CN108465628A - Auto parts and components novel coating line modified technique - Google Patents
Auto parts and components novel coating line modified technique Download PDFInfo
- Publication number
- CN108465628A CN108465628A CN201711418082.1A CN201711418082A CN108465628A CN 108465628 A CN108465628 A CN 108465628A CN 201711418082 A CN201711418082 A CN 201711418082A CN 108465628 A CN108465628 A CN 108465628A
- Authority
- CN
- China
- Prior art keywords
- putty
- auto parts
- paint
- coating line
- line modified
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of auto parts and components novel coating line modified techniques, include the following steps:Paint front surface processing;Phosphatization;It is cleaned and dried;Priming paint;It is dry;Putty is slightly scraped;Putty is carefully scraped;Middle painting;Finishing;Finishing coat;Color separation, removing surface are cleaned with heat alkali liquid and remove degreasing with organic solvent scouring;Phosphorating treatment is handled using film-type zinc salt fast bonderizing, 1 3g/m of phosphorization film quality, 12 μm of film thickness, 1 10 μm of grain size number, and 50 70 DEG C of progress phosphatizations of 25 35 DEG C of low temperature or medium temperature can be used;Putty is scraped on the prime coat parched, is once applied the thickness scraped and is no more than 0.5mm.Auto parts and components novel coating line modified technique of the present invention, cathode electrodip painting is water paint, is good for the environment;The corrosion resistance and wet-hot aging performance of product are improved, paint film coefficient of friction is suitable, and salt spray resistance can reach 240 1000h or more, wet-heat resisting 500h or more, reduces production cost, improves production efficiency.
Description
Technical field
The present invention relates to a kind of coating process, in particular to a kind of auto parts and components novel coating line improves work
Skill.
Background technology
Painting dressing automobiles refer generally to the application of the various types such as car, car, cargo vehicle body of a motor car and parts.Vapour
The vehicles one of of the vehicle as modernization, 90% or more outer surface is painted surface, coating quality (appearance, clarity, light
Pool, color etc.) quality be visual evaluation of the people to car mass, therefore it is the competition for directly affecting automobile labor market
Power.In addition, coating quality is also one of the major measure for improving the corrosion resistance of automobile product and prolonging the service life, so,
Car surface application is all classified as important work by either automobile making or automobile maintenance industry.
The paintings such as automobile assembly line using coatings volatile organic compounds as generated a large amount of VOC, also heavy metal problem.European car
Application film coating technique substitutes application, and application uses aqueous and powdery paints as possible, is far below European Emission laws and regulations requirement.
Since the requirement along with the whole world to environmental protection coating material is higher and higher, more environmentally friendly aqueous and powdery paints at
For Coating Market hot product, wherein requirement of the whole world to environmentally friendly trend is to push a big power of powdery paints development, due to
The approach for reducing product VOC is all being found by manufacturer, therefore in certain field powdery paints naturally instead of liquid coating.Powder
The VOC content of last coating is low, removes and is easy, and crosses the recyclable recycling of coating of spray;Film does not generate pin hole substantially after construction,
Construction usually easier than liquid coating, the film durability of formation are good.Environment-friendly advantage and technical advantage are that powdery paints substitutes biography
The key point of system solvent based coating.
Water paint can greatly reduce the discharge of VOC relative to traditional solvent-borne coating, can effectively reduce to environment
It influences, additionally aids the pathogenetic potential probability of reduction occupation, reduce fire risk and storage hidden danger, simplify and reduce enterprise and is logical
Flow and cost of wind, water process etc. etc., everything demand are also all that certain basis has been established in the development of water paint.
Invention content
Deficiency in for the above-mentioned prior art, the present invention provide a kind of reduction production cost, improve the vapour of production efficiency
Vehicle parts novel coating line modified technique.
The technical solution used in the present invention is:
A kind of auto parts and components novel coating line modified technique, includes the following steps:
Paint front surface processing (oil removing derusts, cleaning, table tune);Phosphatization;It is cleaned and dried;Priming paint;It is dry;Putty is slightly scraped;
(dry, polishing is cleaned;Putty is carefully scraped (dry, polishing is cleaned);It is middle to apply (dry, polishing is cleaned);Finishing (it is applied in quick-drying,
Dry, polishing is cleaned);Finishing coat (dry or Lacquer finish);Color separation (drying),
Removing surface step:It is cleaned with heat alkali liquid and removes degreasing with organic solvent scouring;It is first used in glass fiber reinforced plastic surface
320-400 mesh sand paper is first polished, and is then cleaned with organic solvent and is removed remover;What the yellow rust of bodywork surface was prepared using phosphoric acid
Cleaning solution is cleaned;To ensure that coating has excellent anticorrosive property and coating and coated article surface to have good adhesive force.
Phosphorating treatment step:It is handled using film-type zinc salt fast bonderizing, phosphorization film quality 1-3g/m, 1-2 μm of film thickness, knot
50-70 DEG C of progress phosphatization of 25-35 DEG C of low temperature or medium temperature can be used in 1-10 μm of grain size;
Priming paint should select rustless property strong, salt fog >=500h, the strong adhesive force (can adapt to a variety of base materials simultaneously) with base material,
Good with middle painting or finishing coat binding force, coating machinery performance is good, impact >=50cm, toughness≤1mm, the coating conduct of hardness >=0.5
Priming paint;
Putty is scraped on the prime coat parched, is once applied the thickness scraped and is usually no more than 0.5mm.
Wet on wet method Lian Pen bis-, working viscosity 20-30s, per pass interval 5- can be used in the spray-applied primer
10min flashes 5-10min into drying chamber, 40-50 μm of primer dry films thickness after having sprayed.
Described to scratch putty method using novel large area, it is smooth that this method putty easily forms large area, is not influencing
Under the premise of production process, often scrapes after a putty should all be dried and polish flat, then scrape putty next time again, putty is to scrape 2-
3 times preferably, and first thickness scrapes again thin scrape;The intensity of putty layer can be enhanced in this way and further increase flatness.
Using the method for machine polishing putty, sand paper selects 180-240 mesh.
Using method (airless spraying also can be selected) spray-applied primer of aerial spraying, even sprayed using wet on wet method
Two, working viscosity 20-30s, per pass interval 5-10min flash 5-10min into drying chamber, primer dry films thickness 40-50 after having sprayed
μm。。
It is applied in being sprayed using electrostatic spraying or air spray finishing;The anti-stoning of coating can be improved, is improved attached with priming paint
Put forth effort, improves the flatness and smoothness on coated article surface, to improve the richness and clarity of finishing coat.
Middle painting uses wet on wet continuous spray two, working viscosity 18-24s, per pass interval 5-10min, flash distillation after having sprayed
5-10min is into drying chamber, middle 40-50 μm of painting thickness of dry film.
Topcoating uses electrostatic spraying or air spray finishing, the automobile finish of spraying that can form weatherability, clarity and light
The excellent paint film in pool.
It is 200h or more that priming paint, which uses epoxy ester undercoat, salt spray resistance,.Epoxy polyamide priming paint is such as selected, then salt spray resistance
Performance reaches 500h or more;Such as use ground phosphorating treatment+epoxy polyamide priming paint, ground for galvanized sheet or aluminium alloy plate, then it is resistance to
Salt fog performance reaches 800h or more.
Middle apply applies using in acroleic acid polyurethane or polyester-polyurethane, is applied in the dicoration of semi-gloss or bloom.It can be effective
Raising topcoat richness, while preventing from oozing under finishing coat, improve clarity and gloss of finishing coat etc..
Finishing coat uses acroleic acid polyurethane or polyester modification acrylic polyurethane finish paint;It uses with national treasury aluminium powder and acrylic acid
The metallic finishe prepared based on resin, coating varnish are acroleic acid polyurethane varnish.Background color coating resins are acrylic resin, color
Same opalescent lacquers (one pack system);It is acrylic resin (one pack system) that opalescent lacquers, which uses import pearly-lustre, matrix resin,;Coating varnish is third
Olefin(e) acid polyurethane lacquer.
The advantageous effect of the present invention compared with the prior art:
Auto parts and components novel coating line modified technique of the present invention, cathode electrodip painting is water paint, is good for the environment;It carries
The corrosion resistance and wet-hot aging performance of high product, paint film coefficient of friction is suitable, salt spray resistance can reach 240-1000h or more,
Wet-heat resisting 500h or more reduces production cost, improves production efficiency.
Specific implementation mode
The present invention will be described in detail for following embodiment:
A kind of auto parts and components novel coating line modified technique, includes the following steps:
Paint front surface processing (oil removing derusts, cleaning, table tune);Phosphatization;It is cleaned and dried;Priming paint;It is dry;Putty is slightly scraped;
(dry, polishing is cleaned;Putty is carefully scraped (dry, polishing is cleaned);It is middle to apply (dry, polishing is cleaned);Finishing (it is applied in quick-drying,
Dry, polishing is cleaned);Finishing coat (dry or Lacquer finish);Color separation (drying),
Removing surface step:It is cleaned with heat alkali liquid and removes degreasing with organic solvent scouring;It is first used in glass fiber reinforced plastic surface
320-400 mesh sand paper is first polished, and is then cleaned with organic solvent and is removed remover;What the yellow rust of bodywork surface was prepared using phosphoric acid
Cleaning solution is cleaned;To ensure that coating has excellent anticorrosive property and coating and coated article surface to have good adhesive force.
Phosphorating treatment step:It is handled using film-type zinc salt fast bonderizing, phosphorization film quality 1-3g/m, 1-2 μm of film thickness, knot
50-70 DEG C of progress phosphatization of 25-35 DEG C of low temperature or medium temperature can be used in 1-10 μm of grain size;
Priming paint should select rustless property strong, salt fog >=500h, the strong adhesive force (can adapt to a variety of base materials simultaneously) with base material,
Good with middle painting or finishing coat binding force, coating machinery performance is good, impact >=50cm, toughness≤1mm, the coating conduct of hardness >=0.5
Priming paint;
Putty is scraped on the prime coat parched, is once applied the thickness scraped and is usually no more than 0.5mm.
Wet on wet method Lian Pen bis-, working viscosity 20-30s, per pass interval 5- can be used in the spray-applied primer
10min flashes 5-10min into drying chamber, 40-50 μm of primer dry films thickness after having sprayed.
Described to scratch putty method using novel large area, it is smooth that this method putty easily forms large area, is not influencing
Under the premise of production process, often scrapes after a putty should all be dried and polish flat, then scrape putty next time again, putty is to scrape 2-
3 times preferably, and first thickness scrapes again thin scrape;The intensity of putty layer can be enhanced in this way and further increase flatness.
Using the method for machine polishing putty, sand paper selects 180-240 mesh.
Using method (airless spraying also can be selected) spray-applied primer of aerial spraying, even sprayed using wet on wet method
Two, working viscosity 20-30s, per pass interval 5-10min flash 5-10min into drying chamber, primer dry films thickness 40-50 after having sprayed
μm。。
It is applied in being sprayed using electrostatic spraying or air spray finishing;The anti-stoning of coating can be improved, is improved attached with priming paint
Put forth effort, improves the flatness and smoothness on coated article surface, to improve the richness and clarity of finishing coat.
Middle painting uses wet on wet continuous spray two, working viscosity 18-24s, per pass interval 5-10min, flash distillation after having sprayed
5-10min is into drying chamber, middle 40-50 μm of painting thickness of dry film.
Topcoating uses electrostatic spraying or air spray finishing, the automobile finish of spraying that can form weatherability, clarity and light
The excellent paint film in pool.
It is 200h or more that priming paint, which uses epoxy ester undercoat, salt spray resistance,.Epoxy polyamide priming paint is such as selected, then salt spray resistance
Performance reaches 500h or more;Such as use ground phosphorating treatment+epoxy polyamide priming paint, ground for galvanized sheet or aluminium alloy plate, then it is resistance to
Salt fog performance reaches 800h or more.
Middle apply applies using in acroleic acid polyurethane or polyester-polyurethane, is applied in the dicoration of semi-gloss or bloom.It can be effective
Raising topcoat richness, while preventing from oozing under finishing coat, improve clarity and gloss of finishing coat etc..
Finishing coat uses acroleic acid polyurethane or polyester modification acrylic polyurethane finish paint;It uses with national treasury aluminium powder and acrylic acid
The metallic finishe prepared based on resin, coating varnish are acroleic acid polyurethane varnish.Background color coating resins are acrylic resin, color
Same opalescent lacquers (one pack system);It is acrylic resin (one pack system) that opalescent lacquers, which uses import pearly-lustre, matrix resin,;Coating varnish is third
Olefin(e) acid polyurethane lacquer.
Auto parts and components novel coating line modified technique of the present invention, cathode electrodip painting is water paint, is good for the environment;It carries
The corrosion resistance and wet-hot aging performance paint film coefficients of friction of high product are suitable, salt spray resistance can reach 240-1000h or more,
Wet-heat resisting 500h or more.Production cost is reduced, production efficiency is improved.
Priming paint use weather ability cathode electrophoresis priming paint, cathode electrodip painting have coating efficiency height, economic security, pollute less,
Corrosion Protection is good, can be completely achieved the features such as automatic management, and rapid popularization and application has been obtained on painting dressing automobiles.
Unleaded, Wuxi cathode electrodip painting, low-temperature bake type cathode electrodip painting, high throwing power, the cathode of low solvent content are electric
Swimming paint, the cathode electrodip painting etc. of high sharp edge anti-corrosive properties obtain ripe application in paint line.But due to current cathode
The weather resistance of electrophoretic paint matrix resin (epoxy resin) is poor, with automobile product type increase and the raising of quality requirement,
Some, which only apply the parts of electrophoretic paint and assembly, will not only have higher corrosion resistance, also have certain weather resistance
(such as commercial car frame assembly etc.), therefore external coating development quotient develops weather ability cathode electrophoresis paint.
The cathode electrodip painting of resistance to UV changes original aromatic isocyanate at aliphatic isocyanide by adjusting formulation for coating material
Acid esters, and the pigment of UV stabilizer and UV stabilizations is added to improve weather resistance.Coating development commercialization distinct methods (including air
Exposure, artificial accelerated aging test) the uv-resistance energy that tests the coating, as a result all prove that the cathode electrodip painting uv-resistance can reach
To with apply comparable level in powder.
The matrix resin of layered cathode electrophoretic paint is the mixing of epoxy resin and weatherability resin.In paint film baking process
In, different ingredients embodies respective function by being layered electric precipitating, and there is high-weatherability energy, lower layer to have high anti-corrosive properties on upper layer
Energy.Mainly by controlling resin properties Sp values, epoxy resin and weatherability resin is made to be detached in curing of coating.Layering is cloudy
Pole electrodeposited paint film ability 400h accelerated aging tests, light-protection rate 80%, the corrosion resistance of paint film are suitable with current electrophoretic paint.
The above described is only a preferred embodiment of the present invention, not making in any form to the structure of the present invention
Limitation.It is every according to the technical essence of the invention to any simple modification, equivalent change and modification made by above example,
Belong within the scope of technical scheme of the present invention.
Claims (9)
1. a kind of auto parts and components novel coating line modified technique, includes the following steps:
Paint front surface processing;Phosphatization;It is cleaned and dried;Priming paint;It is dry;Putty is slightly scraped;Putty is carefully scraped;Middle painting;Finishing;Finishing coat;Point
Color, it is characterised in that:
Removing surface step:It is cleaned with heat alkali liquid and removes degreasing with organic solvent scouring;320-400 is first used in glass fiber reinforced plastic surface
Mesh sand paper is first polished, and is then cleaned with organic solvent and is removed remover;The cleaning solution that the yellow rust of bodywork surface is prepared using phosphoric acid
It cleans;
Phosphorating treatment step:It is handled using film-type zinc salt fast bonderizing, phosphorization film quality 1-3g/m, 1-2 μm of film thickness, crystal grain
50-70 DEG C of progress phosphatization of 25-35 DEG C of low temperature or medium temperature can be used in 1-10 μm of degree;
Priming paint salt fog >=500h, good with the strong adhesive force of base material and middle painting or finishing coat binding force, coating machinery performance is good, and impact >=
50cm, toughness≤1mm, the coating of hardness >=0.5 is as priming paint;
Putty is scraped on the prime coat parched, is once applied the thickness scraped and is no more than 0.5mm.
2. auto parts and components novel coating line modified technique according to claim 1, it is characterised in that:The spray-applied primer can
Using wet on wet method Lian Pen bis-, working viscosity 20-30s, per pass interval 5-10min, 5-10min entering to dry is flashed after having sprayed
Room, 40-50 μm of primer dry films thickness.
3. auto parts and components novel coating line modified technique according to claim 1, it is characterised in that:It is described using novel
Large area scratches putty method, often scrapes after a putty should all be dried and polishes flat, then scrapes putty next time again, putty is to scrape 2-
3 times preferably, and first thickness scrapes again thin scrape;
Sand paper selects 180-240 mesh.
4. auto parts and components novel coating line modified technique according to claim 1, it is characterised in that:Using aerial spraying
Method spray-applied primer, using wet on wet method Lian Pen bis-, working viscosity 20-30s, per pass interval 5-10min, sudden strain of a muscle after having sprayed
5-10min is steamed into drying chamber, 40-50 μm of primer dry films thickness.
5. auto parts and components novel coating line modified technique according to claim 1, it is characterised in that:Using electrostatic spraying or
It is applied in air spray finishing spraying;The wet on wet continuous spray two of middle painting use, working viscosity 18-24s, per pass interval 5-10min,
5-10min is flashed after having sprayed into drying chamber, middle 40-50 μm of painting thickness of dry film;
Topcoating uses electrostatic spraying or air spray finishing, the automobile finish of spraying that it is excellent to form weatherability, clarity and gloss
Good paint film.
6. auto parts and components novel coating line modified technique according to claim 1, it is characterised in that:Priming paint uses epoxy-ester
Priming paint, salt spray resistance are 200h or more.
7. auto parts and components novel coating line modified technique according to claim 1, it is characterised in that:Middle apply uses acrylic acid
It applies in polyurethane or polyester-polyurethane, is applied in the dicoration of semi-gloss or bloom.
8. auto parts and components novel coating line modified technique according to claim 1, it is characterised in that:Finishing coat uses acrylic acid
Polyurethane or polyester modification acrylic polyurethane finish paint;Use the flash of light prepared based on national treasury aluminium powder and acrylic resin
Paint, coating varnish are acroleic acid polyurethane varnish.
9. auto parts and components novel coating line modified technique according to claim 1, it is characterised in that:Background color coating resins are third
Olefin(e) acid resin, the same opalescent lacquers of color;Opalescent lacquers uses import pearly-lustre, and matrix resin is acrylic resin;Coating varnish is propylene
Sour polyurethane lacquer.