CN106473094A - A kind of sintering hydrogen manufacturing activated material - Google Patents
A kind of sintering hydrogen manufacturing activated material Download PDFInfo
- Publication number
- CN106473094A CN106473094A CN201610849560.3A CN201610849560A CN106473094A CN 106473094 A CN106473094 A CN 106473094A CN 201610849560 A CN201610849560 A CN 201610849560A CN 106473094 A CN106473094 A CN 106473094A
- Authority
- CN
- China
- Prior art keywords
- activated material
- hydrogen
- sintering
- hydrogen manufacturing
- liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of sintering hydrogen manufacturing activated material, include magnesium powder, tourmaline powder, diatomite, land plaster and cellulose, the sintering hydrogen manufacturing activated material can produce hydrogen in a liquid, the liquid includes water, wine, tea, vinegar, soy sauce, fruit juice, milk and soya-bean milk, the sintering hydrogen manufacturing activated material of the present invention can be soaked half an hour in the drinking water for daily intaking or beverage, the hydrogen of more than concentration 800ppb can just be produced, liquid of the positive potential in oxidizing property is escalated into negative potential in reducing property, do not change in eating habit and reach oxidation-resisting health-care effect.
Description
Technical field
The present invention relates to a kind of sintering hydrogen manufacturing activated material.
Background technology
Why iron can get rusty, people why can aging, be all oxidized result.The 1950's, Hamann doctor
Aging free-radical theory is proposed, medical research over 60 years demonstrates this theory.A lot of diseases, including including aging be all due to
The free radical that cylinder accumulation cannot be removed in time is caused.Free radical is that human body cell produces a class very in metabolic process
Vivaciously, there is the chemical substance of very strong oxidation, be also active oxygen.Free radical is attacked life macromolecule and histocyte can be caused to damage
Wound, is the basic reason for causing body aging, and the important cause of the malignant disease such as induced tumor.Excessive active oxygen freedom
Base can produce destruction, cause the damage of human normal cell and tissue, so as to cause multiple diseases, such as heart disease, old age
Dementia, Parkinson's and tumour etc..Additionally, solar irradiation in external environment, air pollution, flue dust, agricultural chemicals etc. can all promote
Make human body that more active oxygen radicals are produced, cause nucleic acid mutation, this is mankind aging and ill root.And the water of hydrogen
Have and remove biological interior free yl.Inherently a kind of good antioxidant of hydrogen, because hydrogen molecule is very micro-
Carefully, internal energy rapid osmotic is entered to whole body, and penetration cell film, the central pernicious active oxygen for being difficult and eliminating is taken away, is closed
Cheng Shui is excreted, without affecting the running of other benign activity oxygen and body function.Above all can destroyed and
Oxidized cell restores." hydrogen " in water such as ties up him with most strong reducing power, most of antioxidant that we often eat
Life C, is not easy to through cell membrane, and pointedly only pernicious active oxygen can not be eliminated, and still more eats a large amount of vitamins,
Also it is difficult to internal storage and absorbs.
The hydrogen molecule medical science of fast development in recent years, water are the best carriers of hydrogen.Hydrogen rich water manufacturing technology mainly has at present
Three kinds below:One is that strong electrolytic hydrogen production is also named DC electrolysis water hydrogen manufacturing;Two is hydrogen high pressure to be filled with water to make hydrogen rich water;Three
It is non-electrolytic hydrogen production material technology.
DC electrolysis hydrogen producing technology is to do electrode material using platinum, and be passed through direct current carries out forceful electric power solution manufacture hydrogen to water
Gas.Due to controlling using noble metal electrode and circuit board, so manufacturing cost is of a relatively high, cause product price also higher, no
Beneficial to popularization.Meanwhile, the accessory substances such as ozone and hydrogen peroxide are also easy to produce during forceful electric power solution water, cause hydrogen water to have peculiar smell.If
In mineral water, sodium chloride, calcium chloride, content of magnesium chloride are high, can be electrolysed out chlorine, are electrolyzed to produce disinfectant, oxidation water.
Hydrogen is filled with water and is prepared into hydrogen rich water.But the maximum problem of the technology is the volatile problem of hydrogen, and has one
Fixed is ageing.As the penetration of hydrogen is especially strong, glass and plastic bottle can be leaked, and can only be packed using aluminum foil material, packaging
Cost is more than water, and price is too high, is equally unfavorable for popularization.
Non-electrolytic hydrogen manufacturing is reacted using magnesium grain, MAG block and water, generates magnesium hydroxide and hydrogen.Hydrogen manufacturing is convenient and swift, can
So that hot water is used, Chinese drinking habit is more conformed to.Advantage is low cost, has the disadvantage the oxidizable blackening of magnesium grain, causes work(
The problems such as failing, and easily separate out sediment, the easily hardened, poor taste of appearance in water, needs warp to commonly use light-coloured vinegar and soak and regenerates,
Consumer's Experience is bad.
The material of the present invention, will be multiple to 99.99% magnesium powder of purity and the material such as tourmaline powder, diatomite, land plaster, cellulose
Close to bakee through low temperature and porous material is formed, slow down the speed with water reaction, service life is extended, use cost is lower.
Content of the invention
The technical problem to be solved in the present invention is to provide one kind to produce hydrogen in a liquid, improves the original of liquor quality
Material and the sintering hydrogen manufacturing activated material of object.
For solving the above problems, the present invention is adopted the following technical scheme that:
A kind of sintering hydrogen manufacturing activated material, includes magnesium powder, tourmaline powder, diatomite, land plaster and cellulose, the sintering system
Hydrogen activated material can produce hydrogen in a liquid, and the liquid includes water, wine, tea, vinegar, soy sauce, fruit juice, milk and beans
Slurry.
The preparation technology of sintering hydrogen manufacturing activated material, comprises the following steps:
1)By mass fraction proportioning by 10 parts of tourmaline fine powders, the magnesium powder of 80 part of 99.99% purity, 10 parts of diatomite and 100 parts of stones
Cream powder stirs becomes a kind of dry powder of composite;
2)2-5 part cellulose and water are mixed 12 hours by mass fraction proportioning, be made into binding liquid;
3)Step 1)The dry powder of gained composite and step 2)Gained binding liquid mixes, and is then sufficiently stirred for again, at 3 points
Stirring is completed in clock, obtains mixed serum;
4)Step 3)Gained mixed serum is fed in mould, is treated 20 minutes, deviates from mould, obtain stock after slurry solidification,
After drying under stock normal temperature, low-temperature sintering to 250 degree, it is incubated 2 hours;
5)After naturally ringing to room temperature, come out of the stove, with the dust on clean water surface, dried after drying again.
Beneficial effects of the present invention are:First, can be by stoste(The liquid includes water, wine, tea, vinegar, soy sauce, fruit juice, ox
Milk, soya-bean milk)Molecular cluster diminishes, and strengthens penetration, dissolving power, emulsifying ability, extension and the cleaning strength of liquid, helps human body suction
Receive;2nd, the pH value of stoste is lifted(Acid-base value alkali is moved), help neutralization acidic toxins;3rd, reduce the ORP value of stoste(Redox
Current potential becomes negative potential from positive potential), help and harmful free radical removed, play oxidation resistant purpose.
Specific embodiment
A kind of sintering hydrogen manufacturing activated material, includes magnesium powder, tourmaline powder, diatomite, land plaster and cellulose, the burning
Knot hydrogen manufacturing activated material can produce hydrogen in a liquid, and the liquid includes water, wine, tea, vinegar, soy sauce, fruit juice, milk
And soya-bean milk.
The preparation technology of sintering hydrogen manufacturing activated material, comprises the following steps:
1)By mass fraction proportioning by 10 parts of tourmaline fine powders, the magnesium powder of 80 part of 99.99% purity, 10 parts of diatomite and 100 parts of stones
Cream powder stirs becomes a kind of dry powder of composite;
2)2-5 part cellulose and water are mixed 12 hours by mass fraction proportioning, be made into binding liquid;
3)Step 1)The dry powder of gained composite and step 2)Gained binding liquid mixes, and is then sufficiently stirred for again, at 3 points
Stirring is completed in clock, obtains mixed serum;
4)Step 3)Gained mixed serum is fed in mould, is treated 20 minutes, deviates from mould, obtain stock after slurry solidification,
After drying under stock normal temperature, low-temperature sintering to 250 degree, it is incubated 2 hours;
5)After naturally ringing to room temperature, come out of the stove, with the dust on clean water surface, dried after drying again.
In actual process, 50 grams of composites can process 600 liters of water.Through Guangdong Province's marine drug emphasis experiment
Room detects that 17 Isotopes magnetic resonance of control water oxygen, half high fabric width is 94.96Hz, soaks material of the present invention 10 minutes, becomes
51.24Hz, illustrates the molecular cluster of water diminishes;Detect through Shanghai Wei Pu Chemical Engineering Technology Services Co., Ltd, compare water oxygen
Reduction potential is+109mv, in positive potential, is oxidation water, soaks proprietary material of the present invention 10 minutes, become -335mv, in negative electricity
Position, is reductive water.The water of negative potential and liquid, can remove " body rust ", play the effect of anti-aging.
Beneficial effects of the present invention are:First, can be by stoste(The liquid includes water, wine, tea, vinegar, soy sauce, fruit juice, ox
Milk, soya-bean milk)Molecular cluster diminishes, and strengthens penetration, dissolving power, emulsifying ability, extension and the cleaning strength of liquid, helps human body suction
Receive;2nd, the pH value of stoste is lifted(Acid-base value alkali is moved), help neutralization acidic toxins;3rd, reduce the ORP value of stoste(Redox
Current potential becomes negative potential from positive potential), help and harmful free radical removed, play oxidation resistant purpose.
The above, the only specific embodiment of the present invention, but protection scope of the present invention is not limited thereto, and any
The change or replacement that expects without creative work, should all be covered by within protection scope of the present invention.
Claims (2)
1. one kind sinters hydrogen manufacturing activated material, it is characterised in that:Include magnesium powder, tourmaline powder, diatomite, land plaster and fiber
Element, the sintering hydrogen manufacturing activated material can produce hydrogen in a liquid, the liquid include water, wine, tea, vinegar, soy sauce,
Fruit juice, milk and soya-bean milk.
2. as claimed in claim 1 sintering hydrogen manufacturing activated material preparation technology, it is characterised in that:Comprise the following steps:
1)By mass fraction proportioning by 10 parts of tourmaline fine powders, the magnesium powder of 80 part of 99.99% purity, 10 parts of diatomite and 100 parts of stones
Cream powder stirs becomes a kind of dry powder of composite;
2)2-5 part cellulose and water are mixed 12 hours by mass fraction proportioning, be made into binding liquid;
3)Step 1)The dry powder of gained composite and step 2)Gained binding liquid mixes, and is then sufficiently stirred for again, at 3 points
Stirring is completed in clock, obtains mixed serum;
4)Step 3)Gained mixed serum is fed in mould, is treated 20 minutes, deviates from mould, obtain stock after slurry solidification,
After drying under stock normal temperature, low-temperature sintering to 250 degree, it is incubated 2 hours;
5)After naturally ringing to room temperature, come out of the stove, with the dust on clean water surface, dried after drying again.