CN107254185A - 一种新型防辐射材料 - Google Patents

一种新型防辐射材料 Download PDF

Info

Publication number
CN107254185A
CN107254185A CN201710516519.9A CN201710516519A CN107254185A CN 107254185 A CN107254185 A CN 107254185A CN 201710516519 A CN201710516519 A CN 201710516519A CN 107254185 A CN107254185 A CN 107254185A
Authority
CN
China
Prior art keywords
parts
grams
radiation
protection material
agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201710516519.9A
Other languages
English (en)
Inventor
王月斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hefei Tatsu Wire And Cable Technology Co Ltd
Original Assignee
Hefei Tatsu Wire And Cable Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hefei Tatsu Wire And Cable Technology Co Ltd filed Critical Hefei Tatsu Wire And Cable Technology Co Ltd
Priority to CN201710516519.9A priority Critical patent/CN107254185A/zh
Publication of CN107254185A publication Critical patent/CN107254185A/zh
Withdrawn legal-status Critical Current

Abstract

本发明提供了一种新型防辐射材料，包含废旧塑料30‑40份，植物纤维40‑50份，防辐射填料50‑80份，膨润土10‑30份，抗污剂10‑25份，粘结剂5‑10份，改性剂1‑3份，偶联剂1‑3份，抗氧剂1‑2份，光催化剂1‑5份，润滑剂1‑2份，阻燃剂1‑5份，防腐剂1‑2份，无机填料3‑7份，色粉1‑2份，对苯二胺1‑5份，棕榈酸1‑5份，硫醇甲基锡1‑5份和丙烯酸酯‑苯乙烯‑丁二烯共聚物2‑8份。本发明防辐射性能优良，且对环境友好。

Description

一种新型防辐射材料
技术领域
本发明涉及环保材料技术领域，具体涉及一种新型防辐射材料。
背景技术
随着科技的迅速发展，各种射线的使用日益广泛，各种辐射充斥于我们的生活中。辐射对人体造成了一定的伤害，严重影响了人们的身体健康。而辐射是可以对其进行防护的，以降低对我们身体及生活的影响。防辐射主要是通过吸收或消散部分辐射能从而达到降低辐射的影响。传统的X射线和γ射线屏蔽材料一般选用混凝土、水泥、铅板等具有较高密度的物质，后来逐步开发生产了一系列以铅或铅的化合物为填料的有机或无机高分子材料，如铅玻璃、铅橡胶、树脂/纳米铅复合材料等，满足了当时的需要，但是铅固有的毒性以及较高的密度限制了这类材料的应用和发展，所以不含铅的防辐射材料亟待发展。由于稀土元素具有防辐射特性，因此目前针对稀土应用于防辐射的研究越来越多，并用其他重金属氧化物替换有毒的氧化铅。现在市场上流行的防辐射塑木材料均是在塑木材料的结构上加防辐射层，以达到防辐射效果，成本大且不易操作。
发明内容
本发明的目的是针对现有技术的问题，提供一种新型防辐射材料。
为了达到上述目的，本发明通过以下技术方案来实现：
一种新型防辐射材料，其特征在于，包含以下按重量份计的原料：
废旧塑料30-40份， 植物纤维40-50份，
防辐射填料50-80份， 膨润土10-30份，
抗污剂10-25份， 粘结剂5-10份，
改性剂1-3份， 偶联剂1-3份，
抗氧剂1-2份， 光催化剂1-5份，
润滑剂1-2份， 阻燃剂1-5份，
防腐剂1-2份， 无机填料3-7份，
色粉1-2份， 对苯二胺 1-5份，
棕榈酸 1-5份， 硫醇甲基锡1-5份，
丙烯酸酯-苯乙烯-丁二烯共聚物2-8份。
优选地，所述新型防辐射材料包含以下原料：
废旧塑料35克， 植物纤维45克，
防辐射填料65克， 膨润土20克，
抗污剂18克， 粘结剂8克，
改性剂2克， 偶联剂2克，
抗氧剂1克， 光催化剂3克，
润滑剂1克， 阻燃剂3克，
防腐剂2克， 无机填料5克，
色粉2克， 对苯二胺 2克，
棕榈酸3克， 硫醇甲基锡2克，
丙烯酸酯-苯乙烯-丁二烯共聚物5克。
优选地，所述废旧塑料是选自聚乙烯、聚丙烯、聚氯乙烯、聚苯乙烯、丙烯腈-丁二烯-苯乙烯、聚碳酸酯、磷酸三苯酯、邻苯二甲酸二异辛酯或己二酸二（2-乙基）己酯中一种或几种的组合。
优选地，所述防辐射填料为碳酸钡、碳酸锶、硫酸钡、纳米氧化锡、纳米氧化锑、纳米氧化锆、纳米氧化钛与纳米氧化钇的混合物。
优选地，所述抗污剂中含有银、铜、异噻唑啉酮类化合物和金属吡啶硫酮类化合物。
优选地，所述抗污剂包括以下按重量份的原料：银3-8份，铜3-8份，异噻唑啉酮类化合物10-20份和金属吡啶硫酮类化合物10-20份。
优选地，所述粘结剂包括以下原料：天然乳胶、丁苯乳胶、重质碳酸钙、琥珀酸单十八酰胺磺酸钠、PAC聚阴离子纤维素钠盐、硫磺和氧化锌。
优选地，所述粘结剂包括以下按重量份计的原料：天然乳胶7-15份，丁苯乳胶2-5份，重质碳酸钙5-15份，琥珀酸单十八酰胺磺酸钠1-3份，PAC聚阴离子纤维素钠盐1-2份、硫磺1-2份和氧化锌1-2份。
本发明与现有技术相比，具有如下的有益效果：
本发明不含铅、镉，可有效减小环境污染，同时可减少对加工人员的健康伤害，更环保。采用废旧塑料、植物纤维、膨润土、无机填料、对苯二胺、棕榈酸、硫醇甲基锡和丙烯酸酯-苯乙烯-丁二烯共聚物等原料，制得的材料具有很好的韧性，易于加工成形。采用的防辐射填料中含多种纳米金属氧化物和非金属元素的多组分的防辐射材料，既对辐射有普遍的防护能力，又对特定辐射有较强的防护能力，合理配比可以发挥最佳的光谱防护效果既有光谱防辐射的特点，又有针对性、专业性，因此其防护性能优于单质防辐射材料。膨润土使本发明可屏蔽伽马射线，且具有吸附放射性金属离子和防水的功能。膨润土资源丰富、价格低廉，粉体成品可塑性强，可压制各种形状的防辐射砌块，且材料本身无二次污染。因此，本发明防辐射性能优良且对环境友好。
本发明采用的粘结剂通过将天然乳胶和丁苯乳胶相结合，并且在重质碳酸钙、琥珀酸单十八酰胺磺酸钠、PAC聚阴离子纤维素钠盐、硫磺和氧化锌的共同作用下，既保证了环保性，又提高了其耐热、耐老化能力，并提高粘合强度及粘合力的稳定，同时也提高产品的耐水性和柔软性。防污剂可综合治理污损，防污效果高效持久；且其添加量较低且环保。
具体实施方式
下面结合实施例对本发明作进一步说明。
实施例1
一种新型防辐射材料，其特征在于，包含以下原料：
废旧塑料30克， 植物纤维50克，
防辐射填料80克， 膨润土10克，
抗污剂10克， 粘结剂10克，
改性剂3克， 偶联剂1克，
抗氧剂1克， 光催化剂5克，
润滑剂2克， 阻燃剂1克，
防腐剂1克， 无机填料7克，
色粉2克， 对苯二胺 1克，
棕榈酸 1克， 硫醇甲基锡5克，
丙烯酸酯-苯乙烯-丁二烯共聚物8克。
所述废旧塑料是选自聚乙烯、聚丙烯、聚氯乙烯、聚苯乙烯、丙烯腈-丁二烯-苯乙烯、聚碳酸酯、磷酸三苯酯、邻苯二甲酸二异辛酯或己二酸二（2-乙基）己酯中一种或几种的组合。
所述防辐射填料为碳酸钡、碳酸锶、硫酸钡、纳米氧化锡、纳米氧化锑、纳米氧化锆、纳米氧化钛与纳米氧化钇的混合物。
所述抗污剂中含有银、铜、异噻唑啉酮类化合物和金属吡啶硫酮类化合物。
所述抗污剂包括以下按重量份的原料：银3份，铜8份，异噻唑啉酮类化合物10份和金属吡啶硫酮类化合物20份。
所述粘结剂包括以下原料：天然乳胶、丁苯乳胶、重质碳酸钙、琥珀酸单十八酰胺磺酸钠、PAC聚阴离子纤维素钠盐、硫磺和氧化锌。
所述粘结剂包括以下按重量份计的原料：天然乳胶7份，丁苯乳胶5份，重质碳酸钙5份，琥珀酸单十八酰胺磺酸钠3份，PAC聚阴离子纤维素钠盐1份、硫磺2份和氧化锌1份。
实施例2
一种新型防辐射材料，其特征在于，包含以下原料：
废旧塑料40克， 植物纤维40克，
防辐射填料50克， 膨润土30克，
抗污剂25克， 粘结剂5克，
改性剂1克， 偶联剂3克，
抗氧剂2克， 光催化剂1克，
润滑剂1克， 阻燃剂5克，
防腐剂2克， 无机填料3克，
色粉1克， 对苯二胺 5克，
棕榈酸 5克， 硫醇甲基锡1克，
丙烯酸酯-苯乙烯-丁二烯共聚物2克。
所述废旧塑料是选自聚乙烯、聚丙烯、聚氯乙烯、聚苯乙烯、丙烯腈-丁二烯-苯乙烯、聚碳酸酯、磷酸三苯酯、邻苯二甲酸二异辛酯或己二酸二（2-乙基）己酯中一种或几种的组合。
所述防辐射填料为碳酸钡、碳酸锶、硫酸钡、纳米氧化锡、纳米氧化锑、纳米氧化锆、纳米氧化钛与纳米氧化钇的混合物。
所述抗污剂中含有银、铜、异噻唑啉酮类化合物和金属吡啶硫酮类化合物。
所述抗污剂包括以下按重量份的原料：银8份，铜3份，异噻唑啉酮类化合物20份和金属吡啶硫酮类化合物10份。
所述粘结剂包括以下原料：天然乳胶、丁苯乳胶、重质碳酸钙、琥珀酸单十八酰胺磺酸钠、PAC聚阴离子纤维素钠盐、硫磺和氧化锌。
所述粘结剂包括以下按重量份计的原料：天然乳胶15份，丁苯乳胶2份，重质碳酸钙15份，琥珀酸单十八酰胺磺酸钠1份，PAC聚阴离子纤维素钠盐2份、硫磺1份和氧化锌2份。
实施例3
一种新型防辐射材料，其特征在于，包含以下原料：
废旧塑料35克， 植物纤维45克，
防辐射填料65克， 膨润土20克，
抗污剂18克， 粘结剂8克，
改性剂2克， 偶联剂2克，
抗氧剂1克， 光催化剂3克，
润滑剂1克， 阻燃剂3克，
防腐剂2克， 无机填料5克，
色粉2克， 对苯二胺 2克，
棕榈酸3克， 硫醇甲基锡2克，
丙烯酸酯-苯乙烯-丁二烯共聚物5克。
所述废旧塑料是选自聚乙烯、聚丙烯、聚氯乙烯、聚苯乙烯、丙烯腈-丁二烯-苯乙烯、聚碳酸酯、磷酸三苯酯、邻苯二甲酸二异辛酯或己二酸二（2-乙基）己酯中一种或几种的组合。
所述防辐射填料为碳酸钡、碳酸锶、硫酸钡、纳米氧化锡、纳米氧化锑、纳米氧化锆、纳米氧化钛与纳米氧化钇的混合物。
所述抗污剂中含有银、铜、异噻唑啉酮类化合物和金属吡啶硫酮类化合物。
所述抗污剂包括以下按重量份的原料：银5份，铜5份，异噻唑啉酮类化合物15份和金属吡啶硫酮类化合物15份。
所述粘结剂包括以下原料：天然乳胶、丁苯乳胶、重质碳酸钙、琥珀酸单十八酰胺磺酸钠、PAC聚阴离子纤维素钠盐、硫磺和氧化锌。
所述粘结剂包括以下按重量份计的原料：天然乳胶11份，丁苯乳胶4份，重质碳酸钙10份，琥珀酸单十八酰胺磺酸钠2份，PAC聚阴离子纤维素钠盐1份、硫磺2份和氧化锌1份。
本发明不含铅、镉，可有效减小环境污染，同时可减少对加工人员的健康伤害，更环保。采用废旧塑料、植物纤维、膨润土、无机填料、对苯二胺、棕榈酸、硫醇甲基锡和丙烯酸酯-苯乙烯-丁二烯共聚物等原料，制得的材料具有很好的韧性，易于加工成形。采用的防辐射填料中含多种纳米金属氧化物和非金属元素的多组分的防辐射材料，既对辐射有普遍的防护能力，又对特定辐射有较强的防护能力，合理配比可以发挥最佳的光谱防护效果既有光谱防辐射的特点，又有针对性、专业性，因此其防护性能优于单质防辐射材料。膨润土使本发明可屏蔽伽马射线，且具有吸附放射性金属离子和防水的功能。膨润土资源丰富、价格低廉，粉体成品可塑性强，可压制各种形状的防辐射砌块，且材料本身无二次污染。因此，本发明防辐射性能优良且对环境友好。
本发明采用的粘结剂通过将天然乳胶和丁苯乳胶相结合，并且在重质碳酸钙、琥珀酸单十八酰胺磺酸钠、PAC聚阴离子纤维素钠盐、硫磺和氧化锌的共同作用下，既保证了环保性，又提高了其耐热、耐老化能力，并提高粘合强度及粘合力的稳定，同时也提高产品的耐水性和柔软性。防污剂可综合治理污损，防污效果高效持久；且其添加量较低且环保。
以上仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (8)

1.一种新型防辐射材料，其特征在于，包含以下按重量份计的原料：
废旧塑料30-40份， 植物纤维40-50份，
防辐射填料50-80份， 膨润土10-30份，
抗污剂10-25份， 粘结剂5-10份，
改性剂1-3份， 偶联剂1-3份，
抗氧剂1-2份， 光催化剂1-5份，
润滑剂1-2份， 阻燃剂1-5份，
防腐剂1-2份， 无机填料3-7份，
色粉1-2份， 对苯二胺 1-5份，
棕榈酸 1-5份， 硫醇甲基锡1-5份，
丙烯酸酯-苯乙烯-丁二烯共聚物2-8份。
2.根据权利要求1所述的一种新型防辐射材料，其特征在于，所述新型防辐射材料包含以下原料：
废旧塑料35克， 植物纤维45克，
防辐射填料65克， 膨润土20克，
抗污剂18克， 粘结剂8克，
改性剂2克， 偶联剂2克，
抗氧剂1克， 光催化剂3克，
润滑剂1克， 阻燃剂3克，
防腐剂2克， 无机填料5克，
色粉2克， 对苯二胺 2克，
棕榈酸3克， 硫醇甲基锡2克，
丙烯酸酯-苯乙烯-丁二烯共聚物5克。
3.根据权利要求1所述的一种新型防辐射材料，其特征在于，所述废旧塑料是选自聚乙烯、聚丙烯、聚氯乙烯、聚苯乙烯、丙烯腈-丁二烯-苯乙烯、聚碳酸酯、磷酸三苯酯、邻苯二甲酸二异辛酯或己二酸二（2-乙基）己酯中一种或几种的组合。
4.根据权利要求1所述的一种新型防辐射材料，其特征在于，所述防辐射填料为碳酸钡、碳酸锶、硫酸钡、纳米氧化锡、纳米氧化锑、纳米氧化锆、纳米氧化钛与纳米氧化钇的混合物。
5.根据权利要求1所述的一种新型防辐射材料，其特征在于，所述抗污剂中含有银、铜、异噻唑啉酮类化合物和金属吡啶硫酮类化合物。
6.根据权利要求5所述的一种新型防辐射材料，其特征在于，所述抗污剂包括以下按重量份的原料：银3-8份，铜3-8份，异噻唑啉酮类化合物10-20份和金属吡啶硫酮类化合物10-20份。
7.根据权利要求1所述的一种新型防辐射材料，其特征在于，所述粘结剂包括以下原料：天然乳胶、丁苯乳胶、重质碳酸钙、琥珀酸单十八酰胺磺酸钠、PAC聚阴离子纤维素钠盐、硫磺和氧化锌。
8.根据权利要求7所述的一种新型防辐射材料，其特征在于，所述粘结剂包括以下按重量份计的原料：天然乳胶7-15份，丁苯乳胶2-5份，重质碳酸钙5-15份，琥珀酸单十八酰胺磺酸钠1-3份，PAC聚阴离子纤维素钠盐1-2份、硫磺1-2份和氧化锌1-2份。
CN201710516519.9A 2017-06-29 2017-06-29 一种新型防辐射材料 Withdrawn CN107254185A (zh)