CN107201482B - A kind of wind-powered electricity generation pinion steel and preparation method thereof - Google Patents
A kind of wind-powered electricity generation pinion steel and preparation method thereof Download PDFInfo
- Publication number
- CN107201482B CN107201482B CN201710255727.8A CN201710255727A CN107201482B CN 107201482 B CN107201482 B CN 107201482B CN 201710255727 A CN201710255727 A CN 201710255727A CN 107201482 B CN107201482 B CN 107201482B
- Authority
- CN
- China
- Prior art keywords
- steel
- wind
- electricity generation
- powered electricity
- refining
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of wind-powered electricity generation pinion steels, its chemical component mass percent are as follows: C0.12-0.20%, Mn2.6-3.8%, Si0.26-0.35%, Ni0.44-0.56%, Mo1.4-2.5%, Cr1.2-2.0%, Ti0.005-0.010%, W0.33-0.46%, Hf0.15-0.23%, P≤0.030%, S≤0.030%, surplus are Fe and inevitable impurity.Pinion steel inclusion behavior of the invention is low, gas content is low, crystal grain is tiny, dense structure, by reducing a certain proportion of phosphorus content, improve the welding performance of pinion steel, the addition of the elements such as chromium and titanium ensure that the physical properties such as the hardness of wind power gear steel, tungsten and hafnium cooperation, so that pinion steel has very excellent corrosion resistance and heat-resisting quantity, the addition of hafnium element additionally aids refinement crystal grain.
Description
Technical field
The present invention relates to metallurgy industry steelmaking technical fields more particularly to a kind of wind-powered electricity generation pinion steel and preparation method thereof.
Background technique
Pinion steel is the general designation to the steel that can be used for fabricating gear.Pinion steel is automobile, railway, ship, engineering
It is the manufacture material for guaranteeing the core component of safety using one of critical material more demanding in special alloy steel in machinery.
Wind-powered electricity generation is had to that good performance can be kept under lower temperature environments with pinion steel.The excessive note of existing wind-powered electricity generation pinion steel
The low-temperature adaptation ability and intensity of weight pinion steel, and then more Mn, Cr etc. are added, as the additive amount of Mn, Cr etc. improve, tooth
Welding performance, corrosion resistance and the toughness of wheel steel can all have a degree of decline, be unfavorable for making for a long time for wind power gear steel
With.How to prepare that a kind of lower temperature resistance is good, hardness is high, the wind power gear steel of excellent combination property is skill to be solved by this invention
Art problem.
Summary of the invention
That in view of the deficiencies of the prior art, the present invention provides a kind of lower temperature resistances is good, hardness is high, the wind-powered electricity generation of excellent combination property
With pinion steel and preparation method thereof.
The present invention is realized by following technological means solves above-mentioned technical problem:
A kind of wind-powered electricity generation pinion steel, chemical component mass percent are as follows: C0.12-0.20%, Mn2.6-3.8%,
Si0.26-0.35%、Ni0.44-0.56%、Mo1.4-2.5%、Cr1.2-2.0%、Ti0.005-0.010%、W0.33-0.46%、
Hf0.15-0.23%, P≤0.030%, S≤0.030%, surplus are Fe and inevitable impurity.
A kind of preparation method of wind-powered electricity generation pinion steel, comprising the following steps:
(1) electric furnace or converter smelting are adjusted the content of each element in molten steel, no slag or few slag tapping, are carried out using silicomanganese
Pre-deoxidation；
(2) LF refining is carried out using refining rapid slagging slag making technology, Refining Clean Steel in ASEA-SKF technology, by using smart outside furnace
Gas content meets the requirements in refining, Fruit storage to chemical component and steel, and hydrogen content≤2.5ppm, oxygen content in steel≤
20ppm carries out complex deoxidization using compound rare-earth and Ti cooperation；
(3) it is handled by RH or VD vacuum argon blowing degassing method, the vacuum degree≤0.10KPa, retention time 12- of VD degassing
16min, vacuum breaker are kept stirring state, finely tune, and feed S line, finely tune other ingredients, be casting continuously to form base；
(4) it rolls, continuous casting billet is 1150-1250 DEG C in the heating temperature of heating furnace, 1100 DEG C of start rolling temperature, is heated and high
Warm diffusion time is 2-3 hours, 860-960 DEG C of finishing temperature, rolls rear air-cooled or slow cooling.
The present invention has the advantages that pinion steel inclusion behavior of the invention is low, gas content is low, and crystal grain is tiny, tissue
Densification improves the welding performance of pinion steel, the addition of the elements such as chromium and titanium guarantees by reducing a certain proportion of phosphorus content
The physical properties such as the hardness of wind power gear steel, tungsten and hafnium cooperation, so that pinion steel has very excellent corrosion resistance and resistance to
High temperatures, the addition of hafnium element additionally aids refinement crystal grain.
Specific embodiment
In order to make the object, technical scheme and advantages of the embodiment of the invention clearer, below in the embodiment of the present invention
Technical solution is clearly and completely described, it is clear that described embodiments are some of the embodiments of the present invention, rather than complete
The embodiment in portion.Based on the embodiments of the present invention, those of ordinary skill in the art are without creative efforts
Every other embodiment obtained, shall fall within the protection scope of the present invention.
A kind of wind-powered electricity generation pinion steel, chemical component mass percent are as follows: C0.16%, Mn3.2%, Si0.31%,
Ni0.48%, Mo1.9%, Cr1.6%, Ti0.008%, W0.40%, Hf0.19%, P≤0.030%, S≤0.030%, surplus be Fe and
Inevitable impurity, includes P≤0.04% in inevitable impurity, S≤0.04%, N≤0.04%, and oxygen O≤
0.05%.
A kind of preparation method of wind-powered electricity generation pinion steel, comprising the following steps:
(1) electric furnace or converter smelting are adjusted the content of each element in molten steel, no slag or few slag tapping, are carried out using silicomanganese
Pre-deoxidation；
(2) LF refining is carried out using refining rapid slagging slag making technology, Refining Clean Steel in ASEA-SKF technology, by using smart outside furnace
Gas content meets the requirements in refining, Fruit storage to chemical component and steel, and hydrogen content≤2.5ppm, oxygen content in steel≤
20ppm carries out complex deoxidization using compound rare-earth and Ti cooperation；
(3) it is handled by RH or VD vacuum argon blowing degassing method, the vacuum degree≤0.10KPa, retention time 12- of VD degassing
16min, vacuum breaker are kept stirring state, finely tune, and feed S line, finely tune other ingredients, be casting continuously to form base；
(4) it rolls, continuous casting billet is 1200 DEG C in the heating temperature of heating furnace, and 1100 DEG C of start rolling temperature, heating and high temperature expand
Dissipating the time is 3 hours, 920 DEG C of finishing temperature, rolls rear air-cooled or slow cooling.
The mechanical and physical performance of wind-powered electricity generation pinion steel made from the present embodiment is as shown in the table.
| Tensile strength (MPa) | Yield strength (MPa) | Impact flexibility (J) | Fracture toughness (MPa M1/2) | Elongation at break (%) | Hardness (HRC) | Corrosion rate under 3.5%NaCl solution environmental (mm/) | 5%H2SO4Corrosion rate under solution environmental (mm/) | - 60 DEG C of punchings Hit function |
| 1150 | 918 | 240 | 138 | 34 | 49 | 0.0124 | 0.0379 | 227 |
It should be noted that, in this document, such as first and second or the like relational terms are used merely to one if it exists
A entity or operation with another entity or operate distinguish, without necessarily requiring or implying these entities or operation it
Between there are any actual relationship or orders.Moreover, the terms "include", "comprise" or its any other variant are intended to
Cover non-exclusive inclusion, so that the process, method, article or equipment for including a series of elements not only includes those
Element, but also including other elements that are not explicitly listed, or further include for this process, method, article or setting
Standby intrinsic element.In the absence of more restrictions, the element limited by sentence "including a ...", it is not excluded that
There is also other identical elements in the process, method, article or apparatus that includes the element.
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations；Although with reference to the foregoing embodiments
Invention is explained in detail, those skilled in the art should understand that: it still can be to aforementioned each implementation
Technical solution documented by example is modified or equivalent replacement of some of the technical features；And these modification or
Replacement, the spirit and scope for technical solution of various embodiments of the present invention that it does not separate the essence of the corresponding technical solution.
Claims (1)
1. a kind of wind-powered electricity generation pinion steel, which is characterized in that its chemical component mass percent are as follows: C0.12-0.20%, Mn2.6-
3.8%, Si0.26-0.35%, Ni0.44-0.56%, Mo1.4-2.5%, Cr1.2-2.0%, Ti0.005-0.010%,
W0.33-0.46%, Hf0.15-0.23%, P≤0.030%, S≤0.030%, surplus are Fe and inevitable impurity；
The preparation method of the wind-powered electricity generation pinion steel the following steps are included:
(1) electric furnace or converter smelting are adjusted the content of each element in molten steel, no slag or few slag tapping, are carried out using silicomanganese pre- de-
Oxygen；
(2) LF refining is carried out using refining rapid slagging slag making technology, Refining Clean Steel in ASEA-SKF technology, by using external refining, very
Empty degassing process gas content into chemical component and steel meets the requirements, hydrogen content≤2.5ppm, oxygen content≤20ppm in steel,
Complex deoxidization is carried out using compound rare-earth and Ti cooperation；
(3) it is handled by RH or VD vacuum argon blowing degassing method, vacuum degree≤0.10KPa, the retention time 12-16min of VD degassing,
Vacuum breaker is kept stirring state, finely tunes, and feeds S line, finely tunes other ingredients, be casting continuously to form base；
(4) it rolls, continuous casting billet is 1150-1250 DEG C in the heating temperature of heating furnace, and 1100 DEG C of start rolling temperature, heating and high temperature expand
Dissipating the time is 2-3 hours, 860-960 DEG C of finishing temperature, rolls rear air-cooled or slow cooling.