CN105734989A - Spray coating type anti-scratch polyester fabric lining - Google Patents

Spray coating type anti-scratch polyester fabric lining Download PDF

Info

Publication number
CN105734989A
CN105734989A CN201610187888.3A CN201610187888A CN105734989A CN 105734989 A CN105734989 A CN 105734989A CN 201610187888 A CN201610187888 A CN 201610187888A CN 105734989 A CN105734989 A CN 105734989A
Authority
CN
China
Prior art keywords
coating
slurry
hours
spraying
spray coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610187888.3A
Other languages
Chinese (zh)
Inventor
周生保
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Haipeng Special Vehicles Co Ltd
Original Assignee
Jiangsu Haipeng Special Vehicles Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Haipeng Special Vehicles Co Ltd filed Critical Jiangsu Haipeng Special Vehicles Co Ltd
Priority to CN201610187888.3A priority Critical patent/CN105734989A/en
Publication of CN105734989A publication Critical patent/CN105734989A/en
Pending legal-status Critical Current

Abstract

The invention relates to a spray coating type anti-scratch polyester fabric lining. The polyester fabric lining is characterized by decorating the outer surface of a polyester base cloth with a functional coating by adopting spray coating, wherein the coating slurry to which the functional coating relates is prepared by adding a coating adhesive, silane and a crosslinking agent to a slurry preparation tank, stirring the materials uniformly, then regulating the pH value to 7.5-8.5 with ammonia water, standing for 2-4 hours, then applying the slurry to the surface of the polyester base cloth by adopting spray coating, drying the slurry at 80 DEG C for 0.5 hour, curing the slurry at 120-135 DEG C for 1-1.5 hours and finally balancing the slurry under natural conditions for more than 8 hours. After the surface of the polyester fabric lining is protected by the coated material, the fabric has a better anti-scratch characteristic, thus improving the quality in use of the lining.

Description

A kind of spraying cloth of coating-type damage resistant dacron fabric
Technical field
The invention belongs to dacron fabric technical field, be specifically related to the spraying coating dacron fabric of a kind of damage resistant.
Background technology
Terylene is an important kind in synthetic fibers, is the trade name of China's polyester fiber.It is with p-phthalic acid (PTA) or dimethyl terephthalate (DMT) (DMT) and ethylene glycol (EG) for raw material through esterification or ester exchange and polycondensation reaction prepared fiber-forming polymer--polyethylene terephthalate (PET), through the fiber that spinning and post processing are made.
Dacron has higher intensity and elastic recovery capability, therefore, and its strong durable, wash and wear.Dacron hygroscopicity is poor, and dress has a feeling of oppression and heat, simultaneously easily static electrification, stain dust, affect attractive in appearance and comfortableness.After but washing very easily dry, and wet decline hardly by force, indeformable, have good wash and wear performance.Terylene is to close the fabric that in fine fabric, thermostability is best, has thermoplasticity, can manufacture accordion-pleated skirt, and rivel is lasting.Meanwhile, the melt resistance of dacron is poor, meets flue dust, Mars etc. and is easily formed hole.Therefore, the contact of cigarette end, spark etc. should be avoided when wearing as far as possible.The light resistance of dacron is better, and except ratio is except acrylon difference, its sun-proof ability surpasses natural fabric.The New function continually developing fabric is the trend of dacron fabric development.
Summary of the invention
It is an object of the invention to provide the spraying cloth of coating-type dacron fabric of a kind of damage resistant.
This invention address that the technical scheme that the problems referred to above adopt is: a kind of spraying cloth of coating-type damage resistant dacron fabric, be terylene base fabric outer surface adopt spraying coating mode decorate a layer function coating, what the coating involved by described functional coating was starched is prepared by coating adhesive, silane and cross-linking agent add pulping tank, after stirring, pH to 7.5～8.5 scope is regulated with ammonia, stand 2～4 hours, then the mode adopting spraying coating is applied to terylene scrim surfaces, dry 0.5 hour under 80 DEG C of environment, solidify 1～1.5 hour under 120～135 DEG C of environment, last balance more than 8 hours under field conditions (factors).
Preferably, the organizational structure of described terylene base fabric adopts antarafacial tissue, in order to coating is better coated with and the solidification in fabric later stage balances, and increases the service life.
Preferably, antarafacial tissue includes selecting 1/2 twill, 1/3 twill, brokentwlllweave, 1/4 twill or five heddle satin organizational structure.
Compared with prior art, it is an advantage of the current invention that: provide the damage resistant dacron fabric of a kind of cloth of coating-type of spraying, after spray-painting is protected, make dacron fabric have better scratch resistant performance, improve the use quality of dacron fabric.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is described in further detail.
Embodiment 1
Damage resistant dacron fabric, be terylene base fabric outer surface adopt spraying coating mode decorate a layer function coating, what the coating involved by described functional coating was starched is prepared by coating adhesive, silane and cross-linking agent are added pulping tank, after stirring, pH to 8 scope is regulated with ammonia, stand 2～4 hours, then the mode adopting spraying coating is applied to terylene scrim surfaces, dry 0.5 hour under 80 DEG C of environment, solidify 1.5 hours under 120 DEG C of environment, finally balance more than 8 hours under field conditions (factors).
The organizational structure of the terylene base fabric in the present embodiment is 1/2 twill-weave structure.
The present embodiment gained dacron fabric has good damage resistant characteristic.
Embodiment 2
Damage resistant dacron fabric, be terylene base fabric outer surface adopt spraying coating mode decorate a layer function coating, what the coating involved by described functional coating was starched is prepared by coating adhesive, silane and cross-linking agent are added pulping tank, after stirring, pH to 7.5 scope is regulated with ammonia, stand 2～4 hours, then the mode adopting spraying coating is applied to terylene scrim surfaces, dry 0.5 hour under 80 DEG C of environment, solidify 1 hour under 130 DEG C of environment, finally balance more than 8 hours under field conditions (factors).
In the present embodiment, the organizational structure of terylene base fabric is brokentwlllweave organizational structure.
The present embodiment gained dacron fabric has good damage resistant characteristic.
Embodiment 3
Damage resistant dacron fabric, be terylene base fabric outer surface adopt spraying coating mode decorate a layer function coating, what the coating involved by described functional coating was starched is prepared by coating adhesive, silane and cross-linking agent are added pulping tank, after stirring, pH to 8.5 scope is regulated with ammonia, stand 2～4 hours, then the mode adopting spraying coating is applied to terylene scrim surfaces, dry 0.5 hour under 80 DEG C of environment, solidify 1 hour under 120 DEG C of environment, finally balance more than 8 hours under field conditions (factors).
In the present embodiment, the organizational structure of terylene base fabric is five heddle satin organizational structure.
The present embodiment gained dacron fabric has good damage resistant characteristic.

Claims (3)

1. a spraying cloth of coating-type damage resistant dacron fabric, it is characterized in that: be terylene base fabric outer surface adopt spraying coating mode decorate a layer function coating, what the coating involved by described functional coating was starched is prepared by coating adhesive, silane and cross-linking agent add pulping tank, after stirring, pH to 7.5～8.5 scope is regulated with ammonia, stand 2～4 hours, then the mode adopting spraying coating is applied to terylene scrim surfaces, dry 0.5 hour under 80 DEG C of environment, solidify 1～1.5 hour under 120～135 DEG C of environment, last balance more than 8 hours under field conditions (factors).
2. spraying cloth of coating-type damage resistant dacron fabric according to claim 1, it is characterised in that: the organizational structure of described terylene base fabric adopts antarafacial tissue.
3. spraying cloth of coating-type damage resistant dacron fabric according to claim 2, it is characterised in that: described antarafacial tissue includes selecting 1/2 twill, 1/3 twill, brokentwlllweave, 1/4 twill or five heddle satin organizational structure.
CN201610187888.3A 2016-03-30 2016-03-30 Spray coating type anti-scratch polyester fabric lining Pending CN105734989A (en)