CN105671982A - Vacuum evaporation coating type antimicrobial acrylic textile fabric - Google Patents
Vacuum evaporation coating type antimicrobial acrylic textile fabric Download PDFInfo
- Publication number
- CN105671982A CN105671982A CN201610187938.8A CN201610187938A CN105671982A CN 105671982 A CN105671982 A CN 105671982A CN 201610187938 A CN201610187938 A CN 201610187938A CN 105671982 A CN105671982 A CN 105671982A
- Authority
- CN
- China
- Prior art keywords
- coating
- fabric
- acrylic
- vacuum
- evaporation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a vacuum evaporation coating type antimicrobial acrylic textile fabric. The outer surface of acrylic base cloth is decorated with a layer of functional coating by vacuum evaporation coating; and the coating slurry of the functional coating is prepared by the following steps: adding a coating adhesive, silane, a biocide and a cross-linking agent into a slurrying tank; stirring uniformly; adjusting the pH to 7.5-8.5 using ammonia water; standing for 2-4 hours; applying the product to the surface of the acrylic base cloth by vacuum evaporation coating; drying for 0.5 hour at 80 DEG C; curing for 1-1.5 hours at 120-135 DEG C; and finally, balancing for more than or equal to 8 hours in natural conditions. After the surface of the acrylic textile fabric is protected by the coating material, the textile has better antimicrobial characteristic, and the using quality of the fabric is improved.
Description
Technical field
The invention belongs to acrylic fabric fabric technical field, it is specifically related to a kind of antimicrobial vacuum-evaporation coating acrylic fabric fabric.
Background technology
Acrylic fiber has the title of lanital. Have dye soft, bulk, easy, lovely luster, fast light, antibacterial, be not afraid of advantages such as damaging by worms, can pure spin according to the requirement of different purposes or with natural fibre blended, its textiles is widely used in the fields such as clothes, decoration, industry.
Acrylic fabric has higher intensity and elastic recovery capability, therefore, and its strong durable, wash and wear. Acrylic fabric water absorbability is poor, and dress has sultry sense, simultaneously easily band electrostatic, stain dust, affect attractive in appearance and comfortable property. After but washing very easily dry, and wet almost do not decline by force, be not out of shape, have good wash and wear performance. Acrylic fibers close the fabric that in fine fabric, thermotolerance is best, has thermoplasticity, can manufacture accordion-pleated skirt, and rivel is lasting. Meanwhile, the melt resistance of acrylic fabric is poor, meets cigarette ash, Mars etc. and easily forms hole. Therefore, the contact of cigarette end, spark etc. should be avoided when wearing as far as possible. The photostabilization of acrylic fabric is better, except than, except acrylic fibers difference, its resistance to solarization ability surpasses natural fabric. The New function continually developing fabric is the trend of acrylic fabric fabric development.
Summary of the invention
It is an object of the invention to provide a kind of antimicrobial vacuum-evaporation cloth of coating-type acrylic fabric fabric.
The present invention's technical scheme adopted that solves the problem is: a kind of antimicrobial acrylic fabric fabric of vacuum-evaporation cloth of coating-type, be acrylic fibers base cloth outside surface adopt vacuum-evaporation coating mode decorate one layer of functional coating, the preparation of the coating slurry involved by described functional coating is by coating adhesive, silane, biocide and linking agent add pulping tank, stir after evenly, pH to 7.5~8.5 scope is regulated with ammoniacal liquor, leave standstill 2~4 hours, then the mode of vacuum-evaporation coating is adopted to be applied to acrylic fibers base cloth surface, dry 0.5 hour under 80 DEG C of environment, solidify 1~1.5 hour under 120~135 DEG C of environment, finally under natural condition, balance more than 8 hours.
Preferably, the weave construction of described acrylic fibers base cloth adopts different covering weave, so that coating is better coated with and the solidification in fabric later stage balance, extends work-ing life.
Preferably, different covering weave comprises and selects 1/2 twill, 1/3 twill, cross twill, 1/4 twill or five pieces of satin organizational structures.
Compared with prior art; it is an advantage of the current invention that: the antimicrobial acrylic fabric fabric providing a kind of vacuum-evaporation cloth of coating-type; after vacuum-evaporation coating protection, acrylic fabric fabric is made to have better antimicrobial properties, it is to increase the using character of acrylic fabric fabric.
Embodiment
Below in conjunction with embodiment, the present invention is described in further detail.
Embodiment 1
Antimicrobial acrylic fabric fabric, be acrylic fibers base cloth outside surface adopt vacuum-evaporation coating mode decorate one layer of functional coating, the preparation of the coating slurry involved by described functional coating is that coating adhesive, silane, biocide and linking agent are added pulping tank, stir after evenly, pH to 8 scope is regulated with ammoniacal liquor, leave standstill 2~4 hours, then the mode of vacuum-evaporation coating is adopted to be applied to acrylic fibers base cloth surface, dry 0.5 hour under 80 DEG C of environment, solidify 1.5 hours under 120 DEG C of environment, finally under natural condition, balance more than 8 hours.
The weave construction of the acrylic fibers base cloth in the present embodiment is 1/2 twill weave structure.
The present embodiment gained acrylic fabric fabric has good antimicrobial property.
Embodiment 2
Antimicrobial acrylic fabric fabric, be acrylic fibers base cloth outside surface adopt vacuum-evaporation coating mode decorate one layer of functional coating, the preparation of the coating slurry involved by described functional coating is that coating adhesive, silane, biocide and linking agent are added pulping tank, stir after evenly, pH to 7.5 scope is regulated with ammoniacal liquor, leave standstill 2~4 hours, then the mode of vacuum-evaporation coating is adopted to be applied to acrylic fibers base cloth surface, dry 0.5 hour under 80 DEG C of environment, solidify 1 hour under 130 DEG C of environment, finally under natural condition, balance more than 8 hours.
In the present embodiment, the weave construction of acrylic fibers base cloth is cross twill weave construction.
The present embodiment gained acrylic fabric fabric has good antimicrobial property.
Embodiment 3
Antimicrobial acrylic fabric fabric, be acrylic fibers base cloth outside surface adopt vacuum-evaporation coating mode decorate one layer of functional coating, the preparation of the coating slurry involved by described functional coating is that coating adhesive, silane, biocide and linking agent are added pulping tank, stir after evenly, pH to 8.5 scope is regulated with ammoniacal liquor, leave standstill 2~4 hours, then the mode of vacuum-evaporation coating is adopted to be applied to acrylic fibers base cloth surface, dry 0.5 hour under 80 DEG C of environment, solidify 1 hour under 120 DEG C of environment, finally under natural condition, balance more than 8 hours.
In the present embodiment, the weave construction of acrylic fibers base cloth is five pieces of satin organizational structures.
The present embodiment gained acrylic fabric fabric has good antimicrobial property.
Claims (3)
1. the antimicrobial acrylic fabric fabric of vacuum-evaporation cloth of coating-type, it is characterized in that: be acrylic fibers base cloth outside surface adopt vacuum-evaporation coating mode decorate one layer of functional coating, the preparation of the coating slurry involved by described functional coating is by coating adhesive, silane, biocide and linking agent add pulping tank, stir after evenly, pH to 7.5~8.5 scope is regulated with ammoniacal liquor, leave standstill 2~4 hours, then the mode of vacuum-evaporation coating is adopted to be applied to acrylic fibers base cloth surface, dry 0.5 hour under 80 DEG C of environment, solidify 1~1.5 hour under 120~135 DEG C of environment, finally under natural condition, balance more than 8 hours.
2. the antimicrobial acrylic fabric fabric of vacuum-evaporation cloth of coating-type according to claim 1, it is characterised in that: the weave construction of described acrylic fibers base cloth adopts different covering weave.
3. the antimicrobial acrylic fabric fabric of vacuum-evaporation cloth of coating-type according to claim 2, it is characterised in that: described different covering weave comprises and selects 1/2 twill, 1/3 twill, cross twill, 1/4 twill or five pieces of satin organizational structures.