CN107236982A - 钛及钛合金阳极氧化着色工艺 - Google Patents

钛及钛合金阳极氧化着色工艺 Download PDF

Info

Publication number
CN107236982A
CN107236982A CN201710516419.6A CN201710516419A CN107236982A CN 107236982 A CN107236982 A CN 107236982A CN 201710516419 A CN201710516419 A CN 201710516419A CN 107236982 A CN107236982 A CN 107236982A
Authority
CN
China
Prior art keywords
titanium
titanium alloy
sample
acid
alloy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710516419.6A
Other languages
English (en)
Inventor
周倩倩
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tianjin Zhengtian Medical Instrument Co Ltd
Original Assignee
Tianjin Zhengtian Medical Instrument Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tianjin Zhengtian Medical Instrument Co Ltd filed Critical Tianjin Zhengtian Medical Instrument Co Ltd
Priority to CN201710516419.6A priority Critical patent/CN107236982A/zh
Publication of CN107236982A publication Critical patent/CN107236982A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种钛及钛合金阳极氧化着色工艺，所述的工艺流程是将机加工清洗后的钛或钛合金进行如下步骤：（1）预处理，对钛或钛合金的表面进行光研研磨处理，得到钛或钛合金的试样A；（2）酸洗活化，采用酸洗溶液对钛或钛合金的试样A进行酸洗活化处理，得到钛或钛合金的试样B；（3）阳极氧化，采用电解液对钛或钛合金的试样B进行阳极氧化处理，得到钛或钛合金的产品C，钛或钛合金的产品C具有不同颜色的高光亮氧化膜。本发明工艺处理流程短，钛或钛合金表面质量高、有光泽，在保留原彩色氧化膜基本性能的基础上，使产品更加美观。

Description

钛及钛合金阳极氧化着色工艺
技术领域
本发明涉及金属表面处理的技术领域，特别是涉及一种钛及钛合金阳极氧化着色工艺。
背景技术
钛是一种银白色的过渡金属，其特征为重量轻、强度高、具金属光泽，亦有良好的抗腐蚀能力，主要表现为耐湿氯气腐蚀。由于其稳定的化学性质，具有良好的耐高温、耐低温、抗强酸、抗强碱，以及高强度、低密度的优点。
钛合金是以钛为基础加入其他元素组成的合金。钛合金还具有强度高、低密度，机械性能好，韧性和抗蚀性能好的优点。钛合金因具有强度高、耐蚀性好、耐热性高等特点而被广泛用于各个领域。
钛及钛合金在适当的电解液中发生阳极氧化反应，可在其表面生成透明的干涉膜，能够强烈地反射和折射光线，从而形成不同的颜色。但是传统的阳极氧化形成的干涉膜为亚光面、无光泽，产品外观欠缺美观度。
发明内容
本发明为了解决现有技术的问题，而提供一种钛及钛合金阳高光亮极氧化着色工艺。
本发明为解决这一问题所采取的技术方案是：
本发明的钛及钛合金阳极氧化着色工艺，所述的工艺流程是将机加工清洗后的钛或钛合金进行如下步骤：
（1）预处理，对钛或钛合金的表面进行光研研磨处理，去除钛或钛合金表面的氧化皮，得到钛或钛合金的试样A，钛或钛合金的试样A表面形成高光亮状态，并且表面状态均匀一致；
（2）酸洗活化，采用酸洗溶液对钛或钛合金的试样A进行酸洗活化处理，得到钛或钛合金的试样B，钛或钛合金的试样B表面达到活化状态；
（3）阳极氧化，采用电解液对钛或钛合金的试样B进行阳极氧化处理，得到钛或钛合金的产品C，钛或钛合金的产品C具有不同颜色的高光亮氧化膜。
所述的预处理步骤中，光研研磨处理为采用三角锥型的树脂磨料进行研磨，研磨时间为1-5小时。
所述的酸洗活化步骤中，酸洗溶液为硝酸——氟化氢铵酸洗溶液，硝酸与氟化氢铵的比例为50～300：1。
所述的阳极氧化步骤中，电解液为硫酸铵体系电解液或草酸体系电解液。
所述的阳极氧化步骤中，阳极氧化的调节电压为0～110V。
本发明具有的优点和积极效果是：
本发明工艺处理流程短，钛或钛合金表面质量高、有光泽，在保留原彩色氧化膜基本性能的基础上，使产品更加美观。
具体实施方式
以下参照具体实施例对本发明进行详细的说明。
实施例1：
本发明的钛及钛合金阳极氧化着色工艺，所述的工艺流程是将机加工清洗后的钛或钛合金进行如下步骤：
（1）预处理，对钛或钛合金的表面进行光研研磨处理，去除钛或钛合金表面的氧化皮，得到钛或钛合金的试样A，钛或钛合金的试样A表面形成高光亮状态，并且表面状态均匀一致，为阳极氧化处理过程提供优异的基体状态；
（2）酸洗活化，采用酸洗溶液对钛或钛合金的试样A进行酸洗活化处理，得到钛或钛合金的试样B，钛或钛合金的试样B表面达到活化状态，且钛或钛合金的试样B高光亮表面不会受损；
（3）阳极氧化，采用电解液对钛或钛合金的试样B进行阳极氧化处理，得到钛或钛合金的产品C，钛或钛合金的产品C具有不同颜色的高光亮氧化膜。
所述的预处理步骤中，光研研磨处理为采用三角锥型的树脂磨料进行研磨，研磨时间为1-5小时。
所述的酸洗活化步骤中，酸洗溶液为硝酸——氟化氢铵酸洗溶液，硝酸与氟化氢铵的比例为50～300：1。
所述的阳极氧化步骤中，电解液为硫酸铵体系电解液或草酸体系电解液。
所述的阳极氧化步骤中，阳极氧化的调节电压为0～110V。
实施例2：
本发明的钛及钛合金阳极氧化着色工艺，所述的工艺流程是将机加工清洗后的钛或钛合金进行如下步骤：
（1）预处理，对钛或钛合金的表面进行光研研磨处理，去除钛或钛合金表面的氧化皮，得到钛或钛合金的试样A，钛或钛合金的试样A表面形成高光亮状态，并且表面状态均匀一致，为阳极氧化处理过程提供优异的基体状态；
（2）酸洗活化，采用酸洗溶液对钛或钛合金的试样A进行酸洗活化处理，得到钛或钛合金的试样B，钛或钛合金的试样B表面达到活化状态，且钛或钛合金的试样B高光亮表面不会受损；
（3）阳极氧化，采用电解液对钛或钛合金的试样B进行阳极氧化处理，得到钛或钛合金的产品C，钛或钛合金的产品C具有不同颜色的高光亮氧化膜。
所述的预处理步骤中，光研研磨处理为采用三角锥型的树脂磨料进行研磨，研磨时间为3小时。
所述的酸洗活化步骤中，酸洗溶液为硝酸——氟化氢铵酸洗溶液，硝酸与氟化氢铵的比例为200：1。
所述的阳极氧化步骤中，电解液为硫酸铵体系电解液或草酸体系电解液。
所述的阳极氧化步骤中，阳极氧化的调节电压为55V，即阳极氧化槽的调节电压调制为55V，即可得到金黄色高光亮表面的钛或钛合金的产品C。
本发明工艺处理流程短，钛或钛合金表面质量高、有光泽，在保留原彩色氧化膜基本性能的基础上，使产品更加美观。
以上对本发明的实施例进行了详细说明，但所述内容仅为本发明的较佳实施例，不能被认为用于限定本发明的实施范围。凡依本发明申请范围所作的均等变化与改进等，均应仍归属于本发明的专利涵盖范围之内。

Claims (5)

1.一种钛及钛合金阳极氧化着色工艺，其特征在于：所述的工艺流程是将机加工清洗后的钛或钛合金进行如下步骤：
（1）预处理，对钛或钛合金的表面进行光研研磨处理，去除钛或钛合金表面的氧化皮，得到钛或钛合金的试样A，钛或钛合金的试样A表面形成高光亮状态，并且表面状态均匀一致；
（2）酸洗活化，采用酸洗溶液对钛或钛合金的试样A进行酸洗活化处理，得到钛或钛合金的试样B，钛或钛合金的试样B表面达到活化状态；
（3）阳极氧化，采用电解液对钛或钛合金的试样B进行阳极氧化处理，得到钛或钛合金的产品C，钛或钛合金的产品C具有不同颜色的高光亮氧化膜。
2.根据权利要求1所述的钛及钛合金阳极氧化着色工艺，其特征在于：所述的预处理步骤中，光研研磨处理为采用三角锥型的树脂磨料进行研磨，研磨时间为1-5小时。
3.根据权利要求1所述的钛及钛合金阳极氧化着色工艺，其特征在于：所述的酸洗活化步骤中，酸洗溶液为硝酸——氟化氢铵酸洗溶液，硝酸与氟化氢铵的比例为50～300：1。
4.根据权利要求1所述的钛及钛合金阳极氧化着色工艺，其特征在于：所述的阳极氧化步骤中，电解液为硫酸铵体系电解液或草酸体系电解液。
5.根据权利要求1所述的钛及钛合金阳极氧化着色工艺，其特征在于：所述的阳极氧化步骤中，阳极氧化的调节电压为0～110V。
CN201710516419.6A 2017-06-29 2017-06-29 钛及钛合金阳极氧化着色工艺 Pending CN107236982A (zh)