CN107227110A - A kind of high-performance vacuum coating UV finish paints - Google Patents
A kind of high-performance vacuum coating UV finish paints Download PDFInfo
- Publication number
- CN107227110A CN107227110A CN201710507881.XA CN201710507881A CN107227110A CN 107227110 A CN107227110 A CN 107227110A CN 201710507881 A CN201710507881 A CN 201710507881A CN 107227110 A CN107227110 A CN 107227110A
- Authority
- CN
- China
- Prior art keywords
- parts
- resin
- vacuum coating
- activated monomer
- matrix resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high-performance vacuum coating UV finish paints, including：Matrix resin, compounding resin, activated monomer, light trigger, auxiliary agent group and adhesion promoter are closed and formed, wherein, described matrix resin is 33 40 parts, described compounding resin is 20 30 parts, and described activated monomer is 15 22 parts, and described light trigger is 10 15 parts, described auxiliary agent is 58 parts, adhesion promoter is 13 parts, and described matrix resin is urethane acrylate, and described compounding resin is combined by negative resin and positive resin.By the above-mentioned means, the present invention can strengthen the adhesive force between priming paint and plastic basis material and the coat of metal, there is high activity, high glaze, less flexible, high rigidity, while also increasing the aesthetics of product surface.
Description
Technical field
The present invention relates to paint field, more particularly to a kind of high-performance vacuum coating UV finish paints.
Background technology
Traditional solvent-borne vacuum metallizing coating species is more, using wide, but it has many birth defects, such as coating institute
It is difficult to reconcile containing solvent, low boiling, the solvent of high volatile will upset coating surface in coating drying process because quickly volatilizing
Planarization, there is pin hole and surface defect in cured film, and remain in the coating high volatile solvent during vacuum coating
It can escape, coating quality will be caused to reduce, adhesive force, brightness deterioration；Solvent based coating contains substantial amounts of volatile component, right
Environment is unfavorable；In addition, also there is curing efficiency bottom in solvent based coating, the disadvantage such as energy consumption height.
Disadvantages mentioned above has a strong impact on application of the solvent based coating in vacuum coating technology, the appearance of ultraviolet-curing paint
Solvent based coating problems faced is solved well, with prominent advantage, thus is widely used vacuum coating technology
In, and gradually substitute traditional solvent-borne coating.
The content of the invention
The present invention solves the technical problem of a kind of high-performance vacuum coating UV finish paints are provided, can strengthen priming paint with
Adhesive force between plastic basis material and the coat of metal, has the advantages that high activity, high glaze, less flexible, high rigidity, while also increasing
The aesthetics of product surface.
In order to solve the above technical problems, one aspect of the present invention is：A kind of high-performance vacuum coating is provided
UV finish paints, it is characterised in that including：Matrix resin, compounding resin, activated monomer, light trigger, auxiliary agent group and adhesive force promote
Agent is closed and formed, wherein, described matrix resin is 33-40 parts, and described compounding resin is 20-30 parts, described activated monomer
For 15-22 parts, described light trigger is 10-15 parts, and described auxiliary agent is 5-8 parts, and adhesion promoter is 1-3 parts, described
Matrix resin be urethane acrylate, described compounding resin combines by negative resin and positive resin.
In a preferred embodiment of the present invention, described matrix resin is 38 parts, and described compounding resin is 25 parts, institute
The activated monomer stated is 15 parts, and described light trigger is 12 parts, and described auxiliary agent is 6 parts, and adhesion promoter is 1 part.
In a preferred embodiment of the present invention, described activated monomer is the acrylic acid list of the multiple functional radical of two functional groups
Body, described light trigger is cation light initiator, and described auxiliary agent is levelling agent and anti-sagging agent.
In a preferred embodiment of the present invention, according to certain proportioning, first by 33-40 parts of matrix resin, 20-30 parts
Compounding resin and the mixing of 15-22 part of activated monomer, be sufficiently stirred for, 10-15 parts light-initiated added after stirring 45 minutes
Agent, 5-8 parts of auxiliary agent and 1-3 parts of adhesion promoter, were again stirring for after 45 minutes, standstill seal 12 hours, you can obtain
Described high-performance vacuum coating UV finish paints.
The beneficial effects of the invention are as follows：Adhesive force between present invention enhancing priming paint and plastic basis material and the coat of metal, has
The advantages of high activity, high glaze, less flexible, high rigidity, while also increasing the aesthetics of product surface.
Embodiment
Presently preferred embodiments of the present invention is described in detail below so that advantages and features of the invention can be easier to by
It will be appreciated by those skilled in the art that apparent clearly being defined so as to be made to protection scope of the present invention.
Embodiment 1
A kind of high-performance vacuum coating UV finish paints, it is characterised in that including：Matrix resin, compounding resin, activated monomer, light draw
Hair agent, auxiliary agent group and adhesion promoter, which are closed, to be formed, wherein, described matrix resin is 33-40 parts, and described compounding resin is
20-30 parts, described activated monomer is 15-22 parts, and described light trigger is 10-15 parts, and described auxiliary agent is 5-8 parts, attached
Adhesion promoter is 1-3 parts, and described matrix resin is urethane acrylate, and described compounding resin is by negative resin and Yang Shu
Fat is combined.
Further illustrate, described matrix resin is 38 parts, described compounding resin is 25 parts, and described activated monomer is
15 parts, described light trigger is 12 parts, and described auxiliary agent is 6 parts, and adhesion promoter is 1 part.
Further illustrate, described activated monomer is the acrylic monomers of the multiple functional radical of two functional groups, described light draws
Hair agent is cation light initiator, and described auxiliary agent is levelling agent and anti-sagging agent.
Further illustrate, according to certain proportioning, first by 33-40 parts of matrix resin, 20-30 parts of compounding resin and
15-22 parts of activated monomer mixing, is sufficiently stirred for, stirring added after 45 minutes 10-15 parts of light trigger, 5-8 parts help
Agent and 1-3 parts of adhesion promoter, were again stirring for after 45 minutes, standstill seal 12 hours, you can obtain described high-performance
Vacuum coating UV finish paints.
Further illustrating, described urethane acrylate（PUA）Molecule in contain acrylic-functional and amino
Formic acid ester bond, the adhesive after solidification has the high-wearing feature of polyurethane, adhesion, pliability, high-peeling strength and excellent
Resistance to low temperature and polyacrylate remarkable optical property and weatherability, are a kind of radiation curing materials of high comprehensive performance
Material.
Embodiment 2
A kind of high-performance vacuum coating UV finish paints, it is characterised in that including：Matrix resin, compounding resin, activated monomer, light draw
Hair agent, auxiliary agent group and adhesion promoter, which are closed, to be formed, wherein, described matrix resin is 33-40 parts, and described compounding resin is
20-30 parts, described activated monomer is 15-22 parts, and described light trigger is 10-15 parts, and described auxiliary agent is 5-8 parts, attached
Adhesion promoter is 1-3 parts, and described matrix resin is urethane acrylate, and described compounding resin is by negative resin and Yang Shu
Fat is combined.
Further illustrate, described matrix resin is 35 parts, described compounding resin is 28 parts, and described activated monomer is
18 parts, described light trigger is 10 parts, and described auxiliary agent is 7 parts, and adhesion promoter is 1 part.
Further illustrate, described activated monomer is the acrylic monomers of the multiple functional radical of two functional groups, described light draws
Hair agent is cation light initiator, and described auxiliary agent is levelling agent and anti-sagging agent.
Further illustrate, according to certain proportioning, first by 33-40 parts of matrix resin, 20-30 parts of compounding resin and
15-22 parts of activated monomer mixing, is sufficiently stirred for, stirring added after 45 minutes 10-15 parts of light trigger, 5-8 parts help
Agent and 1-3 parts of adhesion promoter, were again stirring for after 45 minutes, standstill seal 12 hours, you can obtain described high-performance
Vacuum coating UV finish paints.
Further illustrating, described urethane acrylate（PUA）Molecule in contain acrylic-functional and amino
Formic acid ester bond, the adhesive after solidification has the high-wearing feature of polyurethane, adhesion, pliability, high-peeling strength and excellent
Resistance to low temperature and polyacrylate remarkable optical property and weatherability, are a kind of radiation curing materials of high comprehensive performance
Material.
Embodiment 3
A kind of high-performance vacuum coating UV finish paints, it is characterised in that including：Matrix resin, compounding resin, activated monomer, light draw
Hair agent, auxiliary agent group and adhesion promoter, which are closed, to be formed, wherein, described matrix resin is 33-40 parts, and described compounding resin is
20-30 parts, described activated monomer is 15-22 parts, and described light trigger is 10-15 parts, and described auxiliary agent is 5-8 parts, attached
Adhesion promoter is 1-3 parts, and described matrix resin is urethane acrylate, and described compounding resin is by negative resin and Yang Shu
Fat is combined.
Further illustrate, described matrix resin is 33 parts, described compounding resin is 30 parts, and described activated monomer is
15 parts, described light trigger is 11 parts, and described auxiliary agent is 8 parts, and adhesion promoter is 3 parts.
Further illustrate, described activated monomer is the acrylic monomers of the multiple functional radical of two functional groups, described light draws
Hair agent is cation light initiator, and described auxiliary agent is levelling agent and anti-sagging agent.
Further illustrate, according to certain proportioning, first by 33-40 parts of matrix resin, 20-30 parts of compounding resin and
15-22 parts of activated monomer mixing, is sufficiently stirred for, stirring added after 45 minutes 10-15 parts of light trigger, 5-8 parts help
Agent and 1-3 parts of adhesion promoter, were again stirring for after 45 minutes, standstill seal 12 hours, you can obtain described high-performance
Vacuum coating UV finish paints.
Further illustrating, described urethane acrylate（PUA）Molecule in contain acrylic-functional and amino
Formic acid ester bond, the adhesive after solidification has the high-wearing feature of polyurethane, adhesion, pliability, high-peeling strength and excellent
Resistance to low temperature and polyacrylate remarkable optical property and weatherability, are a kind of radiation curing materials of high comprehensive performance
Material.
Embodiments of the invention are the foregoing is only, are not intended to limit the scope of the invention, it is every to utilize this hair
Equivalent structure or equivalent flow conversion that bright description is made, or directly or indirectly it is used in other related technology necks
Domain, is included within the scope of the present invention.
Claims (4)
1. a kind of high-performance vacuum coating UV finish paints, it is characterised in that including：Matrix resin, compounding resin, activated monomer, light
Initiator, auxiliary agent group and adhesion promoter are closed and formed, wherein, described matrix resin is 33-40 parts, described compounding resin
For 20-30 parts, described activated monomer is 15-22 points, and described light trigger is 10-15 parts, and described auxiliary agent is 5-8 parts,
Adhesion promoter is 1-3 parts, and described matrix resin is urethane acrylate, and described compounding resin is by negative resin and sun
Resin combination is formed.
2. a kind of high-performance vacuum coating UV finish paints according to claim 1, it is characterised in that：Described matrix resin is
38 parts, described compounding resin is 25 parts, and described activated monomer is 15 parts, and described light trigger is 12 parts, and described helps
Agent is 6 parts, and adhesion promoter is 1 part.
3. a kind of high-performance vacuum coating UV finish paints according to claim 1, it is characterised in that：Described activated monomer is
The acrylic monomers of the multiple functional radical of two functional groups, described light trigger is cation light initiator, and described auxiliary agent is stream
Flat agent and anti-sagging agent.
4. a kind of high-performance vacuum coating UV finish paints according to claim 1, it is characterised in that：According to certain proportioning,
First 33-40 parts of matrix resin, 20-30 parts of compounding resin and 15-22 parts of activated monomer are mixed, is sufficiently stirred for, stirs
10-15 parts of light trigger, 5-8 parts of auxiliary agent and 1-3 parts of adhesion promoter is added after 45 minutes, 45 points are again stirring for
Zhong Hou, standstill seal 12 hours, you can obtain described high-performance vacuum coating UV finish paints.