CN107381731A - Water and method and the application for handling water - Google Patents
Water and method and the application for handling water Download PDFInfo
- Publication number
- CN107381731A CN107381731A CN201710669945.6A CN201710669945A CN107381731A CN 107381731 A CN107381731 A CN 107381731A CN 201710669945 A CN201710669945 A CN 201710669945A CN 107381731 A CN107381731 A CN 107381731A
- Authority
- CN
- China
- Prior art keywords
- water
- quantum
- ceramics
- health products
- processing water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the method and application of a kind of water and processing water, it is related to field of material technology.The method of the processing water is that water is placed in the container provided with quantum ceramics obtained by least 10min；Wherein, quantum ceramics are after by formula, raw material is mixed, and under nitrogen atmosphere, gained are cooled down after sintering, formula includes：Tourmaline, aerolite, stone needle, medical stone, germanite, silica, titanium dioxide, calcium oxide, kaolin, di-iron trioxide, zinc oxide, neodymium, boron and magnesia, effectively purify water, while will reduce water clusters, improve the penetration of water, increase the content of mineral substances in water.The water as made from the method for above-mentioned processing water, it is rich in mineral matter, and permeability is good.Application of the above-mentioned water in health products, effectively improve the health properties of health products.
Description
Technical field
The present invention relates to field of material technology, and more particularly to a kind of water and the method and the application that handle water.
Background technology
Water is not only primary condition existing for life, and the basic structure sheet of life structure, the mankind with water resource is close can not
Point.With the progress of human society and the development in city, water is divided into drinking water and domestic water, but either drinking water is also
It is domestic water, while it is that the mankind service, is also polluted all the time by the mankind, and pollution level is on the rise,
The species of polluter increases increasingly, so that threatening the health and lives of the mankind.At present, it has been recognized that, drinking water
It is the mode of infection of harmful substance, in fact, the breathing of people and skin absorption may also make one to absorb these nuisances during shower
Matter, exactly domestic water is more through the various aspects of our daily lifes, for example, shower water, water for kitchen use, clothes
Water for cleaning, sanitary toilet water.Particularly shower water, due to the hair and skin contact directly with human body, its purification is asked
Topic should attract people's attention.
In recent years, has there is the technology and product of many purified waters, including chemicals treatment technology and production in the market
Product, activated carbon class filtration, purification treatment technology and product, ion exchange resin treatment technology and product, medical stone class purified treatment
Technology and product etc..But facts have proved above-mentioned various technologies and product, such as chemicals treatment technology and product because of excitant or
Generation chemically reacts and is eliminated, and other several treatment technologies and product mostly single effect or imperfection, also do not possess or
Not exclusively possess release anion, sterilization, antibacterial, the effect of dechlorination.
The content of the invention
It is an object of the invention to provide a kind of method for handling water, effectively purify water, while water clusters will be reduced,
The penetration of water is improved, increases the content of mineral substances in water.
Another object of the present invention is to provide a kind of water as made from the method for above-mentioned processing water, it is rich in mineral matter,
Permeability is good.
Another object of the present invention is to provide application of the above-mentioned water in health products, the health of health products is effectively improved
Energy.
The present invention is solved its technical problem and realized using following technical scheme.
The present invention proposes a kind of method for handling water, and water is placed in the container provided with quantum ceramics obtained by least 10min.
Quantum ceramics are after by formula, raw material is mixed, and under nitrogen atmosphere, gained is cooled down after sintering.
It is formulated according to mass percent meter, including：Tourmaline 25%~36%, aerolite 1%~3%, stone needle 7%~
14%, medical stone 7%~25%, germanite 5%~10%, silica 6%~13%, titanium dioxide 0.5%~3.5%, oxygen
Change calcium 1~5%, kaolin 7%~12%, di-iron trioxide 0.5%~3%, zinc oxide 0.5%~3%, neodymium 0.5%~
3%, boron 0.5%~3%, and magnesia 6%~12%.The present invention proposes a kind of as made from the method for above-mentioned processing water
Water.
The present invention proposes a kind of application of above-mentioned water in health products.
The water of the embodiment of the present invention and handle the method for water and the beneficial effect of application and be：
By based on tourmaline, the formula supplemented by other raw materials, reasonable mixture ratio, the quantum ceramics for effectively improving to obtain
Performance, allow the magnetic force and 6~14 microns of infrared ray of its lasting Gauss of generation 2, there is excellent health-care efficacy.Use
The quantum ceramics carry out physical treatment to water, and the quantum ceramics discharges into water bears hydrogen particle, make negative hydrogen particle in water by
0PPM/L brings up to more than 1.2PPM/L, meanwhile, by the oscillation principle of electronic curing ripple, original by 13~16 moisture
Molecular macromolecular mass water, 6~9 hydrone composition small-micelle waters are quickly changed to, simultaneously as it is rich in mineral
Matter, effectively making the pH value of water, to improve to pH be 7.5~8.8, and it be in alkalescent to make water, at the same handle ORP (current potential) values by it is original+
180~250 change between -100~220；Make the water after processing that there is higher activity, be more convenient for absorbing and health care is imitated
Fruit is good.
Meanwhile the quantum ceramics are applied into health products, it can effectively strengthen its health properties.
Embodiment
, below will be in the embodiment of the present invention to make the purpose, technical scheme and advantage of the embodiment of the present invention clearer
Technical scheme be clearly and completely described.Unreceipted actual conditions person, builds according to normal condition or manufacturer in embodiment
The condition of view is carried out.Agents useful for same or the unreceipted production firm person of instrument, it is the conventional production that can be obtained by commercially available purchase
Product.
The method and application of the water to the embodiment of the present invention and processing water are specifically described below.
The present invention provides a kind of method for handling water, and water is placed in the container provided with quantum ceramics obtained by least 10min.
The undesirable element effectively gone by quantum ceramics in water removal, meanwhile, the quantum ceramics carry out physical treatment, quantum ceramics to water
The negative hydrogen particle of Xiang Shuizhong releases, makes the negative hydrogen particle in water bring up to more than 1.2PPM/L by 0PPM/L, meanwhile, pass through high frequency magnetic
Change the oscillation principle of ripple, original by the molecular macromolecular mass water of 13~16 moisture, be quickly changed to 6~9 moisture
Son composition small-micelle water, simultaneously as it be rich in mineral matter, effectively making the pH value of water, to improve to pH be 7.5~8.5, makes water
In alkalescent, while handle is changed into ORP (current potential) value between -100~220 by original+180~250.Processing method letter
It is single convenient, effectively purify water, while water clusters will be reduced, the penetration of water is improved, increases the content of mineral substances in water.
Wherein, evolution processor that container for example can be for quilt, to water etc., is not especially limited, this area herein
This staff can be selected according to actual conditions.
In the present invention, quantum ceramics are after by formula, raw material is mixed, and under nitrogen atmosphere, gained is cooled down after sintering；Its
In, it is formulated according to mass percent meter, including：
Tourmaline 25%~36%, aerolite 1%~3%, stone needle 7%~14%, medical stone 7%~25%, germanite 5%~
10%, silica 6%~13%, titanium dioxide 0.5%~3.5%, calcium oxide 1~5%, kaolin 7%~12%, three oxygen
Change two iron 0.5%~3%, zinc oxide 0.5%~3%, neodymium 0.5%~3%, boron 0.5%~3%, and magnesia 6%~
12%.
It is highly preferred that in preferred embodiments of the present invention, the formula of quantum ceramics, by mass percentage, including：Electricity
Gas stone 26%~36%, aerolite 1%~3%, stone needle 9%~10%, medical stone 8%~22%, germanite 7%~8%, titanium dioxide
Silicon 8%~11%, titanium dioxide 1%~2%, calcium oxide 2~3%, kaolin 9%~10%, di-iron trioxide 1%~3%,
Zinc oxide 1%~3%, neodymium 1%~3%, boron 1%~3%, and magnesia 8%~10%.
By the rational proportion of above-mentioned each raw material, the performance of the quantum ceramics finally given is effectively improved, makes it permanent
Release preferably discharges micro- magnetic and infrared waves, has excellent health-care efficacy, and effective human activin cell, increase blood follow
Ring, the function of adjusting microcirculation in human body.
The ceramic material can adsorb Nanometer Copper, zinc, the silver alloy in water simultaneously, because alloying metal cluster can be effective
The harmful substance such as the chlorine residue gone in water removal, soluble heavy metal ion, nitrate, fluoride, carbonate and sulfate, and can
Control the growth and breeding of the bacterium in water and algae and prevent the accumulation of hard scale, while can remove because of water delivery made of ferrous materials
The ferrous iron oxide colloid formed during pipe corrosion, so as to reach the effect to purify water.
Wherein, tourmaline, the general name of family's cyclic structure silicate mineral of crystal category trigonal system.
Tourmaline can produce anion, have adjustment human body ionic equilibrium, deodorization, activating cell, improve nature and cure
Power etc. acts on, and can suppress the oxidation or aging of body.It can with electrolysis water and reduce water clusters, effectively remove ammonia or
Impurity, while improve the penetration of water.Tourmaline can also radiate far infrared simultaneously, and it can penetrate into deep somatic portion
Position, warm cell, stimulates circulation, and makes metabolism smooth, while tourmaline contains various natural mineral matters, wherein having very
It is more identical with mineral matter necessary to the mankind.Acted on by weak current, mineral matter is readily absorbed by, and is that splendid mineral matter comes
Source.
The present invention is used using tourmaline as principal ingredients, with aerolite, stone needle, medical stone, germanite, silica, titanium dioxide
Titanium, kaolin etc. are used as dispensing, effectively strengthen its magnetic and health-care effect.Increase di-iron trioxide, neodymium, boron etc. simultaneously, enter
The magnetic of one step quantum ceramics effectively made from enhancing.
The present invention provides a kind of preparation method of quantum ceramics, after by above-mentioned formula, raw material is mixed, under nitrogen atmosphere,
Being cooled down after sintering, obtain the finished product of quantum ceramics, the finished product can be ball, block or random geometry, or after obtaining
Regular product further are processed into its shape, it is not specifically limited herein.
Due in sintering process, being related to the redox reaction between each raw material, for avoid influenceing final composition by
Influence, therefore be preferably to be sintered under nitrogen atmosphere, cool down.
Preferably, in preferred embodiments of the present invention, before sintering, raw material is crushed to 410~480 mesh, effectively increased
Contact area between big each raw material, promotes reaction, effectively improves reaction efficiency.
Preferably, in preferred embodiments of the present invention, 0.3~0.7h is incubated at 640~660 DEG C before sintering, is made each
Raw material preheating, while make to carry out solid phase reaction between a raw material.It should be noted that in the present invention, when in 640~660 DEG C of guarantors
After 0.3~0.7h of temperature, directly it is sintered, during which, in room temperature to 640~660 DEG C also with the heating speed of the first stage of sintering
Rate is carried out, i.e., is first warming up to 640~660 DEG C with 2~3 DEG C/min speed, is ensured that each raw material is at the uniform velocity heated, is ensured its property
Stability.
Preferably, in preferred embodiments of the present invention, sintering includes first stage and second stage, and the first stage is：
1000 DEG C first are warming up to 2~3 DEG C/min speed, then 1450 DEG C~1500 DEG C are warming up to 0.5~1 DEG C/min speed.
Effectively improve the magnetic of quantum ceramics.
Second stage is at 1450 DEG C~1500 DEG C, is incubated 0.5~1.5h, effectively increases saturation induction density, simultaneously
A raw material is fully carried out redox reaction, improve the yield rate of product.In preferred embodiments of the present invention, 20 are cooled to
~35 DEG C.
It is highly preferred that in preferred embodiments of the present invention, cooling includes：
1000 DEG C first are cooled to 1~2 DEG C/min speed, is then cooled again with 3~5 DEG C/min speed, effectively carried
The magnetic stability of high product, allow its preferable magnetic force of lasting transmitting.
The present invention proposes a kind of quantum ceramics, and it is made by above-mentioned preparation method, the magnetic for the Gauss of generation 2 that it can be lasting
Power and 6~14 microns of infrared ray, effectively improve its health ability.
The present invention proposes the water as made from the method for above-mentioned processing water, and it is rich in negative hydrogen particle, can neutralize in human body
Oxygen radical caused by metabolite and infection；Wherein, oxygen radical is a kind of extremely unstable material, when by anion
After the excess electron of peripheral institute's band neutralizes, a variety of harm of oxygen radical are eliminated, and such as destroy cell membrane, accelerate artery hard
Change, suppress immunologic function, make human body device palace aging etc..So as to effectively improve body immunity, meanwhile, original by 13~16
The individual molecular macromolecular mass water of moisture, 6~9 hydrone composition small-micelle waters are quickly changed to, and because it is rich in
Mineral matter, effectively make water pH value improve to pH be 7.5~8.8, it be in alkalescent to make water, at the same handle ORP (current potential) value by original
+ 180~250 come are changed between -100~220；Make the water after processing that there is higher activity, be more convenient for absorb and
Health-care effect is good.
The present invention also provides application of the above-mentioned water water in health products.
Specifically, health products are the health products for the treatment of rheumatic arthritis, treat II type of health products or treatment of goat
The health products of diabetes.Its health-care efficacy can be effectively improved, effectively improves its commercial value.
The feature and performance of the present invention are described in further detail with reference to embodiments.
Embodiment 1
A kind of water, it is made by the method for following processing water：
Water is placed in the container provided with quantum ceramics obtained by least 10min.
Quantum ceramics are to mix raw material by formula, after being crushed to 440 mesh, under nitrogen atmosphere, in room temperature first with 2.5
DEG C/min speed is warming up to 1000 DEG C, then is warming up to 1450 DEG C with 1 DEG C/min speed, after 1450 DEG C are incubated 1h, then with
1.6 DEG C/min speed is cooled to 1000 DEG C, is then cooled to 25 DEG C with 4 DEG C/min speed again, produces.
Wherein, it is formulated by mass percentage, including：
Tourmaline 27%, aerolite 2%, stone needle 8%, medical stone 17%, germanite 8%, silica 7%, titanium dioxide
2%, calcium oxide 3%, kaolin 10%, di-iron trioxide 2%, zinc oxide 2%, neodymium 2%, boron 2%, and magnesia 8%.
Embodiment 2
A kind of water, it is made by the method for following processing water：
Water is placed in the container provided with quantum ceramics obtained by least 10min.
Quantum ceramics are to mix raw material by formula, after being crushed to 410 mesh, under nitrogen atmosphere, first with 2.5 DEG C/min's
Speed is warming up to 660 DEG C, after 660 DEG C are incubated 0.7h, is then warming up to 1000 DEG C with 2.5 DEG C/min speed, then with 0.7
DEG C/min speed is warming up to 1500 DEG C, 1000 DEG C are cooled to after 1500 DEG C are incubated 0.7h, then with 2 DEG C/min speed, so
20 DEG C are cooled to 4 DEG C/min speed again afterwards, is produced.
Wherein, it is formulated by mass percentage, including：
Tourmaline 36%, aerolite 3%, stone needle 14%, medical stone 7%%, germanite 8%, silica 8%, titanium dioxide
1%, calcium oxide 4%, kaolin 8%, di-iron trioxide 1%, zinc oxide 1%, neodymium 1%, boron 1%, and magnesia 7%.
Embodiment 3
A kind of water, it is made by the method for following processing water：
Water is placed in the container provided with quantum ceramics obtained by least 10min.
Quantum ceramics are to mix raw material by formula, after being crushed to 460 mesh, under nitrogen atmosphere, first with 2 DEG C/min speed
Degree is warming up to 650 DEG C, after 650 DEG C are incubated 0.5h, is then warming up to 1000 DEG C with 2 DEG C/min speed, then with 1 DEG C/min's
Speed is warming up to 1470 DEG C, 1000 DEG C is cooled to after 1470 DEG C are incubated 1.2h, then with 1 DEG C/min speed, then again with 3
DEG C/min speed is cooled to 25 DEG C, produce.
Wherein, it is formulated by mass percentage, including：
Tourmaline 26%, aerolite 1%, stone needle 10%, medical stone 22%, germanite 6%, silica 6%, titanium dioxide
2%, calcium oxide 2.5%, kaolin 9%, di-iron trioxide 1.5%, zinc oxide 1%, neodymium 1.5%, boron 1.5%, and oxidation
Magnesium 10%.
Embodiment 4
A kind of water, it is made by the method for following processing water：
Water is placed in the container provided with quantum ceramics obtained by least 10min.
Quantum ceramics are to mix raw material by formula, after being crushed to 470 mesh, under nitrogen atmosphere, first with 2.7 DEG C/min's
Speed is warming up to 645 DEG C, after 645 DEG C are incubated 0.6h, is then warming up to 1000 DEG C with 2.7 DEG C/min speed, then with 1 DEG C/
Min speed is warming up to 1460 DEG C, is cooled to 1000 DEG C after 1460 DEG C are incubated 1h, then with 1.8 DEG C/min speed, Ran Houzai
30 DEG C are cooled to 3.5 DEG C/min speed, is produced.
Wherein, it is formulated by mass percentage, including：
Tourmaline 30%, aerolite 1.5%, stone needle 9%, medical stone 15%, germanite 10%, silica 1 2.5%, dioxy
Change titanium 1%, calcium oxide 3%, kaolin 8%, di-iron trioxide 1%, zinc oxide 1%, neodymium 1%, boron 1%, and magnesia
6%.
Embodiment 5
A kind of water, it is made by the method for following processing water：
Water is placed in the container provided with quantum ceramics obtained by least 10min.
Quantum ceramics are to mix raw material by formula, after being crushed to 470 mesh, under nitrogen atmosphere, first with 3 DEG C/min speed
Degree is warming up to 650 DEG C, after 650 DEG C are incubated 0.5h, is then warming up to 1000 DEG C with 3 DEG C/min speed, then with 1 DEG C/min's
Speed is warming up to 1450 DEG C, 1000 DEG C is cooled to after 1450 DEG C are incubated 1.5h, then with 1.5 DEG C/min speed, then again with 4
DEG C/min speed is cooled to 25 DEG C, produce.
Wherein, it is formulated by mass percentage, including：
Tourmaline 25%, aerolite 2%, stone needle 7%, medical stone 18%, germanite 6%, silica 1 0%, titanium dioxide
0.5%, calcium oxide 2.5%, kaolin 11%, di-iron trioxide 2.5%, zinc oxide 2.5%, neodymium 2.5%, boron 2.5%, and
Magnesia 8%.
Embodiment 6
A kind of water, it is made by any one embodiment in embodiment 1~5.
Embodiment 7
A kind of health products for treating rheumatic arthritis, including the water that embodiment 6 provides.
Embodiment 8
A kind of health products for treating goat, including the water that embodiment 6 provides.
Embodiment 9
A kind of health products for treating type II diabetes, including the water that embodiment 6 provides.
Test example 1
Using the method for processing water provided by the invention, pending water immersion is provided with the container of quantum ceramics
20min processing, to the micel of the water after pending water and processing, respectively NMR detection water, using height
The magnetic of this meter detection quantum ceramics, the hydrogen content of water is detected using protium detector, is detected using noctovisor scan instrument
The infrared ray of quantum ceramics, the negative potential of water, and the pH value using pH value reagent detection water are detected using ORP value detector.
As a result it is as follows：
The quantum ceramics can be lasting the Gauss of generation 2 magnetic force and 6~14 microns of infrared ray.Use quantum ceramics
Physical treatment is carried out to water, the negative hydrogen particle in water is brought up to more than 1.2PPM/L by 0PPM/L, meanwhile, original by 13
The molecular macromolecular mass water of~16 moisture, 6~9 hydrone composition small-micelle waters are quickly changed to, effectively make water
It is 7.5~8.8 that pH value, which is improved to pH, and it is in alkalescent to make water, while handle changes ORP (current potential) values by original+180~250
Between -100~220, make the water after processing that there is higher activity, be more convenient for absorbing and health-care effect is good.
Test example 2
Zhang, man, 58 years old.
Suffer from goat to have a surplus for 10 years, drink the water provided by the invention after quantum ceramics processing three times daily, simultaneously
Taken medicine, had an injection according to medication custom before and custom of having an injection, after one month, the state of an illness has taken a turn for the better, and reduces simultaneously
Dosage and the amount of having an injection, discontinue medication, effective relief of symptoms, fully recovered after drinking half a year, so far after continuously drinking three months
Do not recur.
Mr. Wang, female, 39 years old.
Suffer from rheumatic arthritis to have a surplus for 6 years.The water provided by the invention after quantum ceramics processing three times is being drunk daily, together
When taken medicine, had an injection according to medication custom before and custom of having an injection, after drinking two months, the state of an illness has taken a turn for the better, and subtracts
Few dosage and the amount of having an injection, continuously drink three months, withdrawal and have an injection, effectively slow after continuously drinking five months
Solution, fully recover after continuously drinking 8 months, do not recur so far.
Yang, man, 48 years old.
Suffer from type II diabetes to have a surplus for 10 years, constantly take antidiabetic drug during one's sickness.
The water provided by the invention after quantum ceramics processing three times is being drunk daily, while takes the hypoglycemic taken before
On the basis of medicine, the state of an illness has taken a turn for the better, and the dose of antidiabetic drug gradually reduces after first month, after continuously drinking two months,
Withdrawal, after being used continuously three months, effectively alleviate, blood sugar recovery is normal after drinking 1 year, does not recur so far.
Mr. Wang, female, 36 years old.
Suffer from type II diabetes to have a surplus for 5 years.Period constantly takes antidiabetic drug.
The water provided by the invention after quantum ceramics processing three times is being drunk daily, while takes the antidiabetic drug taken before
On the basis of, the state of an illness has taken a turn for the better, and antidiabetic drug cuts out antidiabetic drug after taking medicine 15 days, after continuously drinking two months, the state of an illness
It has been taken a turn for the better that, blood sugar recovery is normal after continuously drinking 9 months, does not recur so far.
Embodiments described above is part of the embodiment of the present invention, rather than whole embodiments.The reality of the present invention
The detailed description for applying example is not intended to limit the scope of claimed invention, but is merely representative of the selected implementation of the present invention
Example.Based on the embodiment in the present invention, what those of ordinary skill in the art were obtained under the premise of creative work is not made
Every other embodiment, belongs to the scope of protection of the invention.
Claims (10)
- A kind of 1. method for handling water, it is characterised in that water is placed in the container provided with quantum ceramics obtained by least 10min；The quantum ceramics are after by formula, raw material is mixed, and under nitrogen atmosphere, gained is cooled down after sintering；It is described to be formulated according to mass percent meter, including：Tourmaline 25%~36%, aerolite 1%~3%, stone needle 7%~ 14%, medical stone 7%~25%, germanite 5%~10%, silica 6%~13%, titanium dioxide 0.5%~3.5%, oxygen Change calcium 1~5%, kaolin 7%~12%, di-iron trioxide 0.5%~3%, zinc oxide 0.5%~3%, neodymium 0.5%~ 3%, boron 0.5%~3%, and magnesia 6%~12%.
- 2. the method for processing water according to claim 1, it is characterised in that the formula is according to mass percent meter, bag Include：The tourmaline 26%~36%, the aerolite 1%~3%, the stone needle 9%~10%, the medical stone 8%~ 22%, the germanite 7%~8%, the silica 8%~11%, the titanium dioxide 1%~2%, the calcium oxide 2 ~3%, the kaolin 9%~10%, the di-iron trioxide 1%~3%, the zinc oxide 1%~3%, the neodymium 1% ~3%, the boron 1%~3%, and the magnesia 8%~10%.
- 3. the method for processing water according to claim 1, it is characterised in that be incubated 0.3 at 640~660 DEG C before sintering ~0.7h.
- 4. the method for processing water according to claim 3, it is characterised in that sintering includes first stage and second stage, First stage is：1000 DEG C first are warming up to 2~3 DEG C/min speed, then 1450 are warming up to 0.5~1 DEG C/min speed DEG C~1500 DEG C.
- 5. it is according to claim 4 processing water method, it is characterised in that second stage be at 1450 DEG C~1500 DEG C, It is incubated 0.5~1.5h.
- 6. the method for processing water according to claim 1, it is characterised in that cooling includes：First with 1~2 DEG C/min speed Degree is cooled to 1000 DEG C, is then cooled to 20~35 DEG C again with 3~5 DEG C/min speed.
- 7. the method for processing water according to claim 1, it is characterised in that the raw material is crushed to 410 before sintering ~480 mesh.
- 8. water made from the method for the processing water as described in claim 1~7 any one.
- 9. application of the water as claimed in claim 8 in health products.
- 10. application according to claim 9, the health products are the health products for the treatment of rheumatic arthritis, treatment gout The health products of disease or the health products for treating type II diabetes.