CN107299771A - A kind of diamond dust abrasion-proof terrace defect mending construction method - Google Patents
A kind of diamond dust abrasion-proof terrace defect mending construction method Download PDFInfo
- Publication number
- CN107299771A CN107299771A CN201710514079.3A CN201710514079A CN107299771A CN 107299771 A CN107299771 A CN 107299771A CN 201710514079 A CN201710514079 A CN 201710514079A CN 107299771 A CN107299771 A CN 107299771A
- Authority
- CN
- China
- Prior art keywords
- construction
- diamond dust
- repairing
- ethene
- vinyl acetate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of diamond dust abrasion-proof terrace defect mending construction method, it is characterised in that is carried out by following construction procedure：First, the method for repairing and mending of 1~2mm degree is destroyed, 1, to the neat cutting of repair part, repairing face is cleaned up；2nd, water and ethene-Vinyl acetate copolymer latex are applied to construction surface as base layer dope；3rd, with screen out diamond dust abrasive aggregates with and slurry is made by mix in water and ethene-Vinyl acetate copolymer latex, with iron spatula repairing；4th, conserved after Surface hardened layer with roller；2nd, more than 10mm deep part method for repairing and mending is destroyed, 1, to the neat cutting of repair part, construction surface chisel goes >=basic unit of 50mm thickness, then clear up, soak, smear cement mortar one；2nd, in concrete unhardened state, Wear-resisting terrace material iron spatula finished surface is dispensed；3rd, conserved after Surface hardened layer with roller.It is an advantage of the invention that ensureing repairing quality, overall aesthetic degree is good, and efficiency of construction is high, and easy to operate, cost is low.
Description
Technical field
Repaiied the present invention relates to diamond dust abrasion-proof terrace technical field of construction, more particularly to a kind of diamond dust abrasion-proof terrace defect
Mend construction method.
Background technology
Need to bear vehicle frequently walk, often there is weight to hit, often thering is sharp hardening to rub, non-corrosiveness chemical drugs
Product exist, it is not high to purity requirements, to the less demanding all types of industries of aesthetics, civilian, commercial terrace largely using gold
Emery terrace, but be due to reason in terms of construction technology and material, large area diamond dust abrasion-proof terrace often occur crackle,
The defects such as decortication, pitted skin and dusting, not only directly affect the use function on ground, and directly affect the overall perception of terrace.
The content of the invention
There is provided a kind of diamond dust abrasion-proof terrace defect mending for the problem of purpose of the present invention exists aiming at prior art
Construction method, efficiently solves the difficult problem of diamond dust terrace defect mending.
The object of the present invention is achieved like this：A kind of diamond dust abrasion-proof terrace defect mending construction method, its feature exists
In by the progress of following construction procedure：
First, the repairing of 1~2mm degree is destroyed
1st, material：Diamond dust high-abrasive material, ethene-Vinyl acetate copolymer latex
2nd, construction method：
2.1 pairs of repair part are first neatly cut, and repairing face is cleaned up；
2.2 water and ethene-Vinyl acetate copolymer latex are pressed 2:1 ratio is mixed, and is applied to and is applied as base layer dope
Work face；
2.3 screen out diamond dust abrasive aggregates with screen cloth, and water and ethene-Vinyl acetate copolymer latex then are pressed into 5:1 ratio
Mixing, and be added into the diamond dust high-abrasive material of no aggregate, mixing is made after slurry, reuses iron spatula by material
Material is repaired in construction surface；
2.4 after after its Surface hardened layer with roller application sealing compound conserve；
2nd, destruction more than 10mm deep part repairing
1st, material：Diamond dust high-abrasive material
2nd, construction method：
2.1 pairs of repair part are first neatly cut, and the construction surface chisel that will be repaired goes to >=the basic unit of 50mm thickness, then
Cleaning, wetting, smear cement mortar together, and incorporation weighs 4% building adhesive in cement mortar, is put into reinforced mesh, pours pea gravel concreten；
2.2 in concrete unhardened state, dispenses Wear-resisting terrace material and with iron spatula finished surface until completing；
2.3 after after its Surface hardened layer with roller application sealing compound conserve.
Compared with prior art, it is an advantage of the invention that：Repairing at diamond dust floor construction rejected region has been effectively ensured
Quality is mended, overall aesthetic degree is good, and substantially increases efficiency of construction, and easy to operate, cost is low.
Embodiment
To further describe the present invention, with reference to embodiment, the invention will be further described.
Diamond dust abrasion-proof terrace destroys the repairing of 1~2mm degree：Repair part first will neatly be cut, be repaiied first
Benefit face is cleaned up；Water and ethene-Vinyl acetate copolymer latex are pressed 2 again:1 ratio is mixed, and is applied as base layer dope
In construction surface；Then diamond dust abrasive aggregates is screened out with screen cloth, water and ethene-Vinyl acetate copolymer latex are then pressed 5:1 ratio
Example mixing, and be added into the diamond dust high-abrasive material of no aggregate, mixing is made after slurry, and reusing iron spatula will
Materials repairing is in construction surface；Finally after after its Surface hardened layer with roller application sealing compound conserve.Diamond dust abrasion-proof terrace is destroyed
More than 10mm deep part repairing：Repair part first will neatly be cut first, the construction surface that will repair chisel goes >=
The basic unit of 50mm thickness, then clear up, soak, smear cement mortar together, incorporation water mixing weighs 4% building adhesive in cement mortar, is put into steel
Muscle mesh sheet, pours pea gravel concreten；Then in concrete unhardened state, dispense Wear-resisting terrace material and processed with iron spatula
Surface is until complete；Finally after after its Surface hardened layer with roller application sealing compound conserve.
Claims (1)
1. a kind of diamond dust abrasion-proof terrace defect mending construction method, it is characterised in that carried out by following construction procedure：
First, the repairing of 1~2mm degree is destroyed
1st, material：Diamond dust high-abrasive material, ethene-Vinyl acetate copolymer latex
2nd, construction method：
2.1 pairs of repair part are first neatly cut, and repairing face is cleaned up；
Water and ethene-Vinyl acetate copolymer latex are pressed 2 by 2.2:1 ratio is mixed, and is applied to construction as base layer dope
Face；
2.3 screen out diamond dust abrasive aggregates with screen cloth, and water and ethene-Vinyl acetate copolymer latex then are pressed into 5:1 ratio is mixed
Close, and be added into the diamond dust high-abrasive material of no aggregate, mixing is made after slurry, reuses iron spatula by material
Repair in construction surface；
2.4 after after its Surface hardened layer with roller application sealing compound conserve；
2nd, destruction more than 10mm deep part repairing
1st, material：Diamond dust high-abrasive material
2nd, construction method：
2.1 pairs of repair part are first neatly cut, and the construction surface chisel that will be repaired goes to >=the basic unit of 50mm thickness, then clearly
Reason, wetting, smear cement mortar together, and incorporation weighs 4% building adhesive in cement mortar, is put into reinforced mesh, pours pea gravel concreten；
2.2 in concrete unhardened state, dispenses Wear-resisting terrace material and with iron spatula finished surface until completing；
2.3 after after its Surface hardened layer with roller application sealing compound conserve.