CN105671974A - Dip coated type antimicrobial acrylic fabric - Google Patents

Dip coated type antimicrobial acrylic fabric Download PDF

Info

Publication number
CN105671974A
CN105671974A CN201610187889.8A CN201610187889A CN105671974A CN 105671974 A CN105671974 A CN 105671974A CN 201610187889 A CN201610187889 A CN 201610187889A CN 105671974 A CN105671974 A CN 105671974A
Authority
CN
China
Prior art keywords
fabric
coating
dip coated
acrylic
acrylon
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610187889.8A
Other languages
Chinese (zh)
Inventor
周生保
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Haipeng Special Vehicles Co Ltd
Original Assignee
Jiangsu Haipeng Special Vehicles Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Haipeng Special Vehicles Co Ltd filed Critical Jiangsu Haipeng Special Vehicles Co Ltd
Priority to CN201610187889.8A priority Critical patent/CN105671974A/en
Publication of CN105671974A publication Critical patent/CN105671974A/en
Pending legal-status Critical Current

Abstract

The invention relates to dip coated antimicrobial acrylic fabric which is characterized by decorating the outer surface of acrylic base cloth with a functional coating. Preparation of coating size related to the functional coating includes: adding coating glue, silane, biocide and cross linking agent into a sizing tank; using ammonia water to adjust pH to 7.5-8.5 after well stirring; allowing standing for 2-4 h; adopting a mode of dip coating to apply on the surface of the acrylic base cloth; drying for 0.5 h at temperature of 80 DEG C, curing for 1-1.5 h at temperature of 20-135 DEG C, and balancing for more than 8 h under natural conditions. After the surface of the acrylic fabric is protected by a coating material, the fabric has better antimicrobial characteristics, so that using quality of the fabric is improved.

Description

A kind of dip coated formula antimicrobial acrylic fabric fabric
Technical field
The invention belongs to acrylic fabric fabric technical field, be specifically related to a kind of antimicrobial dip coated acrylic fabric fabric.
Background technology
Acrylic fiber has the title of artificial wool. Have dye soft, bulk, easy, lovely luster, fast light, antibacterial, be not afraid of advantages such as damaging by worms, can pure spin or with natural fibre blended according to the requirement of different purposes, its textile is widely used in the fields such as clothing, decoration, industry.
Acrylic fabric has higher intensity and elastic recovery capability, therefore, and its strong durable, wash and wear. Acrylic fabric hygroscopicity is poor, and dress has a feeling of oppression and heat, simultaneously easily static electrification, stain dust, affect attractive in appearance and comfortableness. After but washing very easily dry, and wet decline hardly by force, indeformable, have good wash and wear performance. Acrylon are to close the fabric that in fine fabric, thermostability is best, have thermoplasticity, can manufacture accordion-pleated skirt, and rivel is lasting. Meanwhile, the melt resistance of acrylic fabric is poor, meets flue dust, Mars etc. and is easily formed hole. Therefore, the contact of cigarette end, spark etc. should be avoided when wearing as far as possible. The light resistance of acrylic fabric is better, and except ratio is except acrylon difference, its sun-proof ability surpasses natural fabric. The New function continually developing fabric is the trend of acrylic fabric fabric development.
Summary of the invention
It is an object of the invention to provide a kind of antimicrobial dip coated formula acrylic fabric fabric.
This invention address that the technical scheme that the problems referred to above adopt is: a kind of dip coated formula antimicrobial acrylic fabric fabric, be acrylon base fabric outer surface adopt dip coated mode decorate a layer function coating, what the coating involved by described functional coating was starched is prepared by coating adhesive, silane, Biocide and cross-linking agent add pulping tank, after stirring, pH to 7.5～8.5 scope is regulated with ammonia, stand 2～4 hours, then the mode adopting dip coated is applied to acrylon scrim surfaces, dry 0.5 hour under 80 DEG C of environment, solidify 1～1.5 hour under 120～135 DEG C of environment, last balance more than 8 hours under field conditions (factors).
Preferably, the organizational structure of described acrylon base fabric adopts antarafacial tissue, in order to coating is better coated with and the solidification in fabric later stage balances, and increases the service life.
Preferably, antarafacial tissue includes selecting 1/2 twill, 1/3 twill, brokentwlllweave, 1/4 twill or five heddle satin organizational structure.
Compared with prior art; it is an advantage of the current invention that: provide the antimicrobial acrylic fabric fabric of a kind of dip coated formula; after dip coating is protected, make acrylic fabric fabric have better antimicrobial properties, improve the use quality of acrylic fabric fabric.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is described in further detail.
Embodiment 1
Antimicrobial acrylic fabric fabric, be acrylon base fabric outer surface adopt dip coated mode decorate a layer function coating, what the coating involved by described functional coating was starched is prepared by coating adhesive, silane, Biocide and cross-linking agent are added pulping tank, after stirring, pH to 8 scope is regulated with ammonia, stand 2～4 hours, then the mode adopting dip coated is applied to acrylon scrim surfaces, dry 0.5 hour under 80 DEG C of environment, solidify 1.5 hours under 120 DEG C of environment, finally balance more than 8 hours under field conditions (factors).
The organizational structure of the acrylon base fabric in the present embodiment is 1/2 twill-weave structure.
The present embodiment gained acrylic fabric fabric has good antimicrobial property.
Embodiment 2
Antimicrobial acrylic fabric fabric, be acrylon base fabric outer surface adopt dip coated mode decorate a layer function coating, what the coating involved by described functional coating was starched is prepared by coating adhesive, silane, Biocide and cross-linking agent are added pulping tank, after stirring, pH to 7.5 scope is regulated with ammonia, stand 2～4 hours, then the mode adopting dip coated is applied to acrylon scrim surfaces, dry 0.5 hour under 80 DEG C of environment, solidify 1 hour under 130 DEG C of environment, finally balance more than 8 hours under field conditions (factors).
In the present embodiment, the organizational structure of acrylon base fabric is brokentwlllweave organizational structure.
The present embodiment gained acrylic fabric fabric has good antimicrobial property.
Embodiment 3
Antimicrobial acrylic fabric fabric, be acrylon base fabric outer surface adopt dip coated mode decorate a layer function coating, what the coating involved by described functional coating was starched is prepared by coating adhesive, silane, Biocide and cross-linking agent are added pulping tank, after stirring, pH to 8.5 scope is regulated with ammonia, stand 2～4 hours, then the mode adopting dip coated is applied to acrylon scrim surfaces, dry 0.5 hour under 80 DEG C of environment, solidify 1 hour under 120 DEG C of environment, finally balance more than 8 hours under field conditions (factors).
In the present embodiment, the organizational structure of acrylon base fabric is five heddle satin organizational structure.
The present embodiment gained acrylic fabric fabric has good antimicrobial property.

Claims (3)

1. a dip coated formula antimicrobial acrylic fabric fabric, it is characterized in that: be acrylon base fabric outer surface adopt dip coated mode decorate a layer function coating, what the coating involved by described functional coating was starched is prepared by coating adhesive, silane, Biocide and cross-linking agent add pulping tank, after stirring, pH to 7.5～8.5 scope is regulated with ammonia, stand 2～4 hours, then the mode adopting dip coated is applied to acrylon scrim surfaces, dry 0.5 hour under 80 DEG C of environment, solidify 1～1.5 hour under 120～135 DEG C of environment, last balance more than 8 hours under field conditions (factors).
2. dip coated formula antimicrobial acrylic fabric fabric according to claim 1, it is characterised in that: the organizational structure of described acrylon base fabric adopts antarafacial tissue.
3. dip coated formula antimicrobial acrylic fabric fabric according to claim 2, it is characterised in that: described antarafacial tissue includes selecting 1/2 twill, 1/3 twill, brokentwlllweave, 1/4 twill or five heddle satin organizational structure.
CN201610187889.8A 2016-03-30 2016-03-30 Dip coated type antimicrobial acrylic fabric Pending CN105671974A (en)