CN107287909A - A kind of dip coated formula damage resistant dacron fabric - Google Patents
A kind of dip coated formula damage resistant dacron fabric Download PDFInfo
- Publication number
- CN107287909A CN107287909A CN201610187916.1A CN201610187916A CN107287909A CN 107287909 A CN107287909 A CN 107287909A CN 201610187916 A CN201610187916 A CN 201610187916A CN 107287909 A CN107287909 A CN 107287909A
- Authority
- CN
- China
- Prior art keywords
- dip coated
- fabric
- coating
- damage resistant
- terylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of dip coated formula damage resistant dacron fabric, it is to decorate a layer function coating by the way of dip coated in the outer surface of terylene base fabric, the preparation of coating slurry involved by the functional coating is by coating adhesive, silane and crosslinking agent add pulping tank, after stirring, pH is adjusted to 7.5~8.5 scopes with ammoniacal liquor, stand 2~4 hours, then terylene scrim surfaces are applied to by the way of dip coated, in drying 0.5 hour under 80 DEG C of environment, in solidification 1~1.5 hour under 120~135 DEG C of environment, finally balance more than 8 hours under field conditions (factors).After the coated material protection of dacron web surface, fabric has more preferable scratch-resistant Flaw characterization, improves the use quality of fabric.
Description
Technical field
The invention belongs to dacron fabric technical field, and in particular to a kind of dacron fabric of the dip coated of damage resistant.
Background technology
Terylene is an important kind in synthetic fibers, is the trade name of China's polyester fiber.It with p-phthalic acid (PTA) or dimethyl terephthalate (DMT) (DMT) and ethylene glycol (EG) is raw material through esterification or fiber-forming polymer -- polyethylene terephthalate (PET), the fiber being made through spinning and post processing prepared by ester exchange and polycondensation reaction that it, which is,.
Dacron has higher intensity and elastic recovery capability, therefore, its strong durable, wash and wear.Dacron hygroscopicity is poor, and dress has feeling of oppression and heat, while easily static electrification, contamination dust, influences attractive in appearance and comfortableness.After but washing easily dry, and it is wet hardly decline by force, it is indeformable, have good well-flushing truck energy.Terylene is to close the best fabric of heat resistance in fine fabric, with thermoplasticity, can manufacture accordion-pleated skirt, rivel is lasting.Meanwhile, the melt resistance of dacron is poor, meets cigarette ash, Mars etc. and easily forms hole.Therefore, it should be tried one's best when wearing and avoid the contact of cigarette end, spark etc..Preferably, in addition to poorer than acrylic fibers, its sun-proof ability surpasses natural fabric to the light resistance of dacron.The New function for continually developing fabric is the trend of dacron fabric development.
The content of the invention
It is an object of the invention to provide a kind of dip coated formula dacron fabric of damage resistant.
The present invention the used technical scheme that solves the above problems is:A kind of dip coated formula damage resistant dacron fabric, it is to decorate a layer function coating by the way of dip coated in the outer surface of terylene base fabric, the preparation of coating slurry involved by the functional coating is that coating adhesive, silane and crosslinking agent are added into pulping tank, after stirring, pH is adjusted to 7.5~8.5 scopes with ammoniacal liquor, stand 2~4 hours, then terylene scrim surfaces are applied to by the way of dip coated, in drying 0.5 hour under 80 DEG C of environment, in solidifying under 120~135 DEG C of environment 1~1.5 hour, finally balance more than 8 hours under field conditions (factors).
Preferably, the institutional framework of the terylene base fabric use antarafacial tissue, in order to coating be preferably coated with and the fabric later stage solidification balance, increase the service life.
Preferably, antarafacial tissue includes selecting 1/2 twill, 1/3 twill, brokentwlllweave, 1/4 twill or five heddle satin institutional framework.
Compared with prior art, the advantage of the invention is that:There is provided a kind of damage resistant dacron fabric of dip coated formula, after dip coating is protected, make dacron fabric that there is more preferable scratch resistant performance, improve the use quality of dacron fabric.
Embodiment
The present invention is described in further detail with reference to embodiments.
Embodiment 1
Damage resistant dacron fabric, it is to decorate a layer function coating by the way of dip coated in the outer surface of terylene base fabric, the preparation of coating slurry involved by the functional coating is that coating adhesive, silane and crosslinking agent are added into pulping tank, after stirring, pH is adjusted to 8 scopes with ammoniacal liquor, stand 2~4 hours, then terylene scrim surfaces are applied to by the way of dip coated, in drying 0.5 hour under 80 DEG C of environment, in solidifying under 120 DEG C of environment 1.5 hours, finally balance more than 8 hours under field conditions (factors).
The institutional framework of terylene base fabric in the present embodiment is 1/2 twill-weave structure.
Dacron fabric obtained by the present embodiment has good scratch-resistant Flaw characterization.
Embodiment 2
Damage resistant dacron fabric, it is to decorate a layer function coating by the way of dip coated in the outer surface of terylene base fabric, the preparation of coating slurry involved by the functional coating is that coating adhesive, silane and crosslinking agent are added into pulping tank, after stirring, pH is adjusted to 7.5 scopes with ammoniacal liquor, stand 2~4 hours, then terylene scrim surfaces are applied to by the way of dip coated, in drying 0.5 hour under 80 DEG C of environment, in solidifying under 130 DEG C of environment 1 hour, finally balance more than 8 hours under field conditions (factors).
The institutional framework of terylene base fabric is brokentwlllweave institutional framework in the present embodiment.
Dacron fabric obtained by the present embodiment has good scratch-resistant Flaw characterization.
Embodiment 3
Damage resistant dacron fabric, it is to decorate a layer function coating by the way of dip coated in the outer surface of terylene base fabric, the preparation of coating slurry involved by the functional coating is that coating adhesive, silane and crosslinking agent are added into pulping tank, after stirring, pH is adjusted to 8.5 scopes with ammoniacal liquor, stand 2~4 hours, then terylene scrim surfaces are applied to by the way of dip coated, in drying 0.5 hour under 80 DEG C of environment, in solidifying under 120 DEG C of environment 1 hour, finally balance more than 8 hours under field conditions (factors).
The institutional framework of terylene base fabric is five heddle satin institutional framework in the present embodiment.
Dacron fabric obtained by the present embodiment has good scratch-resistant Flaw characterization.
Claims (3)
1. a kind of dip coated formula damage resistant dacron fabric, it is characterised in that:It is to decorate a layer function coating by the way of dip coated in the outer surface of terylene base fabric, the preparation of coating slurry involved by the functional coating is that coating adhesive, silane and crosslinking agent are added into pulping tank, after stirring, pH is adjusted to 7.5~8.5 scopes with ammoniacal liquor, stand 2~4 hours, then terylene scrim surfaces are applied to by the way of dip coated, in drying 0.5 hour under 80 DEG C of environment, in solidifying under 120~135 DEG C of environment 1~1.5 hour, finally balance more than 8 hours under field conditions (factors).
2. dip coated formula damage resistant dacron fabric according to claim 1, it is characterised in that:The institutional framework of the terylene base fabric uses antarafacial tissue.
3. dip coated formula damage resistant dacron fabric according to claim 2, it is characterised in that:The antarafacial tissue includes selecting 1/2 twill, 1/3 twill, brokentwlllweave, 1/4 twill or five heddle satin institutional framework.