CN107299534A - A kind of anti-vacuum evaporation cloth of coating-type acrylic fabric fabric hazed - Google Patents

A kind of anti-vacuum evaporation cloth of coating-type acrylic fabric fabric hazed Download PDF

Info

Publication number
CN107299534A
CN107299534A CN201610233817.2A CN201610233817A CN107299534A CN 107299534 A CN107299534 A CN 107299534A CN 201610233817 A CN201610233817 A CN 201610233817A CN 107299534 A CN107299534 A CN 107299534A
Authority
CN
China
Prior art keywords
coating
fabric
acrylic
hazed
vacuum evaporation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610233817.2A
Other languages
Chinese (zh)
Inventor
黄磊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610233817.2A priority Critical patent/CN107299534A/en
Publication of CN107299534A publication Critical patent/CN107299534A/en
Pending legal-status Critical Current

Abstract

The present invention relates to a kind of anti-vacuum evaporation cloth of coating-type acrylic fabric fabric hazed, it is to decorate a layer function coating by the way of coating is evaporated in vacuo in the outer surface of acrylic fibers base fabric, the preparation of coating slurry involved by the functional coating is by coating adhesive, silane, antifoggant and crosslinking agent add pulping tank, after stirring, pH is adjusted to 7.5~8.5 scopes with ammoniacal liquor, stand 2~4 hours, then acrylic fibers scrim surfaces are applied to by the way of coating is evaporated in vacuo, in drying 0.5 hour under 80 DEG C of environment, in solidification 1~1.5 hour under 120~135 DEG C of environment, finally balance more than 8 hours under field conditions (factors).After the coated material protection of acrylic fabric web surface, fabric, which has, has preferably resisted mist characteristic, improves the use quality of fabric.

Description

A kind of anti-vacuum evaporation cloth of coating-type acrylic fabric fabric hazed
Technical field
The invention belongs to acrylic fabric fabric technical field, and in particular to a kind of anti-vacuum evaporation coating acrylic fabric fabric hazed.
Background technology
Acrylic fiber has the title of artificial wool.There is soft, bulk, easy dye, bright in colour, fast light, antibacterial, be not afraid of and damage by worms, according to the requirement of different purposes can it is pure spinning or with it is natural fibre blended, its textile is widely used in the fields such as clothes, decoration, industry.
Acrylic fabric has higher intensity and elastic recovery capability, therefore, its strong durable, wash and wear.Acrylic fabric hygroscopicity is poor, and dress has feeling of oppression and heat, while easily static electrification, contamination dust, influences attractive in appearance and comfortableness.After but washing easily dry, and it is wet hardly decline by force, it is indeformable, have good well-flushing truck energy.Acrylic fibers are to close the best fabric of heat resistance in fine fabric, with thermoplasticity, can manufacture accordion-pleated skirt, rivel is lasting.Meanwhile, the melt resistance of acrylic fabric is poor, meets cigarette ash, Mars etc. and easily forms hole.Therefore, it should be tried one's best when wearing and avoid the contact of cigarette end, spark etc..Preferably, in addition to poorer than acrylic fibers, its sun-proof ability surpasses natural fabric to the light resistance of acrylic fabric.The New function for continually developing fabric is the trend of acrylic fabric fabric development.
The content of the invention
It is an object of the invention to provide a kind of anti-vacuum evaporation cloth of coating-type acrylic fabric fabric hazed.
The present invention the used technical scheme that solves the above problems is：A kind of anti-vacuum evaporation cloth of coating-type acrylic fabric fabric hazed, it is to decorate a layer function coating by the way of coating is evaporated in vacuo in the outer surface of acrylic fibers base fabric, the preparation of coating slurry involved by the functional coating is by coating adhesive, silane, antifoggant and crosslinking agent add pulping tank, after stirring, pH is adjusted to 7.5~8.5 scopes with ammoniacal liquor, stand 2~4 hours, then acrylic fibers scrim surfaces are applied to by the way of coating is evaporated in vacuo, in drying 0.5 hour under 80 DEG C of environment, in solidification 1~1.5 hour under 120~135 DEG C of environment, finally balance more than 8 hours under field conditions (factors).
Preferably, the institutional framework of the acrylic fibers base fabric use antarafacial tissue, in order to coating be preferably coated with and the fabric later stage solidification balance, increase the service life.
Preferably, antarafacial tissue includes selecting 1/2 twill, 1/3 twill, brokentwlllweave, 1/4 twill or five heddle satin institutional framework.
Compared with prior art, the advantage of the invention is that：There is provided a kind of anti-acrylic fabric fabric that hazes for being evaporated in vacuo cloth of coating-type, after being evaporated in vacuo Coating protection, make acrylic fabric fabric that there is the preferably anti-performance that hazes, improve the use quality of acrylic fabric fabric.
Embodiment
The present invention is described in further detail with reference to embodiments.
Embodiment 1
The anti-acrylic fabric fabric that hazes, it is to decorate a layer function coating by the way of coating is evaporated in vacuo in the outer surface of acrylic fibers base fabric, the preparation of coating slurry involved by the functional coating is that coating adhesive, silane, antifoggant and crosslinking agent are added into pulping tank, after stirring, pH is adjusted to 8 scopes with ammoniacal liquor, stand 2~4 hours, then acrylic fibers scrim surfaces are applied to by the way of coating is evaporated in vacuo, in drying 0.5 hour under 80 DEG C of environment, in solidifying under 120 DEG C of environment 1.5 hours, finally balance more than 8 hours under field conditions (factors).
The institutional framework of acrylic fibers base fabric in the present embodiment is 1/2 twill-weave structure.
Acrylic fabric fabric obtained by the present embodiment has has resisted mist characteristic well.
Embodiment 2
The anti-acrylic fabric fabric that hazes, it is to decorate a layer function coating by the way of coating is evaporated in vacuo in the outer surface of acrylic fibers base fabric, the preparation of coating slurry involved by the functional coating is that coating adhesive, silane, antifoggant and crosslinking agent are added into pulping tank, after stirring, pH is adjusted to 7.5 scopes with ammoniacal liquor, stand 2~4 hours, then acrylic fibers scrim surfaces are applied to by the way of coating is evaporated in vacuo, in drying 0.5 hour under 80 DEG C of environment, in solidifying under 130 DEG C of environment 1 hour, finally balance more than 8 hours under field conditions (factors).
The institutional framework of acrylic fibers base fabric is brokentwlllweave institutional framework in the present embodiment.
Acrylic fabric fabric obtained by the present embodiment has has resisted mist characteristic well.
Embodiment 3
The anti-acrylic fabric fabric that hazes, it is to decorate a layer function coating by the way of coating is evaporated in vacuo in the outer surface of acrylic fibers base fabric, the preparation of coating slurry involved by the functional coating is that coating adhesive, silane, antifoggant and crosslinking agent are added into pulping tank, after stirring, pH is adjusted to 8.5 scopes with ammoniacal liquor, stand 2~4 hours, then acrylic fibers scrim surfaces are applied to by the way of coating is evaporated in vacuo, in drying 0.5 hour under 80 DEG C of environment, in solidifying under 120 DEG C of environment 1 hour, finally balance more than 8 hours under field conditions (factors).
The institutional framework of acrylic fibers base fabric is five heddle satin institutional framework in the present embodiment.
Acrylic fabric fabric obtained by the present embodiment has has resisted mist characteristic well.

Claims (3)

1. a kind of anti-vacuum evaporation cloth of coating-type acrylic fabric fabric hazed, it is characterised in that：It is to decorate a layer function coating by the way of coating is evaporated in vacuo in the outer surface of acrylic fibers base fabric, the preparation of coating slurry involved by the functional coating is that coating adhesive, silane, antifoggant and crosslinking agent are added into pulping tank, after stirring, pH is adjusted to 7.5~8.5 scopes with ammoniacal liquor, stand 2~4 hours, then acrylic fibers scrim surfaces are applied to by the way of coating is evaporated in vacuo, in drying 0.5 hour under 80 DEG C of environment, in solidifying under 120~135 DEG C of environment 1~1.5 hour, finally balance more than 8 hours under field conditions (factors).
2. the anti-vacuum evaporation cloth of coating-type acrylic fabric fabric hazed according to claim 1, it is characterised in that：The institutional framework of the acrylic fibers base fabric uses antarafacial tissue.
3. the anti-vacuum evaporation cloth of coating-type acrylic fabric fabric hazed according to claim 2, it is characterised in that：The antarafacial tissue includes selecting 1/2 twill, 1/3 twill, brokentwlllweave, 1/4 twill or five heddle satin institutional framework.
CN201610233817.2A 2016-04-16 2016-04-16 A kind of anti-vacuum evaporation cloth of coating-type acrylic fabric fabric hazed Pending CN107299534A (en)