CN107268156A - Weave the method and tmaterial of warp-direction stretch tmaterial - Google Patents
Weave the method and tmaterial of warp-direction stretch tmaterial Download PDFInfo
- Publication number
- CN107268156A CN107268156A CN201710377196.XA CN201710377196A CN107268156A CN 107268156 A CN107268156 A CN 107268156A CN 201710377196 A CN201710377196 A CN 201710377196A CN 107268156 A CN107268156 A CN 107268156A
- Authority
- CN
- China
- Prior art keywords
- yarn
- tmaterial
- warp
- dye
- warp thread
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The application provides a kind of method and tmaterial for weaving warp-direction stretch tmaterial.This method comprises the following steps:75D+40D empty bag polyester bag spandex filament is warp thread;40S combed cotton yarns and 40S acrylic staples yarn are weft yarn;Warp thread uses raw white yarn, and cheese is obtained after excessively soft winder after pre-treatment;Acrylic staples yarn carry out successively loose yarn, deoil, dye, cleaning, excessively soft or upper electrostatic agent, dehydration, rewinding processing;Combed cotton yarn sequentially pass through winder, loose yarn, pre-treatment, dye, soap, fixation, softness, dehydration, rewinding processing;Using sectional warper, the unwinding tension of warping is more than winding tension, allows warp thread to be tensioned in warp beam;Speed of the speed less than sizing roller of yarn roller is drawn in control during slurry silk;Weave obtaining fabric using big computer jacquard, computer input flower pattern.The tmaterial that the method for the weaving warp-direction stretch tmaterial that the application is provided is obtained, with larger broadwise elasticity, dress is flexible big, and covering property is good.
Description
Technical field
The application is related to field of textiles, more particularly, to a kind of method and tmaterial for weaving warp-direction stretch tmaterial.
Background technology
Decorative pattern on jacquard fabric, which weaves, to be come, and is not common stamp, nor embroidering.Longitude and latitude group is used during face weave
Knit change and form flower case, yarn count is fine, and its needlework density is high, use indeformable, colour-fast, comfort is good, current jacquard weave
Fabric is commercially popular.
Current jacquard fabric, is all Weftwise stretch.Stretch yarn, the tmaterial of big elastic force, in the market are used in warp-wise
Or blank.But people for various profiles clothes demand and three-dimensional cutting the need for so that this kind of jacquard fabric tool
There is the great market space.
In consideration of it, special propose the present invention.
The content of the invention
This application provides a kind of method and tmaterial for weaving warp-direction stretch tmaterial, to solve the above problems.
What the application was realized in:
The application provides a kind of method for weaving warp-direction stretch tmaterial, comprises the following steps:
A. raw material is chosen:75D+40D empty bag polyester bag spandex filament is warp thread;40S combed cotton yarns and 40S acrylic fibers are short
Fine yarn is weft yarn;
B. integrated treatment:
The warp thread uses raw white yarn, and cheese is obtained after excessively soft winder after pre-treatment;
The acrylic staples yarn carry out successively loose yarn, deoil, dye, cleaning, excessively soft or upper electrostatic agent, dehydration, at rewinding
Reason;
The combed cotton yarn sequentially pass through winder, loose yarn, pre-treatment, dye, soap, fixation, softness, dehydration, at rewinding
Reason;
C. warping:Using sectional warper, the unwinding tension of warping is more than winding tension, allows warp thread to be tensioned in warp beam;
D. silk is starched:Speed of the speed less than sizing roller of yarn roller is drawn in control during slurry silk;
E. weave:Weave obtaining fabric using big computer jacquard, computer input flower pattern.
Preferably, methods described also includes Desizing Step, and the Desizing Step is:
Padded under the fabric after machine by amylase liquid, add sodium chloride as catalyst, 40-50 DEG C to bank up 2 small
When, starch size is fully dissolved.
It is further preferred that methods described also includes Final finishing step, the Final finishing step is:
Fabric after being handled through the Desizing Step is subjected to wash water, dried, overfeeding is shaped under the conditions of 170 DEG C, sizing
20 ms/min of speed.
With 70D+40D ACY polyester bag ammonia long filaments, weft yarn is knitted using 40S combed cotton yarns and 40S acrylic staples yarn, color
Weaving, after being produced according to pattern jacquard weave, after weaving, boiling-off, washing, sizing, finished product is the elastic color of more than 30% elastic warp-wise
Knit tmaterial.
Preferably, the method for the dyeing of the acrylic staples yarn is:
The dye of positive ion is first tuned into uniform pulpous state with 40% spirit of vinegar, water dissolving is reheated;By sodium acetate and spirit of vinegar
Being added to the water preparation turns into buffer, adds in dye bath and causes dye bath to keep pH to be 4-5.
It is further preferred that being additionally added retarding agents in the dye bath, the retarding agents is glauber salt or the slow dye of cation
Agent.
Alternatively, the method for the dyeing of the combed cotton yarn is:
The pH for adjusting dye bath is more than 7, bath raio 1: 10, and it is 40 minutes to control heating, soaking time.
Alternatively, in the step c, it is 13 to control warping bar number, and bobbin cradle maximum number is 504, and total quantity of warps is 6300
Root.
Alternatively, in the step d, yarn speed is drawn for 90m/min.
Preferably, in the step e, the warp thread denting uses the acrylic staples yarn and the essence in the weft yarn
Carded cotton yarn 1 is controlled into latitude rate 900m/min every 1 weaving.
The application also provides a kind of tmaterial, and the tmaterial above method is made.
The method and tmaterial of a kind of weaving warp-direction stretch tmaterial provided by the application, can bring following beneficial
Effect:
First, finished product just has very big warp-wise elasticity;Retractility and covering property after ready-made clothes is made good;Second, tmaterial
Dyefastness is good;3rd, production cost is low.
Embodiment
The application is described in further detail with reference to embodiment.It is understood that tool described herein
Body embodiment is used only for explaining the application, rather than the restriction to the application.
Embodiment 1
A kind of method for weaving warp-direction stretch tmaterial, comprises the following steps:
Raw material is chosen:75D+40D empty bag polyester bag spandex filament is warp thread;The acrylic staples of 40S combed cotton yarns and 40S
Yarn is weft yarn;
Integrated treatment:Warp thread uses raw white yarn, and cheese is obtained after excessively soft winder after pre-treatment;Acrylic staples yarn is successively
Carry out loose yarn, deoil, dye, cleaning, excessively soft or upper electrostatic agent, dehydration, rewinding processing;Combed cotton yarn sequentially pass through winder,
Loose yarn, pre-treatment, dye, soap, fixation, softness, dehydration, rewinding processing;
Warping:Using sectional warper, the unwinding tension of warping is more than winding tension, allows warp thread to be tensioned in warp beam;
Starch silk:Speed of the speed less than sizing roller of yarn roller is drawn in control during slurry silk;
Weaving:Weave obtaining fabric using big computer jacquard, computer input flower pattern.
Embodiment 2
A kind of method for weaving warp-direction stretch tmaterial, comprises the following steps:
Raw material is chosen:75D+40D empty bag polyester bag spandex filament is warp thread;The acrylic staples of 40S combed cotton yarns and 40S
Yarn is weft yarn;
Integrated treatment:Warp thread uses raw white yarn, and cheese is obtained after excessively soft winder after pre-treatment;Acrylic staples yarn is successively
Carry out loose yarn, deoil, dye, cleaning, excessively soft or upper electrostatic agent, dehydration, rewinding processing;Combed cotton yarn sequentially pass through winder,
Loose yarn, pre-treatment, dye, soap, fixation, softness, dehydration, rewinding processing;
Warping:Using sectional warper, the unwinding tension of warping is more than winding tension, allows warp thread to be tensioned in warp beam;
Starch silk:Speed of the speed less than sizing roller of yarn roller is drawn in control during slurry silk;
Weaving:Weave obtaining fabric using big computer jacquard, computer input flower pattern;
Desizing:Padded under fabric after machine by amylase liquid, add sodium chloride as catalyst, 40 DEG C are banked up 2 hours,
Starch size is fully dissolved;
Final finishing:Fabric after being handled through Desizing Step carries out wash water, dried, and overfeeding is shaped under the conditions of 170 DEG C, fixed
20 ms/min of type speed.
Embodiment 3
A kind of method for weaving warp-direction stretch tmaterial, comprises the following steps:
Raw material is chosen:75D+40D empty bag polyester bag spandex filament is warp thread;The acrylic staples of 40S combed cotton yarns and 40S
Yarn is weft yarn;
Integrated treatment:Warp thread uses raw white yarn, and cheese is obtained after excessively soft winder after pre-treatment;Acrylic staples yarn is successively
Carry out loose yarn, deoil, dye, cleaning, excessively soft or upper electrostatic agent, dehydration, rewinding processing;Combed cotton yarn sequentially pass through winder,
Loose yarn, pre-treatment, dye, soap, fixation, softness, dehydration, rewinding processing;The method of the dyeing of acrylic staples yarn is:First by sun
Ionic dye is tuned into uniform pulpous state with 40% spirit of vinegar, reheats water dissolving;Sodium acetate and spirit of vinegar are added to the water and are prepared into
For buffer, add in dye bath and cause dye bath to keep pH to be 4;In order to ensure Color, retarding agents has been additionally added in dye bath,
Retarding agents can select glauber salt or cation retarder;The method of the dyeing of combed cotton yarn is:The pH for adjusting dye bath is 7.5
(meta-alkalescence), bath raio 1: 10, it is 40 minutes to control heating, soaking time;
Warping:Using sectional warper, the unwinding tension of warping is more than winding tension, allows warp thread to be tensioned in warp beam;
Starch silk:Speed of the speed less than sizing roller of yarn roller is drawn in control during slurry silk;
Weaving:Weave obtaining fabric using big computer jacquard, computer input flower pattern;
Desizing:Padded under fabric after machine by amylase liquid, add sodium chloride as catalyst, 50 DEG C are banked up 2 hours,
Starch size is fully dissolved;
Final finishing:Fabric after being handled through Desizing Step carries out wash water, dried, and overfeeding is shaped under the conditions of 170 DEG C, fixed
20 ms/min of type speed.
Embodiment 4
A kind of method for weaving warp-direction stretch tmaterial, comprises the following steps:
Raw material is chosen:75D+40D empty bag polyester bag spandex filament is warp thread;The acrylic staples of 40S combed cotton yarns and 40S
Yarn is weft yarn;
Integrated treatment:Warp thread uses raw white yarn, and cheese is obtained after excessively soft winder after pre-treatment;Acrylic staples yarn is successively
Carry out loose yarn, deoil, dye, cleaning, excessively soft or upper electrostatic agent, dehydration, rewinding processing;Combed cotton yarn sequentially pass through winder,
Loose yarn, pre-treatment, dye, soap, fixation, softness, dehydration, rewinding processing;The method of the dyeing of acrylic staples yarn is:First by sun
Ionic dye is tuned into uniform pulpous state with 40% spirit of vinegar, reheats water dissolving;Sodium acetate and spirit of vinegar are added to the water and are prepared into
For buffer, add in dye bath and cause dye bath to keep pH to be 5;In order to ensure Color, retarding agents has been additionally added in dye bath,
Retarding agents can select glauber salt or cation retarder;The method of the dyeing of combed cotton yarn is:Adjust the pH of dye bath (inclined for 8
Alkalescence), bath raio 1: 10, control heating, soaking time be 40 minutes;
Warping:Using sectional warper, the unwinding tension of warping is more than winding tension, allows warp thread to be tensioned in warp beam;Control
Warping bar number processed is 13, and bobbin cradle maximum number is 504, and total quantity of warps is 6300;
Starch silk:Speed of the speed less than sizing roller of yarn roller is drawn in control during slurry silk;
Weaving:Weave obtaining fabric using big computer jacquard, computer input flower pattern;
Desizing:Padded under fabric after machine by amylase liquid, add sodium chloride as catalyst, 45 DEG C are banked up 2 hours,
Starch size is fully dissolved;
Final finishing:Fabric after being handled through Desizing Step carries out wash water, dried, and overfeeding is shaped under the conditions of 170 DEG C, fixed
20 ms/min of type speed.It should be noted that the temperature and speed of overfeeding sizing are adjustable.
Embodiment 5
A kind of method for weaving warp-direction stretch tmaterial, comprises the following steps:
Raw material is chosen:75D+40D empty bag polyester bag spandex filament is warp thread;The acrylic staples of 40S combed cotton yarns and 40S
Yarn is weft yarn;
Integrated treatment:Warp thread uses raw white yarn, and cheese is obtained after excessively soft winder after pre-treatment;Acrylic staples yarn is successively
Carry out loose yarn, deoil, dye, cleaning, excessively soft or upper electrostatic agent, dehydration, rewinding processing;Combed cotton yarn sequentially pass through winder,
Loose yarn, pre-treatment, dye, soap, fixation, softness, dehydration, rewinding processing;The method of the dyeing of acrylic staples yarn is:First by sun
Ionic dye is tuned into uniform pulpous state with 40% spirit of vinegar, reheats water dissolving;Sodium acetate and spirit of vinegar are added to the water and are prepared into
For buffer, add in dye bath and cause dye bath to keep pH to be 4;In order to ensure Color, retarding agents has been additionally added in dye bath,
Retarding agents can select glauber salt or cation retarder;The method of the dyeing of combed cotton yarn is:Adjust the pH of dye bath (inclined for 8
Alkalescence), bath raio 1: 10, control heating, soaking time be 40 minutes;
Warping:Using sectional warper, the unwinding tension of warping is more than winding tension, allows warp thread to be tensioned in warp beam;Control
Warping bar number processed is 13, and bobbin cradle maximum number is 504, and total quantity of warps is 6300;
Starch silk:Speed of the speed less than sizing roller of yarn roller is drawn in control during slurry silk;Draw yarn speed for 90m/min;
Weaving:Inputted using big computer jacquard, computer and acrylic staples yarn and essence are used in flower pattern, warp thread denting, weft yarn
Carded cotton yarn 1 controls into latitude rate 900m/min weave obtaining fabric every 1 weaving;
Desizing:Padded under fabric after machine by amylase liquid, add sodium chloride as catalyst, 48 DEG C are banked up 2 hours,
Starch size is fully dissolved;
Final finishing:Fabric after being handled through Desizing Step carries out wash water, dried, and overfeeding is shaped under the conditions of 170 DEG C, fixed
20 ms/min of type speed.It should be noted that the temperature and speed of overfeeding sizing are adjustable.
Because ACY polyester bag ammonia long filaments are all used in warp-wise, warp beam pulling force is big during weaving, and fabric has very big warp-wise to stretch
It is long, through to 30-40% is shunk, finished product just has very big warp-wise elasticity after lower machine;When cutting is cut on fabric, it can be done with warp-wise
Broadwise, is carried out after ready-made clothes, and the broadwise of clothes has more than 30% elasticity, and retractility and covering property are good.
Such jacquard fabric, because broadwise elasticity is big, can make the clothes of various profiles, be adapted to three-dimensional cutting, clothes
Broadwise is flexible big, is easy to design the clothes of CRUX style and big profile.
The preferred embodiment of the application is the foregoing is only, the application is not limited to, for the skill of this area
For art personnel, the application can have various modifications and variations.It is all within spirit herein and principle, made any repair
Change, equivalent substitution, improvement etc., should be included within the protection domain of the application.
Claims (10)
1. a kind of method for weaving warp-direction stretch tmaterial, it is characterised in that comprise the following steps:
A. raw material is chosen:75D+40D empty bag polyester bag spandex filament is warp thread;The acrylic staples yarn of 40S combed cotton yarns and 40S
For weft yarn;
B. integrated treatment:
The warp thread uses raw white yarn, and cheese is obtained after excessively soft winder after pre-treatment;
The acrylic staples yarn carry out successively loose yarn, deoil, dye, cleaning, excessively soft or upper electrostatic agent, dehydration, rewinding processing;
The combed cotton yarn sequentially pass through winder, loose yarn, pre-treatment, dye, soap, fixation, softness, dehydration, rewinding processing;
C. warping:Using sectional warper, the unwinding tension of warping is more than winding tension, allows warp thread to be tensioned in warp beam;
D. silk is starched:Speed of the speed less than sizing roller of yarn roller is drawn in control during slurry silk;
E. weave:Weave obtaining fabric using big computer jacquard, computer input flower pattern.
2. according to the method described in claim 1, it is characterised in that methods described also includes Desizing Step, the Desizing Step
For:
Padded under the fabric after machine by amylase liquid, add sodium chloride as catalyst, 40-50 DEG C is banked up 2 hours, will be formed sediment
Slurry material fully dissolves.
3. method according to claim 2, it is characterised in that methods described also includes Final finishing step, the Final finishing
Step is:
Fabric after being handled through the Desizing Step is subjected to wash water, dried, overfeeding is shaped under the conditions of 170 DEG C, sizing speed
20 ms/min.
4. according to the method described in claim 1, it is characterised in that the method for the dyeing of the acrylic staples yarn is:
The dye of positive ion is first tuned into uniform pulpous state with 40% spirit of vinegar, water dissolving is reheated;Sodium acetate and spirit of vinegar are added
Being prepared in water turns into buffer, adds in dye bath and causes dye bath to keep pH to be 4-5.
5. method according to claim 4, it is characterised in that retarding agents, the retarding agents have been additionally added in the dye bath
For glauber salt or cation retarder.
6. according to the method described in claim 1, it is characterised in that the method for the dyeing of the combed cotton yarn is:
The pH for adjusting dye bath is more than 7, bath raio 1: 10, and it is 40 minutes to control heating, soaking time.
7. it is 13, bobbin cradle according to the method described in claim 1, it is characterised in that in the step c, to control warping bar number
Maximum number is 504, and total quantity of warps is 6300.
8. according to the method described in claim 1, it is characterised in that in the step d, draw yarn speed for 90m/min.
9. according to the method described in claim 1, it is characterised in that in the step e, the warp thread denting, the weft yarn
Using the acrylic staples yarn and the combed cotton yarn 1 every 1 weaving, control into latitude rate 900m/min.
10. a kind of tmaterial, it is characterised in that method of the tmaterial according to claim any one of 1-9 is made.