CN106609074A - Multifunctional waterborne wood diatom ooze paint - Google Patents
Multifunctional waterborne wood diatom ooze paint Download PDFInfo
- Publication number
- CN106609074A CN106609074A CN201510693674.9A CN201510693674A CN106609074A CN 106609074 A CN106609074 A CN 106609074A CN 201510693674 A CN201510693674 A CN 201510693674A CN 106609074 A CN106609074 A CN 106609074A
- Authority
- CN
- China
- Prior art keywords
- water
- diatom ooze
- polyurethanes
- parts
- multifunctional aqueous
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a multifunctional waterborne wood diatom ooze paint, which is prepared from the following components in parts by mass: 20 to 25 parts of diatom ooze, 28 to 32 parts of polyacrylic emulsion, 20 to 30 parts of water-soluble alkyd resin, 13 to 17 parts of alkyd resin, 5 to 10 parts of nanometer activated carbon, 2 to 7 parts of polyurethane, 3 to 9 parts of formaldehyde absorbent, and 30 to 60 parts of water. The multifunctional waterborne wood diatom ooze paint provided by the invention only requires pure clear water free from impurities as a diluent so as to have an incomparable environment-friendly advantage, and additionally has a superstrong odor removing function so as to meet the better interior decoration requirement.
Description
Technical field
The present invention relates to a kind of house ornamentation paint field, in particular it relates to a kind of multifunctional aqueous woodenware diatom ooze paint.
Background technology
Research shows that coating is one of major pollutants of home room.With the formulation and the raising of consumer's environmental consciousness of relevant national standard, water paint is popularized comprehensively.But, the coating that furniture surface is used still based on conventional oil-based woodcare paint, virtually increased the pollution of home room, and the water paint furniture of environmental protection is still " non-mainstream " in market.The oil paint of generally existing mainly uses the banana oil containing a large amount of poisonous and harmful substances, thinner as diluent, and impayable environment-friendly advantage is the characteristics of water paint is maximum.In pay attention to day by day coating safety and today of environmental protection index, water-borne wood coating just because of less harmful, low stain characteristic that it has, is gradually received by market.
The content of the invention
For above-mentioned deficiency present in prior art, the technical problem to be solved is to provide a kind of good multifunctional aqueous woodenware diatom ooze paint of effect.
The technical solution adopted for the present invention to solve the technical problems is：A kind of multifunctional aqueous woodenware diatom ooze paint, including diatom ooze, acrylic emulsion, water-soluble Chun Acid resins, alkyd resin, active carbon nanoparticles, polyurethanes, formaldehyde absorbent, water are provided, the mass fraction of each component is：Diatom ooze 20-25, acrylic emulsion 28-32, water-soluble Chun Acid resin 20-30, alkyd resin 13-17, active carbon nanoparticles 5-10, polyurethanes 2-7, formaldehyde absorbent 3-9, water 30-60.
Preferably, the mass fraction of the multifunctional aqueous woodenware diatom ooze paint each component is：Diatom ooze 20, acrylic emulsion 30, water-soluble Chun Acid resins 23, alkyd resin 16, active carbon nanoparticles 8, polyurethanes 3, formaldehyde absorbent 8, water 50.
Preferably, the polyurethanes is Fructus Citri Limoniae polyurethanes.
Preferably, the formaldehyde absorbent is activated alumina.
Preferably, the pore radius of the active carbon nanoparticles are in 2nm.
Preferably, the water is distilled water.
The preparation method of the multifunctional aqueous woodenware diatom ooze paint, it is characterised in that comprise the steps：
1) diatom ooze, acrylic emulsion and the water-soluble Chun Acid resins of definite quality number are put in clean coating kettle, blender is started, are slowly stirred with the speed less than 300r/min.；
2) water will be slowly added in stainless steel in formula.The water wanted needed for production must be distilled water, not handy tap water, well water without purification process etc..Added water with the mode of Deca, in order to avoid there is the phenomenons such as layering, caking, then 5 ~ 10min of stir about；
3) alkyd resin is added, stirs 5 ~ 10min.
4) polyurethanes is added.3 ~ 5min of stirring or so.Mixing speed can be down to 200 r/min, reduce the volatilization of spice.
5) active carbon nanoparticles and formaldehyde absorbent are eventually adding, whole materials add Hou and are stirred for 10 ~ 15min.Therebetween mixing speed is gradually decreased to 100 r/min by 300 ~ 500 r/min, until terminating stirring.
Multifunctional aqueous woodenware diatom ooze paint of the present invention only needs to pure pure clear water as diluent, with impayable environment-friendly advantage, additionally, also having the functions such as superpower net taste, meets more preferable interior decoration demand.
Specific embodiment
A kind of multifunctional aqueous woodenware diatom ooze paint that the present invention is provided, including diatom ooze, acrylic emulsion, water-soluble Chun Acid resins, alkyd resin, active carbon nanoparticles, polyurethanes, formaldehyde absorbent, water, the mass fraction of each component is：Diatom ooze 20-25, acrylic emulsion 28-32, water-soluble Chun Acid resin 20-30, alkyd resin 13-17, active carbon nanoparticles 5-10, polyurethanes 2-7, formaldehyde absorbent 3-9, water 30-60.
Preferably, the mass fraction of the multifunctional aqueous woodenware diatom ooze paint each component is：Diatom ooze 20, acrylic emulsion 30, water-soluble Chun Acid resins 23, alkyd resin 16, active carbon nanoparticles 8, polyurethanes 3, formaldehyde absorbent 8, water 50.
Preferably, the polyurethanes is Fructus Citri Limoniae polyurethanes.
Preferably, the formaldehyde absorbent is activated alumina.
Preferably, the pore radius of the active carbon nanoparticles are in 2nm.
Preferably, the water is distilled water.
The preparation method of the multifunctional aqueous woodenware diatom ooze paint, it is characterised in that comprise the steps：
1) diatom ooze, acrylic emulsion and the water-soluble Chun Acid resins of definite quality number are put in clean coating kettle, blender is started, are slowly stirred with the speed less than 300r/min.；
2) water will be slowly added in stainless steel in formula.The water wanted needed for production must be distilled water, not handy tap water, well water without purification process etc..Added water with the mode of Deca, in order to avoid there is the phenomenons such as layering, caking, then 5 ~ 10min of stir about；
3) alkyd resin is added, stirs 5 ~ 10min.
4) polyurethanes is added.3 ~ 5min of stirring or so.Mixing speed can be down to 200 r/min, reduce the volatilization of spice.
5) active carbon nanoparticles and formaldehyde absorbent are eventually adding, whole materials add Hou and are stirred for 10 ~ 15min.Therebetween mixing speed is gradually decreased to 100 r/min by 300 ~ 500 r/min, until terminating stirring.
The above, is only, to presently preferred embodiments of the present invention, the restriction of other forms not to be done to the present invention, and any those skilled in the art are changed or be modified as the Equivalent embodiments of equal change possibly also with the technology contents of the disclosure above.It is every without departing from the present invention program content, according to the technical spirit of the present invention to any simple modification made for any of the above embodiments, equivalent variations and remodeling, all fall within protection scope of the present invention.
Claims (7)
1. a kind of multifunctional aqueous woodenware diatom ooze paint, it is characterised in that：Including diatom ooze, acrylic emulsion, water-soluble Chun Acid resins, alkyd resin, active carbon nanoparticles, polyurethanes, formaldehyde absorbent, water, the mass fraction of each component is：Diatom ooze 20-25, acrylic emulsion 28-32, water-soluble Chun Acid resin 20-30, alkyd resin 13-17, active carbon nanoparticles 5-10, polyurethanes 2-7, formaldehyde absorbent 3-9, water 30-60.
2. multifunctional aqueous woodenware diatom ooze paint according to claim 1, it is characterised in that：The mass fraction of the multifunctional aqueous woodenware diatom ooze paint each component is：Diatom ooze 20, acrylic emulsion 30, water-soluble Chun Acid resins 23, alkyd resin 16, active carbon nanoparticles 8, polyurethanes 3, formaldehyde absorbent 8, water 50.
3. multifunctional aqueous woodenware diatom ooze paint according to claim 2, it is characterised in that：The polyurethanes is Fructus Citri Limoniae polyurethanes.
4. multifunctional aqueous woodenware diatom ooze paint according to claim 2, it is characterised in that：The formaldehyde absorbent is activated alumina.
5. multifunctional aqueous woodenware diatom ooze paint according to claim 2, it is characterised in that：The pore radius of the active carbon nanoparticles exist
2nm。
6. multifunctional aqueous woodenware diatom ooze paint according to claim 2, it is characterised in that：The water is distilled water.
7. the preparation method of multifunctional aqueous woodenware diatom ooze paint described in claim 1, it is characterised in that comprise the steps：
1) diatom ooze, acrylic emulsion and the water-soluble Chun Acid resins of definite quality number are put in clean coating kettle, blender is started, are slowly stirred with the speed less than 300r/min；
2) water will be slowly added in stainless steel in formula, the water wanted needed for production must be distilled water, not handy tap water, well water without purification process etc. is added water with the mode of Deca, in order to avoid there is the phenomenons such as layering, caking, then 5 ~ 10min of stir about；
3) alkyd resin is added, stirs 5 ~ 10min；
4) polyurethanes, 3 ~ 5min of stirring or so are added, mixing speed can be down to 200
R/min, reduces the volatilization of spice；
5) active carbon nanoparticles and formaldehyde absorbent are eventually adding, whole materials add Hou and are stirred for 10 ~ 15min, and therebetween mixing speed is gradually decreased to 100 r/min by 300 ~ 500 r/min, until terminating stirring.