CN107351488A - 一种保温防潮指接板材 - Google Patents
一种保温防潮指接板材 Download PDFInfo
- Publication number
- CN107351488A CN107351488A CN201710581481.3A CN201710581481A CN107351488A CN 107351488 A CN107351488 A CN 107351488A CN 201710581481 A CN201710581481 A CN 201710581481A CN 107351488 A CN107351488 A CN 107351488A
- Authority
- CN
- China
- Prior art keywords
- contiguous block
- mounting groove
- adhesive linkage
- sheet material
- finger
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种保温防潮指接板材，包括依次设置的面板层、芯板层、底板层，所述底板层的底部设有第二粘接层，所述芯板层的两面对称设有安装槽，所述安装槽底端的表面设有第一粘接层；所述面板层的底面对称设有第一连接块，所述底板层的表面对称设有第二连接块；所述第一连接块与安装槽配合连接，所述第二连接块与安装槽配合连接。本发明具有防水性好，并且在潮湿环境下，不变形、不发生翘曲、不开裂，使用寿命长，可广泛用于墙面、地面等多种场景。
Description
技术领域
本发明具体涉及一种保温防潮指接板材。
背景技术
指接板材由一定数量相同的树种、相同截面尺寸的长短不一木料，沿着纵向指接长料，通过加工成板材。该板材的原材料是通过圆盘锯把木材横截，把纤维截短，边、心、根、梢部位重新自然组合，使木材天然缩胀的不均匀性得到改善，故该板材在使用中纵向变形大大地缩小，不易出现扭、弯、瓢、裂等不良现象。由于指接板材纵向尺寸加长，既不易变形，又提高了铺设效率，缩短工期。在木材资源越来越紧张的情况下不浪费资源，既做到环保又合理利用了资源。由于指接板材的强度和外观质量获得了改进，因而受到了广大消费者的认可，然而由于受到拼接强度的限制，容易受潮而产生涨缩、翘曲、开裂等现象。为此，现有的防护措施是在木质基材的背面涂覆一层防水薄膜或者防水涂料。虽然能起到防潮作用，但是当长时间处于潮湿或积水的环境下，仍不可避免的发生变形、翘曲以及开裂等现象。
发明内容
有鉴于此，本发明提供一种保温防潮指接板材，具有防水性好，并且在潮湿环境下，不变形、不发生翘曲、不开裂，使用寿命长，可广泛用于墙面、地面等多种场景。
本发明的技术方案为：一种保温防潮指接板材,包括依次设置的面板层、芯板层、底板层，所述底板层的底部设有第二粘接层，所述芯板层的两面对称设有安装槽，所述安装槽底端的表面设有第一粘接层；所述面板层的底面对称设有第一连接块，所述底板层的表面对称设有第二连接块；所述第一连接块与安装槽配合连接，所述第二连接块与安装槽配合连接。
进一步的，所述安装槽的水平截面为等腰梯形。
进一步的，所述第一连接块的两侧对称设有弧形突块。所述第二连接块的两侧对称设有弧形突块。
进一步的，所述安装槽两侧的表面对称设有弓形槽。本发明中的弓形槽，具有排湿透气、以及与弧形突块配合固定的作用。
特别的，所述弧形突块为膨体纱突块。膨体纱是先由两种不同收缩率的纤维混纺成纱线，然后将纱线放在蒸汽或热空气或沸水中处理，此时，收缩率高的纤维产生较大收缩，位于纱的中心，而混在一起的低收缩纤维，由于收缩小，而被挤压在纱线的表面形成圈形，从而得到蓬松、丰满、富有弹性的膨体纱。本发明采用的膨体纱突块，内部均匀排布有活性炭颗粒，防潮防霉，基于其丰富的弹性，可以与安装槽的弓形槽配合，锁紧固定，同时避免硬力作用使板材内部变形，对复合板材提供保护。
通过第一粘接层分别与第一连接块和第二连接块、第一连接块与安装槽、第二连接块与安装槽的配合连接，再结合弧形突块过盈配合的作用，可以保证本发明连接的密封性、高度配合性能，有效提高产品的质量。
进一步的，所述面板层表面设有耐磨涂层。
进一步的，所述耐磨涂层包括以下重量份数的组分：九水合硝酸铝28-35、正硅酸乙酯13-18、无水乙醇10-14、氟烯烃5-8、叔丁基乙烯醚2-5、羟丁基乙烯醚0.7-1.6、丙烯酸树脂11-15、氯代三氟乙烯0.2-0.6。
本发明的耐磨涂层可有效提高木板层的涂层附着力和耐刮力，同时节省了耐磨涂层的涂料用量，可节约生产成本。本发明的耐磨涂层可均匀细腻的附着在木板层的表面，使得涂覆的木板表面更加美观。
进一步的，所述第一粘接层包括以下重量份数的组分：纳米级铜粉1.2-1.9、甘露醇0.22-0.37、尼龙粉0.07-0.13、咪唑硅烷22-32、聚乙烯醇15-19。特别的，所述第一粘接层与第二粘接层的组成一致。
本发明的第一粘接层、第二粘接层不含甲醛；在使用本发明的不含甲醛的粘接层生产实木复合板材时，安全环保。本发明的复合板材用粘接层粘接力强，制得的实木复合板材的剪切强度高，测试证明，即使将木材与木材或其他材料的连接破坏掉，也难以将通过该粘接层粘接在一起的两层单板分离开；本发明复合板材具有良好的耐高温和防水性能；本发明是一种环保板材，不会污染室内环境，有益于人们的身体健康。
本发明使用木板材企业生产中的边角料拼接而成的指接板为原料制作具有良好耐磨和防水性能的实木板材，提高了木材的利用率，使得珍贵的实木资源得到了最大限度的充分利用；本发明以指接板为基板，在其上下依次设置的各材料层，并使相邻各层之间的纤维纵横向交错排列，增加了板材纵横向的强度；同时在芯板层的两面均设置安装槽，并将将第一连接块、第二连接块分别深入指接板内，从而获得了具有高抗变形力的板材。本发明的基板间可实现形成无缝隙的结合，即保证了结合强度，提供了足够的耐磨性，又能有效防止水分渗入；本发明的板材结构简单，易于制备，且成本较低，适于工业化规模生产。
附图说明
图1为本发明的结构示意图；
图2为本发明的局部结构示意图。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
一种保温防潮指接板材,包括依次设置的面板层1、芯板层2、底板层3，所述底板层3的底部设有第二粘接层31，所述芯板层2的两面对称设有安装槽21，所述安装槽21底端的表面设有第一粘接层211；所述面板层1的底面对称设有第一连接块12，所述底板层3的表面对称设有第二连接块32；所述第一连接块12与安装槽21配合连接，所述第二连接块32与安装槽21配合连接。
进一步的，所述安装槽21的水平截面为等腰梯形。
进一步的，所述第一连接块12的两侧对称设有弧形突块4。所述第二连接块32的两侧对称设有弧形突块4。
进一步的，所述安装槽21两侧的表面对称设有弓形槽212。本发明中的弓形槽212，具有排湿透气、以及与弧形突块4配合固定的作用。
特别的，所述弧形突块4为膨体纱突块。膨体纱是先由两种不同收缩率的纤维混纺成纱线，然后将纱线放在蒸汽或热空气或沸水中处理，此时，收缩率高的纤维产生较大收缩，位于纱的中心，而混在一起的低收缩纤维，由于收缩小，而被挤压在纱线的表面形成圈形，从而得到蓬松、丰满、富有弹性的膨体纱。本发明采用的膨体纱突块，内部均匀排布有活性炭颗粒，防潮防霉，基于其丰富的弹性，可以与安装槽21的弓形槽212配合，锁紧固定，同时避免硬力作用使板材内部变形，对复合板材提供保护。
通过第一粘接层211分别与第一连接块12和第二连接块32、第一连接块12与安装槽21、第二连接块32与安装槽21的配合连接，再结合弧形突块4过盈配合的作用，可以保证本发明连接的密封性、高度配合性能，有效提高产品的质量。
进一步的，所述面板层1表面设有耐磨涂层11。
进一步的，所述耐磨涂层11包括以下重量份数的组分：九水合硝酸铝31、正硅酸乙酯15、无水乙醇12、氟烯烃7、叔丁基乙烯醚3、羟丁基乙烯醚0.9、丙烯酸树脂13、氯代三氟乙烯0.45。
本发明的耐磨涂层11可有效提高木板层的涂层附着力和耐刮力，同时节省了耐磨涂层11的涂料用量，可节约生产成本。本发明的耐磨涂层11可均匀细腻的附着在木板层的表面，使得涂覆的木板表面更加美观。
进一步的，所述第一粘接层211包括以下重量份数的组分：纳米级铜粉1.4、甘露醇0.29、尼龙粉0.1、咪唑硅烷27、聚乙烯醇17。特别的，所述第一粘接层211与第二粘接层31的组成一致。
本发明的第一粘接层、第二粘接层不含甲醛；在使用本发明的不含甲醛的粘接层生产实木复合板材时，安全环保。本发明的复合板材用粘接层粘接力强，制得的实木复合板材的剪切强度高，测试证明，即使将木材与木材或其他材料的连接破坏掉，也难以将通过该粘接层粘接在一起的两层单板分离开；本发明复合板材具有良好的耐高温和防水性能；本发明是一种环保板材，不会污染室内环境，有益于人们的身体健康。
本发明以指接板为基板，在其上下依次设置面板层、芯板层、底板层，并使相邻各层之间的纤维纵横向交错排列，增加了板材纵横向的强度；所述的第一粘接层、第二粘接层不含甲醛、酚类等污染物，具有绿色环保的优点；更为突出的是，将粘结的面板层、芯板层、底板层暴露在潮湿空气下数月，或者在水中浸泡数天至数十天，粘结强度也不会显著降低，更不会在粘结部发生剥离或者开裂；进而赋予了本发明所述的板材不变形、不发生翘曲、不开裂，使用寿命长的优点。而在芯板层上设置安装槽，，并将将第一连接块、第二连接块分别深入指接板内，从而获得了具有高抗变形力的板材。本发明的基板间可实现形成无缝隙的结合，即保证了结合强度，提供了足够的耐磨性，又能有效防止水分渗入。
实施例2
本实施例提供一种结构与实施例1一致的保温防潮指接板材，所不同的是，所述面板层表面设有耐磨涂层，所述耐磨涂层包括以下重量份数的组分：九水合硝酸铝28、正硅酸乙酯13、无水乙醇10、氟烯烃5、叔丁基乙烯醚2、羟丁基乙烯醚0.7、丙烯酸树脂11、氯代三氟乙烯0.2。
本发明的耐磨涂层可有效提高木板层的涂层附着力和耐刮力，同时节省了耐磨涂层的涂料用量，可节约生产成本。本发明的耐磨涂层可均匀细腻的附着在木板层的表面，使得涂覆的木板表面更加美观。
进一步的，所述第一粘接层包括以下重量份数的组分：纳米级铜粉1.9、甘露醇0.37、尼龙粉0.13、咪唑硅烷32、聚乙烯醇19。特别的，所述第一粘接层与第二粘接层的组成一致。
本发明的第一粘接层、第二粘接层不含甲醛；在使用本发明的不含甲醛的粘接层生产实木复合板材时，安全环保。本发明的复合板材用粘接层粘接力强，制得的实木复合板材的剪切强度高，测试证明，即使将木材与木材或其他材料的连接破坏掉，也难以将通过该粘接层粘接在一起的两层单板分离开；本发明复合板材具有良好的耐高温和防水性能；本发明是一种环保板材，不会污染室内环境，有益于人们的身体健康。
实施例3
本实施例提供一种结构与实施例1一致的保温防潮指接板材，所不同的是，所述面板层表面设有耐磨涂层，所述耐磨涂层包括以下重量份数的组分：九水合硝酸铝35、正硅酸乙酯18、无水乙醇14、氟烯烃8、叔丁基乙烯醚5、羟丁基乙烯醚1.6、丙烯酸树脂15、氯代三氟乙烯0.6。
本发明的耐磨涂层可有效提高木板层的涂层附着力和耐刮力，同时节省了耐磨涂层的涂料用量，可节约生产成本。本发明的耐磨涂层可均匀细腻的附着在木板层的表面，使得涂覆的木板表面更加美观。
进一步的，所述第一粘接层包括以下重量份数的组分：纳米级铜粉1.2-1.9、甘露醇0.22、尼龙粉0.07、咪唑硅烷22、聚乙烯醇15。特别的，所述第一粘接层与第二粘接层的组成一致。
本发明的第一粘接层、第二粘接层不含甲醛；在使用本发明的不含甲醛的粘接层生产实木复合板材时，安全环保。本发明的复合板材用粘接层粘接力强，制得的实木复合板材的剪切强度高，测试证明，即使将木材与木材或其他材料的连接破坏掉，也难以将通过该粘接层粘接在一起的两层单板分离开；本发明复合板材具有良好的耐高温和防水性能；本发明是一种环保板材，不会污染室内环境，有益于人们的身体健康。
实施例4
本实施例提供一种结构与实施例1一致的保温防潮指接板材，所不同的是，所述面板层表面设有耐磨涂层，所述耐磨涂层包括以下重量份数的组分：九水合硝酸铝31、正硅酸乙酯14、无水乙醇13、氟烯烃7、叔丁基乙烯醚4、羟丁基乙烯醚1.1、丙烯酸树脂12、氯代三氟乙烯0.5。
本发明的耐磨涂层可有效提高木板层的涂层附着力和耐刮力，同时节省了耐磨涂层的涂料用量，可节约生产成本。本发明的耐磨涂层可均匀细腻的附着在木板层的表面，使得涂覆的木板表面更加美观。
进一步的，所述第一粘接层包括以下重量份数的组分：纳米级铜粉1.2-1.9、甘露醇0.29、尼龙粉0.09、咪唑硅烷28、聚乙烯醇16。特别的，所述第一粘接层与第二粘接层的组成一致。
本发明的第一粘接层、第二粘接层不含甲醛；在使用本发明的不含甲醛的粘接层生产实木复合板材时，安全环保。本发明的复合板材用粘接层粘接力强，制得的实木复合板材的剪切强度高，测试证明，即使将木材与木材或其他材料的连接破坏掉，也难以将通过该粘接层粘接在一起的两层单板分离开；本发明复合板材具有良好的耐高温和防水性能；本发明是一种环保板材，不会污染室内环境，有益于人们的身体健康。
实施例5
本实施例提供一种结构与实施例1一致的保温防潮指接板材，所不同的是，所述面板层表面设有耐磨涂层，所述耐磨涂层包括以下重量份数的组分：九水合硝酸铝35、正硅酸乙酯13、无水乙醇14、氟烯烃5、叔丁基乙烯醚5、羟丁基乙烯醚0.7、丙烯酸树脂11、氯代三氟乙烯0.6。
本发明的耐磨涂层可有效提高木板层的涂层附着力和耐刮力，同时节省了耐磨涂层的涂料用量，可节约生产成本。本发明的耐磨涂层可均匀细腻的附着在木板层的表面，使得涂覆的木板表面更加美观。
进一步的，所述第一粘接层包括以下重量份数的组分：纳米级铜粉1.2-1.9、甘露醇0.37、尼龙粉0.07、咪唑硅烷32、聚乙烯醇15。特别的，所述第一粘接层与第二粘接层的组成一致。
本发明的第一粘接层、第二粘接层不含甲醛；在使用本发明的不含甲醛的粘接层生产实木复合板材时，安全环保。本发明的复合板材用粘接层粘接力强，制得的实木复合板材的剪切强度高，测试证明，即使将木材与木材或其他材料的连接破坏掉，也难以将通过该粘接层粘接在一起的两层单板分离开；本发明复合板材具有良好的耐高温和防水性能；本发明是一种环保板材，不会污染室内环境，有益于人们的身体健康。
对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
此外，应当理解，虽然本说明书按照实施方式加以描述，但并非每个实施方式仅包含一个独立的技术方案，说明书的这种叙述方式仅仅是为清楚起见，本领域技术人员应当将说明书作为一个整体，各实施例中的技术方案也可以经适当组合，形成本领域技术人员可以理解的其他实施方式。需注意的是，本发明中所未详细描述的技术特征，均可以通过本领域中的任一现有技术实现。
Claims (8)
1.一种保温防潮指接板材，其特征在于，包括依次设置的面板层、芯板层、底板层，所述底板层的底部设有第二粘接层，所述芯板层的两面对称设有安装槽，所述安装槽底端的表面设有第一粘接层；所述面板层的底面对称设有第一连接块，所述底板层的表面对称设有第二连接块；所述第一连接块与安装槽配合连接，所述第二连接块与安装槽配合连接。
2.根据权利要求1所述的保温防潮指接板材，其特征在于，所述安装槽的水平截面为等腰梯形。
3.根据权利要求1所述的保温防潮指接板材，其特征在于，所述第一连接块的两侧对称设有弧形突块。
4.根据权利要求1所述的保温防潮指接板材，其特征在于，所述第二连接块的两侧对称设有弧形突块。
5.根据权利要求1所述的保温防潮指接板材，其特征在于，所述安装槽两侧的表面对称设有弓形槽。
6.根据权利要求1所述的复合板材，其特征在于，所述面板层表面设有耐磨涂层。
7.根据权利要求6所述的复合板材，其特征在于，所述耐磨涂层包括以下重量份数的组分：九水合硝酸铝28-35、正硅酸乙酯13-18、无水乙醇10-14、氟烯烃5-8、叔丁基乙烯醚2-5、羟丁基乙烯醚0.7-1.6、丙烯酸树脂11-15、氯代三氟乙烯0.2-0.6。
8.根据权利要求1所述的复合板材，其特征在于，所述第一粘接层包括以下重量份数的组分：纳米级铜粉1.2-1.9、甘露醇0.22-0.37、尼龙粉0.07-0.13、咪唑硅烷22-32、聚乙烯醇15-19。