CN107352869A - 高性能轻质高强防水找平系统 - Google Patents
高性能轻质高强防水找平系统 Download PDFInfo
- Publication number
- CN107352869A CN107352869A CN201710572795.7A CN201710572795A CN107352869A CN 107352869 A CN107352869 A CN 107352869A CN 201710572795 A CN201710572795 A CN 201710572795A CN 107352869 A CN107352869 A CN 107352869A
- Authority
- CN
- China
- Prior art keywords
- strength
- layer
- waterproofing
- water
- leveling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高性能轻质高强防水找平系统，包括：基层墙体、轻质高强防水找平底层、轻质高强防水找平面层、腻子层和涂料层，所述的基层墙体的外表面上从内往外依次设置有所述的轻质高强防水找平底层、轻质高强防水找平面层、腻子层和涂料层。本发明的轻质高强防水找平底层和轻质高强防水找平面层替代了传统的找平砂浆与防水砂浆，同时轻质高强防水找平底层、涂料层均可兼具保温隔热作用，替代传统保温层构造，既简化了工序又具有较高的经济性。
Description
技术领域
本发明涉及墙体材料领域，特别是涉及一种高性能轻质高强防水找平系统。
背景技术
目前传统建筑外墙做法是基层墙体的外表面上从内往外依次设置有预拌砂浆找平、防水砂浆、保温层、抗裂防护层、腻子层和涂料层，建筑外墙外保温及装饰工程普遍存在不同程度的开裂、渗水、空鼓、脱落等质量问题，往往交付使用几年内就出现质量问题需要翻新修复，不仅严重破坏了建筑物的外观和节能效果，还大大降低了建筑物的寿命以及居住者的生活质量。
发明内容
本发明主要解决的技术问题是提供一种高性能轻质高强防水找平系统，兼具找平、防水、保温的功能，可以替代传统保温层构造，既质量可靠又可降低工程造价。
为解决上述技术问题，本发明采用的一个技术方案是：提供一种高性能轻质高强防水找平系统，包括：基层墙体、轻质高强防水找平底层、轻质高强防水找平面层、腻子层和涂料层，所述的基层墙体的外表面上从内往外依次设置有所述的轻质高强防水找平底层、轻质高强防水找平面层、腻子层和涂料层。
在本发明一个较佳实施例中，所述的轻质高强防水找平底层由以下重量配比的原料组成：硅酸盐水泥25~45%，粉煤灰0~15%，中粗砂40~60%，保水剂0.03~0.07%，触变剂0~0.5%，憎水剂 0.1~0.5%，纤维0.1~0.3%，可再分散乳胶粉3~6%，轻骨料为余量。
在本发明一个较佳实施例中，所述的保水剂为甲基纤维素醚、乙基纤维素醚和丙基纤维素醚中的一种，触变剂为凹凸棒土和膨润土中的一种，憎水剂为硅烷基、硅氧烷基和脂肪酸金属盐憎水剂中的一种，所述的纤维为矿物纤维、聚酯纤维和聚丙烯纤维中的一种或多种，可再分散乳胶粉为丙烯酸乳胶粉和醋酸乙烯乳胶粉中的一种。
在本发明一个较佳实施例中，所述的轻质高强防水找平面层由以下重量配比的原料组成：硅酸盐水泥15~25%，细砂40~60%，丙烯酸乳胶粉15~20%，憎水剂0.5~1.5%，消泡剂0.02~0.04%，减水剂0.01~0.04%，活性掺和料为余量。
在本发明一个较佳实施例中，所述的活性掺和料为硅灰和偏高岭土中的一种，所述的憎水剂为硅烷基、硅氧烷基和脂肪酸金属盐憎水剂中的一种，减水剂为聚羧酸、萘系和密胺系中的一种。
在本发明一个较佳实施例中，所述的腻子层为普通腻子层。
在本发明一个较佳实施例中，所述的涂料层为普通涂料层或反射隔热涂料层。
在本发明一个较佳实施例中，所述的反射隔热涂料层由以下重量配比的原料组成：丙烯酸乳液30~45%，第一填料10~15%，颜料0~8%，第二填料10~20%，醇酯-12 0.8~1.5%，增稠剂 0.2~0.4%，消泡剂0.3~0.4%，分散剂0.5~0.8%，氨水0.01~0.05%，水为余量。
在本发明一个较佳实施例中，所述的第一填料为改性钛白粉、隔热粉和中空微珠中的一种或多种，第二填料为重钙、云母粉、高岭土、滑石粉和轻钙中的一种或多种，增稠剂为纤维素醚、碱溶胀增稠剂和聚酯改性增稠剂中的一种或多种。
本发明的有益效果是：本发明的轻质高强防水找平底层和轻质高强防水找平面层替代了传统的找平砂浆与防水砂浆，同时轻质高强防水找平底层、涂料层均可兼具保温隔热作用，替代传统保温层构造，既简化了工序又具有较高的经济性。
附图说明
为了更清楚地说明本发明实施例中的技术方案，下面将对实施例描述中所需要使用的附图作简单地介绍，显而易见地，下面描述中的附图仅仅是本发明的一些实施例，对于本领域普通技术人员来讲，在不付出创造性劳动的前提下，还可以根据这些附图获得其它的附图，其中：
图1是本发明高性能轻质高强防水找平系统一较佳实施例的结构示意图；
附图中各部件的标记如下：1、基层墙体，2、轻质高强防水找平底层，3、轻质高强防水找平面层，4、腻子层，5、涂料层。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
请参阅图1，实施例1
一种高性能轻质高强防水找平系统，包括：基层墙体1、轻质高强防水找平底层2、轻质高强防水找平面层3、腻子层4和涂料层5，所述的基层墙体1的外表面上从内往外依次设置有所述的轻质高强防水找平底层2、轻质高强防水找平面层3、腻子层4和涂料层5，所述的轻质高强防水找平底层2的厚度为3cm，所述的轻质高强防水找平面层3的厚度为3mm，所述的腻子层4为普通腻子层，所述的普通腻子层的厚度为3mm，所述的涂料层5的厚度为0.9mm。
所述的轻质高强防水找平底层2由以下重量配比的原料组成：硅酸盐水泥25%，粉煤灰15%，中粗砂40%，甲基纤维素醚保水剂0.03%，硅烷基憎水剂 0.1%，矿物纤维0.1%，丙烯酸乳胶粉3%，轻骨料16.77%。
所述的轻质高强防水找平面层3由以下重量配比的原料组成：硅酸盐水泥20%，细砂60%，丙烯酸乳胶粉15%，硅烷基憎水剂0.5%，消泡剂0.02%，聚羧酸减水剂0.01%，硅灰活性掺和料为4.47%。
所述的涂料层5为反射隔热涂料层，所述的反射隔热涂料层5由以下重量配比的原料组成：丙烯酸乳液37%，改性钛白粉12%，颜料5%，重钙15%，醇酯-12 1.2%，纤维素醚增稠剂0.3%，消泡剂0.4%，分散剂0.7%，氨水0.03%，水为余量。
请参阅图1，实施例2
一种高性能轻质高强防水找平系统，包括：基层墙体1、轻质高强防水找平底层2、轻质高强防水找平面层3、腻子层4和涂料层5，所述的基层墙体1的外表面上从内往外依次设置有所述的轻质高强防水找平底层2、轻质高强防水找平面层3、腻子层4和涂料层5，所述的轻质高强防水找平底层2的厚度为3cm，所述的轻质高强防水找平面层3的厚度为5mm，所述的腻子层4为普通腻子层，所述的普通腻子层的厚度为2mm，所述的涂料层5的厚度为0.2mm。
所述的轻质高强防水找平底层2由以下重量配比的原料组成：硅酸盐水泥45%，中粗砂50%，乙基纤维素醚保水剂0.07%，膨润土触变剂0.5%，硅氧烷基憎水剂 0.5%，聚酯纤维0.3%，醋酸乙烯乳胶粉3.63%。
所述的轻质高强防水找平面层3由以下重量配比的原料组成：硅酸盐水泥15%，细砂50%，丙烯酸乳胶粉15%，硅氧烷基憎水剂0.8%，消泡剂0.03%，萘系减水剂0.03%，偏高岭土活性掺和料为19.14%。
所述的涂料层5为反射隔热涂料层，所述的反射隔热涂料层5由以下重量配比的原料组成：丙烯酸乳液30%，隔热粉15%，颜料8%，云母粉20%，醇酯-12 1.5%，碱溶胀增稠剂0.4%，消泡0.4%，分散剂0.8%，氨水0.05%，水为余量。
请参阅图1，实施例3
一种高性能轻质高强防水找平系统，包括：基层墙体1、轻质高强防水找平底层2、轻质高强防水找平面层3、腻子层4和涂料层5，所述的基层墙体1的外表面上从内往外依次设置有所述的轻质高强防水找平底层2、轻质高强防水找平面层3、腻子层4和涂料层5，所述的轻质高强防水找平底层2的厚度为2.5cm，所述的轻质高强防水找平面层3的厚度为4mm，所述的腻子层4为普通腻子层，所述的普通腻子层的厚度为2.5mm，所述的涂料层5的厚度为0.6mm。
所述的轻质高强防水找平底层2由以下重量配比的原料组成：硅酸盐水泥30%，粉煤灰3%，中粗砂60%，丙基纤维素醚保水剂0.05%，凹凸棒土触变剂0.3%，脂肪酸金属盐憎水剂 0.3%，聚丙烯纤维0.2%，丙烯酸乳胶粉5%，轻骨料1.15%。
所述的轻质高强防水找平面层3由以下重量配比的原料组成：硅酸盐水泥25%，细砂40%，丙烯酸乳胶粉18%，脂肪酸金属盐憎水剂1.5%，消泡剂0.04%，密胺系减水剂0.04%，硅灰活性掺和料为15.42%。
所述的涂料层5为反射隔热涂料层，所述的反射隔热涂料层5由以下重量配比的原料组成：丙烯酸乳液45%，中空微珠10%，滑石粉10%，醇酯-12 0.8%，聚酯改性增稠剂 0.2%，消泡剂0.3%，分散剂0.5%，氨水0.01%，水为余量。
本发明高性能轻质高强防水找平系统的有益效果是：本发明的轻质高强防水找平底层和轻质高强防水找平面层替代了传统的找平砂浆与防水砂浆，同时轻质高强防水找平底层、涂料层均可兼具保温隔热作用，替代传统保温层构造，既简化了工序又具有较高的经济性。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其它相关的技术领域，均同理包括在本发明的专利保护范围内。
Claims (9)
1.一种高性能轻质高强防水找平系统，其特征在于，包括：基层墙体、轻质高强防水找平底层、轻质高强防水找平面层、腻子层和涂料层，所述的基层墙体的外表面上从内往外依次设置有所述的轻质高强防水找平底层、轻质高强防水找平面层、腻子层和涂料层。
2.根据权利要求1所述的高性能轻质高强防水找平系统，其特征在于，所述的轻质高强防水找平底层由以下重量配比的原料组成：硅酸盐水泥25~45%，粉煤灰0~15%，中粗砂40~60%，保水剂0.03~0.07%，触变剂0~0.5%，憎水剂 0.1~0.5%，纤维0.1~0.3%，可再分散乳胶粉3~6%，轻骨料为余量。
3.根据权利要求2所述的高性能轻质高强防水找平系统，其特征在于，所述的保水剂为甲基纤维素醚、乙基纤维素醚和丙基纤维素醚中的一种，触变剂为凹凸棒土和膨润土中的一种，憎水剂为硅烷基、硅氧烷基和脂肪酸金属盐憎水剂中的一种，所述的纤维为矿物纤维、聚酯纤维和聚丙烯纤维中的一种或多种，可再分散乳胶粉为丙烯酸乳胶粉和醋酸乙烯乳胶粉中的一种。
4.根据权利要求1所述的高性能轻质高强防水找平系统，其特征在于，所述的轻质高强防水找平面层由以下重量配比的原料组成：硅酸盐水泥15~25%，细砂40~60%，丙烯酸乳胶粉15~20%，憎水剂0.5~1.5%，消泡剂0.02~0.04%，减水剂0.01~0.04%，活性掺和料为余量。
5.根据权利要求4所述的高性能轻质高强防水找平系统，其特征在于，所述的活性掺和料为硅灰和偏高岭土中的一种，所述的憎水剂为硅烷基、硅氧烷基和脂肪酸金属盐憎水剂中的一种，减水剂为聚羧酸、萘系和密胺系中的一种。
6.根据权利要求1所述的高性能轻质高强防水找平系统，其特征在于，所述的腻子层为普通腻子层。
7.根据权利要求1所述的高性能轻质高强防水找平系统，其特征在于，所述的涂料层为普通涂料层或反射隔热涂料层。
8.根据权利要求7所述的高性能轻质高强防水找平系统，其特征在于，所述的反射隔热涂料层由以下重量配比的原料组成：丙烯酸乳液30~45%，第一填料10~15%，颜料0~8%，第二填料10~20%，醇酯-12 0.8~1.5%，增稠剂 0.2~0.4%，消泡剂0.3~0.4%，分散剂0.5~0.8%，氨水0.01~0.05%，水为余量。
9.根据权利要求8所述的高性能轻质高强防水找平系统，其特征在于，所述的第一填料为改性钛白粉、隔热粉和中空微珠中的一种或多种，第二填料为重钙、云母粉、高岭土、滑石粉和轻钙中的一种或多种，增稠剂为纤维素醚、碱溶胀增稠剂和聚酯改性增稠剂中的一种或多种。