CN105755839A - Anti-fogging flow coating type acrylic fabric - Google Patents
Anti-fogging flow coating type acrylic fabric Download PDFInfo
- Publication number
- CN105755839A CN105755839A CN201610232566.6A CN201610232566A CN105755839A CN 105755839 A CN105755839 A CN 105755839A CN 201610232566 A CN201610232566 A CN 201610232566A CN 105755839 A CN105755839 A CN 105755839A
- Authority
- CN
- China
- Prior art keywords
- fabric
- coating
- flow coat
- acrylic
- environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to anti-fogging flow coating type acrylic fabric.The anti-fogging flow coating type acrylic fabric is characterized in that a functional coating layer is decorated on the outer surface of acrylic base cloth in a flow coating manner.A preparation method of the coating slurry related to the functional coating layer includes: adding coating adhesive, silane, anti-fogging agent and crosslinking agent into a slurry preparing pot, evenly stirring, using ammonia water to adjust pH to 7.5-8.5, and standing for 2-4 hours.The coating slurry is applied to the surface of the acrylic base cloth in a flow coating manner, dried for 0.5 hours under an environment of 80 DEG C, cured for 1-1.5 hours under an environment of 120-135 DEG C and balanced for more than 8 hours under a natural condition.Due to the fact that the surface of the acrylic fabric is protected by the coating layer, the fabric has good anti-fogging property, and the use quality of the fabric is increased.
Description
Technical field
The invention belongs to acrylic fabric fabric technical field, be specifically related to a kind of anti-flow coat acrylic fabric fabric hazed.
Background technology
Acrylic fiber has the title of artificial wool.Have dye soft, bulk, easy, lovely luster, fast light, antibacterial, be not afraid of advantages such as damaging by worms, can pure spin or with natural fibre blended according to the requirement of different purposes, its textile is widely used in the fields such as clothing, decoration, industry.
Acrylic fabric has higher intensity and elastic recovery capability, therefore, and its strong durable, wash and wear.Acrylic fabric hygroscopicity is poor, and dress has a feeling of oppression and heat, simultaneously easily static electrification, stain dust, affect attractive in appearance and comfortableness.After but washing very easily dry, and wet decline hardly by force, indeformable, have good wash and wear performance.Acrylon are to close the fabric that in fine fabric, thermostability is best, have thermoplasticity, can manufacture accordion-pleated skirt, and rivel is lasting.Meanwhile, the melt resistance of acrylic fabric is poor, meets flue dust, Mars etc. and is easily formed hole.Therefore, the contact of cigarette end, spark etc. should be avoided when wearing as far as possible.The light resistance of acrylic fabric is better, and except ratio is except acrylon difference, its sun-proof ability surpasses natural fabric.The New function continually developing fabric is the trend of acrylic fabric fabric development.
Summary of the invention
It is an object of the invention to provide a kind of anti-flow coat formula acrylic fabric fabric hazed.
This invention address that the technical scheme that the problems referred to above adopt is: a kind of anti-flow coat formula acrylic fabric fabric hazed, be acrylon base fabric outer surface adopt flow coat mode decorate a layer function coating, what the coating involved by described functional coating was starched is prepared by coating adhesive, silane, antifoggant and cross-linking agent add pulping tank, after stirring, pH to 7.5~8.5 scope is regulated with ammonia, stand 2~4 hours, then the mode adopting flow coat is applied to acrylon scrim surfaces, dry 0.5 hour under 80 DEG C of environment, solidify 1~1.5 hour under 120~135 DEG C of environment, last balance more than 8 hours under field conditions (factors).
Preferably, the organizational structure of described acrylon base fabric adopts antarafacial tissue, in order to coating is better coated with and the solidification in fabric later stage balances, and increases the service life.
Preferably, antarafacial tissue includes selecting 1/2 twill, 1/3 twill, brokentwlllweave, 1/4 twill or five heddle satin organizational structure.
Compared with prior art, it is an advantage of the current invention that: provide the anti-acrylic fabric fabric that hazes of a kind of flow coat formula, after flow coat coating is protected, make acrylic fabric fabric have the better anti-performance that hazes, improve the use quality of acrylic fabric fabric.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is described in further detail.
Embodiment 1
The anti-acrylic fabric fabric that hazes, be acrylon base fabric outer surface adopt flow coat mode decorate a layer function coating, what the coating involved by described functional coating was starched is prepared by coating adhesive, silane, antifoggant and cross-linking agent are added pulping tank, after stirring, pH to 8 scope is regulated with ammonia, stand 2~4 hours, then the mode adopting flow coat is applied to acrylon scrim surfaces, dry 0.5 hour under 80 DEG C of environment, solidify 1.5 hours under 120 DEG C of environment, finally balance more than 8 hours under field conditions (factors).
The organizational structure of the acrylon base fabric in the present embodiment is 1/2 twill-weave structure.
The present embodiment gained acrylic fabric fabric has and has well resisted mist characteristic.
Embodiment 2
The anti-acrylic fabric fabric that hazes, be acrylon base fabric outer surface adopt flow coat mode decorate a layer function coating, what the coating involved by described functional coating was starched is prepared by coating adhesive, silane, antifoggant and cross-linking agent are added pulping tank, after stirring, pH to 7.5 scope is regulated with ammonia, stand 2~4 hours, then the mode adopting flow coat is applied to acrylon scrim surfaces, dry 0.5 hour under 80 DEG C of environment, solidify 1 hour under 130 DEG C of environment, finally balance more than 8 hours under field conditions (factors).
In the present embodiment, the organizational structure of acrylon base fabric is brokentwlllweave organizational structure.
The present embodiment gained acrylic fabric fabric has and has well resisted mist characteristic.
Embodiment 3
The anti-acrylic fabric fabric that hazes, be acrylon base fabric outer surface adopt flow coat mode decorate a layer function coating, what the coating involved by described functional coating was starched is prepared by coating adhesive, silane, antifoggant and cross-linking agent are added pulping tank, after stirring, pH to 8.5 scope is regulated with ammonia, stand 2~4 hours, then the mode adopting flow coat is applied to acrylon scrim surfaces, dry 0.5 hour under 80 DEG C of environment, solidify 1 hour under 120 DEG C of environment, finally balance more than 8 hours under field conditions (factors).
In the present embodiment, the organizational structure of acrylon base fabric is five heddle satin organizational structure.
The present embodiment gained acrylic fabric fabric has and has well resisted mist characteristic.
Claims (3)
1. the anti-flow coat formula acrylic fabric fabric hazed, it is characterized in that: be acrylon base fabric outer surface adopt flow coat mode decorate a layer function coating, what the coating involved by described functional coating was starched is prepared by coating adhesive, silane, antifoggant and cross-linking agent add pulping tank, after stirring, pH to 7.5~8.5 scope is regulated with ammonia, stand 2~4 hours, then the mode adopting flow coat is applied to acrylon scrim surfaces, dry 0.5 hour under 80 DEG C of environment, solidify 1~1.5 hour under 120~135 DEG C of environment, last balance more than 8 hours under field conditions (factors).
2. the anti-flow coat formula acrylic fabric fabric hazed according to claim 1, it is characterised in that: the organizational structure of described acrylon base fabric adopts antarafacial tissue.
3. the anti-flow coat formula acrylic fabric fabric hazed according to claim 2, it is characterised in that: described antarafacial tissue includes selecting 1/2 twill, 1/3 twill, brokentwlllweave, 1/4 twill or five heddle satin organizational structure.