CN107216757A - Quick-drying Stripable paint containing acid alcohol-soluble Ludox and preparation method thereof - Google Patents
Quick-drying Stripable paint containing acid alcohol-soluble Ludox and preparation method thereof Download PDFInfo
- Publication number
- CN107216757A CN107216757A CN201710457087.9A CN201710457087A CN107216757A CN 107216757 A CN107216757 A CN 107216757A CN 201710457087 A CN201710457087 A CN 201710457087A CN 107216757 A CN107216757 A CN 107216757A
- Authority
- CN
- China
- Prior art keywords
- alcohol
- soluble
- parts
- drying
- ludox
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of quick-drying Stripable paint containing acid alcohol-soluble Ludox of the present invention, calculate, be made up of 60 70 parts of multiple cross-linked resins of alcohol-soluble, 60 70 parts of alcohol-soluble Ludox, 0.05 0.1 parts of levelling agent, 1 10 parts of wetting agent, 0.2 1 parts of defoamer, 38 parts of composite iron-titanium powders and 10 20 parts of functional stuffings by weight.Present invention also offers the preparation method of above-mentioned coating, according to formula, added in high speed dispersor partially wetted dose, defoamer, composite iron-titanium powder and alcoholic solvent, functional stuffing is added after scattered, the multiple cross-linked resin of alcohol-soluble, alcohol-soluble Ludox and remaining defoamer, wetting agent, levelling agent are added after redisperse and is stirred, continue scattered, through being filtered to remove filter residue after being well mixed, that is, obtain the quick-drying Stripable paint containing acid alcohol-soluble Ludox.The quick-drying Stripable paint of the present invention has fast rate of drying, preferable rust-preventing characteristic and preferable rippability.
Description
Technical field
The invention belongs to technical field of polymer materials, it is related to a kind of coating, it is specifically a kind of molten containing acid alcohol
Quick-drying Stripable paint of property Ludox and preparation method thereof.
Background technology
Strippable coatings is a kind of temporary protection material using macromolecule as main film forming substance, and object is sprayed on when using
On surface, protective effect in short-term is played to coated article after film forming；In coated article in use, by film layer from coated article surface with hand gently
Peel off, do not result in injury not only to coated article surface, can also the original device appearance of energy it is sparkling clean.Strippable coatings due to
Application is convenient, it is easy to peel off, thus is extensively welcome by industries such as instrument, instrument, household electrical appliances, machinery, automobile, electronic apparatus, develops
Rapidly.
At present, it is mainly solvent-borne type rippability coating and the aqueous class of rippability coating two on domestic market.Wherein, contain
Although the solvent-borne type rippability coating better performances of aromatic hydrocarbons, it gradually fades out market due to being unsatisfactory for environmental requirement, and mesh
Although preceding aqueous Stripable paint meets environmental protection, there is drying time long（2 ~ 3 hours）, used in metal object surface when gold
The problems such as metal surface easily gets rusty, it is difficult to meet the need of the quick production of high-speed production streamline and social development to high-performance coating
Will, it greatly limit its popularization and application.
Based on background above, it is necessary to develop a kind of environmental protection, the Stripable paint that drying time is short, peeling effect is good and its system
Preparation Method.
The content of the invention
For above-mentioned technical problem of the prior art, contain the fast of acid alcohol-soluble Ludox the invention provides a kind of
Dry Stripable paint and preparation method thereof, the described this quick-drying Stripable paint containing acid alcohol-soluble Ludox and its system
Preparation Method will solve aqueous Stripable paint drying time length of the prior art, used in metal object surface when metal surface it is easy
The technical problem got rusty.
The invention provides a kind of quick-drying Stripable paint containing acid alcohol-soluble Ludox, calculate by weight,
Its raw material is constituted and content is as follows：
Multiple cross-linked resin 60-70 parts of alcohol-soluble；
Acid 60-70 parts of alcohol-soluble Ludox；
0.05-0.1 parts of levelling agent；
1-10 parts of wetting agent；
0.2-1 parts of defoamer；
3-8 parts of composite iron-titanium powder；
10-20 parts of functional stuffing；
Wherein, the multiple cross-linked resin of described alcohol-soluble is the multiple cross-linked acrylate of alcohol-soluble；
Described levelling agent is Germany BYK Bi Ke BYK-3510, BYK-341, BYK-344, BYK-345, BYK-346, BYK-
347th, in BYK-348 any one or two or more mixtures；
Described wetting agent is the NP-100 of LG-DOW company；
Described defoamer is the Nopco NXZ of Henkel KGaA company；
Described functional stuffing is mica.
Further, a kind of described quick-drying Stripable paint containing acid alcohol-soluble Ludox, is counted by weight
Calculate, its raw material composition and content are as follows：
60 parts of the multiple cross-linked resin of alcohol-soluble；
Acid 60 parts of alcohol-soluble Ludox；
0.05 part of levelling agent；
1 part of wetting agent；
0.2 part of defoamer；
3 parts of composite iron-titanium powder；
10 parts of functional stuffing；
Wherein, the multiple cross-linked resin of described alcohol-soluble is the multiple cross-linked acrylate of alcohol-soluble；
Described levelling agent is the BYK 346 of BYK companies；
Described wetting agent is the NP-100 of LG-DOW company；
Described defoamer is the Nopco NXZ of Henkel KGaA company；
Described composite iron-titanium powder is the H-803 composite iron-titanium powders of Jinan Ward Chemical Co., Ltd.；
Described functional stuffing is mica.
Further, a kind of described quick-drying Stripable paint containing acid alcohol-soluble Ludox, is counted by weight
Calculate, its raw material composition and content are as follows：
70 parts of the multiple cross-linked resin of alcohol-soluble；
Acid 70 parts of alcohol-soluble Ludox；
0.1 part of levelling agent；
10 parts of wetting agent；
1 part of defoamer；
8 parts of composite iron-titanium powder；
20 parts of functional stuffing；
Wherein, the multiple cross-linked resin of described alcohol-soluble is the multiple cross-linked acrylate of alcohol-soluble；
Described composite iron-titanium powder is the H-803 composite iron-titanium powders of Jinan Ward Chemical Co., Ltd.；
Described levelling agent is Germany BYK Bi Ke BYK-3510；
Described wetting agent is the NP-100 of LG-DOW company；
Described defoamer is the Nopco NXZ of Henkel KGaA company；
Described functional stuffing is mica.
Present invention also offers a kind of preparation side of above-mentioned quick-drying Stripable paint containing acid alcohol-soluble Ludox
Method, comprises the following steps：According to formula, the wetting agent of addition 70 ~ 90%, 10 ~ 30% defoamers, compound iron in high speed dispersor
Titanium valve and alcoholic solvent, through disperseing 15-20min under 600-800r/min rotating speeds, add functional stuffing, through 1600-2800r/min
Disperse under rotating speed after 30-50min, rotating speed is down to 300r/min, add the multiple cross-linked resin of alcohol-soluble, acid alcohol-soluble silicon molten
Glue and remaining defoamer, wetting agent, levelling agent simultaneously stir, and continue scattered 5-10min, through being filtered to remove after being well mixed
Filter residue, that is, obtain the quick-drying Stripable paint containing acid alcohol-soluble Ludox.
A kind of quick-drying Stripable paint containing acid alcohol-soluble Ludox of the present invention, in environment-friendly type solvent alcoholic solvent
Under effect, the rate of drying for making coating overall is greatly speeded up, and drying time shortens dramatically, through being scratched in treated tinplate sheet
Twice, drying time is 30-60min, far faster than the drying time of 2~3 hours of current aqueous Stripable paint.The present invention's
A kind of functional stuffing in quick-drying Stripable paint containing acid alcohol-soluble Ludox, the raw material of addition is to fill to tie with lamella
The filler of structure, with stronger barrier, is delayed corrosion of the external environment to ground, while assigning film excellent stripping
From performance.When determining the drying of film by drying time GB/T 1728-1979 " paint film, putty membrane drying time determination method "
Between be 30-60min；Peel strength newly thinks carefully the CMT5104 electronic tension testers of company at room temperature by GB/ using Shenzhen
T2790-1995 standards " 180 ° of peeling strength test methods of adhesive " carry out 180 ° of peel test, draw speed 50mm/
min；Peel strength is measured for 0.25 ~ 0.91kN/m.
The present invention is compared with prior art, and its technological progress is significant.The present invention's contains acid alcohol-soluble Ludox
Quick-drying Stripable paint there is fast rate of drying, preferable rust-preventing characteristic and preferable rippability, and its preparation method due to
Technique is simple, and easy to control, technology maturation can be used in the industry skill such as instrument, instrument, household electrical appliances, machinery, automobile, electronic apparatus
Art field.
Embodiment
The present invention is described in further detail below by embodiment, but is not intended to limit the present invention.
In raw material used in various embodiments of the present invention in addition to the special producer shown and specification, other raw materials be it is commercially available,
Specification is that chemistry is pure.
The model of various equipment used in the present invention and the information of manufacturer are as follows：
GFJ-0.4 type high speed dispersors, the new promise experimental instruments and equipment limited production in Shanghai；
Newly think carefully that company produces in CMT5104 electronic tension testers, Shenzhen；
GS450 small-size vibration screens, the production of Laizhou City Jingtai chemical.
Embodiment 1
A kind of quick-drying Stripable paint containing acid alcohol-soluble Ludox, is calculated by weight, its raw material composition and content
It is as follows：
60 parts of the multiple cross-linked resin of alcohol-soluble
Acid 60 parts of alcohol-soluble Ludox
0.05 part of levelling agent
1 part of wetting agent
0.2 part of defoamer
3 parts of composite iron-titanium powder
10 parts of functional stuffing
Wherein, the multiple cross-linked resin of described alcohol-soluble is the multiple cross-linked acrylate of alcohol-soluble；
Described composite iron-titanium powder is the H-803 composite iron-titanium powders of Jinan Ward Chemical Co., Ltd.；
Described levelling agent is the BYK 346 of BYK companies；
Described wetting agent is the NP-100 of LG-DOW company；
Described defoamer is the Nopco NXZ of Henkel KGaA company；
Described functional stuffing is mica；
A kind of preparation method of above-mentioned quick-drying Stripable paint containing acid alcohol-soluble Ludox, specifically includes following step
Suddenly：
According to formula, add 0.7 part of wetting agent, 0.02 part of defoamer, 3 parts of composite iron-titanium powders and 20ml alcoholic solvents and be added to GFJ-
0.4 type high speed dispersor（The new promise experimental instruments and equipment limited in Shanghai）In, through disperseing 15min under 600r/min rotating speeds, add
10 parts of functional stuffings, after disperseing 30min under 1600r/min rotating speeds, 300r/min is down to by rotating speed, 60 parts of alcohol-solubles are added many
Weight crosslinked resin, 60 parts of alcohol-soluble Ludox and 0.18 part of defoamer, 0.3 part of wetting agent, 0.05 part of levelling agent simultaneously stir,
Continue scattered 5min, through GS450 small-size vibration screens after being well mixed（Laizhou City Jingtai chemical）Filtering, that is, contained
The quick-drying Stripable paint of acid alcohol-soluble Ludox.
By the quick-drying Stripable paint obtained above containing acid alcohol-soluble Ludox using knife coating in by acetone,
Twice are scratched in the treated tinplate sheet of alcoholic solvent, ventilation drying at room temperature is placed on.According to GB/T 1728-1979 " paint film,
The drying time that putty membrane drying time determination method " determines film is 30min；
Peel strength newly thinks carefully the CMT5104 electronic tension testers of company at room temperature by GB/T2790-1995 using Shenzhen
Standard " 180 ° of peeling strength test methods of adhesive " carries out 180 ° of peel test, draw speed 50mm/min；Measure stripping
Intensity is 0.25kN/m；
Have in summary after the quick-drying Stripable paint film containing acid alcohol-soluble Ludox obtained by the present invention faster
Drying time and preferable rust-preventing characteristic, relatively low peel strength.
Embodiment 2
A kind of quick-drying Stripable paint containing acid alcohol-soluble Ludox, is calculated by weight, its raw material composition and content
It is as follows：
70 parts of the multiple cross-linked resin of alcohol-soluble
Acid 70 parts of alcohol-soluble Ludox
0.1 part of levelling agent
10 parts of wetting agent
1 part of defoamer
8 parts of composite iron-titanium powder
20 parts of functional stuffing
Wherein, the multiple cross-linked resin of described alcohol-soluble is the multiple cross-linked acrylate of alcohol-soluble；
Described composite iron-titanium powder is the H-803 composite iron-titanium powders of Jinan Ward Chemical Co., Ltd.；
Described levelling agent is Germany BYK Bi Ke BYK-3510；
Described wetting agent is the NP-100 of LG-DOW company；
Described defoamer is the Nopco NXZ of Henkel KGaA company；
Described functional stuffing is mica；
A kind of preparation method of above-mentioned quick-drying Stripable paint containing acid alcohol-soluble Ludox, specifically includes following step
Suddenly：
According to formula, add 9 parts of wetting agents, 0.3 part of defoamer, 8 parts of composite iron-titanium powders and 40ml alcoholic solvents and be added to GFJ-0.4
Type high speed dispersor（The new promise experimental instruments and equipment limited in Shanghai）In, through disperseing 20min under 800r/min rotating speeds, add 20 parts
Functional stuffing, after disperseing 50min under 2800r/min rotating speeds, 300r/min is down to by rotating speed, adds the multiple friendship of 70 parts of alcohol-solubles
Connection resin, 70 parts of alcohol-soluble Ludox and remaining 0.7 part of defoamer, 1 part of wetting agent, 0.1 part of levelling agent simultaneously stir, after
Continuous scattered 10min, through GS450 small-size vibration screens after being well mixed（Laizhou City Jingtai chemical）Filtering, that is, contained
The quick-drying Stripable paint of acid alcohol-soluble Ludox.
By the quick-drying Stripable paint obtained above containing acid alcohol-soluble Ludox using knife coating in by acetone,
Twice are scratched in the treated tinplate sheet of alcoholic solvent, ventilation drying at room temperature is placed on.According to GB/T 1728-1979 " paint film,
The drying time that putty membrane drying time determination method " determines film is 60min；
Peel strength newly thinks carefully the CMT5104 electronic tension testers of company at room temperature by GB/T2790-1995 using Shenzhen
Standard " 180 ° of peeling strength test methods of adhesive " carries out 180 ° of peel test, draw speed 50mm/min；Measure stripping
Intensity is 0.91kN/m；
There is faster drying time after the quick-drying Stripable paint film containing acid alcohol-soluble Ludox obtained by the present invention
With preferable rust-preventing characteristic, relatively low peel strength.
The multiple cross-linked resin of alcohol-soluble and alcohol-soluble Ludox in summary in the raw material obtained by the present invention is molten in alcohol
Crosslinked formation tridimensional network in the volatilization process of agent, the volatilization auxiliary of alcoholic solvent makes coating have after quick-drying, film
With shorter drying time（30-60min）；The complexing power of the composite iron-titanium powder bind metal ion of addition make it have compared with
Good protection effect.Functional stuffing in raw material is the filler with lamella assembling structure, with stronger barrier, is effectively subtracted
The low tack into membrane interface, with preferable rippability, peel strength is 0.25 ~ 0.91kN/m.
The content is only the basic explanation under present inventive concept, and according to technical scheme made it is any etc.
Effect conversion, all should belong to protection scope of the present invention.
Claims (4)
1. a kind of quick-drying Stripable paint containing acid alcohol-soluble Ludox, it is characterised in that calculate by weight, it is former
Material composition and content are as follows：
Multiple cross-linked resin 60-70 parts of alcohol-soluble；
Acid 60-70 parts of alcohol-soluble Ludox；
0.05-0.1 parts of levelling agent；
1-10 parts of wetting agent；
0.2-1 parts of defoamer；
3-8 parts of composite iron-titanium powder；
10-20 parts of functional stuffing；
Wherein, the multiple cross-linked resin of described alcohol-soluble is the multiple cross-linked acrylate of alcohol-soluble；
Described levelling agent is Germany BYK Bi Ke BYK-3510, BYK-341, BYK-344, BYK-345, BYK-346, BYK-
347th, in BYK-348 any one or two or more mixtures；
Described wetting agent is the NP-100 of LG-DOW company；
Described defoamer is the Nopco NXZ of Henkel KGaA company；
Described functional stuffing is mica.
2. a kind of quick-drying Stripable paint containing acid alcohol-soluble Ludox as claimed in claim 1, it is characterised in that press
Parts by weight are calculated, and its raw material composition and content are as follows：
60 parts of the multiple cross-linked resin of alcohol-soluble；
Acid 60 parts of alcohol-soluble Ludox；
0.05 part of levelling agent；
1 part of wetting agent；
0.2 part of defoamer；
3 parts of composite iron-titanium powder；
10 parts of functional stuffing；
Wherein, the multiple cross-linked resin of described alcohol-soluble is the multiple cross-linked acrylate of alcohol-soluble；
Described levelling agent is the BYK 346 of BYK companies；
Described wetting agent is the NP-100 of LG-DOW company；
Described defoamer is the Nopco NXZ of Henkel KGaA company；
Described composite iron-titanium powder is the H-803 composite iron-titanium powders of Jinan Ward Chemical Co., Ltd.；
Described functional stuffing is mica.
3. a kind of quick-drying Stripable paint containing acid alcohol-soluble Ludox as claimed in claim 1, it is characterised in that press
Parts by weight are calculated, and its raw material composition and content are as follows：
70 parts of the multiple cross-linked resin of alcohol-soluble；
Acid 70 parts of alcohol-soluble Ludox；
0.1 part of levelling agent；
10 parts of wetting agent；
1 part of defoamer；
8 parts of composite iron-titanium powder；
20 parts of functional stuffing；
Wherein, the multiple cross-linked resin of described alcohol-soluble is the multiple cross-linked acrylate of alcohol-soluble；
Described composite iron-titanium powder is the H-803 composite iron-titanium powders of Jinan Ward Chemical Co., Ltd.；
Described levelling agent is Germany BYK Bi Ke BYK-3510；
Described wetting agent is the NP-100 of LG-DOW company；
Described defoamer is the Nopco NXZ of Henkel KGaA company；
Described functional stuffing is mica.
4. a kind of preparation method of quick-drying Stripable paint containing acid alcohol-soluble Ludox described in claim 1,2 or 3,
It is characterized in that comprising the following steps：According to formula, the wetting agent of addition 70 ~ 90%, 10 ~ 30% froth breakings in high speed dispersor
Agent, composite iron-titanium powder and alcoholic solvent, through disperseing 15-20min under 600-800r/min rotating speeds, add functional stuffing, through 1600-
Disperse under 2800r/min rotating speeds after 30-50min, rotating speed is down to 300r/min, add the multiple cross-linked resin of alcohol-soluble, acidity
Alcohol-soluble Ludox and remaining defoamer, wetting agent, levelling agent simultaneously stir, and continue scattered 5-10min, after being well mixed
Filter residue is removed by filtration, that is, obtains the quick-drying Stripable paint containing acid alcohol-soluble Ludox.