CN104497663A - Antibacterial latex paint - Google Patents
Antibacterial latex paint Download PDFInfo
- Publication number
- CN104497663A CN104497663A CN201410842400.7A CN201410842400A CN104497663A CN 104497663 A CN104497663 A CN 104497663A CN 201410842400 A CN201410842400 A CN 201410842400A CN 104497663 A CN104497663 A CN 104497663A
- Authority
- CN
- China
- Prior art keywords
- parts
- emulsion paint
- agent
- antibiotic
- agents
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the field of a wall coating for indoor decoration, and particularly relates to an antibacterial latex paint. The antibacterial latex paint is characterized by being prepared from the following raw materials in parts by mass: 150-350 parts of water-based acrylic acid, 1-5 parts of defoaming agents, 2-4 parts of preservative agents, 5-10 parts of dispersing agents, 150-300 parts of pigments, 150-350 parts of fillers, 2-9 parts of thickening agents, 1-10 parts of levelling agents, 6-15 parts of nanometer inorganic negative ion antibacterial agents, 50-90 parts of nanometer polymer hollow microspheres, 50-90 parts of bamboo vinegar, 1-5 parts of cosolvents, 10-20 parts of citronella oil and 100-350 parts of water. The antibacterial latex paint disclosed by the invention can be coated on a wall and a wood. A paint film has the advantages of mild smell, good water solubility, low VOC, good covering power, low cost and optimal environment-friendly property. The antibacterial latex paint disclosed by the invention is a product which perfectly combines three themes, namely decoration, functionality and environmental friendliness, and has long-term continuous bacteriostatic effect.
Description
Technical field
The invention belongs to indoor decorating wallcovering field, be specifically related to a kind of antibiotic emulsion paint.
Background technology
Emulsion paint has easy construction, the feature that color is various, dominate in inner wall decoration at home, but conventional latex paint does not have anti-microbial effect, in hospital, children or room, classroom easily because bacterial adsorption is on body of wall, people just becomes easily infected by bacterium with body of wall contact because of carelessness, thus produces harm to health.At present, common antibiotic emulsion paint on the market generally adopts the mixture of organic antibacterial agent CMIT/MIT/ organic bromine, or inorganic silver ion antimicrobial agent, the mixture of organic antibacterial agent CMIT/MIT/ organic bromine is responsive to PH, addition is large, and toxicity is relatively greatly, irritant to people and animals.
Summary of the invention
For the above-mentioned defect existed in prior art, the present invention aims to provide a kind of for indoor wall decoration, has the emulsion paint of good antibacterial effect.
The technical solution used in the present invention: a kind of antibiotic emulsion paint, is characterized in that being made up of the raw material of following masses part: water soluble acrylic acid 150 ~ 350 parts, defoamer 1 ~ 5 part, sanitas 2 ~ 4 parts, dispersion agent 5 ~ 10 parts, pigment 150 ~ 300, filler 150 ~ 350 parts, thickening material 2 ~ 9 parts, flow agent 1 ~ 10 part, nano inorganic negative ion antibiotic agent 6 ~ 15 parts, nanometer polymer tiny balloon 50 ~ 90 parts, bamboo vinegar liquid 50 ~ 90 parts, solubility promoter 1 ~ 5 part, pamorusa oil 10 ~ 20 parts, water 100-350 part.
Described defoamer comprises silicone antifoam agent, polyether antifoam agent.
Described sanitas is selected from one or more in 1,2-benzisothiazole-3-ketone, methylisothiazolinone, CMIT.
Described dispersion agent is selected from sodium polyacrylate salt, modified polypropene acid solution class or modified polycarboxylic acid salt.
Described pigment comprises rutile TiO_2, modified phosphate.
Described filler be selected from calcined kaolin, water-ground limestone, diatomite, talcum powder, wollastonite or process white more than one.
Described thickening material is nano fumed silica or Natvosol.
Described flow agent is selected from cross-linking organosilicon polyoxyalkylene acrylate lipin polymer, dimethyl polysiloxane emulsion or polysiloxane-polyether copolymer.
Described nano inorganic negative-ion auxiliary agent is nano rare earth element mixture.
Described nanometer polymer tiny balloon polymethyl acrylic acid-divinylbenzene tiny balloon, its particle diameter is 100nm.
Described solubility promoter comprises 1,2-PD and ethanol.
Preparation process of the present invention: 1) nanometer polymer tiny balloon, bamboo vinegar liquid are mixed by weight the ratio of 1: 1, then pamorusa oil is added, stir 24h, make bamboo vinegar liquid infiltrate into tiny balloon inside, for subsequent use; 2) water, sanitas, dispersion agent and defoamer are mixed, stir; 3) filler and pigment high speed dispersion is added to less than 50 microns; 4) add water soluble acrylic acid, the agent of nano inorganic negative ion antibiotic, flow agent, thickening material and solubility promoter, stir; 5) add the mixed solution for subsequent use that the first step is done, thickening material stirs.
The present invention selects bamboo vinegar liquid and the pamorusa oil of Pure natural nontoxic, wherein, bamboo vinegar liquid contains more than 200 kind of organic compound, absorption can be played, decompose peculiar smell and smelly eliminating effect harmful chemicals such as sulfide, hydride, methyl alcohol, benzene, phenol, to unwanted bacterias such as intestinal bacteria, there is effective killing action, meanwhile, pamorusa oil has mosquito repellent, antibacterial effect.Under stirring, bamboo vinegar liquid and pamorusa oil is made to infiltrate into polymer nanocomposite tiny balloon inner, form embedding structure, by bury function, when emulsion paint drying and volatilizing, prevent bamboo vinegar liquid to volatilize with moisture with pamorusa oil, make effective bacteriocidal substance wherein continue slow releasing for a long time.
Advantageous Effects of the present invention: it is inner that the present invention selects the bamboo vinegar liquid of Pure natural nontoxic and pamorusa oil to infiltrate into polymer nanocomposite tiny balloon, form embedding structure, long-term slow release, reaches sterilization, antibacterial effect.The present invention can be coated with and be contained on metope and timber, and it is light that paint film has smell, good water solubility, and VOC is low, and cost is low, and environmental-protecting performance is good, is a product ornamental, the large theme perfection of functional environment-friendly three merged, has long-term lasting antibacterial effect.
Embodiment
Following examples only for illustration of the present invention, but are not used for limiting the scope of the invention.
Embodiment 1
Embodiment 1: first select water soluble acrylic acid 150 parts, defoamer 1 part, sanitas 2 parts, dispersion agent 5 parts, pigment 150, filler 150 parts, thickening material 2 parts, flow agent 1 part, nano inorganic negative ion antibiotic agent 6 parts, nanometer polymer tiny balloon 50 parts, bamboo vinegar liquid 50 parts, solubility promoter 1 part, pamorusa oil 10 parts, 100 parts, water; 1) nanometer polymer tiny balloon, bamboo vinegar liquid are mixed by weight the ratio of 1: 1, then pamorusa oil is added, stir 24h, make bamboo vinegar liquid infiltrate into tiny balloon inside, for subsequent use; 2) water, sanitas, dispersion agent and defoamer are mixed, stir; 3) filler and pigment high speed dispersion is added to less than 50 microns; 4) add water soluble acrylic acid, the agent of nano inorganic negative ion antibiotic, flow agent, thickening material and solubility promoter, stir; 5) add the mixed solution for subsequent use that the first step is done, thickening material stirs.
By a kind of antibiotic emulsion paint that embodiment 1 manufactures, its prevailing quality technical indicator is as table 1.
Table 1
Embodiment 2
Embodiment 2: first select water soluble acrylic acid 250 parts, defoamer 3 parts, sanitas 3 parts, dispersion agent 8 parts, pigment 200, filler 200 parts, thickening material 5 parts, flow agent 5 parts, nano inorganic negative ion antibiotic agent 10 parts, nanometer polymer tiny balloon 80 parts, bamboo vinegar liquid 80 parts, solubility promoter 3 parts, pamorusa oil 15 parts, 200 parts, water; 1) nanometer polymer tiny balloon, bamboo vinegar liquid are mixed by weight the ratio of 1: 1, then pamorusa oil is added, stir 24h, make bamboo vinegar liquid infiltrate into tiny balloon inside, for subsequent use; 2) water, sanitas, dispersion agent and defoamer are mixed, stir; 3) filler and pigment high speed dispersion is added to less than 50 microns; 4) add water soluble acrylic acid, the agent of nano inorganic negative ion antibiotic, flow agent, thickening material and solubility promoter, stir; 5) add the mixed solution for subsequent use that the first step is done, thickening material stirs.
By a kind of antibiotic emulsion paint that embodiment 2 manufactures, its prevailing quality technical indicator is as table 2.
Table 2
Embodiment 3
Embodiment 3: first select water soluble acrylic acid 350 parts, defoamer 5 parts, sanitas 4 parts, dispersion agent 10 parts, pigment 300, filler 350 parts, thickening material 9 parts, flow agent 10 parts, nano inorganic negative ion antibiotic agent 15 parts, nanometer polymer tiny balloon 90 parts, bamboo vinegar liquid 90 parts, solubility promoter 5 parts, pamorusa oil 20 parts, 350 parts, water; 1) nanometer polymer tiny balloon, bamboo vinegar liquid are mixed by weight the ratio of 1: 1, then pamorusa oil is added, stir 24h, make bamboo vinegar liquid infiltrate into tiny balloon inside, for subsequent use; 2) water, sanitas, dispersion agent and defoamer are mixed, stir; 3) filler and pigment high speed dispersion is added to less than 50 microns; 4) add water soluble acrylic acid, the agent of nano inorganic negative ion antibiotic, flow agent, thickening material and solubility promoter, stir; 5) add the mixed solution for subsequent use that the first step is done, thickening material stirs.
By a kind of antibiotic emulsion paint that embodiment 3 manufactures, its prevailing quality technical indicator is as table 3.
Table 3
Embodiment 4: antibacterial Indexs measure
The antibacterial effect of the generic latex paint that antibiotic emulsion paint of the present invention and the prior art of embodiment of the present invention 1-3 gained are produced compares: Setup Experiments, the iron sheet box of 51 cubic metre is put into respectively in the airtight room of 30 cubic metres, wherein 1 box not mopping left blank standard, the 0.5m having brushed generic latex paint and embodiment 1-3 antibiotic emulsion paint put into respectively by all the other 4 boxes
2each four pieces of model, respectively to the bacterium of injecting some amount in 5 detection cases, measures the concentration of the starting point concentration of bacterium in 5 casees, 24 hours and 48 hours respectively.Concrete outcome is in table 4.
Table 4: antibacterial effect compares
3 kinds of antibiotic emulsion paints that embodiment of the present invention 1-3 prepares sterilization rate after brushing 48h reaches more than 70%, far above the antibacterial effect of generic latex paint, so antibiotic emulsion paint provided by the invention has good anti-microbial effect.
Claims (7)
1. an antibiotic emulsion paint, is characterized in that being made up of the raw material of following masses part: water soluble acrylic acid 150 ~ 350 parts, defoamer 1 ~ 5 part, sanitas 2 ~ 4 parts, dispersion agent 5 ~ 10 parts, pigment 150 ~ 300, filler 150 ~ 350 parts, thickening material 2 ~ 9 parts, flow agent 1 ~ 10 part, nano inorganic negative ion antibiotic agent 6 ~ 15 parts, nanometer polymer tiny balloon 50 ~ 90 parts, bamboo vinegar liquid 50 ~ 90 parts, solubility promoter 1 ~ 5 part, pamorusa oil 10 ~ 20 parts, water 100-350 part.
2. a kind of antibiotic emulsion paint according to claim 1, is characterized in that: described defoamer comprises silicone antifoam agent, polyether antifoam agent.
3. a kind of antibiotic emulsion paint according to claim 1, is characterized in that: described sanitas is selected from one or more in 1,2-benzisothiazole-3-ketone, methylisothiazolinone, CMIT.
4. a kind of antibiotic emulsion paint according to claim 1, is characterized in that: described dispersion agent is selected from sodium polyacrylate salt, modified polypropene acid solution class or modified polycarboxylic acid salt.
5. a kind of antibiotic emulsion paint according to claim 1, is characterized in that: described pigment comprises rutile TiO_2, modified phosphate.
6. a kind of antibiotic emulsion paint according to claim 1, is characterized in that: described filler be selected from calcined kaolin, water-ground limestone, diatomite, talcum powder, wollastonite or process white more than one.
7. a kind of antibiotic emulsion paint according to claim 1, is characterized in that: described thickening material is nano fumed silica or Natvosol.