming retarding fabric layer, 2- disinfection filtering purifying layer, 3- hot melt adhesive film, 4- nonwoven layer, 5- are ventilative Waterproof layer.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts all other Embodiment shall fall within the protection scope of the present invention.
Below by way of specific embodiment and in conjunction with attached drawing in the present invention production method and device be described in detail, But these embodiments are only the purpose illustrated, it is no intended to carry out any restriction to the scope of the present invention.
Embodiment 1:
It is the structural schematic diagram of automobile cabin decorative panel of the invention referring to Fig. 1, Fig. 1.It includes at least four-layer structure, Including inflaming retarding fabric layer 1, disinfection filtering purifying layer 2, hot melt adhesive film 3 and nonwoven layer 4, wherein filtration, purification layer 2 is located at fire-retardant Between precoat 1 and hot melt adhesive film 3, nonwoven layer 4 is used as substrate, positioned at the bottom of hot melt adhesive film 3.The ornament materials is rolling Material, to facilitate storage to transport and processing use.
Core of the invention is the manufacturing of disinfection filtering purifying layer 2, and the disinfection filtering purifying layer 2 is by polypropylene (PP) resin, polyethylene (PE) resin and inorganic nano bactericidal purifying solution is processed is made, specific method is by parts by weight: 50% polypropylene (PP), 50% polyethylene (PE) resin are mixed, and will account for the 1.5%-3.0%'s of above-mentioned hybrid resin weight Inorganic nano bactericidal purifying solution and hybrid resin pour into blender jointly, and it is Celsius as 35-40 to set temperature in blender jar Degree is stirred 15-20 minutes with 360-400 revs/min of speed, and low temperature drying is after taking-up to independent obtained bactericidal purifying tree Rouge master batch;Electretization melt-blown (ECMB) equipment is added, through giving birth in the non-woven melt-blown of TANDEC in above-mentioned bactericidal purifying masterbatch resin It is produced in producing line, is produced into non-woven fabric fiber body, be made into 3-10mm thickness non-inductive windings filter core and disinfection filtering purifying layer is made 2, disinfection filtering purifying layer 2 with a thickness of 3-10mm.
The inorganic nano bactericidal purifying solution uses following preparation method: by 33-35% parts by weight, concentration for The N doping activity of the nano silver aqueous solution of 38000ppm, average grain diameter≤10nm with self-cleaning function, 57-59% parts by weight Nano-titanium dioxide powder, purity >=99.5%, average grain diameter≤5nm, the N doping activity of energy activated wavelength≤800nm Nano-titanium dioxide powder, 2.5-4.5% parts by weight AGS-WB (nanometre Ag antibacterial aqueous coating) purification additive and Nitrogenous active carbon nanoparticles, the partial size≤15nm of 3.5-5.5% parts by weight are stirred and are mixed.Wherein using partial size 10nm, Solid content (Ag) 30000ppm, effective antimicrobial component 90ppm, abrasion resistance > 10000 times nano-silver water solutions.Wherein nitrogen is mixed Miscellaneous nano-titanium dioxide powder is anatase titanium dioxide, and nitrogen doped changes the molecular structure of titanium dioxide, improves titanium dioxide The performance of titanium makes the excitation wave band of titanium dioxide, expands to visible region from ultraviolet region, as long as under daylight and light being light wave Lower than 800nm, does not have to ultraviolet light, there can be excitation to it, and performance greatly enhances.Vehicle can quickly and efficiently be decomposed Interior formaldehyde, benzene, ammonia, organic volatile etc. improve antibacterial deodorizing ability to human body and the harmful gas of environment.
The inorganic nano bactericidal purifying solution also can be used to be made following preparation method: will be by the dense of 33% parts by weight Degree be 12000ppm, average grain diameter≤10nm nano-silver water solution, 58% parts by weight N doping active nano titanic oxide The AGS-WB purification of powder (purity >=99.5%, average grain diameter≤5nm, energy activated wavelength≤800nm), 6.4% parts by weight Its main content of additive, 1% parts by weight reaches 59.5% active nano palladium oxide powder, the NRT- of 1.2% parts by weight The nano active graphene of P20000 active nano anion powder and 0.4% parts by weight content 99.9%, average grain diameter 14nm Powder be thoroughly mixed being made.Experiment proves that disinfection filtering purifying layer 2 made of the method is with more beneficial Filter sterilization effect.
Embodiment 2:
Referring to fig. 2, Fig. 2 is the structural schematic diagram of automobile cabin decorative panel of the invention.It includes at least five-layer structure, It further include breathable water repellant layer 5, fire-retardant face including inflaming retarding fabric layer 1, disinfection filtering purifying layer 2, hot melt adhesive film 3 and nonwoven layer 4 The bed of material 1 and breathable water repellant layer 5 abut combination to play the role of fire-retardant and waterproof, and wherein filtration, purification layer 2 is located at air permeable waterproof Between layer 5 and hot melt adhesive film 3, nonwoven layer 4 is used as substrate, positioned at the bottom of hot melt adhesive film 3.The ornament materials is rolling simultaneously Material, to facilitate storage to transport and processing use.
It is same as Example 1, the disinfection filtering purifying layer 2 by polypropylene (PP) resin, polyethylene (PE) resin and Inorganic nano bactericidal purifying solution is processed to be made, and specific method is by parts by weight: 50% polypropylene (PP), 50% poly- second Alkene (PE) resin is mixed, will account for the inorganic nano bactericidal purifying solution of the 1.5%-3.0% of above-mentioned hybrid resin weight with Hybrid resin pours into blender jointly, set in blender jar temperature as 35-40 degrees Celsius, with 360-400 revs/min Speed stirs 15-20 minutes, and low temperature drying is after taking-up to independent obtained bactericidal purifying masterbatch resin;By above-mentioned bactericidal purifying tree Electretization melt-blown (ECMB) equipment is added, through producing on the non-woven meltblown line of TANDEC in rouge master batch, is produced into on-woven Fibres body is made into 3-10mm thickness non-inductive windings filter core and disinfection filtering purifying layer 2, the thickness of disinfection filtering purifying layer 2 is made For 3-10mm.The inorganic nano bactericidal purifying solution also can be used to be made following preparation method: will be by 33% parts by weight Concentration be 12000ppm, average grain diameter≤10nm nano-silver water solution, 58% parts by weight N doping active nano titanium dioxide Titanium valve body (purity >=99.5%, average grain diameter≤5nm, energy activated wavelength≤800nm), the AGS-WB of 6.4% parts by weight are net Change additive, 1% parts by weight its main contents reaches 59.5% active nano palladium oxide powder, the NRT- of 1.2% parts by weight The nano active graphene of P20000 active nano anion powder and 0.4% parts by weight content 99.9%, average grain diameter 14nm Powder be thoroughly mixed being made.
Although the detailed description and description of the specific embodiments of the present invention are given above, it should be noted that We can carry out various equivalent changes and modification to above embodiment according to the concept of the present invention, and generated function is made It, should all be within protection scope of the present invention when with the spirit still covered without departing from specification and attached drawing.The above, only Presently preferred embodiments of the present invention is not intended to limit the invention, according to the technical essence of the invention to above embodiments institute Any trickle amendment, equivalent replacement and the improvement made, all should be included in the scope of protection of the technical solution of the present invention.

Claims (1)

1. a kind of automobile cabin decorative panel, there is five-layer structure, including inflaming retarding fabric layer (1), disinfection filtering purifying layer (2), Hot melt adhesive film (3) and nonwoven layer (4), further include breathable water repellant layer (5), and inflaming retarding fabric layer (1) and breathable water repellant layer (5) abut Combination is to play the role of fire-retardant and waterproof, and wherein disinfection filtering purifying layer (2) is located at breathable water repellant layer (5) and hot melt adhesive film (3) between, nonwoven layer (4) is used as substrate, is located at the bottom of hot melt adhesive film (3), which is characterized in that
The disinfection filtering purifying layer (2) is molten by polypropylene (PP) resin, polyethylene (PE) resin and inorganic nano bactericidal purifying Liquid is processed to be made, and specific method is by parts by weight: 50% polypropylene (PP), 50% polyethylene (PE) resin mix, The inorganic nano bactericidal purifying solution for accounting for the 1.5%-3.0% of above-mentioned hybrid resin weight and hybrid resin are poured into stirring jointly In machine, sets temperature in blender jar and stirred 15-20 minutes as 35-40 degrees Celsius, with 360-400 revs/min of speed, taken out Low temperature drying is afterwards to independent obtained bactericidal purifying masterbatch resin;Electretization melt-blown is added in above-mentioned bactericidal purifying masterbatch resin to set It is standby, produced on non-woven meltblown line, be produced into non-woven fabric fiber body, be made into 3-10mm thickness non-inductive windings filter core i.e. Be made disinfection filtering purifying layer (2), disinfection filtering purifying layer (2) with a thickness of 3-10mm;
The inorganic nano bactericidal purifying solution uses following preparation method: by by the concentration of 33% parts by weight for 12000ppm, average grain diameter≤10nm nano-silver water solution, 58% parts by weight N doping active nano titanic oxide powder, The nanometre Ag antibacterial aqueous coating AGS-WB purification additives of 6.4% parts by weight, 1% parts by weight its main contents reach 59.5% Active nano palladium oxide powder, the NRT-P20000 active nano anion powder of 1.2% parts by weight and 0.4% parts by weight content 99.9%, the nano active graphene powder of average grain diameter 14nm be thoroughly mixed being made;Above-mentioned N doping activity is received Purity >=99.5%, average grain diameter≤5nm, the energy activated wavelength≤800nm of rice titanium dioxide powder.
CN201710594097.7A 2015-09-16 2015-09-16 A kind of automobile cabin decorative panel Active CN107399130B (en)