CN110016270A - One kind removing aldehyde Antibacterial Waterborne Emulsion Paint - Google Patents
One kind removing aldehyde Antibacterial Waterborne Emulsion Paint Download PDFInfo
- Publication number
- CN110016270A CN110016270A CN201910364183.8A CN201910364183A CN110016270A CN 110016270 A CN110016270 A CN 110016270A CN 201910364183 A CN201910364183 A CN 201910364183A CN 110016270 A CN110016270 A CN 110016270A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- emulsion paint
- antibacterial
- waterborne emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses one kind to remove aldehyde Antibacterial Waterborne Emulsion Paint, according to parts by weight, it is grouped as by following group: 200-300 parts of water, 10-15 parts of hydroxyethyl cellulose, organosilicon -100-200 parts of acrylic emulsion, 20-30 parts of talcum powder, 25-40 parts of titanium dioxide, 2-4 parts of antifreezing agent, 8-12 parts of dispersing agent, 1-2 parts of wetting agent, 2-3 parts of defoaming agent, 16-20 parts of coalescing agent, 2-4 parts of antibacterial agent, 2-3 parts of levelling agent, 2-4 parts of preservative, 4-6 parts of thickener, 1-2 parts of mould inhibitor, 3-5 parts of formaldehyde absorbent.Aqueous latex paint VOC of the invention is low, Antimicrobial preservative performance is good, adsorbs the formaldehyde in coating and prevents volatilization, environmentally protective, meets market and consumer demand.
Description
Technical field
The present invention relates to aqueous latex paint fields, more particularly to a kind of to remove aldehyde Antibacterial Waterborne Emulsion Paint.
Background technique
Emulsion paint is water-dispersible paint, it is using synthetic resin emulsion as base-material, and filler is added after grinding distribution
The various refined coating of auxiliary agent.Emulsion paint has many merits different from traditional metope coating, is such as easy to brush, is dry
It is dry rapidly, paint film is water-fast, scrub resistance is good etc..Emulsion paint is that film forming matter is done with some aqueous solutions of polymers, water removal and peace
Except harmful different types of polymers or polymer, also contain a small amount of emulsifiers and micro unpolymerized free monomer, trip
It is some small-molecule substances that can be volatilized from monomer, there are different degrees of toxicity problems.Emulsion paint is by lotion, pigment, fills out
Charge, auxiliary agent, fungicide and water composition, judge whether emulsion paint is toxic, being primarily to see these raw materials itself that it is added is
It is no to contain toxic component.Some inferior building coatings, although being known as emulsion paint, its above-mentioned lotion no at all, and
It is to make binder with industrial chemicals, the things of even starch etc such as polyvinyl alcohol, polyvinyl formals, especially poly- second
Enol formal, often because the technique of synthesis is unqualified, containing a large amount of free formaldehyde, this can bring about damage.
In addition, emulsion paint is after storage process or drying and forming-film, the pollution for the microorganism being nowhere not present, in addition
There are preference temperature and humidity, easily ruin very the paint in paint can, demulsification generates stench, and then mould growth, nigrescence fall off paint film.
The growth of microorganism in order to prevent, manufacturer will add a little fungicide, current selectable various types, as long as choosing
It is appropriate to select, and addition quantity is correct, will not cause harm to the human body.But a small number of manufacturing enterprises are not precluded in order to reduce cost, add
Enter a possibility that mercury salt is as fungicide.
Therefore, it in conjunction with the above problem, provides a kind of environmentally protective, removes the aqueous latex paint of formaldehyde antibacterial and mouldproof, be this
The problem of field technical staff's urgent need to resolve.
Summary of the invention
In view of this, the present invention provides one kind to remove aldehyde Antibacterial Waterborne Emulsion Paint, aqueous latex paint VOC is low, antibacterial is anti-
Rotten performance is good, adsorbs the formaldehyde in coating and prevents volatilization, environmentally protective, meets market and consumer demand.
To achieve the goals above, The technical solution adopted by the invention is as follows:
One kind removing aldehyde Antibacterial Waterborne Emulsion Paint, and the emulsion paint according to parts by weight, is made of following raw material: 200-300 parts of water,
10-15 parts of hydroxyethyl cellulose, organosilicon -100-200 parts of acrylic emulsion, 25-40 parts of titanium dioxide, are prevented 20-30 parts of talcum powder
Rotten agent 2-4 parts, 1-2 parts of mould inhibitor, 2-4 parts of antibacterial agent, 2-4 parts of antifreezing agent, 8-12 parts of BYK dispersing agent, 1-2 parts of wetting agent, disappear
2-3 parts of infusion, 16-20 parts of coalescing agent, 2-3 parts of BYK levelling agent, 3-5 parts of formaldehyde absorbent, 4-6 parts of thickener.
Preferably, the preservative is sorbic acid and its esters.
Preferably, the mould inhibitor is N- octyl -4- isothiazoline -3- ketone.
Preferably, the antibacterial agent is isothiazolinone antibacterial agent, nano-inorganic substance antibacterial agent, anionic species antibacterial agent
One of or it is a variety of.
Preferably, the antifreezing agent be 2-Butoxyethyl acetate, butyl glycol ether, in methylene chloride, propandiol butyl ether
One of.
Preferably, the wetting agent is α-phenyl methyl-ω-[(1,1,3,3- tetramethyl butyl) phenoxy group]-poly- (oxygen-
1,2- ethylidene).
Preferably, the defoaming agent is polysiloxane-polyether copolymer.
Preferably, the coalescing agent is propylene glycol methyl ether acetate, propandiol butyl ether, one in butyl
Kind.
Preferably, the formaldehyde absorbent is activated alumina.
Preferably, the thickener is hydroxyethyl cellulose class thickener.
As can be seen from the above technical solutions, compared with prior art, beneficial effects of the present invention are as follows:
Of the invention removes aldehyde Antibacterial Waterborne Emulsion Paint, and absorption has been carried out in the volatile hazardous substances such as formaldehyde and has been eliminated, suction is passed through
Attached and film forming anchors in emulsion paint film, forms film barrier, reduces the precipitation and volatilization of the substances such as the formaldehyde being detrimental to health,
Reach and actively adsorbed, purifying formaldehyde reduces VOC, efficiently administers the purpose of formaldehyde；Other than it can eliminate free formaldehyde,
The antibacterial mildew inhibitor added in raw material of the present invention, moreover it is possible to which the procreation for inhibiting pathogenic microorganism is being suitable for the temperature of mould reproduction and wet
Under degree, aqueous latex paint of the invention reduces the stench that demulsification generates, and eliminates peculiar smell, reduces mould and breeds, product of the invention
It is environmentally protective, it is at low cost, there is good adhesive force, water resistance, pollution resistance, environment friendly corrosion protection to have excellent performance, meet market and disappears
The demand of the person of expense.
Specific embodiment
The following is a clear and complete description of the technical scheme in the embodiments of the invention, it is clear that described embodiment
Only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, the common skill in this field
Art personnel every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
Embodiment 1:
The embodiment of the present invention 1 discloses one kind except aldehyde Antibacterial Waterborne Emulsion Paint, the technical solution adopted is as follows:
One kind removing aldehyde Antibacterial Waterborne Emulsion Paint, and the emulsion paint according to parts by weight, is made of following raw material: 200 parts of water, hydroxyl second
15 parts of base cellulose, 150 parts of organosilicon-acrylic emulsion, 20 parts of talcum powder, 40 parts of titanium dioxide, 2 parts of sorbic acid, N- octyl -4-
Isothiazoline -3- ketone is 1 part, 2 parts of isothiazolinone antibacterial agent, 4 parts of 2-Butoxyethyl acetate, 12 parts of BYK dispersing agent, α -
Phenyl methyl-ω-[(1,1,3,3- tetramethyl butyl) phenoxy group]-poly- (oxygen -1,2- ethylidene) is 2 parts, polysiloxane-polyether
3 parts of copolymer, 16 parts of propylene glycol methyl ether acetate, 2 parts of BYK levelling agent, 5 parts of activated alumina, the thickening of hydroxyethyl cellulose class
4 parts of agent.
Embodiment 2:
The embodiment of the present invention 2 discloses one kind except aldehyde Antibacterial Waterborne Emulsion Paint, the technical solution adopted is as follows:
One kind removing aldehyde Antibacterial Waterborne Emulsion Paint, and the emulsion paint according to parts by weight, is made of following raw material: 210 parts of water, hydroxyl second
14 parts of base cellulose, 170 parts of organosilicon-acrylic emulsion, 23 parts of talcum powder, 27 parts of titanium dioxide, 2 parts of sorbic acid, N- octyl -4-
Isothiazoline -3- ketone is 2 parts, 3 parts of nano-inorganic substance antibacterial agent, 4 parts of butyl glycol ether, 8 parts of BYK dispersing agent, α-phenyl methyl -
ω-[(1,1,3,3- tetramethyl butyl) phenoxy group]-poly- (oxygen -1,2- ethylidene) is 1 part, polysiloxane-polyether copolymer 2
Part, 20 parts of propandiol butyl ether, 3 parts of BYK levelling agent, 4 parts of activated alumina, 6 parts of hydroxyethyl cellulose class thickener.
Embodiment 3:
The embodiment of the present invention 3 discloses one kind except aldehyde Antibacterial Waterborne Emulsion Paint, the technical solution adopted is as follows:
One kind removing aldehyde Antibacterial Waterborne Emulsion Paint, and the emulsion paint according to parts by weight, is made of following raw material: 250 parts of water, hydroxyl second
13 parts of base cellulose, 200 parts of organosilicon-acrylic emulsion, 25 parts of talcum powder, 25 parts of titanium dioxide, 3 parts of sorbic acid, N- octyl -4-
Isothiazoline -3- ketone is 1 part, 4 parts of anionic species antibacterial agent, 3 parts, 9 parts of BYK dispersing agent, α-phenyl methyl-in methylene chloride
ω-[(1,1,3,3- tetramethyl butyl) phenoxy group]-poly- (oxygen -1,2- ethylidene) is 1 part, polysiloxane-polyether copolymer 2
Part, 18 parts of butyl, 2 parts of BYK levelling agent, 3 parts of activated alumina, 6 parts of hydroxyethyl cellulose class thickener.
Embodiment 4:
The embodiment of the present invention 4 discloses one kind except aldehyde Antibacterial Waterborne Emulsion Paint, the technical solution adopted is as follows:
One kind removing aldehyde Antibacterial Waterborne Emulsion Paint, and the emulsion paint according to parts by weight, is made of following raw material: 270 parts of water, hydroxyl second
12 parts of base cellulose, 110 parts of organosilicon-acrylic emulsion, 28 parts of talcum powder, 33 parts of titanium dioxide, 4 parts of sorbic acid, N- octyl -4-
Isothiazoline -3- ketone is 1 part, 2 parts of isothiazolinone antibacterial agent, 2 parts of 2-Butoxyethyl acetate, 10 parts of BYK dispersing agent, α -
Phenyl methyl-ω-[(1,1,3,3- tetramethyl butyl) phenoxy group]-poly- (oxygen -1,2- ethylidene) is 2 parts, polysiloxane-polyether
3 parts of copolymer, 17 parts of propylene glycol methyl ether acetate, 2 parts of BYK levelling agent, 3 parts of activated alumina, the thickening of hydroxyethyl cellulose class
5 parts of agent.
Embodiment 5:
The embodiment of the present invention 5 discloses one kind except aldehyde Antibacterial Waterborne Emulsion Paint, the technical solution adopted is as follows:
One kind removing aldehyde Antibacterial Waterborne Emulsion Paint, and the emulsion paint according to parts by weight, is made of following raw material: 300 parts of water, hydroxyl second
10 parts of base cellulose, 100 parts of organosilicon-acrylic emulsion, 30 parts of talcum powder, 30 parts of titanium dioxide, 4 parts of sorbic acid, N- octyl -4-
Isothiazoline -3- ketone is 2 parts, 3 parts of nano-inorganic substance antibacterial agent, 2 parts of 2-Butoxyethyl acetate, 11 parts of BYK dispersing agent, α-benzene
Ylmethyl-ω-[(1,1,3,3- tetramethyl butyl) phenoxy group]-poly- (oxygen -1,2- ethylidene) is 2 parts, polysiloxane-polyether is total
3 parts of polymers, 19 parts of propylene glycol methyl ether acetate, 3 parts of BYK levelling agent, 4 parts of activated alumina, hydroxyethyl cellulose class thickener 4
Part.
Each embodiment in this specification is described in a progressive manner, the highlights of each of the examples are with other
The difference of embodiment, the same or similar parts in each embodiment may refer to each other.
The foregoing description of the disclosed embodiments enables those skilled in the art to implement or use the present invention.
Various modifications to these embodiments will be readily apparent to those skilled in the art, as defined herein
General Principle can be realized in other embodiments without departing from the spirit or scope of the present invention.Therefore, of the invention
It is not intended to be limited to the embodiments shown herein, and is to fit to and the principles and novel features disclosed herein phase one
The widest scope of cause.
Claims (10)
1. one kind remove aldehyde Antibacterial Waterborne Emulsion Paint, which is characterized in that the emulsion paint according to parts by weight, by following raw material group
At: 200-300 parts of water, 10-15 parts of hydroxyethyl cellulose, organosilicon -100-200 parts of acrylic emulsion, 20-30 parts of talcum powder,
25-40 parts of titanium dioxide, 2-4 parts of preservative, 1-2 parts of mould inhibitor, 2-4 parts of antibacterial agent, 2-4 parts of antifreezing agent, BYK dispersing agent 8-12
Part, increases 1-2 parts of wetting agent, 2-3 parts of defoaming agent, 16-20 parts of coalescing agent, 2-3 parts of BYK levelling agent, 3-5 parts of formaldehyde absorbent
Thick dose 4-6 parts.
2. according to claim 1 a kind of except aldehyde Antibacterial Waterborne Emulsion Paint, which is characterized in that the preservative is sorbic acid
And its esters.
3. according to claim 1 a kind of except aldehyde Antibacterial Waterborne Emulsion Paint, which is characterized in that the mould inhibitor is that N- is pungent
Base -4- isothiazoline -3- ketone.
4. according to claim 1 a kind of except aldehyde Antibacterial Waterborne Emulsion Paint, which is characterized in that the antibacterial agent is isothiazole
One of quinoline ketone antibacterial agent, nano-inorganic substance antibacterial agent, anionic species antibacterial agent are a variety of.
5. according to claim 1 a kind of except aldehyde Antibacterial Waterborne Emulsion Paint, which is characterized in that the antifreezing agent is ethylene glycol
Monobutyl ether acetate, butyl glycol ether, in methylene chloride, one of propandiol butyl ether.
6. according to claim 1 a kind of except aldehyde Antibacterial Waterborne Emulsion Paint, which is characterized in that the wetting agent is α-phenyl
Methyl-ω-[(1,1,3,3- tetramethyl butyl) phenoxy group]-poly- (oxygen -1,2- ethylidene).
7. according to claim 1 a kind of except aldehyde Antibacterial Waterborne Emulsion Paint, which is characterized in that the defoaming agent is poly- silicon oxygen
Alkane-copolyether.
8. a kind of aldehyde Antibacterial Waterborne Emulsion Paint is removed according to claim 1, which is characterized in that the coalescing agent is the third two
One of alcohol methyl ether acetate, propandiol butyl ether, butyl.
9. according to claim 1 a kind of except aldehyde Antibacterial Waterborne Emulsion Paint, which is characterized in that the formaldehyde absorbent is to live
Property aluminium oxide.
10. according to claim 1 a kind of except aldehyde Antibacterial Waterborne Emulsion Paint, which is characterized in that the thickener is hydroxyl second
Base cellulose thickener.