CN107384082A - A kind of diatom ooze aqueous latex paint - Google Patents
A kind of diatom ooze aqueous latex paint Download PDFInfo
- Publication number
- CN107384082A CN107384082A CN201710767164.0A CN201710767164A CN107384082A CN 107384082 A CN107384082 A CN 107384082A CN 201710767164 A CN201710767164 A CN 201710767164A CN 107384082 A CN107384082 A CN 107384082A
- Authority
- CN
- China
- Prior art keywords
- diatom ooze
- water
- latex paint
- aqueous latex
- hydroxyethyl cellulose
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of diatom ooze aqueous latex paint, including diatom ooze, isopropanol, aqueous acrylic emulsion, tetraethyl orthosilicate, hydroxyethyl cellulose, the coalescents of alcohol ester 12, formaldehyde absorbent, water, the mass fraction of each component to be：Diatom ooze 20 25, isopropanol 28 32, aqueous acrylic emulsion 200 300, tetraethyl orthosilicate 13 17, hydroxyethyl cellulose 5 10, the coalescents 27 of alcohol ester 12, formaldehyde absorbent 39, water 30 60.Diatom ooze aqueous latex paint of the present invention only needs the clear water of pure free from admixture to have impayable environment-friendly advantage as diluent, in addition, also having the functions such as superpower net taste, meet more preferable interior decoration demand.
Description
Technical field
The present invention relates to a kind of house ornamentation paint field, in particular it relates to a kind of diatom ooze aqueous latex paint.
Background technology
Research shows that coating is one of major pollutants of home room.With the formulation and consumption of relevant national standard
The raising of person's environmental consciousness, water paint are popularized comprehensively.But the coating that furniture surface uses, still with traditional oils
Property woodcare paint based on, virtually add the pollution of home room, and the water paint furniture of environmental protection is still " non-master in market
Stream ".The oil paint of generally existing mainly uses the banana oil for containing a large amount of poisonous and harmful substances, thinner as diluent,
The characteristics of impayable environment-friendly advantage is water paint maximum.It is water-based in pay attention to day by day coating safety and today of environmental protection index
Woodwork coating just because of its less harmful, low stain characteristic, is gradually received by market.
The content of the invention
For above shortcomings in the prior art, it is good that the technical problems to be solved by the invention are to provide a kind of effect
Diatom ooze aqueous latex paint.
The technical solution adopted for the present invention to solve the technical problems is：A kind of diatom ooze aqueous latex paint is provided, including
Diatom ooze, isopropanol, aqueous acrylic emulsion, tetraethyl orthosilicate, hydroxyethyl cellulose, the coalescents of alcohol ester 12, formaldehyde are inhaled
Agent, water are received, the mass fraction of each component is：Diatom ooze 20-25, isopropanol 28-32, aqueous acrylic emulsion 200-300, positive silicon
Acetoacetic ester 13-17, hydroxyethyl cellulose 5-10, the coalescents 2-7 of alcohol ester 12, formaldehyde absorbent 3-9, water 30-60.
Preferably, the mass fraction of the diatom ooze aqueous latex paint each component is：Diatom ooze 20, isopropanol 30, water
Property acrylic emulsion 250, tetraethyl orthosilicate 16, hydroxyethyl cellulose 8, the coalescents 3 of alcohol ester 12, formaldehyde absorbent 8, water
50。
Preferably, the formaldehyde absorbent is activated alumina.
Preferably, the pore radius of the hydroxyethyl cellulose are in 2nm.
Preferably, the water is distilled water.
The preparation method of the diatom ooze aqueous latex paint, it is characterised in that comprise the steps：
1) diatom ooze, isopropanol and aqueous acrylic emulsion of definite quality number are put into clean coating kettle, starts and stirs
Machine is mixed, is slowly stirred with the speed no more than 300r/min.；
2) water will be slowly added into stainless steel in formula.Water required in production must be distilled water, not handy without pure
Change running water, well water of processing etc..Add water with the mode of dropwise addition, so as not to occur layering, caking phenomena such as, then stir about 5 ~
10min；
3) tetraethyl orthosilicate is added, stirs 5 ~ 10min.
4) coalescents of alcohol ester 12 are added.Stir 3 ~ 5min or so.Mixing speed can be down to 200 r/min, reduce fragrant
The volatilization of material.
5) hydroxyethyl cellulose and formaldehyde absorbent are eventually adding, whole materials add Hou and are stirred for 10 ~ 15min.Therebetween
Mixing speed is gradually decreased to 100 r/min by 300 ~ 500 r/min, until terminating stirring.
Diatom ooze aqueous latex paint of the present invention only needs the clear water of pure free from admixture as diluent, have without with
The environment-friendly advantage of rival, in addition, also having the functions such as superpower net taste, meet more preferable interior decoration demand.
Embodiment
A kind of diatom ooze aqueous latex paint provided by the invention, including diatom ooze, isopropanol, aqueous acrylic emulsion, just
Silester, hydroxyethyl cellulose, the coalescents of alcohol ester 12, formaldehyde absorbent, water, the mass fraction of each component are：Diatom
Mud 20-25, isopropanol 28-32, aqueous acrylic emulsion 200-300, tetraethyl orthosilicate 13-17, hydroxyethyl cellulose 5-10, alcohol
The coalescents 2-7 of ester 12, formaldehyde absorbent 3-9, water 30-60.
Preferably, the mass fraction of the diatom ooze aqueous latex paint each component is：Diatom ooze 20, isopropanol 30, water
Property acrylic emulsion 250, tetraethyl orthosilicate 16, hydroxyethyl cellulose 8, the coalescents 3 of alcohol ester 12, formaldehyde absorbent 8, water
50。
Preferably, the formaldehyde absorbent is activated alumina.
Preferably, the pore radius of the hydroxyethyl cellulose are in 2nm.
Preferably, the water is distilled water.
The preparation method of the diatom ooze aqueous latex paint, it is characterised in that comprise the steps：
1) diatom ooze, isopropanol and aqueous acrylic emulsion of definite quality number are put into clean coating kettle, starts and stirs
Machine is mixed, is slowly stirred with the speed no more than 300r/min.；
2) water will be slowly added into stainless steel in formula.Water required in production must be distilled water, not handy without pure
Change running water, well water of processing etc..Add water with the mode of dropwise addition, so as not to occur layering, caking phenomena such as, then stir about 5 ~
10min；
3) tetraethyl orthosilicate is added, stirs 5 ~ 10min.
4) coalescents of alcohol ester 12 are added.Stir 3 ~ 5min or so.Mixing speed can be down to 200 r/min, reduce fragrant
The volatilization of material.
5) hydroxyethyl cellulose and formaldehyde absorbent are eventually adding, whole materials add Hou and are stirred for 10 ~ 15min.Therebetween
Mixing speed is gradually decreased to 100 r/min by 300 ~ 500 r/min, until terminating stirring.
It is described above, it is only the preferred embodiments of the present invention, not limits the present invention, appoints
What what those skilled in the art was changed or be modified as possibly also with the technology contents of the disclosure above to change on an equal basis etc.
Imitate embodiment.It is every without departing from the present invention program content, the technical spirit according to the present invention is to made for any of the above embodiments any
Simple modification, equivalent variations and remodeling, all fall within protection scope of the present invention.
Claims (6)
- A kind of 1. diatom ooze aqueous latex paint, it is characterised in that：Including diatom ooze, isopropanol, aqueous acrylic emulsion, positive silicic acid Ethyl ester, hydroxyethyl cellulose, the coalescents of alcohol ester 12, formaldehyde absorbent, water, the mass fraction of each component are：Diatom ooze 20- 25th, isopropanol 28-32, aqueous acrylic emulsion 200-300, tetraethyl orthosilicate 13-17, hydroxyethyl cellulose 5-10, alcohol ester ten Two coalescents 2-7, formaldehyde absorbent 3-9, water 30-60.
- 2. diatom ooze aqueous latex paint according to claim 1, it is characterised in that：The diatom ooze aqueous latex paint each group Point mass fraction be：Diatom ooze 20, isopropanol 30, aqueous acrylic emulsion 250, tetraethyl orthosilicate 16, hydroxyethyl cellulose 8th, the coalescents 3 of alcohol ester 12, formaldehyde absorbent 8, water 50.
- 3. diatom ooze aqueous latex paint according to claim 2, it is characterised in that：The formaldehyde absorbent is active oxidation Aluminium.
- 4. diatom ooze aqueous latex paint according to claim 2, it is characterised in that：The micropore of the hydroxyethyl cellulose half Footpath is in 2nm.
- 5. diatom ooze aqueous latex paint according to claim 2, it is characterised in that：The water is distilled water.
- 6. the preparation method of diatom ooze aqueous latex paint described in claim 1, it is characterised in that comprise the steps：1) diatom ooze, isopropanol and aqueous acrylic emulsion of definite quality number are put into clean coating kettle, starts and stirs Machine is mixed, is slowly stirred with the speed no more than 300r/min；2) water will be slowly added into stainless steel in formula, the water required in production must be distilled water, not handy without pure Change running water, well water etc. of processing, add water with the mode of dropwise addition, in order to avoid there is phenomena such as layering, caking, then stir about 5 ~ 10min；3) tetraethyl orthosilicate is added, stirs 5 ~ 10min；4) coalescents of alcohol ester 12,3 ~ 5min of stirring or so are added, mixing speed can be down to 200 r/min, reduce spices Volatilization；5) hydroxyethyl cellulose and formaldehyde absorbent are eventually adding, whole materials add Hou and are stirred for 10 ~ 15min, stir therebetween Speed is gradually decreased to 100 r/min by 300 ~ 500 r/min, until terminating stirring.