CN105862440A - Roll-coated anti-scratch terylene fabric - Google Patents
Roll-coated anti-scratch terylene fabric Download PDFInfo
- Publication number
- CN105862440A CN105862440A CN201610193484.5A CN201610193484A CN105862440A CN 105862440 A CN105862440 A CN 105862440A CN 201610193484 A CN201610193484 A CN 201610193484A CN 105862440 A CN105862440 A CN 105862440A
- Authority
- CN
- China
- Prior art keywords
- coating
- terylene
- fabric
- roller coat
- environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a roll-coated anti-scratch terylene fabric. The external surface of a terylene base cloth is decorated with a functional coating in a roll coating manner, and a coating slurry involved in the functional coating is prepared through the following steps: adding a coating adhesive, silane and a cross-linking agent to a pulping tank, uniformly stirring above materials, adjusting the obtained mixture to 7.5-8.5 by using ammonia water, standing the mixture for 2-4h, applying the obtained mixture to the surface of the terylene base cloth in a roll coating manner, drying the obtained terylene base cloth in 80DEG C environment for 0.5h, solidifying the dried terylene base cloth in 120-135DEG C environment for 1-1.5h, and balancing the cured cloth under natural conditions for 8h or above. The fabric obtained after carrying out coating material protection on the surface of the terylene fabric has the advantages of good scratch resistance and improved use quality.
Description
Technical field
The invention belongs to dacron fabric technical field, be specifically related to the dacron fabric of the roller coat of a kind of damage resistant.
Background technology
Terylene is an important kind in synthetic fibers, is the trade name of China's polyester fiber.It is with p-phthalic acid (PTA) or dimethyl terephthalate (DMT) (DMT) and ethylene glycol (EG) prepared fiber-forming polymer--the polyethylene terephthalate (PET) that is raw material through esterification or ester exchange and polycondensation reaction, through the fiber that spinning and post processing are made.
Dacron has higher intensity and elastic recovery capability, therefore, its strong durable, wash and wear.Dacron hygroscopicity is poor, and dress has feeling of oppression and heat, and the most easily static electrification, contamination dust, affect attractive in appearance and comfortableness.After but washing the driest, and wet decline hardly by force, indeformable, have good wash and wear performance.Terylene is to close the fabric that in fine fabric, heat resistance is best, has thermoplasticity, can manufacture accordion-pleated skirt, and rivel is lasting.Meanwhile, the melt resistance of dacron is poor, meets cigarette ash, Mars etc. and is easily formed hole.Therefore, the contact of cigarette end, spark etc. should be avoided when wearing as far as possible.The light resistance of dacron is preferable, except ratio is in addition to acrylic fibers difference, and its sun-proof ability surpasses natural fabric.The New function continually developing fabric is the trend of dacron fabric development.
Summary of the invention
It is an object of the invention to provide the roller coat formula dacron fabric of a kind of damage resistant.
The present invention solves the technical scheme that the problems referred to above are used: a kind of roller coat formula damage resistant dacron fabric, be terylene base fabric outer surface use roller coat mode decorate a layer function coating, the preparation of the coating slurry involved by described functional coating is by coating adhesive, silane and crosslinking agent add pulping tank, after stirring, with ammoniacal liquor regulation pH to 7.5～8.5 scopes, stand 2～4 hours, then the mode using roller coat is applied to terylene scrim surfaces, dry 0.5 hour under 80 DEG C of environment, solidify 1～1.5 hour under 120～135 DEG C of environment, last balance more than 8 hours under field conditions (factors).
Preferably, the institutional framework of described terylene base fabric uses antarafacial tissue, in order to coating is preferably coated with and the solidification balance in fabric later stage, increases the service life.
Preferably, antarafacial tissue includes selecting 1/2 twill, 1/3 twill, brokentwlllweave, 1/4 twill or five heddle satin institutional framework.
Compared with prior art, it is an advantage of the current invention that: provide the damage resistant dacron fabric of a kind of roller coat formula, after roll-coated coatings is protected, make dacron fabric have more preferable scratch resistant performance, improve the use quality of dacron fabric.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is described in further detail.
Embodiment 1
Damage resistant dacron fabric, be terylene base fabric outer surface use roller coat mode decorate a layer function coating, the preparation of the coating slurry involved by described functional coating is that coating adhesive, silane and crosslinking agent are added pulping tank, after stirring, regulate pH to 8 scope with ammoniacal liquor, stand 2～4 hours, then the mode using roller coat is applied to terylene scrim surfaces, dry 0.5 hour under 80 DEG C of environment, solidify under 120 DEG C of environment 1.5 hours, balance more than 8 hours the most under field conditions (factors).
The institutional framework of the terylene base fabric in the present embodiment is 1/2 twill-weave structure.
The present embodiment gained dacron fabric has good damage resistant characteristic.
Embodiment 2
Damage resistant dacron fabric, be terylene base fabric outer surface use roller coat mode decorate a layer function coating, the preparation of the coating slurry involved by described functional coating is that coating adhesive, silane and crosslinking agent are added pulping tank, after stirring, regulate pH to 7.5 scope with ammoniacal liquor, stand 2～4 hours, then the mode using roller coat is applied to terylene scrim surfaces, dry 0.5 hour under 80 DEG C of environment, solidify under 130 DEG C of environment 1 hour, balance more than 8 hours the most under field conditions (factors).
In the present embodiment, the institutional framework of terylene base fabric is brokentwlllweave institutional framework.
The present embodiment gained dacron fabric has good damage resistant characteristic.
Embodiment 3
Damage resistant dacron fabric, be terylene base fabric outer surface use roller coat mode decorate a layer function coating, the preparation of the coating slurry involved by described functional coating is that coating adhesive, silane and crosslinking agent are added pulping tank, after stirring, regulate pH to 8.5 scope with ammoniacal liquor, stand 2～4 hours, then the mode using roller coat is applied to terylene scrim surfaces, dry 0.5 hour under 80 DEG C of environment, solidify under 120 DEG C of environment 1 hour, balance more than 8 hours the most under field conditions (factors).
In the present embodiment, the institutional framework of terylene base fabric is five heddle satin institutional framework.
The present embodiment gained dacron fabric has good damage resistant characteristic.
Claims (3)
1. a roller coat formula damage resistant dacron fabric, it is characterized in that: be terylene base fabric outer surface use roller coat mode decorate a layer function coating, the preparation of the coating slurry involved by described functional coating is that coating adhesive, silane and crosslinking agent are added pulping tank, after stirring, with ammoniacal liquor regulation pH to 7.5～8.5 scopes, stand 2～4 hours, then the mode using roller coat is applied to terylene scrim surfaces, dry 0.5 hour under 80 DEG C of environment, solidify under 120～135 DEG C of environment 1～1.5 hour, balance more than 8 hours the most under field conditions (factors).
Roller coat formula damage resistant dacron fabric the most according to claim 1, it is characterised in that: the institutional framework of described terylene base fabric uses antarafacial tissue.
Roller coat formula damage resistant dacron fabric the most according to claim 2, it is characterised in that: described antarafacial tissue includes selecting 1/2 twill, 1/3 twill, brokentwlllweave, 1/4 twill or five heddle satin institutional framework.