CN107236356A - A kind of environment-friendly water-based printing-ink - Google Patents
A kind of environment-friendly water-based printing-ink Download PDFInfo
- Publication number
- CN107236356A CN107236356A CN201710590708.0A CN201710590708A CN107236356A CN 107236356 A CN107236356 A CN 107236356A CN 201710590708 A CN201710590708 A CN 201710590708A CN 107236356 A CN107236356 A CN 107236356A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- environment
- ink
- based printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environment-friendly water-based printing-ink, including 20 30 parts of deionized water in parts by weight, 10 16 parts of polyalcohol, 8 12 parts of polyvinyl alcohol, 38 parts of aqueous rosin milk, 10 15 parts of aqueous alkide resin, 10 15 parts of water-based acrylic resin, 8 12 parts of water-compatible amino resin, 2 10 parts of aqueous polyamide resin, 0.1 2 parts of nano-aluminum hydroxide, 0.1 2 parts of sub-nano silica micro mist, 12 parts of defoamer, 24 parts of dispersant, 3 18 parts of pigment.The aqueous degree of the present patent application is high, and due to the reinforcing of nanometer and sub- nano material, is relatively specific for most behaviour in service, water-based ink printing quick-drying, coloring is good, preserves lasting, and than the more environmental protection of general water-based ink.
Description
Technical field
The present invention relates to printing-ink field, more particularly to a kind of environment-friendly water-based printing-ink.
Background technology
Ink is to ensure one of very crucial factor of printing quality.The existing ink for being used to print always has various
The problem of:Some ink contains benzene, ketones derivant, and environmental pollution is larger;Some ink adaptability is poor, for different
Paper adhesive force it cannot be guaranteed that, or total adhesive force is not strong enough;Some ink combination properties are good, but composition toxicity is too big, to print
Dataller people has chronic body harm.
For problem above, the characteristics of water-based ink has environmental protection in itself, and for the current water-based ink of retention property
Beneficial environmental properties can decline, and in order to continue the beneficial environmental properties for strengthening water-based ink, constantly develop new raw material formula, more lumping weight
Will.
The content of the invention
It is an object of the invention to provide a kind of environment-friendly water-based printing-ink, have on the basis of basic performance is kept, use
Material is degradable all using environmentally friendly raw material, and pigment is also environmentally friendly composition, overcomes problems of the prior art.
In order to realize the above object the technical scheme is that:
A kind of environment-friendly water-based printing-ink, includes the component of following parts by weight:
20-30 parts of deionized water
10-16 parts of polyalcohol
8-12 parts of polyvinyl alcohol
Aqueous rosin milk 3-8 parts
10-15 parts of aqueous alkide resin
10-15 parts of water-based acrylic resin
8-12 parts of water-compatible amino resin
2-10 parts of aqueous polyamide resin
0.1-2 parts of nano-aluminum hydroxide
0.1-2 parts of sub-nano silica micro mist
1-2 parts of defoamer
2-4 parts of dispersant
3-18 parts of pigment.
Preferably, the polyalcohol is the composition of ethylene glycol and glycerine, and its ratio is 2 ~ 3:1.
Preferably, ratio of the sub-nano silica grain size of micropowder in the range of 100 ~ 400nm of interval is more than 95%.
Preferably, the particle diameter of the nano-aluminum hydroxide is in 60 ~ 200nm.
Preferably, the molecular weight of the polyvinyl alcohol is in 20000-80000.
Preferably, the pigment is carbon black, titanium dioxide, ferric tannate, tannic acid ferrous iron, cobalt green, copper naphthenate, iron oxide red
In one kind or its combination.
The beneficial effects of the present invention are:Environmental protection of the invention, high-performance.Formula all components be it is aqueous, without phenyl ring,
The noxious materials such as ketone;Nano-aluminum hydroxide and sub-nano silica micro mist have special effect, make ink colorant finer and smoother, are difficult
Scatter, overcome the weakness of water-based ink;Pigment is also environmental protection, and black, white, blue, green, red cooperation can meet most of printings
The use requirement of color.The aqueous degree of the present patent application is high, and due to the reinforcing of nanometer and sub- nano material, is relatively specific for big
Most behaviours in service, water-based ink printing quick-drying, coloring is good, preserves lasting and more more green than general water-based ink
Environmental protection.
Embodiment
In order to illustrate more clearly of the embodiment of the present application or technical scheme of the prior art, letter will be made to embodiment below
Singly introduce.
Embodiment 1
A kind of environment-friendly water-based printing-ink, includes the component of following parts by weight:
25 parts of deionized water
10 parts of polyalcohol
8 parts of polyvinyl alcohol
Aqueous 3 parts of rosin milk
12 parts of aqueous alkide resin
11 parts of water-based acrylic resin
10 parts of water-compatible amino resin
2 parts of aqueous polyamide resin
2 parts of nano-aluminum hydroxide
0.9 part of sub-nano silica micro mist
1.5 parts of defoamer
2 parts of dispersant
3 parts of pigment;
The polyalcohol is the composition of ethylene glycol and glycerine, and its ratio is 2:1;The sub-nano silica grain size of micropowder is in area
Between ratio in the range of 100 ~ 400nm more than 95%;The particle diameter of the nano-aluminum hydroxide is in 60 ~ 200nm;The polyvinyl alcohol
Molecular weight in 20000-80000;The pigment is carbon black, titanium dioxide, ferric tannate, tannic acid ferrous iron, cobalt green, copper naphthenate, oxygen
Change one kind in iron oxide red or its combination.
Experiment shows that the water-based ink quick-drying, coloring are good, and attachment fastness is high and for a long time colour-fast.
Embodiment 2
A kind of environment-friendly water-based printing-ink, includes the component of following parts by weight:
20 parts of deionized water
12 parts of polyalcohol
12 parts of polyvinyl alcohol
Aqueous 8 parts of rosin milk
15 parts of aqueous alkide resin
10 parts of water-based acrylic resin
8 parts of water-compatible amino resin
10 parts of aqueous polyamide resin
0.1 part of nano-aluminum hydroxide
2 parts of sub-nano silica micro mist
2 parts of defoamer
3 parts of dispersant
18 parts of pigment;
The polyalcohol is the composition of ethylene glycol and glycerine, and its ratio is 3:1;The sub-nano silica grain size of micropowder is in area
Between ratio in the range of 100 ~ 400nm more than 95%;The particle diameter of the nano-aluminum hydroxide is in 60 ~ 200nm;The polyvinyl alcohol
Molecular weight in 20000-80000;The pigment is carbon black, titanium dioxide, ferric tannate, tannic acid ferrous iron, cobalt green, copper naphthenate, oxygen
Change one kind in iron oxide red or its combination.
Experiment shows that the water-based ink quick-drying, coloring are good, and attachment fastness is high and for a long time colour-fast.
Embodiment 3
A kind of environment-friendly water-based printing-ink, includes the component of following parts by weight:
30 parts of deionized water
16 parts of polyalcohol
11 parts of polyvinyl alcohol
Aqueous 6 parts of rosin milk
10 parts of aqueous alkide resin
15 parts of water-based acrylic resin
12 parts of water-compatible amino resin
6 parts of aqueous polyamide resin
0.7 part of nano-aluminum hydroxide
0.1 part of sub-nano silica micro mist
1 part of defoamer
4 parts of dispersant
12 parts of pigment;
The polyalcohol is the composition of ethylene glycol and glycerine, and its ratio is 2:1;The sub-nano silica grain size of micropowder is in area
Between ratio in the range of 100 ~ 400nm more than 95%;The particle diameter of the nano-aluminum hydroxide is in 60 ~ 200nm;The polyvinyl alcohol
Molecular weight in 20000-80000;The pigment is carbon black, titanium dioxide, ferric tannate, tannic acid ferrous iron, cobalt green, copper naphthenate, oxygen
Change one kind in iron oxide red or its combination.
Experiment shows that the water-based ink quick-drying, coloring are good, and attachment fastness is high and for a long time colour-fast.
Above example is only to illustrate the preferred technical solution of the present invention, it is noted that for the general of the art
For logical technical staff, under the premise without departing from the principles of the invention, some improvement made or equivalent substitution are accordingly to be regarded as this
The protection domain of invention, should cover in scope of the presently claimed invention.
Claims (6)
1. a kind of environment-friendly water-based printing-ink, it is characterised in that include the component of following parts by weight:
20-30 parts of deionized water
10-16 parts of polyalcohol
8-12 parts of polyvinyl alcohol
Aqueous rosin milk 3-8 parts
10-15 parts of aqueous alkide resin
10-15 parts of water-based acrylic resin
8-12 parts of water-compatible amino resin
2-10 parts of aqueous polyamide resin
0.1-2 parts of nano-aluminum hydroxide
0.1-2 parts of sub-nano silica micro mist
1-2 parts of defoamer
2-4 parts of dispersant
3-18 parts of pigment.
2. a kind of environment-friendly water-based printing-ink according to claim 1, it is characterised in that the polyalcohol be ethylene glycol and
The composition of glycerine, and its ratio is 2 ~ 3:1.
3. a kind of environment-friendly water-based printing-ink according to claim 1, it is characterised in that the sub-nano silica grain size of micropowder
Ratio in the range of 100 ~ 400nm of interval is more than 95%.
4. a kind of environment-friendly water-based printing-ink according to claim 1, it is characterised in that the grain of the nano-aluminum hydroxide
Footpath is in 60 ~ 200nm.
5. a kind of environment-friendly water-based printing-ink according to claim 1, it is characterised in that the molecular weight of the polyvinyl alcohol
In 20000-80000.
6. a kind of environment-friendly water-based printing-ink according to claim 1, it is characterised in that the pigment is carbon black, titanium white
Powder, ferric tannate, tannic acid ferrous iron, cobalt green, copper naphthenate, one kind in iron oxide red or its combination.