CN107226730A - 一种生物有机肥的制备方法 - Google Patents
一种生物有机肥的制备方法 Download PDFInfo
- Publication number
- CN107226730A CN107226730A CN201710368382.7A CN201710368382A CN107226730A CN 107226730 A CN107226730 A CN 107226730A CN 201710368382 A CN201710368382 A CN 201710368382A CN 107226730 A CN107226730 A CN 107226730A
- Authority
- CN
- China
- Prior art keywords
- selenium
- rich
- fertilizer
- powder
- organic fertilizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种生物有机肥的制备方法,得到的富硒富硅生物有机肥,有机硒,有机硅含量高,作物吸收硒硅量大,复合菌剂的使用可以起到解磷、固氮以及增强土壤肥力的功效,能显著提高果实各种微量矿物元素含量,制备工艺简单,制造成本低,适于工业化生产。养分不易流失,肥效更为长久,原料经过发酵后含有丰富的硒元素,能够增加作物果实中硒的含量,提高瓜果的经济价值,种植效益获得明显提升。施用效果能够显著提高农产品的含硒量,并显著提高有机硒占农产品总硒的百分含量,适用于我国缺硒或低硒地区应用,对提高人群硒水平具有积极意义。该专利复合菌剂的使用可以起到解磷、固氮以及增强土壤肥力的功效,能显著提高果实各种微量矿物元素含量。
Description
技术领域
本发明涉及一种有机肥的制备方法,特别涉及一种富硒富硅生物有机肥的制备方法。
背景技术
近年来,随着人们对饮食健康,食品安全等的日益重视,对农产品的品质要求越来越高,一般的废料已不能满足农作物的养分供应,多采用农家肥作为肥料。可是,农家肥的数量有限,肥效表现不可控,难以适应高标准的要求。在这种情况下,微生物菌肥的作用得到凸显。生物菌肥可通过微生物的代谢为作物提供各种养分,改良作物生存环境,甚至参与作物某些生理过程,增强抗逆性,提高产品数量和品质,且无污染,无农药残留,具有良好的应用前景。
微生物菌肥是指一类含有活微生物的特定制剂,应用于农业生产中,能够获得特定的肥料效应,近年来,许多国家开始致力于筛选和利用生物技术研制新型微生物肥料,并建立了自己的行业或国家标准,以及相应产品质量检查监督机构。我国微生物肥料的研究应用和国际上一样,是从豆科植物上应用根瘤菌接种剂开始的,起初只有大豆和花生根瘤剂,50年代,从原苏联引进自生固氮菌、磷细菌和硅酸盐细菌剂,称为细菌肥料,60年代又推广使用放线菌制成的“5406”抗生菌肥料和固氮蓝绿藻肥;70-80年代中期,又开始研究VA菌根,80年代中期至90年代,农业生产中又相继应用联合国固氮菌和生物钾肥作为拌种剂,近几年来又推广应用由固氮菌、磷细菌、钾细菌和有机肥复合制成的生物肥料做基肥施用,同时大量引进了酵素菌、EM菌群制剂,部分科研院所研制了新型生物菌肥。目前我国微生物肥料发展势头很好,基本上形成了微生物肥料产业,约有1000家企业,年产量达到1000万吨,已逐渐形成肥料家族中的重要成员,且产品种类繁多,微生物肥料使用菌种类型已达90种以上。同时,使用效果也逐渐被农民等使用者认可,应用面积累计达2亿亩,质量意识开始深入人心,质检体系初步形成,少数产品开始进入国际市场,国家产业政策对行业的发展给予了一定的重视和支持。
硒是人体必需的微量元素,参与合成人体内多种含硒酶和含硒蛋白。其中谷胱甘肽过氧化物酶,在生物体内催化氢过氧化物或脂质过氧化物转变为水或各种醇类,消除自由基对生物膜的攻击,保护生物膜免受氧化损伤。硒能提高人体免疫,促进淋巴细胞的增值及抗体和免疫球蛋白的合成。硒对结肠癌、皮肤癌、肝癌、乳腺癌等多种癌症具有明显的拟制和防护的作用,其在体内的中间代谢产物甲基烯醇具有较强的抗癌活性。硒与维生素E、大蒜素、亚油酸、锗、锌等营养元素具有协同抗氧化的功效,增加抗氧化活性。同时,硒具有减轻和缓解重金属毒性的作用。可以被人体所吸收的硒分为元素硒、无机硒和有机硒三种。硒的特点是生物活性和毒性之间范围极端狭窄,为此,各国科学家研究了许多硒化合物,试图寻找活性高、毒性低的硒形式。随着纳米技术的成熟,科学家采用先进的纳米技术,将零价硒制成纳米颗粒硒。纳米硒与一般零价硒相比,发生了生物性质的突变。
肥料中有两种非常重要的元素,硅和钾,硅是植物体组成的重要营养元素之一,硅肥有利于提高作物的光和作用;硅肥能增加作物茎秆的机械强度,提高抗倒伏能力;硅肥能提高作物对病虫害的抵抗力,减少各种病虫害的发生;硅肥能使作物体内通气性增强,可预防根系腐烂和早衰;硅肥能增强作物的抗旱、抗干热风、抗寒等抗逆能力;硅肥能增强瓜果类作物的花粉活力,提高成果率;硅肥能提高磷肥的利用率,调节氮磷钾的平衡吸收;硅肥能改良土壤,促进有机肥分解,拟制土壤病菌及减轻重金属污染;硅肥是品质肥料,可明显改善农产品品质,延长保鲜期。
CN201610073654.6公开了一种富硒肥料,主要由以下组分按重量份数配比组成:鸡粪70~90份,鸽子粪10~16份,蛤蚧粪5~8份,穿山甲粪4~7份,秸秆20~30份,牡蛎壳粉10~16份,菌种2~5份,腐植酸钾12~25份,活化硒矿粉15~22份;其生产方法包括以下步骤:(1)将秸秆粉碎与鸡粪、鸽子粪、蛤蚧粪和穿山甲粪混合均匀进行一次发酵;(2)加入KOH溶液,将pH调节至7.2~7.5,然后加入腐植酸钾,搅拌均匀,再取部分活化硒矿粉与牡蛎壳粉加入发酵池中,搅拌均匀,混合发酵8~10天;(3)加入余下的活化硒矿粉,搅拌均匀,得富硒肥料。该专利为单一富硒有机肥,同时肥料碱性强,对有些农作物不适用。
CN201510567718.3提供了一种富硒营养活力素及制备方法,活力素主要由以下原料制得:以质量份数计,天然矿物肥料5-90份,含钾化合物1-25份,含镁化合物1-25份,氧化钙1-35份,生化黄腐酸粉1-10份,维生素0.25-2.5份,二氧化硅1-45份,亚硒酸钠0.001-0.1份,微量元素补充剂0.25-2.5份。制备方法包括:将富硒营养活力素的各原料混合搅拌均匀,经过造粒干燥、粉碎、过筛后,即得富硒营养活力素。该专利为单一的富硒有机肥,硒含量较低。
CN201610337960.6提供了一种长效矿物富硒肥,包括粉煤灰和沸石;粉煤灰中Se含量为27.9~36.3mg/kg;其制备方法包括如下步骤:将沸石研磨加工成粒级200目以下的沸石粉;将粉煤灰研磨加工成粒级200目以下的粉煤灰粉;将沸石粉与粉煤灰粉按照比例混合,搅拌均匀;在混合物上喷洒质量浓度为5%的食盐水,然后将喷洒食盐水后的混合物制成直径为1~1.5mm的球状颗粒;在430~450℃下烘烤至含水量不大于5%;成品包装。该专利使用化学活化硒成本高,并且制备过程对环境影响较大,不适应大规模生产。
CN201310714813.2提出一种成本低,肥效长,使用方便的富硒有机肥及其制备方法。本发明是以硒矿岩、富硒农作物废弃物、碳源、氮源、氢氧化钙、微生物菌剂和微肥为原料,将硒矿岩粉碎的超微粉与富硒农作废弃物混合后用氢氧化钙调整混合物的pH值,加入微生物菌剂混合发酵,加入碳源、氮源和微肥,搅拌混合制为颗粒得富硒有机肥。该专利直接使用硒矿岩,硒很难直接被植物吸收,使用效果差。
CN201410140864.3涉及一种微纳米矿物硒肥料的制备方法,其特征在于包括以下步骤:1)原料富硒矿物通过第一粉碎机粗粉碎成粗硒矿粉;2)再通过第二粉碎机细粉碎成细硒矿粉;3)细硒矿粉加入腐植酸、添加剂,并用水混合;4)将步骤3)中所得混合物加入搅拌磨中湿法处理0.2-5小时;5)将步骤4)中所得物浓缩处理,再用烘干机干燥打散。该专利直接使用硒矿岩,硒很难直接被植物吸收,使用效果差。
CN201610073653.1发明公开了一种富硒缓释肥料,主要由以下组分按重量份数配比组成:鸡粪70~90份,鸽子粪10~16份,蛤蚧粪5~8份,穿山甲粪4~7份,秸秆20~30份,牡蛎壳粉10~16份,菌种2~5份,腐植酸钾12~25份,活化硒矿粉15~22份;其生产方法包括以下步骤:(1)将秸秆粉碎与鸡粪、鸽子粪、蛤蚧粪和穿山甲粪混合均匀进行一次发酵;(2)加入KOH溶液,将pH调节至7.2~7.5,然后加入腐植酸钾,搅拌均匀,再取部分活化硒矿粉与牡蛎壳粉加入发酵池中,搅拌均匀,混合发酵8~10天;(3)加入余下的活化硒矿粉,搅拌均匀,得富硒缓释肥料。该专利直接使用硒矿岩,硒很难直接被植物吸收,使用效果差。
CN201510504713.6发明涉及一种硒矿物有机肥料,包括发酵产物和硒矿物活性粉;发酵产物各组分按照重量百分比例组成如下:秸秆类有机物质30~80%、畜禽粪便类物质20~50%、秸秆发酵菌0.1~0.3%以及生化黄腐酸菌0.1~0.3%,各组分的质量百分比总和为100%;硒矿物有机肥料由发酵产物与硒矿物活性粉按以下质量比例组成:发酵产物60-75%,硒矿物活性粉25-40%。该专利使用化学活化硒成本高,并且制备过程对环境影响较大,不适应大规模生产。
CN201010600981.5涉及一种有机富硒生物肥及其制备方法:含有下列重量百分比的组份组成:畜禽粪便10%~40%、秸秆粉或腐植土20%~50%、含硒500ppm80目的硒矿粉20%~40%、微生物土壤修复剂0.02%~0.07%、发酵菌0.01%~0.03%。上述原料充分的搅拌均匀堆积发酵,温度达到40℃开始翻堆,两天翻堆一次,当温度达到65℃出现菌丝后翻堆,再堆积发酵三天,粉碎、过筛、包装入库。该专利直接使用硒矿岩,硒很难直接被植物吸收,使用效果差。
CN02113524.X涉及含多种微量元素的复合肥料,目的是提供专门的富硒微量元素肥料,并提供其制法。该肥料是一种含有多种微量元素的液体肥料,其硒含量在3mg/l以上。其制法包括将富硒矿物粉碎、磨粉,得到矿粉;用碱液浸泡1周,取其上的浸泡液,弃去矿渣;用稀酸中和过剩的碱液,至pH=5~6;再加入EM酶制剂发酵6~12天,发酵结束即得到成品。该专利直接使用硒矿岩,硒很难直接被植物吸收,使用效果差。
CN201410820126.3涉及一种富硒生物长效有机肥及其制备方法,包括:富硒植物蛋白、磷、钾、元素硒、锌、铁、镁、锰、铜、钼、硼、钙、稀、铬、钠、锗的含量均大于等于25.0,优选比例总养分:≥30.0最优选比例总养分:≥41.0。其制备方法如下:将富硒生物秸秆、腐植酸、有机酸、土壤改良剂成分按比例混合制成有机混合物,再将菌熟7~10小时,把菌熟与有机混合物进行混合、搅拌匀可包装生产。菌熟选优时间为15~24小时,或20~30小时更佳。该专利肥料中有机硅含量低,肥料营养成分少,施用工序较多。
CN201510421931.3通过制备复合氨基酸水溶液、制备发酵粉、制备有机堆肥、制备微生物菌剂、制备富硒氨基酸微生物有机肥等步骤完成。该专利肥料中有机硅含量低,肥料营养成分少,施用工序较多。
CN201610189805.4发明公开一种富硒富碘营养剂、其制备方法及栽培富硒富碘生菜的方法。该富硒富碘营养剂包括以下质量份数的组分:硒源,以硒质量计:0.05~1;碘源,以碘质量计:0.2~5;有机肥:60~90;硼砂:0.2~0.5;硫酸锰:0.4~1.1;肥料粘结剂:0.4~1.2。其制备方法为:将硒源、碘源分别超微粉碎为粒径小于50μm的粉末,且其中纳米级别所占的比例为5~20wt%;将硼砂和硫酸锰粉碎至粉末状,过150目筛;将有机肥烘干,粉碎,备用;将根据上述步骤处理得到的硒源、碘源、硼砂、硫酸锰和有机肥混匀,在圆盘造粒机上造粒,圆盘造粒时添加肥料粘结剂。栽培富硒富碘生菜的方法:在生菜移栽成活后,施入富硒富碘营养剂,收获富硒富碘生菜。该专利肥料中有机硅含量低,肥料营养成分少,施用工序较多。
CN201310138455.5涉及一种富硒有机肥的制备方法,包括如下步骤:(1)将富硒食用菌培养废料和禽畜粪便经粉碎,混合得到基料,向基料中加入发酵菌曲进行发酵,得到发酵料;(2)向步骤(1)得到的发酵料中加入生物氮、生物磷、生物钾、腐殖酸和微量元素,经过混匀、粉碎、筛选,得到细粉状产品;可选地,步骤(2)之后进行步骤(3):将细粉状产品造粒得到颗粒状产品。该专利肥料中有机硅含量低,肥料营养成分少,施用工序较多。
CN201310480212.X涉及生物有机肥,是将城市污泥、牛粪按照一定比例混合后加入无机硒作为蚯蚓饵料,经蚯蚓新陈代谢的富集作用,转化为富含有机硒的蚯蚓粪,富硒蚯蚓粪经混匀、制料、粪干制备为肥料颗粒后,再经涂膜工序在肥料颗粒上加涂一层微生物菌剂,最后制备为富硒有机肥。该专利肥料中有机硅含量低,肥料营养成分少,施用工序较多。
CN201510756190.4涉及一种油茶富硒生物有机肥、制备方法及其应用。该生物有机肥按照质量百分比包括以下组分:糖渣有机物60%,菜枯5%,尿素10%,速效磷钾10%,钙镁磷肥8%,硼酸2%,七水硫酸锌2%,氨基酸螯合锌、铜、铁、锰1.5%,有机硒酶0.1―0.5%,酵母粉0.5%,糖化酶0.5%。该专利肥料中有机硅含量低,肥料营养成分少,施用工序较多。
CN201410501835.5选择食用菌富硒栽培后的菌渣为主要原材料,同时添加外源无机硒,接种外源微生物发酵菌剂,并采取固态混合发酵方式进行扩大繁殖获得发酵菌种,利用发酵微生物菌群富集优势,通过对堆肥静态强制式通风系统供氧和堆肥二次发酵等关键技术,采取菌渣预处理、发酵微生物菌种扩繁、发酵料配制、建堆发酵和熟化工艺流程,高效率生产高品质的富硒有机肥。该专利肥料中有机硅含量低,肥料营养成分少,施用工序较多。
CN201510200582.2涉及富硒生物有机肥。该富硒生物有机肥包括:猪粪400~500份;地瓜秧70~110份;氮磷钾肥60~100份;豆粕70~100份;硅藻土20~40份;石秸秆80~120份;糖类10~30份;废菌孢10~20份。该专利肥料中有机硅含量低,肥料营养成分少,施用工序较多。
CN201110376234.2公开一种抗菌生物活性富硒有机肥制作方法,是由蚕沙和鸡粪为载体,根据植物生理学、植物病理学、植物免疫学、土壤微生物学和生物工程学原理,加入能够分泌天然免疫物质的微生物菌群,利用现代生物发酵技术发酵处理后,再添加多种微量元素制备成纯生物有机免疫肥料。所述一种抗菌生物活性富硒有机肥是用重量比5~10份的蚕沙和10~80份鸡粪加1~5份糖蜜水和1~3份的80日膨润土混合搅拌均匀后接种重量比0.6~1.6份的液体微生物菌种经微氧32度恒温发酵48h后添加重量比为0.1~0.39份粉体微量元素经造粒、低温干燥或风干到湿度在12%左右时即得。该专利肥料中有机硅含量低,肥料营养成分少,施用工序较多。
CN201510063244.9公开了一种富硒水稻专用微生物有机肥,按照重量份的原料为:预发酵料:12~18份、矿物质:6~10份、枯草芽孢杆菌ATCC 6633:0.5~0.8份、富硒水稻统糠:30~40份、中药药渣:5~10份、腐植酸:15~20份;所述预发酵料按照重量份的原料为:豆粕10~20份、腐植酸:1~3份、糖蜜3~5份、亚硒酸钠0.1~0.2份、枯草芽孢杆菌ATCC6633:0.1~0.2份;所述矿物质按照重量份的原料为:所述矿物质按照重量份的原料为:磷矿粉:40-60份、麦饭石40~60份、硅粉:1~3份。该专利采用的硒源为化工原料,比有机硒的吸收效果差,成本高。
CN201610194868.9提供一种水稻种植用富硒缓释有机肥,包括如下重量份的成分:尿素,家禽粪便,玉米秸秆,甘蔗渣,莱饼,EM菌种,三氮唑核苷,三唑酮,亚硒酸钠,缓释剂,EDTA螯合铁,EDTA螯合锌,EDTA螯合铜,氨基酸螯合锰,氨基酸螯合铁,氨基酸螯合钼,脲酶抑制剂,硝化抑制剂。该专利采用的硒源为化工原料,比有机硒的吸收效果差,成本高。
CN201410434171.5公开了一种富硒生物有机肥,其中,包括重量份数的如下组分:猪粪和富硒膨润土混合物400~500份,草籽与麦穗按照质量比4:1粉碎混合物30~50份,氮磷钾肥80~120份,带玉米粒的玉米棒与微生物菌剂按照质量比50:1配制的混合物50~80份,腐殖质与蟹壳粉按照质量比1:6配制的混合物40~60份,炉甘石粉末10~30份,牡蛎粉80~120份。本发明的配比简单,有机肥中硒含量高,能够显著提高土壤含硒量,进而明显提高作物吸收率。本发明使用的原材料中,腐熟后,通过翻抛调节含水量在造粒得到富硒生物有机肥,施用此有机肥的贫硒土地,种植的作物的含硒量较传统提高35%,这种作物所得的食品的含硒量提高18~22%。该专利采用的硒源为化工原料,比有机硒的吸收效果差,成本高。
CN201510062719.2公开了一种富硒水稻专用微生物有机肥及其制备方法,按照重量份的原料为:预发酵料:12~18份、矿物质:6~10份、枯草芽孢杆菌ATCC 6633:0.5~0.8份、富硒水稻统糠:30~40份、木薯粉:5~10份、腐植酸:15~20份;所述预发酵料按照重量份的原料为:豆粕10~20份、腐植酸:1~3份、糖蜜3~5份、亚硒酸钠0.1~0.2份、枯草芽孢杆菌ATCC 6633:0.1~0.2份;所述矿物质按照重量份的原料为:所述矿物质按照重量份的原料为:磷矿粉:40-60份、麦饭石40~60份、硅粉:1~3份。该专利采用的硒源为化工原料,比有机硒的吸收效果差,成本高。
CN201410433892.4公开了一种富硒生物有机肥的制造方法,其中,包括如下步骤:A、将带玉米粒的玉米棒与微生物菌剂按照质量比50:1配制的混合物粉碎,牡蛎粉粉碎,豆科类秸秆粉碎,均粉碎至大小100~120目,备用;B、将猪粪和富硒膨润土混合物,草籽与麦穗按照质量比4:1粉碎混合物,氮磷钾肥,带玉米粒的玉米棒与微生物菌剂按照质量比50:1配制的混合物,腐殖质与蟹壳粉按照质量比1:6配制的混合物,炉甘石粉末,牡蛎粉投入到发酵池中,加水至没过物料,上面封盖塑料膜,发酵25~30天;C、去1~3份酵素配比到500倍体积浓度,倒入到发酵池内,继续封盖发酵10~12天,至配料中的固体成份溶解;本发明制造方法简单,有机肥中硒含量高,能够显著提高土壤含硒量,进而明显提高作物吸收率。该专利肥料中有机硅含量低,肥料营养成分少,施用工序较多。
CN201410433893.9公开了一种富硒生物有机肥的使用方法,其中,包括如下步骤:A、测定待施肥地块的硒含量;B、根据测定结果选择施肥量:测定结果土地内硒含量低于0.006g/平米的地块,每平米施肥400~600g,测定结果土地内硒含量0.006~0.01g/平米的地块,富硒生物有机肥的组分为:猪粪和富硒膨润土混合物,草籽与麦穗按照质量比4:1粉碎混合物,氮磷钾肥,带玉米粒的玉米棒与微生物菌剂按照质量比50:1配制的混合物,腐殖质与蟹壳粉按照质量比1:6配制的混合物,炉甘石粉末、牡蛎粉。该专利肥料中有机硅含量低,肥料营养成分少,施用工序较多。
CN201510770731.9涉一种富硒生物有机肥及其制备方法,所述富硒生物有机肥是使用酵素扩大菌与固体载体混合后,经过发酵、粉碎、翻堆、造粒、干燥后制得。该专利肥料中有机硅含量低,肥料营养成分少,施用工序较多。
CN201510352797.6公开了一种硒肥,其中,包括重量份数的如下组分:赭石和富硒土的混合物400~500份,菠菜叶与地瓜页按照质量比5:2粉碎混合物30~50份,质量比12%的吲哚乙酸溶液80~120份,带玉米粒的玉米棒与微生物菌剂按照质量比75;2配制的混合物50~80份,腐殖质与蟹壳粉按照质量比1:6配制的混合物40~60份,草炭10~30份,贝壳粉与亚硒酸钠质量比25:1的混合物80~120份。该专利肥料中有机硅含量低,肥料营养成分少,施用工序较多。
CN201610356572.2公开一种富硅有机肥及其制备方法,所述富硒有机肥包括以下重量份原料:硅藻土5~8份、稻草5~10份、节节草20~40份、玉米芯3~8份、豆秸10~20份、EDTA:5~7份、过磷酸钙3~5份、发酵菌剂0.5~0.8份。但该肥料中不含有机硒,营养成分少,施用工序繁多。
CN201310551028.X提供了一种富硒生物有机肥的生产新技术。其特征在于设计者将自己研制成功的选用以出完菇的黑木耳或其它食用菌培养基菌袋每袋含硒量在30~100μg的废菌糠和鸡粪为原料生产富硒菌糠生物有机肥。该肥料使用范围单一,且有效菌剂含量低。
CN201510352798.0公开了一种硒肥的制造方法,其中,包括如下步骤:A、将带玉米粒的玉米棒与微生物菌剂按照质量比75;2配制的混合物粉碎,贝壳粉与亚硒酸钠质量比25:1的混合物粉碎,豆科类秸秆粉碎,均粉碎至大小100~120目,备用;B、将赭石和富硒土的混合物,菠菜叶与地瓜页按照质量比5:2粉碎混合物,质量比12%的吲哚乙酸溶液,带玉米粒的玉米棒与微生物菌剂按照质量比75;2配制的混合物,腐殖质与蟹壳粉按照质量比1:6配制的混合物,草炭,贝壳粉与亚硒酸钠质量比25:1的混合物投入到发酵池中,加水至没过物料,上面封盖塑料膜,发酵25~30天;C、去1~3份酵素配比到500倍体积浓度,倒入到发酵池内,继续封盖发酵10~12天,至配料中的固体成份溶解。该肥料为单纯的硒肥,微量元素含量低。
CN200910213522.9涉及一种富硒生物有机肥及其制备方法,该硒肥主要的由螯合硒溶液10~30%,螯合锌溶液10~30%,螯合铁溶液20~40%,硼酸溶液10~30%,拮抗剂1~10%,水10~30%的螯合硒30~50%,配比加工合成。该肥料仅为富硒有机肥,不含有机硅,且各种微量矿物元素含量低,肥效差。
CN201510023869.2公开了一种纳米硒生物有机肥及其制备方法,由鸡粪、秸秆、富硒膨润土、草炭土、纳米二氧化硒、亚硒酸钠、碳酸氢钠、红糖、尿素、尿素酶抑制剂和复合菌剂制备而成,制备方法包括称量、混合和发酵等步骤。该肥料为单纯的硒肥,微量元素含量低。
CN201210390566.0涉及一种富硒生物有机肥及其制备方法。由以下原料制成:富硒农作物废弃物100份;离子态硒0.005~0.15份;碳源0.2~2.5份;氮源0.5~3.5份;微生物菌剂2~4.2份;助剂0.4~5份。该肥料为单纯的硒肥,微量元素含量低。
CN201310327762.8公开了一种富硒生物有机肥,所述富硒生物有机肥包括按质量百分比组成的下列成分:蚯蚓粪75%~80%,亚硒酸钠10%~15%,土壤腐殖酸5%~10%,生物发酵菌2%~3%。该肥料为单纯的硒肥,微量元素含量低。
CN201310150128.1公开了一种富硒生物有机肥的生产制备方法,包括原料准备、制备微生物复合菌剂、配制发酵物料和生物发酵等步骤。该肥料为单纯的硒肥,微量元素含量低。
CN201610188413.6提供一种富硒生物有机肥,按质量份数计,由以下成分组成:有机残渣40~80份、含硒化合物0.01~0.1份、氮磷钾肥10~15份、微生物菌剂0.5~1份、助剂5~10份,所述微生物菌剂由地衣芽孢杆菌、淡紫拟青霉菌、解淀粉芽孢杆菌组成,所述地衣芽孢杆菌、淡紫拟青霉菌、解淀粉芽孢杆菌的有效活菌数比为,地衣芽孢杆菌:淡紫拟青霉菌:解淀粉芽孢杆菌=1~100:1~200:10~100,微生物菌剂的有效活菌数为大于2亿/克。该肥料为单纯的硒肥,微量元素含量低。
CN201310714813.2提出一种成本低,肥效长,使用方便的富硒有机肥及其制备方法。本发明是以硒矿岩、富硒农作物废弃物、碳源、氮源、氢氧化钙、微生物菌剂和微肥为原料,将硒矿岩粉碎的超微粉与富硒农作废弃物混合后用氢氧化钙调整混合物的pH值,加入微生物菌剂混合发酵,加入碳源、氮源和微肥,搅拌混合制为颗粒得富硒有机肥。该肥料为单纯的硒肥,微量元素含量低。
CN201510421928.1通过制备复合氨基酸水溶液、制备发酵粉、制备富硒有机堆肥、制备微生物菌剂、制备富硒氨基酸微生物有机肥等步骤完成。该肥料为单纯的硒肥,微量元素含量低。
CN201510062652.2公开了一种富硒微生物有机肥及其制备方法,所述富硒微生物有机肥,按照重量份的原料为:预发酵料:12~18份、矿物质:6~10份、枯草芽孢杆菌10147:0.5~0.8份、食用菌下脚料:30~40份、窑灰:5~10份、沼气水:15~20份;所述预发酵料按照重量份的原料为:蝇蛆10~20份、沼气水:1~3份、糖蜜3~5份、亚硒酸钠0.1~0.2份、枯草芽孢杆菌10147:0.1~0.2份;所述矿物质按照重量份的原料为:所述矿物质按照重量份的原料为:磷矿粉:40-60份、煤矸石40~60份、硅粉:1~3份。该肥料仅为富硒有机肥,不含有机硅,且各种微量矿物元素含量低,肥效差。
CN201510781946.0涉及一种农业生产中的有机肥,具体涉及一种富硒生物有机肥,是由以下重量份数的原料制成:生态羊粪60~85份;桐麸10~20份:草炭5~15份:硒微肥或硒矿粉0.5~2份;枯草芽孢杆菌或放线菌活菌剂0.5~3份;其生产方法是将生态羊粪、桐麸、草炭混合均匀,然后加入硒微肥或硒矿粉、枯草芽孢杆菌或放线菌活菌剂,混合均匀,建堆,常温发酵而得。该肥料仅为富硒有机肥,不含有机硅,且各种微量矿物元素含量低,肥效差。
CN200910047269.4将含硒煤矸石、含硒麦饭石和木鱼石分别经粉碎、球磨成粉状原料;然后按比例混合成矿物质原料并加入醋酸溶液混合成酸化矿物质原料;最后将所得酸化矿物质原料与生物有机肥混合进行发酵,发酵成熟后即得到富硒有机肥产品。该肥料仅为富硒有机肥,不含有机硅,且各种微量矿物元素含量低,肥效差。
CN200910044507.6一种富硒生物有机肥,它的组分及其重量百分比为鸡粪或猪粪55%~65%,枯饼9%~7%,谷糠21%~12.1%,硒矿粉14%~15%,微肥0.9%~0.8%,富硒增甜素0.05%和FW1生物制剂0.05%,它的生产工艺是备料、激活、去臭、拌合、拌料、接种、发酵、干燥、委检和包装。该肥料仅为富硒有机肥,不含有机硅,且各种微量矿物元素含量低,肥效差。
CN201210038814.5涉及一种酵素麦饭石富硒生物有机肥。该肥选用当地油脂业、种植业和养殖业生产出的副产品有机质,麦饭石粉和富硒元素微肥适量混合后加入酵素菌,再加水均匀混拌后堆堆盖帘保温,经反复升温翻堆充氧发酵而制成。该肥料仅为富硒有机肥,不含有机硅,且各种微量矿物元素含量低,肥效差。
CN201610073653.1公开了一种富硒缓释肥料,主要由以下组分按重量份数配比组成:鸡粪70~90份,鸽子粪10~16份,蛤蚧粪5~8份,穿山甲粪4~7份,秸秆20~30份,牡蛎壳粉10~16份,菌种2~5份,腐植酸钾12~25份,活化硒矿粉15~22份;其生产方法包括以下步骤:(1)将秸秆粉碎与鸡粪、鸽子粪、蛤蚧粪和穿山甲粪混合均匀进行一次发酵;(2)加入KOH溶液,将pH调节至7.2~7.5,然后加入腐植酸钾,搅拌均匀,再取部分活化硒矿粉与牡蛎壳粉加入发酵池中,搅拌均匀,混合发酵8~10天;(3)加入余下的活化硒矿粉,搅拌均匀,得富硒缓释肥料。该肥料仅为富硒有机肥,不含有机硅,且各种微量矿物元素含量低,肥效差。
发明内容
本发明的目的在于克服上述现有技术的缺点,提供了一种生物有机肥的制备方法。按照本发明制备方法得到的富硒富硅生物有机肥,有机硒,有机硅含量高,作物吸收硒硅量大,复合菌剂的使用可以起到解磷、固氮以及增强土壤肥力的功效,能显著提高果实各种微量矿物元素含量,该方法制备工艺简单,制造成本低,适于工业化生产。
为达到上述目的,本发明采用的技术方案是:
第一步,富硒矿石的活化
首先,将富硒矿石采用颚式破碎机破碎至0.01~3cm的颗粒;
然后,按照质量分数将40~80%的富硒矿石颗粒,10~40%的石灰,5~10的钾长石,5~10%的碳酸钾放入球磨机中,球磨4~6h得粉料;
然后,将球磨后的粉料通过100~150目的标准筛后形成配合料;
然后,将配合料放入回转炉中自室温经10~20min升温至400~490℃,并保温30分钟;
最后,通过30~60min将配合料降温至室温,破碎粉磨至100~150目既得活化富硒矿粉;
第二步,富硅液体溶剂的制备
首先,按SiO2:K2O=2~2.7:1的摩尔比取石英砂和碳酸钾,然后加入石英砂和碳酸钾质量1~2%的硒粉混合至均匀度大于98%成为配合料;
然后,将配合料加入已经升温至1350~1450℃的石英坩埚中得熔融的玻璃液;
然后,将熔融的玻璃液倒入蒸馏水中放入球磨机中球磨2~4h,其中,玻璃液与水的质量比为1:1.2~1.5;
最后,将球磨的硅酸钾溶液通过100目标准筛后,既得富硅液体溶剂;
第三步,微生物菌剂的扩培
首先,按质量百分比将0.2~0.8%的淀粉,0.05~0.15%的硫酸镁,0.1~0.5%的磷酸二氢钾,0.006~0.012%的硫酸锰置于水中,调节pH至6.8~7.2制备发酵培养基,将枯草芽孢杆菌菌种接种到已灭菌发酵培养基中,其中,发酵条件为发酵罐容积:每分钟通入无菌空气体积等于0.9~1.1:0.5,培养温度35~40℃,搅拌转数100~200rpm,溶氧不低于30%,pH值不低于6.5,搅拌培养6~8小时,使活菌含量达到1010pfu/ml得到发酵液,然后向发酵液中分别加入5g·L-1的磷酸氢二钠和0.1g·L-1氯化钠絮凝,絮凝完成后采用板框压滤方式获得菌泥,菌泥45~50℃鼓风干燥到含水量25~35%,旋风分离菌粉,放入粉碎机中粉碎,过30目筛得枯草芽孢杆菌菌剂;
然后,按照质量百分比将0.2~0.8%的淀粉,0.2~0.8%的葡萄糖,0.01~0.08%的酵母膏,0.005~0.0158%的硫酸锰,0.0052~0.018%的VB12置于水中,调节pH至6.8~7.2得发酵培养基,将固氮巨大芽孢杆菌菌种接种到已灭菌的发酵培养基中,其中发酵条件为:培养温度32~38℃,搅拌转数100~200rpm,pH值不低于6.5,搅拌培养6~8小时,使活菌含量达到1010pfu/ml得到发酵液,然后向发酵液中分别加入5g·L-1的磷酸氢二钠和0.1g·L-1的氯化钙絮凝,和絮凝完成后采用板框压滤方式获得菌泥,鼓风干燥到含水量25~35%,旋风分离菌粉,放入粉碎机中粉碎,过30目筛得到巨大芽孢杆菌菌剂;
最后,按照1:0.1~1的重量比将所制备的枯草芽孢杆菌菌剂和巨大芽孢杆菌菌剂混合均匀得扩培的微生物菌剂;
第四步,富硒富硅生物有机肥的制备
首先,用5~10倍量的秸秆粉与微生物菌剂混合均匀得混合物,按质量百分比1:24~40,将混合物与牛羊粪混合堆积发酵,水分控制在50%~60%,发酵时用薄膜覆盖,待内部温度升到25~30℃时,将覆盖物揭开,堆温升至60~80℃时开始翻倒,每天一次,直到牛羊粪完全腐熟得腐熟牛羊粪;
然后,按照重量分数将40~60%腐熟牛羊粪,10~20%富硒石煤,10~20%活化富硒矿粉,0.1~1%硒酸钠,添加10~20%的腐殖酸干物质,保持水分在10~30%,并混合均匀;
然后,将混合均匀的配合料放入圆盘造粒机中,调整造粒机转数70~90转/分,同时喷入配合料质量3~20%的富硅液体,,将配合料制备成2~3mm的球形颗粒;
最后,将造好的颗粒放入回转炉中,30~50min通过120~150℃的回转炉,冷却至室温既得富硒富硅生物有机肥。
所述的石灰,钾长石,碳酸钾,石英砂,硒粉,硫酸镁,磷酸二氢钾,硫酸锰,磷酸二氢钠,均为工业原料,粒度为30~50目。
所述的球磨机中的研磨介质采用平均直径为5~8mm的玛瑙球。
同现有技术相比,本发明具有以下优点:
(1)本发明中所制备的富硒生物有机肥通过不同的硒源引入,保证了在植物生长过程中都可以有充足浓度的硒进行吸收,硒源使用时间长,农作物中硒的含量高。
(2)本发明采用熔融法制备富硅有机溶剂作为粘结剂,保证了有机肥中硅的含量,同时造粒后肥料颗粒的强度有了明显的提升,且外观质量比用水作为粘结剂要高,而且可以起到肥料的缓释溶解的效果。使肥料的肥效比其他方法增加30~40%以上。
(3)本发明在对硒进行活化的同时,对矿石中其他微量元素也进行了活化,所以该发明制备的有机肥中微量元素Fe,Zn,Sr,Ba,Cu,Mg等含量高,且易被植物吸收。
具体实施方式
实施例1:
第一步,富硒矿石的活化
首先,将富硒矿石采用颚式破碎机破碎至0.6cm的颗粒;
然后,按照质量分数将67%的富硒矿石颗粒,23%的石灰,5%的钾长石,5%的碳酸钾放入球磨机中,球磨4h得粉料;
然后,将球磨后的粉料通过100~150目的标准筛后形成配合料;
然后,将配合料放入回转炉中自室温经10min升温至400℃,并保温30分钟;
最后,通过30min将配合料降温至室温,破碎粉磨至100~150目既得活化富硒矿粉;
第二步,富硅液体溶剂的制备
首先,按SiO2:K2O=2:1的摩尔比取石英砂和碳酸钾,然后加入石英砂和碳酸钾质量1%的硒粉混合至均匀度大于98%成为配合料;
然后,将配合料加入已经升温至1350℃的石英坩埚中得熔融的玻璃液;
然后,将熔融的玻璃液倒入蒸馏水中放入球磨机中球磨2h,其中,玻璃液与水的质量比为1:1.2;
最后,将球磨的硅酸钾溶液通过100目标准筛后,既得富硅液体溶剂;
第三步,微生物菌剂的扩培
首先,按质量百分比将0.2%的淀粉,0.05%的硫酸镁,0.1%的磷酸二氢钾,0.006%的硫酸锰置于水中,调节pH至6.8制备发酵培养基,将枯草芽孢杆菌菌种接种到已灭菌发酵培养基中,其中,发酵条件为发酵罐容积:每分钟通入无菌空气体积等于0.9:0.5,培养温度35℃,搅拌转数115rpm,溶氧不低于30%,pH值不低于6.5,搅拌培养6小时,使活菌含量达到1010pfu/ml得到发酵液,然后向发酵液中分别加入5g·L-1的磷酸氢二钠和0.1g·L-1氯化钠絮凝,絮凝完成后采用板框压滤方式获得菌泥,菌泥45℃鼓风干燥到含水量25%,旋风分离菌粉,放入粉碎机中粉碎,过30目筛得枯草芽孢杆菌菌剂;
然后,按照质量百分比将0.2%的淀粉,0.2%的葡萄糖,0.01%的酵母膏,0.005%的硫酸锰,0.0052%的VB12置于水中,调节pH至6.8得发酵培养基,将固氮巨大芽孢杆菌菌种接种到已灭菌的发酵培养基中,其中发酵条件为:培养温度32℃,搅拌转数100rpm,pH值不低于6.5,搅拌培养6小时,使活菌含量达到1010pfu/ml得到发酵液,然后向发酵液中分别加入5g·L-1的磷酸氢二钠和0.1g·L-1的氯化钙絮凝,和絮凝完成后采用板框压滤方式获得菌泥,鼓风干燥到含水量25%,旋风分离菌粉,放入粉碎机中粉碎,过30目筛得到巨大芽孢杆菌菌剂;
最后,按照1:0.1的重量比将所制备的枯草芽孢杆菌菌剂和巨大芽孢杆菌菌剂混合均匀得扩培的微生物菌剂;
第四步,富硒富硅生物有机肥的制备
首先,用5倍量的秸秆粉与微生物菌剂混合均匀得混合物,按质量百分比1:24,将混合物与牛羊粪混合堆积发酵,水分控制在50%,发酵时用薄膜覆盖,待内部温度升到25℃时,将覆盖物揭开,堆温升至60℃时开始翻倒,每天一次,直到牛羊粪完全腐熟得腐熟牛羊粪;
然后,按照重量分数将40%腐熟牛羊粪,20%富硒石煤,19%活化富硒矿粉,1%硒酸钠,添加20%的腐殖酸干物质,保持水分在10%,并混合均匀;
然后,将混合均匀的配合料放入圆盘造粒机中,调整造粒机转数70转/分,同时喷入配合料质量3%的富硅液体,,将配合料制备成2~3mm的球形颗粒;
最后,将造好的颗粒放入回转炉中,20min通过120℃的回转炉,冷却至室温既得富硒富硅生物有机肥。
实施例2:
第一步,富硒矿石的活化
首先,将富硒矿石采用颚式破碎机破碎至0.01cm的颗粒;
然后,按照质量分数将80%的富硒矿石颗粒,10%的石灰,5%的钾长石,5%的碳酸钾放入球磨机中,球磨5h得粉料;
然后,将球磨后的粉料通过100~150目的标准筛后形成配合料;
然后,将配合料放入回转炉中自室温经15min升温至450℃,并保温30分钟;
最后,通过40min将配合料降温至室温,破碎粉磨至100~150目既得活化富硒矿粉;
第二步,富硅液体溶剂的制备
首先,按SiO2:K2O=2.5:1的摩尔比取石英砂和碳酸钾,然后加入石英砂和碳酸钾质量2%的硒粉混合至均匀度大于98%成为配合料;
然后,将配合料加入已经升温至1380℃的石英坩埚中得熔融的玻璃液;
然后,将熔融的玻璃液倒入蒸馏水中放入球磨机中球磨3h,其中,玻璃液与水的质量比为1:1.5;
最后,将球磨的硅酸钾溶液通过100目标准筛后,既得富硅液体溶剂;
第三步,微生物菌剂的扩培
首先,按质量百分比将0.5%的淀粉,0.1%的硫酸镁,0.5%的磷酸二氢钾,0.008%的硫酸锰置于水中,调节pH至7制备发酵培养基,将枯草芽孢杆菌菌种接种到已灭菌发酵培养基中,其中,发酵条件为发酵罐容积:每分钟通入无菌空气体积等于1.0:0.5,培养温度40℃,搅拌转数100rpm,溶氧不低于30%,pH值不低于6.5,搅拌培养8小时,使活菌含量达到1010pfu/ml得到发酵液,然后向发酵液中分别加入5g·L-1的磷酸氢二钠和0.1g·L-1氯化钠絮凝,絮凝完成后采用板框压滤方式获得菌泥,菌泥48℃鼓风干燥到含水量28%,旋风分离菌粉,放入粉碎机中粉碎,过30目筛得枯草芽孢杆菌菌剂;
然后,按照质量百分比将0.6%的淀粉,0.8%的葡萄糖,0.05%的酵母膏,0.007%的硫酸锰,0.008%的VB12置于水中,调节pH至7得发酵培养基,将固氮巨大芽孢杆菌菌种接种到已灭菌的发酵培养基中,其中发酵条件为:培养温度38℃,搅拌转数200rpm,pH值不低于6.5,搅拌培养8小时,使活菌含量达到1010pfu/ml得到发酵液,然后向发酵液中分别加入5g·L-1的磷酸氢二钠和0.1g·L-1的氯化钙絮凝,和絮凝完成后采用板框压滤方式获得菌泥,鼓风干燥到含水量30%,旋风分离菌粉,放入粉碎机中粉碎,过30目筛得到巨大芽孢杆菌菌剂;
最后,按照1:0.5的重量比将所制备的枯草芽孢杆菌菌剂和巨大芽孢杆菌菌剂混合均匀得扩培的微生物菌剂;
第四步,富硒富硅生物有机肥的制备
首先,用8倍量的秸秆粉与微生物菌剂混合均匀得混合物,按质量百分比1:30,将混合物与牛羊粪混合堆积发酵,水分控制在55%,发酵时用薄膜覆盖,待内部温度升到30℃时,将覆盖物揭开,堆温升至65℃时开始翻倒,每天一次,直到牛羊粪完全腐熟得腐熟牛羊粪;
然后,按照重量分数将60%腐熟牛羊粪,10%富硒石煤,15%活化富硒矿粉,0.1%硒酸钠,添加14.9%的腐殖酸干物质,保持水分在25%,并混合均匀;
然后,将混合均匀的配合料放入圆盘造粒机中,调整造粒机转数75转/分,同时喷入配合料质量15%的富硅液体,,将配合料制备成2~3mm的球形颗粒;
最后,将造好的颗粒放入回转炉中,50min通过130℃的回转炉,冷却至室温既得富硒富硅生物有机肥。
实施例3:
第一步,富硒矿石的活化
首先,将富硒矿石采用颚式破碎机破碎至0.1cm的颗粒;
然后,按照质量分数将40%的富硒矿石颗粒,40%的石灰,10%的钾长石,10%的碳酸钾放入球磨机中,球磨6h得粉料;
然后,将球磨后的粉料通过100~150目的标准筛后形成配合料;
然后,将配合料放入回转炉中自室温经20min升温至490℃,并保温30分钟;
最后,通过50min将配合料降温至室温,破碎粉磨至100~150目既得活化富硒矿粉;
第二步,富硅液体溶剂的制备
首先,按SiO2:K2O=2.3:1的摩尔比取石英砂和碳酸钾,然后加入石英砂和碳酸钾质量1.3%的硒粉混合至均匀度大于98%成为配合料;
然后,将配合料加入已经升温至1400℃的石英坩埚中得熔融的玻璃液;
然后,将熔融的玻璃液倒入蒸馏水中放入球磨机中球磨4h,其中,玻璃液与水的质量比为1:1.3;
最后,将球磨的硅酸钾溶液通过100目标准筛后,既得富硅液体溶剂;
第三步,微生物菌剂的扩培
首先,按质量百分比将0.3%的淀粉,0.08%的硫酸镁,0.3%的磷酸二氢钾,0.01%的硫酸锰置于水中,调节pH至7.2制备发酵培养基,将枯草芽孢杆菌菌种接种到已灭菌发酵培养基中,其中,发酵条件为发酵罐容积:每分钟通入无菌空气体积等于1.1:0.5,培养温度38℃,搅拌转数200rpm,溶氧不低于30%,pH值不低于6.5,搅拌培养6.5小时,使活菌含量达到1010pfu/ml得到发酵液,然后向发酵液中分别加入5g·L-1的磷酸氢二钠和0.1g·L-1氯化钠絮凝,絮凝完成后采用板框压滤方式获得菌泥,菌泥46℃鼓风干燥到含水量35%,旋风分离菌粉,放入粉碎机中粉碎,过30目筛得枯草芽孢杆菌菌剂;
然后,按照质量百分比将0.5%的淀粉,0.6%的葡萄糖,0.03%的酵母膏,0.01%的硫酸锰,0.01%的VB12置于水中,调节pH至7.2得发酵培养基,将固氮巨大芽孢杆菌菌种接种到已灭菌的发酵培养基中,其中发酵条件为:培养温度36℃,搅拌转数150rpm,pH值不低于6.5,搅拌培养6.5小时,使活菌含量达到1010pfu/ml得到发酵液,然后向发酵液中分别加入5g·L-1的磷酸氢二钠和0.1g·L-1的氯化钙絮凝,和絮凝完成后采用板框压滤方式获得菌泥,鼓风干燥到含水量32%,旋风分离菌粉,放入粉碎机中粉碎,过30目筛得到巨大芽孢杆菌菌剂;
最后,按照1:0.3的重量比将所制备的枯草芽孢杆菌菌剂和巨大芽孢杆菌菌剂混合均匀得扩培的微生物菌剂;
第四步,富硒富硅生物有机肥的制备
首先,用6倍量的秸秆粉与微生物菌剂混合均匀得混合物,按质量百分比1:36,将混合物与牛羊粪混合堆积发酵,水分控制在53%,发酵时用薄膜覆盖,待内部温度升到28℃时,将覆盖物揭开,堆温升至80℃时开始翻倒,每天一次,直到牛羊粪完全腐熟得腐熟牛羊粪;
然后,按照重量分数将54%腐熟牛羊粪,15.5%富硒石煤,20%活化富硒矿粉,0.5%硒酸钠,添加10%的腐殖酸干物质,保持水分在15%,并混合均匀;
然后,将混合均匀的配合料放入圆盘造粒机中,调整造粒机转数90转/分,同时喷入配合料质量10%的富硅液体,,将配合料制备成2~3mm的球形颗粒;
最后,将造好的颗粒放入回转炉中,40min通过150℃的回转炉,冷却至室温既得富硒富硅生物有机肥。
实施例4:
第一步,富硒矿石的活化
首先,将富硒矿石采用颚式破碎机破碎至1cm的颗粒;
然后,按照质量分数将50%的富硒矿石颗粒,35%的石灰,7%的钾长石,8%的碳酸钾放入球磨机中,球磨6h得粉料;
然后,将球磨后的粉料通过100~150目的标准筛后形成配合料;
然后,将配合料放入回转炉中自室温经18min升温至480℃,并保温30分钟;
最后,通过60min将配合料降温至室温,破碎粉磨至100~150目既得活化富硒矿粉;
第二步,富硅液体溶剂的制备
首先,按SiO2:K2O=2.7:1的摩尔比取石英砂和碳酸钾,然后加入石英砂和碳酸钾质量1.8%的硒粉混合至均匀度大于98%成为配合料;
然后,将配合料加入已经升温至1420℃的石英坩埚中得熔融的玻璃液;
然后,将熔融的玻璃液倒入蒸馏水中放入球磨机中球磨2.5h,其中,玻璃液与水的质量比为1:1.4;
最后,将球磨的硅酸钾溶液通过100目标准筛后,既得富硅液体溶剂;
第三步,微生物菌剂的扩培
首先,按质量百分比将0.6%的淀粉,0.12%的硫酸镁,0.2%的磷酸二氢钾,0.012%的硫酸锰置于水中,调节pH至6.7制备发酵培养基,将枯草芽孢杆菌菌种接种到已灭菌发酵培养基中,其中,发酵条件为发酵罐容积:每分钟通入无菌空气体积等于0.95:0.5,培养温度36℃,搅拌转数150rpm,溶氧不低于30%,pH值不低于6.5,搅拌培养7.5小时,使活菌含量达到1010pfu/ml得到发酵液,然后向发酵液中分别加入5g·L-1的磷酸氢二钠和0.1g·L-1氯化钠絮凝,絮凝完成后采用板框压滤方式获得菌泥,菌泥50℃鼓风干燥到含水量30%,旋风分离菌粉,放入粉碎机中粉碎,过30目筛得枯草芽孢杆菌菌剂;
然后,按照质量百分比将0.3%的淀粉,0.4%的葡萄糖,0.06%的酵母膏,0.0158%的硫酸锰,0.013%的VB12置于水中,调节pH至6.7得发酵培养基,将固氮巨大芽孢杆菌菌种接种到已灭菌的发酵培养基中,其中发酵条件为:培养温度33℃,搅拌转数180rpm,pH值不低于6.5,搅拌培养7.5小时,使活菌含量达到1010pfu/ml得到发酵液,然后向发酵液中分别加入5g·L-1的磷酸氢二钠和0.1g·L-1的氯化钙絮凝,和絮凝完成后采用板框压滤方式获得菌泥,鼓风干燥到含水量28%,旋风分离菌粉,放入粉碎机中粉碎,过30目筛得到巨大芽孢杆菌菌剂;
最后,按照1:0.8的重量比将所制备的枯草芽孢杆菌菌剂和巨大芽孢杆菌菌剂混合均匀得扩培的微生物菌剂;
第四步,富硒富硅生物有机肥的制备
首先,用9倍量的秸秆粉与微生物菌剂混合均匀得混合物,按质量百分比1:40,将混合物与牛羊粪混合堆积发酵,水分控制在58%,发酵时用薄膜覆盖,待内部温度升到26℃时,将覆盖物揭开,堆温升至75℃时开始翻倒,每天一次,直到牛羊粪完全腐熟得腐熟牛羊粪;
然后,按照重量分数将58%腐熟牛羊粪,18%富硒石煤,10%活化富硒矿粉,0.8%硒酸钠,添加13.2%的腐殖酸干物质,保持水分在20%,并混合均匀;
然后,将混合均匀的配合料放入圆盘造粒机中,调整造粒机转数85转/分,同时喷入配合料质量8%的富硅液体,,将配合料制备成2~3mm的球形颗粒;
最后,将造好的颗粒放入回转炉中,30min通过140℃的回转炉,冷却至室温既得富硒富硅生物有机肥。
实施例5:
第一步,富硒矿石的活化
首先,将富硒矿石采用颚式破碎机破碎至2cm的颗粒;
然后,按照质量分数将60%的富硒矿石颗粒,25%的石灰,8%的钾长石,7%的碳酸钾放入球磨机中,球磨5h得粉料;
然后,将球磨后的粉料通过100~150目的标准筛后形成配合料;
然后,将配合料放入回转炉中自室温经13min升温至420℃,并保温30分钟;
最后,通过35min将配合料降温至室温,破碎粉磨至100~150目既得活化富硒矿粉;
第二步,富硅液体溶剂的制备
首先,按SiO2:K2O=2.4:1的摩尔比取石英砂和碳酸钾,然后加入石英砂和碳酸钾质量1.5%的硒粉混合至均匀度大于98%成为配合料;
然后,将配合料加入已经升温至1450℃的石英坩埚中得熔融的玻璃液;
然后,将熔融的玻璃液倒入蒸馏水中放入球磨机中球磨3.5h,其中,玻璃液与水的质量比为1:1.3;
最后,将球磨的硅酸钾溶液通过100目标准筛后,既得富硅液体溶剂;
第三步,微生物菌剂的扩培
首先,按质量百分比将0.8%的淀粉,0.15%的硫酸镁,0.4%的磷酸二氢钾,0.009%的硫酸锰置于水中,调节pH至7.1制备发酵培养基,将枯草芽孢杆菌菌种接种到已灭菌发酵培养基中,其中,发酵条件为发酵罐容积:每分钟通入无菌空气体积等于1.05:0.5,培养温度39℃,搅拌转数180rpm,溶氧不低于30%,pH值不低于6.5,搅拌培养7小时,使活菌含量达到1010pfu/ml得到发酵液,然后向发酵液中分别加入5g·L-1的磷酸氢二钠和0.1g·L-1氯化钠絮凝,絮凝完成后采用板框压滤方式获得菌泥,菌泥49℃鼓风干燥到含水量32%,旋风分离菌粉,放入粉碎机中粉碎,过30目筛得枯草芽孢杆菌菌剂;
然后,按照质量百分比将0.8%的淀粉,0.5%的葡萄糖,0.08%的酵母膏,0.013%的硫酸锰,0.015%的VB12置于水中,调节pH至7.1得发酵培养基,将固氮巨大芽孢杆菌菌种接种到已灭菌的发酵培养基中,其中发酵条件为:培养温度35℃,搅拌转数130rpm,pH值不低于6.5,搅拌培养7小时,使活菌含量达到1010pfu/ml得到发酵液,然后向发酵液中分别加入5g·L-1的磷酸氢二钠和0.1g·L-1的氯化钙絮凝,和絮凝完成后采用板框压滤方式获得菌泥,鼓风干燥到含水量30%,旋风分离菌粉,放入粉碎机中粉碎,过30目筛得到巨大芽孢杆菌菌剂;
最后,按照1:1的重量比将所制备的枯草芽孢杆菌菌剂和巨大芽孢杆菌菌剂混合均匀得扩培的微生物菌剂;
第四步,富硒富硅生物有机肥的制备
首先,用10倍量的秸秆粉与微生物菌剂混合均匀得混合物,按质量百分比1:27,将混合物与牛羊粪混合堆积发酵,水分控制在60%,发酵时用薄膜覆盖,待内部温度升到29℃时,将覆盖物揭开,堆温升至70℃时开始翻倒,每天一次,直到牛羊粪完全腐熟得腐熟牛羊粪;
然后,按照重量分数将50%腐熟牛羊粪,13%富硒石煤,18%活化富硒矿粉,0.3%硒酸钠,添加18.7%的腐殖酸干物质,保持水分在30%,并混合均匀;
然后,将混合均匀的配合料放入圆盘造粒机中,调整造粒机转数80转/分,同时喷入配合料质量18%的富硅液体,,将配合料制备成2~3mm的球形颗粒;
最后,将造好的颗粒放入回转炉中,35min通过135℃的回转炉,冷却至室温既得富硒富硅生物有机肥。
实施例6:
第一步,富硒矿石的活化
首先,将富硒矿石采用颚式破碎机破碎至3cm的颗粒;
然后,按照质量分数将70%的富硒矿石颗粒,15%的石灰,6%的钾长石,9%的碳酸钾放入球磨机中,球磨6h得粉料;
然后,将球磨后的粉料通过100~150目的标准筛后形成配合料;
然后,将配合料放入回转炉中自室温经16min升温至465℃,并保温30分钟;
最后,通过45min将配合料降温至室温,破碎粉磨至100~150目既得活化富硒矿粉;
第二步,富硅液体溶剂的制备
首先,按SiO2:K2O=2.6:1的摩尔比取石英砂和碳酸钾,然后加入石英砂和碳酸钾质量1.6%的硒粉混合至均匀度大于98%成为配合料;
然后,将配合料加入已经升温至1400℃的石英坩埚中得熔融的玻璃液;
然后,将熔融的玻璃液倒入蒸馏水中放入球磨机中球磨4h,其中,玻璃液与水的质量比为1:1.5;
最后,将球磨的硅酸钾溶液通过100目标准筛后,既得富硅液体溶剂;
第三步,微生物菌剂的扩培
首先,按质量百分比将0.4%的淀粉,0.07%的硫酸镁,0.3%的磷酸二氢钾,0.011%的硫酸锰置于水中,调节pH至7.2制备发酵培养基,将枯草芽孢杆菌菌种接种到已灭菌发酵培养基中,其中,发酵条件为发酵罐容积:每分钟通入无菌空气体积等于0.9:0.5,培养温度37℃,搅拌转数130rpm,溶氧不低于30%,pH值不低于6.5,搅拌培养8小时,使活菌含量达到1010pfu/ml得到发酵液,然后向发酵液中分别加入5g·L-1的磷酸氢二钠和0.1g·L-1氯化钠絮凝,絮凝完成后采用板框压滤方式获得菌泥,菌泥47℃鼓风干燥到含水量30%,旋风分离菌粉,放入粉碎机中粉碎,过30目筛得枯草芽孢杆菌菌剂;
然后,按照质量百分比将0.4%的淀粉,0.3%的葡萄糖,0.07%的酵母膏,0.0145%的硫酸锰,0.018%的VB12置于水中,调节pH至7.2得发酵培养基,将固氮巨大芽孢杆菌菌种接种到已灭菌的发酵培养基中,其中发酵条件为:培养温度38℃,搅拌转数165rpm,pH值不低于6.5,搅拌培养8小时,使活菌含量达到1010pfu/ml得到发酵液,然后向发酵液中分别加入5g·L-1的磷酸氢二钠和0.1g·L-1的氯化钙絮凝,和絮凝完成后采用板框压滤方式获得菌泥,鼓风干燥到含水量35%,旋风分离菌粉,放入粉碎机中粉碎,过30目筛得到巨大芽孢杆菌菌剂;
最后,按照1:0.6的重量比将所制备的枯草芽孢杆菌菌剂和巨大芽孢杆菌菌剂混合均匀得扩培的微生物菌剂;
第四步,富硒富硅生物有机肥的制备
首先,用7倍量的秸秆粉与微生物菌剂混合均匀得混合物,按质量百分比1:33,将混合物与牛羊粪混合堆积发酵,水分控制在55%,发酵时用薄膜覆盖,待内部温度升到27℃时,将覆盖物揭开,堆温升至80℃时开始翻倒,每天一次,直到牛羊粪完全腐熟得腐熟牛羊粪;
然后,按照重量分数将45%腐熟牛羊粪,17%富硒石煤17%活化富硒矿粉,1%硒酸钠,添加20%的腐殖酸干物质,保持水分在18%,并混合均匀;
然后,将混合均匀的配合料放入圆盘造粒机中,调整造粒机转数70转/分,同时喷入配合料质量18%的富硅液体,,将配合料制备成2~3mm的球形颗粒;
最后,将造好的颗粒放入回转炉中,45min通过145℃的回转炉,冷却至室温既得富硒富硅生物有机肥。
本发明所制备的生物有机肥,养分不易流失,肥效更为长久,原料经过发酵后含有丰富的硒元素,能够增加作物果实中硒的含量,提高瓜果的经济价值,种植效益获得明显提升。该专利所制备的富硒富硅生物有机肥施用效果能够显著提高农产品的含硒量,并显著提高有机硒占农产品总硒的百分含量,适用于我国缺硒或低硒地区应用,对提高人群硒水平具有积极意义。该专利复合菌剂的使用可以起到解磷、固氮以及增强土壤肥力的功效,能显著提高果实各种微量矿物元素含量,该专利制备工艺简单,制造成本低,适于工业化生产。
Claims (3)
1.一种生物有机肥的制备方法,其特征在于:
第一步,富硒矿石的活化
首先,将富硒矿石采用颚式破碎机破碎至0.01~3cm的颗粒;
然后,按照质量分数将40~80%的富硒矿石颗粒,10~40%的石灰,5~10的钾长石,5~10%的碳酸钾放入球磨机中,球磨4~6h得粉料;
然后,将球磨后的粉料通过100~150目的标准筛后形成配合料;
然后,将配合料放入回转炉中自室温经10~20min升温至400~490℃,并保温30分钟;
最后,通过30~60min将配合料降温至室温,破碎粉磨至100~150目既得活化富硒矿粉;
第二步,富硅液体溶剂的制备
首先,按SiO2:K2O=2~2.7:1的摩尔比取石英砂和碳酸钾,然后加入石英砂和碳酸钾质量1~2%的硒粉混合至均匀度大于98%成为配合料;
然后,将配合料加入已经升温至1350~1450℃的石英坩埚中得熔融的玻璃液;
然后,将熔融的玻璃液倒入蒸馏水中放入球磨机中球磨2~4h,其中,玻璃液与水的质量比为1:1.2~1.5;
最后,将球磨的硅酸钾溶液通过100目标准筛后,既得富硅液体溶剂;
第三步,微生物菌剂的扩培
首先,按质量百分比将0.2~0.8%的淀粉,0.05~0.15%的硫酸镁,0.1~0.5%的磷酸二氢钾,0.006~0.012%的硫酸锰置于水中,调节pH至6.8~7.2制备发酵培养基,将枯草芽孢杆菌菌种接种到已灭菌发酵培养基中,其中,发酵条件为发酵罐容积:每分钟通入无菌空气体积等于0.9~1.1:0.5,培养温度35~40℃,搅拌转数100~200rpm,溶氧不低于30%,pH值不低于6.5,搅拌培养6~8小时,使活菌含量达到1010pfu/ml得到发酵液,然后向发酵液中分别加入5g·L-1的磷酸氢二钠和0.1g·L-1氯化钠絮凝,絮凝完成后采用板框压滤方式获得菌泥,菌泥45~50℃鼓风干燥到含水量25~35%,旋风分离菌粉,放入粉碎机中粉碎,过30目筛得枯草芽孢杆菌菌剂;
然后,按照质量百分比将0.2~0.8%的淀粉,0.2~0.8%的葡萄糖,0.01~0.08%的酵母膏,0.005~0.0158%的硫酸锰,0.0052~0.018%的VB12置于水中,调节pH至6.8~7.2得发酵培养基,将固氮巨大芽孢杆菌菌种接种到已灭菌的发酵培养基中,其中发酵条件为:培养温度32~38℃,搅拌转数100~200rpm,pH值不低于6.5,搅拌培养6~8小时,使活菌含量达到1010pfu/ml得到发酵液,然后向发酵液中分别加入5g·L-1的磷酸氢二钠和0.1g·L-1的氯化钙絮凝,和絮凝完成后采用板框压滤方式获得菌泥,鼓风干燥到含水量25~35%,旋风分离菌粉,放入粉碎机中粉碎,过30目筛得到巨大芽孢杆菌菌剂;
最后,按照1:0.1~1的重量比将所制备的枯草芽孢杆菌菌剂和巨大芽孢杆菌菌剂混合均匀得扩培的微生物菌剂;
第四步,富硒富硅生物有机肥的制备
首先,用5~10倍量的秸秆粉与微生物菌剂混合均匀得混合物,按质量百分比1:24~40,将混合物与牛羊粪混合堆积发酵,水分控制在50%~60%,发酵时用薄膜覆盖,待内部温度升到25~30℃时,将覆盖物揭开,堆温升至60~80℃时开始翻倒,每天一次,直到牛羊粪完全腐熟得腐熟牛羊粪;
然后,按照重量分数将40~60%腐熟牛羊粪,10~20%富硒石煤,10~20%活化富硒矿粉,0.1~1%硒酸钠,添加10~20%的腐殖酸干物质,保持水分在10~30%,并混合均匀;
然后,将混合均匀的配合料放入圆盘造粒机中,调整造粒机转数70~90转/分,同时喷入配合料质量3~20%的富硅液体,,将配合料制备成2~3mm的球形颗粒;
最后,将造好的颗粒放入回转炉中,30~50min通过120~150℃的回转炉,冷却至室温既得富硒富硅生物有机肥。
2.根据权利要求1所述的生物有机肥的制备方法,其特征在于:所述的石灰,钾长石,碳酸钾,石英砂,硒粉,硫酸镁,磷酸二氢钾,硫酸锰,磷酸二氢钠,均为工业原料,粒度为30~50目。
3.根据权利要求1所述的生物有机肥的制备方法,其特征在于:所述的球磨机中的研磨介质采用平均直径为5~8mm的玛瑙球。