CN1320575A - Hardening agent for antiwear colour ground and its application method - Google Patents
Hardening agent for antiwear colour ground and its application method Download PDFInfo
- Publication number
- CN1320575A CN1320575A CN 01112694 CN01112694A CN1320575A CN 1320575 A CN1320575 A CN 1320575A CN 01112694 CN01112694 CN 01112694 CN 01112694 A CN01112694 A CN 01112694A CN 1320575 A CN1320575 A CN 1320575A
- Authority
- CN
- China
- Prior art keywords
- ground
- stiffening agent
- agent
- wear
- trowel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A hardening agent for antiwear colour ground surface is prepared from hydraulic silicate cement, high-strength and high-toughness aggregate, active additive, efficient water-reducing agent of cement, colouring filler, organic thickening agent and redispersive polymer-rubber powder through proportional mixing and stirring to obtain powder product. It is applied through spreading concrete slurry on foundation, spreading said hardening agent, grinding, mechanical throweling, curing, removing thutterings and cutting contraction joints. Its advantages are high performance, multiple colours, low cost and high antiwear nature.
Description
The present invention relates to a kind of wear-resisting colour ground stiffening agent and constructional method thereof, concrete novel superpower wear-resistant colour ground stiffening agent of particularly a kind of employing special high-performance and mechanized construction method thereof.
At present, the general direct use portland cement concrete in the ground of various buildingss, its shortcoming is that wear resistance is low, plays dirt easily, intensity is on the low side, and permeability resistance is low, the cleaning difficulty, and the management and maintenance expense is higher relatively, the surfacing degree is not high, and beautiful and comfortable sense is relatively poor, and wearing quality, weather resistance are relatively poor.For overcoming these shortcomings, the solution that people usually adopt is to lay floor tile, timber floor or directly at all kinds of organic polymer terrace paint such as the whole coating resin lacquer in concrete floor surface, hard floor paint at terrace surface, but these two kinds of solutions all have certain separately shortcoming: the former terrace surface exists and connects the slit, actual use can be subjected to certain limitation, and cost and management and maintenance expense are than higher; The latter has eliminated surperficial slit, but is subjected to the influence of the speciality of organic polymer own, and ground intensity is low, difference of hardness, wear resistance are low, and wearing quality and weather resistance are poor, and comprehensive cost is also relative with the management and maintenance expense higher.
The object of the invention is to provide the whole application that a kind of wear resistance is good, performance is high, cost is low wear-resisting colour ground stiffening agent at above-mentioned prior art present situation.
Another goal of the invention of the present invention is to provide a kind of constructional method of above-mentioned wear-resisting colour ground stiffening agent.
The object of the present invention is achieved like this: wear-resisting colour ground stiffening agent is the Powdered goods of a kind of premix, wherein include following composition by weight: suitable positions 30～50, tough aggregate 40～70, active additive 4～15, high-efficiency cement water reducer 0.2～0.8, color stuffing 0.01～6, organic thickening agent 0.01～0.1, redispersible polymer rubber powder 0.01～10.
The constructional method of above-mentioned wear-resisting colour ground stiffening agent may further comprise the steps:
1. the laitance of terrace substrate concrete is handled: substrate concrete cast, tamping and floating, maintenance were treated after its initial set in 0.5～4 hour, used the mechanical trowel that installs disk additional equably the laitance layer of concrete surface to be destroyed;
2. the spreading of stiffening agent and disk polishing operation: the total amount of using of stiffening agent is generally 3～10kg/m2; 60%～70% the ground hardening agent that at first will use total amount is spread in uniform on the initial set concrete surface of defined area, finish spreading operation for the first time, treat stiffening agent absorb certain moisture evenly wetting after, use the mechanical trowel that installs disk additional the ground of under low speed, polishing equably; After the completion, immediately remaining 30%～40% ground hardening agent is spread in uniform on the first layer, finishes spreading operation for the second time, treat that stiffening agent is evenly wetting after, reuse the mechanical trowel that installs disk additional the ground of polishing equably under low speed, the disk polishing operation should crisscross carrying out;
3. mechanical trowel operation: after polishing operation was finished, the sclerosis situation of looking ground was carried out at least twice mechanical trowel operation of not installing disk additional, and the sclerosis situation that the changing conditions of the running speed of mechanical trowel and mechanical trowel angle should be looked ground adjusts; Crisscross carrying out answered in the operation of machinery trowel;
4. ground maintenance: stiffening agent platform construction is finished after with the last equating in ground 2～6 hours, employing is carried out the maintenance on ground in the method for terrace surface sprinkling or coating maintenance wax, to prevent the sharp acute evaporation of surface-moisture, cause surface cracking, guarantee the steady growth of ground intensity, curing time is more than 7 days;
5. mould unloading and shrinkage joint cutting: the mould unloading operation can be carried out second day that the stiffening agent platform is constructed after finishing, should note not damaging the ground edge of table during mould unloading operation; The cutting of shrinkage joint can be carried out the 3rd day that the stiffening agent platform is constructed after finishing;
6. enabling time: decide on the cement that envrionment temperature and ground base concrete use, but walking in common 24～48 hours can be born underloading in 7～10 days, 28 days later can normally uses.
The special concrete terrace that adopts ground hardening agent of the present invention and mechanized construction method thereof to be obtained has following relatively more outstanding advantage:
1. high-wearing feature: owing to adopted good special tough aggregate of grating and special mechanized construction method, under identical abrasive conditions, its abrasion are 1/10～1/20 of normal concrete only, are very suitable for the ground of the frequent and anti-mechanical wear of traffic;
2. globality and weather resistance: owing to construct simultaneously with concrete substrate and form an integral body, ground can not produce delamination, long service life;
3. high permeability resistance: this ground hardening agent can form very fine and close microstructure, can minimize for the infiltration of liquid such as grease;
4. do not play dust: use the terrace of this ground hardening agent to have the characteristic of high-strength compact, can not play dirt, all most suitable for place that has cleaning to require and finished-product material warehouse etc.;
5. high shock resistance: owing to adopted special high-performance concrete formulation and polymer modification technology, this special concrete terrace is when having very high compressive strength and folding strength, the ability that also has certain toughness and viscous deformation, therefore the ability of anti-foreign impacts is very high;
6. color is abundant, and bright in luster: this stiffening agent can be selected multiple inorganic and pigment dyestuff for use, can obtain cement true qualities and the versicolor terrace through allocating;
7. easy construction: directly be spread on the fresh concrete surface and method of mechanization construct owing to adopted, this floor construction is simple and easy to do, and quality is controlled easily;
8. good and economic: the application techniques economy of this terrace surface is good, and what its comprehensive cost was lower than that people adopt usually lays floor tile and timber floor or the direct method of all kinds of organic polymer terrace paint such as coating resin lacquer, hard floor paint at terrace surface.
Below in conjunction with specific embodiment the present invention is described in further detail:
Wear-resisting colour ground stiffening agent, it is a kind of employing suitable positions, tough aggregate, active additive, the high-efficiency cement water reducer, color stuffing, organic thickening agent and redispersible polymer rubber powder etc. are component, and through the Powdered goods of premix that stirrer mixes, these components content by weight is: suitable positions 30～50, tough aggregate 40～70, active additive 4～15, high-efficiency cement water reducer 0.2～0.8, color stuffing 0.01～6, organic thickening agent 0.01～0.1, redispersible polymer rubber powder 0.01～10.
Above-mentioned tough aggregate is the modulated quartz sand of grain composition, sandstone, silicon carbide, the carbonization silica sand, emergy, quartzite, stone chippings, the particle of waste ceramic and metal particle etc. or their mixture, active additive is silicon powder and flyash etc. or their mixture, color stuffing is a titanium dioxide, zinc sulfide white, iron oxide red, iron oxide yellow, chrome green, phthalocyanine blue and phthalocyanine green etc. or their mixture, organic thickening agent is cellulose family and propylene class organic thickening agent etc., and the redispersible polymer rubber powder is a polyethylene kind, polypropylene-base, polyacrylate(s), polyvinyl acetate (PVA) class and polystyrene type rubber powder or their mixture.
Embodiment one:
By weight, get the quartz sand fine aggregate 40 of 16,0.5 millimeters of the quartz sand coarse aggregates of 40,2.0 millimeters of common 525# silicate cements, silicon powder 4, high-efficiency cement water reducer 0.5, titanium be from powder 2, chrome green 4, sodium polyacrylate thickening material 0.08, redispersible polyvinyl acetate glue powder 4 after stirrer mixes half hour, promptly obtains viridian Powdered ground hardening agent.
Under the environment about 20 degree Celsius, the mechanized construction method of this superpower wear-resistant colour ground stiffening agent is: 1. the laitance of terrace substrate concrete is handled: substrate concrete cast, tamping and floating, maintenance was treated after its initial set in 1 hour, used the mechanical trowel that installs disk additional equably the laitance layer of concrete surface to be destroyed;
2. the spreading of stiffening agent and disk polishing operation: the total amount of using of stiffening agent is generally 5kg/m2; 60% the ground hardening agent that at first will use total amount is spread in uniform on the initial set concrete surface of defined area, finish spreading operation for the first time, treat stiffening agent absorb certain moisture evenly wetting after, use the mechanical trowel that installs disk additional the ground of under low speed, polishing equably; After the completion, immediately remaining 40% ground hardening agent is spread in uniform on the first layer, finishes spreading operation for the second time, treat that stiffening agent is evenly wetting after, reuse the mechanical trowel that installs disk additional the ground of polishing equably under low speed, the disk polishing operation is crisscross to carry out;
3. mechanical trowel operation: after polishing operation was finished, the sclerosis situation of looking ground carried out not installing additional for twice the mechanical trowel operation of disk, and the sclerosis situation that the changing conditions of the running speed of mechanical trowel and mechanical trowel angle is looked ground adjusts; Crisscross the carrying out of machinery trowel operation;
4. ground maintenance: after with the last equating in ground 4 hours are finished in stiffening agent platform construction, employing is carried out the maintenance on ground in the method for terrace surface coating maintenance wax, prevent the sharp acute evaporation of surface-moisture, guarantee the steady growth of ground intensity, curing time is 7 days;
5. mould unloading and shrinkage joint cutting: carry out mould unloading operation second day after stiffening agent platform construction is finished, and notes not damaging the ground edge of table during mould unloading operation; Carry out the cutting of shrinkage joint the 3rd day after stiffening agent platform construction is finished.
The ultimate compression strength of this terrace is greater than 80MPa (28 days), and folding strength is greater than 10MPa (28 days), under identical abrasive conditions, its abrasion only are about 1/11 of normal concrete, and color is an emerald green, and color and luster is beautiful and comfortable, superior performance is a kind of very ideal sclerosis floor material.
Embodiment two:
By weight, get the quartz sand coarse aggregate 22 of 44,1.2 millimeters of 525# silicate white cements, 0.4 the stainless steel fine aggregate 20 of millimeter, silicon powder 6, flyash 8, high-efficiency cement water reducer 0.6, titanium dioxide 1, phthalocyanine blue 2, Vltra tears thickening material 0.02, redispersible polyacrylic ester rubber powder 2, after stirrer mixes half hour, promptly obtain the Powdered ground hardening agent of vivid blue containing metal aggregate.
The mechanized construction method of this wear-resisting colour ground stiffening agent is with embodiment one.
The ultimate compression strength of this terrace is greater than 91MPa (28 days), and folding strength is greater than 12MPa (28 days), under identical abrasive conditions, its abrasion only are about 1/18 of normal concrete, color is vivid blue, and color and luster is beautiful and comfortable, is the very superior senior hardened ground material of a kind of performance.
Claims (7)
1. wear-resisting colour ground stiffening agent, be the Powdered goods of a kind of premix, it is characterized in that including by weight following composition: suitable positions 30～50, tough aggregate 40～70, active additive 4～15, high-efficiency cement water reducer 0.2～0.8, color stuffing 0.01～6, organic thickening agent 0.01～0.1, redispersible polymer rubber powder 0.01～10.
2. strong wear-resisting colour ground stiffening agent as claimed in claim 1 is characterized in that described tough aggregate is particle, metal particle or their mixture of the modulated quartz sand of grain composition, sandstone, silicon carbide, carbonization silica sand, emergy, quartzite, stone chippings, waste ceramic.
3. as according to the described superpower wear-resistant colour ground of claim 1 stiffening agent, it is characterized in that described active additive is silicon powder or flyash or their mixture.
4. a kind of superpower wear-resistant colour ground stiffening agent according to claim 1 is characterized in that one of following or their mixture of described color stuffing: titanium dioxide, zinc sulfide white, iron oxide red, iron oxide yellow, chrome green, phthalocyanine blue, phthalocyanine green.
5. strong wear-resisting colour ground stiffening agent as claimed in claim 1 is characterized in that described organic thickening agent is cellulose family or propylene class organic thickening agent.
6. wear-resisting colour ground stiffening agent as claimed in claim 1 is characterized in that described redispersible polymer rubber powder is one of following or their miscellany: polyethylene kind, polypropylene-base, polyacrylate(s), polyvinyl acetate (PVA) class, polystyrene type rubber powder.
7. constructional method that is exclusively used in wear-resisting colour ground stiffening agent as claimed in claim 1 is characterized in that may further comprise the steps:
1. the laitance of terrace substrate concrete is handled: substrate concrete cast, tamping and floating, maintenance were treated after its initial set in 0.5～4 hour, used the mechanical trowel that installs disk additional equably the laitance layer of concrete surface to be destroyed;
2. the spreading of stiffening agent and disk polishing operation: the total amount of using of stiffening agent is generally 3～10kg/m2; 60%～70% the ground hardening agent that at first will use total amount is spread in uniform on the initial set concrete surface of defined area, finish spreading operation for the first time, treat stiffening agent absorb certain moisture evenly wetting after, use the mechanical trowel that installs disk additional the ground of under low speed, polishing equably; After the completion, immediately remaining 30%～40% ground hardening agent is spread in uniform on the first layer, finishes spreading operation for the second time, treat that stiffening agent is evenly wetting after, reuse the mechanical trowel that installs disk additional the ground of polishing equably under low speed, the disk polishing operation should crisscross carrying out;
3. mechanical trowel operation: after polishing operation was finished, the sclerosis situation of looking ground was carried out at least twice mechanical trowel operation of not installing disk additional, and the sclerosis situation that the changing conditions of the running speed of mechanical trowel and mechanical trowel angle should be looked ground adjusts; Crisscross carrying out answered in the operation of machinery trowel;
4. ground maintenance: stiffening agent platform construction is finished after with the last equating in ground 2～6 hours, employing is carried out the maintenance on ground in the method for terrace surface sprinkling or coating maintenance wax, to prevent the sharp acute evaporation of surface-moisture, cause surface cracking, guarantee the steady growth of ground intensity, curing time is more than 7 days;
5. mould unloading and shrinkage joint cutting: the mould unloading operation can be carried out second day that the stiffening agent platform is constructed after finishing, should note not damaging the ground edge of table during mould unloading operation; The cutting of shrinkage joint can be carried out the 3rd day that the stiffening agent platform is constructed after finishing;
6. enabling time: decide on the cement that envrionment temperature and ground base concrete use, but walking in common 24～48 hours can be born underloading in 7～10 days, 28 days later can normally uses.