CN105671985A - Flow coating type anti-corrosion terylene textile fabric - Google Patents
Flow coating type anti-corrosion terylene textile fabric Download PDFInfo
- Publication number
- CN105671985A CN105671985A CN201610187956.6A CN201610187956A CN105671985A CN 105671985 A CN105671985 A CN 105671985A CN 201610187956 A CN201610187956 A CN 201610187956A CN 105671985 A CN105671985 A CN 105671985A
- Authority
- CN
- China
- Prior art keywords
- coating
- stream
- base cloth
- hours
- terylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a flow coating type anti-corrosion terylene textile fabric. The outer surface of terylene base cloth is decorated with a layer of functional coating by flow coating; and the coating slurry of the functional coating is prepared by the following steps: adding a coating adhesive, silane, a preservative and a cross-linking agent into a slurrying tank; stirring uniformly; adjusting the pH to 7.5-8.5 using ammonia water; standing for 2-4 hours; applying the product to the surface of the terylene base cloth by flow coating; drying for 0.5 hour at 80 DEG C; curing for 1-1.5 hours at 120-135 DEG C; and finally, balancing for more than or equal to 8 hours in natural conditions. After the surface of the terylene textile fabric is protected by the coating material, the textile has better anti-corrosion characteristic, and the using quality of the fabric is improved.
Description
Technical field
The invention belongs to polyester piece good fabric technical field, it is specifically related to a kind of anticorrosive stream and is coated with polyester piece good fabric.
Background technology
Terylene is the important kind of in synthon, is the trade name of China's trevira. It is by raw material of pure terephthalic acid (PTA) or dimethyl terephthalate (DMT) (DMT) and ethylene glycol (EG) through esterification or transesterify and polycondensation and obtained fiber-forming polymer--polyethylene terephthalate (PET), through the fiber that spinning and aftertreatment are made.
Polyester piece good has higher intensity and elastic recovery capability, therefore, and its strong durable, wash and wear. Polyester piece good water absorbability is poor, and dress has sultry sense, simultaneously easily band electrostatic, stain dust, affect attractive in appearance and comfortable property. After but washing very easily dry, and wet almost do not decline by force, be not out of shape, have good wash and wear performance. Terylene closes the fabric that in fine fabric, thermotolerance is best, has thermoplasticity, can manufacture accordion-pleated skirt, and rivel is lasting. Meanwhile, the melt resistance of polyester piece good is poor, meets cigarette ash, Mars etc. and easily forms hole. Therefore, the contact of cigarette end, spark etc. should be avoided when wearing as far as possible. The photostabilization of polyester piece good is better, except than, except acrylic fibers difference, its resistance to solarization ability surpasses natural fabric. The New function continually developing fabric is the trend of polyester piece good fabric development.
Summary of the invention
It is an object of the invention to provide a kind of anticorrosive stream and it is coated with formula polyester piece good fabric.
The present invention's technical scheme adopted that solves the problem is: a kind of stream anticorrosive polyester piece good fabric of painting formula, be terylene base cloth outside surface adopt stream be coated with mode decorate one layer of functional coating, the preparation of the coating slurry involved by described functional coating is by coating adhesive, silane, sanitas and linking agent add pulping tank, stir after evenly, pH to 7.5～8.5 scope is regulated with ammoniacal liquor, leave standstill 2～4 hours, then the mode adopting stream to be coated with is applied to terylene base cloth surface, dry 0.5 hour under 80 DEG C of environment, solidify 1～1.5 hour under 120～135 DEG C of environment, finally under natural condition, balance more than 8 hours.
Preferably, the weave construction of described terylene base cloth adopts different covering weave, so that coating is better coated with and the solidification in fabric later stage balance, extends work-ing life.
Preferably, different covering weave comprises and selects 1/2 twill, 1/3 twill, cross twill, 1/4 twill or five pieces of satin organizational structures.
Compared with prior art, it is an advantage of the current invention that: provide a kind of anticorrosive polyester piece good fabric flowing painting formula, after overcurrent coating layer is protected, make polyester piece good fabric have better corrosion resistance, it is to increase the using character of polyester piece good fabric.
Embodiment
Below in conjunction with embodiment, the present invention is described in further detail.
Embodiment 1
Anticorrosive polyester piece good fabric, be terylene base cloth outside surface adopt stream be coated with mode decorate one layer of functional coating, the preparation of the coating slurry involved by described functional coating is that coating adhesive, silane, sanitas and linking agent are added pulping tank, stir after evenly, pH to 8 scope is regulated with ammoniacal liquor, leave standstill 2～4 hours, then the mode adopting stream to be coated with is applied to terylene base cloth surface, dry 0.5 hour under 80 DEG C of environment, solidify 1.5 hours under 120 DEG C of environment, finally under natural condition, balance more than 8 hours.
The weave construction of the terylene base cloth in the present embodiment is 1/2 twill weave structure.
The present embodiment gained polyester piece good fabric has good anticorrosion properties.
Embodiment 2
Anticorrosive polyester piece good fabric, be terylene base cloth outside surface adopt stream be coated with mode decorate one layer of functional coating, the preparation of the coating slurry involved by described functional coating is that coating adhesive, silane, sanitas and linking agent are added pulping tank, stir after evenly, pH to 7.5 scope is regulated with ammoniacal liquor, leave standstill 2～4 hours, then the mode adopting stream to be coated with is applied to terylene base cloth surface, dry 0.5 hour under 80 DEG C of environment, solidify 1 hour under 130 DEG C of environment, finally under natural condition, balance more than 8 hours.
In the present embodiment, the weave construction of terylene base cloth is cross twill weave construction.
The present embodiment gained polyester piece good fabric has good anticorrosion properties.
Embodiment 3
Anticorrosive polyester piece good fabric, be terylene base cloth outside surface adopt stream be coated with mode decorate one layer of functional coating, the preparation of the coating slurry involved by described functional coating is that coating adhesive, silane, sanitas and linking agent are added pulping tank, stir after evenly, pH to 8.5 scope is regulated with ammoniacal liquor, leave standstill 2～4 hours, then the mode adopting stream to be coated with is applied to terylene base cloth surface, dry 0.5 hour under 80 DEG C of environment, solidify 1 hour under 120 DEG C of environment, finally under natural condition, balance more than 8 hours.
In the present embodiment, the weave construction of terylene base cloth is five pieces of satin organizational structures.
The present embodiment gained polyester piece good fabric has good anticorrosion properties.
Claims (3)
1. the stream anticorrosive polyester piece good fabric of painting formula, it is characterized in that: be terylene base cloth outside surface adopt stream be coated with mode decorate one layer of functional coating, the preparation of the coating slurry involved by described functional coating is by coating adhesive, silane, sanitas and linking agent add pulping tank, stir after evenly, pH to 7.5～8.5 scope is regulated with ammoniacal liquor, leave standstill 2～4 hours, then the mode adopting stream to be coated with is applied to terylene base cloth surface, dry 0.5 hour under 80 DEG C of environment, solidify 1～1.5 hour under 120～135 DEG C of environment, finally under natural condition, balance more than 8 hours.
2. the anticorrosive polyester piece good fabric of stream painting formula according to claim 1, it is characterised in that: the weave construction of described terylene base cloth adopts different covering weave.
3. the anticorrosive polyester piece good fabric of stream painting formula according to claim 2, it is characterised in that: described different covering weave comprises and selects 1/2 twill, 1/3 twill, cross twill, 1/4 twill or five pieces of satin organizational structures.