CN107189654A - A kind of power equipment anti-oxidant insulated paint of waterproof - Google Patents
A kind of power equipment anti-oxidant insulated paint of waterproof Download PDFInfo
- Publication number
- CN107189654A CN107189654A CN201710593349.4A CN201710593349A CN107189654A CN 107189654 A CN107189654 A CN 107189654A CN 201710593349 A CN201710593349 A CN 201710593349A CN 107189654 A CN107189654 A CN 107189654A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- waterproof
- oxidant
- power equipment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention belongs to technical field of coatings, and in particular to a kind of power equipment anti-oxidant insulated paint of waterproof, and protection paint is made up of protective primer and waterproof finish paint.The composition of protective primer includes：Dimethylbenzene, alkyd resin, aluminium powder slurry, china clay, talcum powder, plasticizer, silica and glycol ether；The composition of waterproof finish paint includes：PPG, isocyanates, titanium dioxide, tri-methyl-chlorosilane, AEO, levelling agent and cosolvent.First spray-applied primer when using, after priming paint is dried, then spray paint；The protective paint has good anti-oxidant, corrosion-resistant, water resistance, and adhesive force is strong, lacquer painting uniform and smooth, is highly suitable as the protective paint on power equipment surface.
Description
Technical field
The invention belongs to technical field of coatings, and in particular to a kind of power equipment anti-oxidant insulated paint of waterproof.
Background technology
Power equipment is to be applied to, from generating electricity, transmitting electricity to power transformation, distribution and the whole link of electricity consumption, constitute power generation and disappear
The equipment for the holonomic system taken.These equipment are high in technological content, are worth high；Equipment workplace is except a small number of accurate nucleus equipments
Positioned at interior, most equipment is all located at outdoor, directly facing severe natural conditions, so comparing the requirement of shelter of equipment
It is high.It is a part for safeguard procedures in the surface mopping of some metal parts.
The conventional equipment metal protection paint of in the market can also be used, but these paints and non-expert electric power is set
Standby usage scenario particular arrangement, the performance such as anti-oxidant, wear-resisting, fire prevention is perhaps relatively good, but not good waterproof
And insulation characterisitic.
The content of the invention
For problem above, it is an object of the invention to provide a kind of power equipment anti-oxidant insulated paint of waterproof, the oil
Paint can provide protection with good anti-oxidant, wear-resisting, decay resistance for equipment surface, also prevent with very outstanding
Water, insulation effect, are highly suitable as the protective paint of power equipment.
A kind of power equipment anti-oxidant insulated paint of waterproof, including protective primer and waterproof finish paint, it is characterised in that：It is described
The composition of protective primer is by mass fraction：30-40 parts of dimethylbenzene, 30-35 parts of alkyd resin, 10-15 parts of aluminium powder slurry, china clay
10-15 parts, 3-8 parts of talcum powder, 2-3 parts of plasticizer, -2 parts of silica 1,15-25 parts of glycol ether.
The composition of the waterproof finish paint is by mass fraction：40-55 parts of PPG, 30-40 parts of isocyanates, titanium white
25-30 parts of powder, 11-15 parts of tri-methyl-chlorosilane, 3-4 parts of AEO, 2-3 parts of levelling agent, cosolvent 40-50
Part.
It is preferred that, the composition of the protective primer is by mass fraction：35 parts of dimethylbenzene, 33 parts of alkyd resin, aluminum paste
13 parts of material, 12 parts of china clay, 5 parts of talcum powder, 2 parts of plasticizer, silica 1 part, 20 parts of glycol ether.
It is preferred that, the composition of the waterproof finish paint is by mass fraction：50 parts of PPG, 35 parts of isocyanates, titanium
27 parts of white powder, 13 parts of tri-methyl-chlorosilane, 4 parts of AEO, 3 parts of levelling agent, 45 parts of cosolvent.
It is preferred that, the plasticizer is dibutyl tin laurate.
It is preferred that, levelling agent is polysiloxane-based levelling agent.
It is preferred that, the cosolvent is No. 120 solvent naphthas.
It is preferred that, the preparation method of the priming paint is：By alkyd resin, aluminium powder slurry, china clay, silica and talcum powder
It is well mixed, put into and fineness≤45 μm are ground in three-roller, be then dissolved into xylene solvent, be mixed evenly
Afterwards, plasticizer and glycol ether are added, compound is continued to stir, required protective primer is obtained.
It is preferred that, the preparation method of the waterproof finish paint is：By cosolvent heating and thermal insulation, temperature is 35-50 DEG C, Ran Houyi
It is secondary that tri-methyl-chlorosilane, AEO and levelling agent are added in cosolvent, stir while adding, again finally
PPG, isocyanates and titanium dioxide are added, mixed, 300-400 mesh stainless steel filter screens are used after stirring
Filtering, obtains waterproof finish paint.
It is preferred that, the application method of the anti-oxidant insulated paint of waterproof is：Protective primer is first sprayed, after lacquer painting is dried,
Waterproof finish paint is sprayed again.
A kind of anti-oxidant insulated paint of power equipment waterproof that the present invention is provided, compared with prior art, with following excellent
Point：
The type protective paint is made up of protective primer and waterproof finish paint, and priming paint has paint vehicle uniform and smooth, the stable spy of lacquer painting
Point, with good anti-oxidant and decay resistance, also with it is wear-resisting, weather-proof the characteristics of, in the environment that high temperature changes,
Film quality can also keep stable, will not fall off or rupture, protection effect is very outstanding.
Waterproof finish paint then has good waterproof effect, and moisture can be prevented to invade and cause corrosion inside lacquer painting to equipment,
Lacquer painting also have good ageing resistace, surface layer be not easy turn yellow, with guard time it is long the characteristics of, lacquer painting is moist,
It is not easy adhesive dust or other particulate matters.
This two layers of paint vehicle also has fire-retardant, and the characteristics of insulation, the protection that the protective paint of composition is especially suitable for power equipment makes
With.
Embodiment
The embodiment to the present invention is described in detail below.It should be appreciated that described herein specific
Embodiment is merely to illustrate and explain the present invention, and is not intended to limit the invention.
Embodiment 1
A kind of power equipment anti-oxidant insulated paint of waterproof, including protective primer and waterproof finish paint, the composition of protective primer
It is by mass fraction：30 parts of dimethylbenzene, 30 parts of alkyd resin, 10 parts of aluminium powder slurry, 10 parts of china clay, 3 parts of talcum powder, tin dilaurate
2 parts of dibutyl tin, silica 1 part, 15 parts of glycol ether,
The composition of waterproof finish paint is by mass fraction：40 parts of PPG, 30 parts of isocyanates, 25 parts of titanium dioxide, three
11 parts of one chlorosilane of methyl, 3 parts of AEO, polysiloxane-based 2 parts of levelling agent, No. 120 40 parts of solvent naphthas.
The preparation method of protective primer is：Alkyd resin, aluminium powder slurry, china clay, silica and talcum powder are mixed equal
It is even, put into and fineness≤45 μm are ground in three-roller, be then dissolved into xylene solvent, after being mixed evenly, then add
Enter dibutyl tin laurate and glycol ether, compound is continued to stir, required protective primer is obtained.
The preparation method of waterproof finish paint is：By No. 120 solvent naphtha heating and thermal insulations, temperature is 35 DEG C, then successively by front three
The chlorosilane of base one, AEO and polysiloxane-based levelling agent are added in No. 120 solvent naphthas, are stirred when adding
Mix, finally again add PPG, isocyanates and titanium dioxide, mix, with 300 mesh stainless steel mistakes after stirring
Strainer filtering, obtains waterproof finish paint.
The type power equipment is with the application method of the anti-oxidant insulated paint of waterproof：Protective primer is first sprayed, treats that lacquer painting is dried
Afterwards, then waterproof finish paint is sprayed.
Embodiment 2
A kind of power equipment anti-oxidant insulated paint of waterproof, including protective primer and waterproof finish paint, the composition of protective primer
It is by mass fraction：40 parts of dimethylbenzene, 35 parts of alkyd resin, 15 parts of aluminium powder slurry, 15 parts of china clay, 8 parts of talcum powder, tin dilaurate
3 parts of dibutyl tin, 2 parts of silica, 25 parts of glycol ether,
The composition of waterproof finish paint is by mass fraction：55 parts of PPG, 40 parts of isocyanates, 30 parts of titanium dioxide, three
15 parts of one chlorosilane of methyl, 4 parts of AEO, polysiloxane-based 3 parts of levelling agent, No. 120 50 parts of solvent naphthas.
The preparation method of protective primer is：Alkyd resin, aluminium powder slurry, china clay, silica and talcum powder are mixed equal
It is even, put into and fineness≤45 μm are ground in three-roller, be then dissolved into xylene solvent, after being mixed evenly, then add
Enter dibutyl tin laurate and glycol ether, compound is continued to stir, required protective primer is obtained.
The preparation method of waterproof finish paint is：By No. 120 solvent naphtha heating and thermal insulations, temperature is 50 DEG C, then successively by front three
The chlorosilane of base one, AEO and polysiloxane-based levelling agent are added in No. 120 solvent naphthas, are stirred when adding
Mix, finally again add PPG, isocyanates and titanium dioxide, mix, with 400 mesh stainless steel mistakes after stirring
Strainer filtering, obtains waterproof finish paint.
The type power equipment is with the application method of the anti-oxidant insulated paint of waterproof：Protective primer is first sprayed, treats that lacquer painting is dried
Afterwards, then waterproof finish paint is sprayed.
Embodiment 3
A kind of power equipment anti-oxidant insulated paint of waterproof, including protective primer and waterproof finish paint, the composition of protective primer
It is by mass fraction：35 parts of dimethylbenzene, 33 parts of alkyd resin, 12 parts of aluminium powder slurry, 14 parts of china clay, 5 parts of talcum powder, tin dilaurate
2 parts of dibutyl tin, silica 1 part, 20 parts of glycol ether,
The composition of waterproof finish paint is by mass fraction：50 parts of PPG, 35 parts of isocyanates, 27 parts of titanium dioxide, three
13 parts of one chlorosilane of methyl, 3 parts of AEO, polysiloxane-based 2 parts of levelling agent, No. 120 45 parts of solvent naphthas.
The preparation method of protective primer is：Alkyd resin, aluminium powder slurry, china clay, silica and talcum powder are mixed equal
It is even, put into and fineness≤45 μm are ground in three-roller, be then dissolved into xylene solvent, after being mixed evenly, then add
Enter dibutyl tin laurate and glycol ether, compound is continued to stir, required protective primer is obtained.
The preparation method of waterproof finish paint is：By No. 120 solvent naphtha heating and thermal insulations, temperature is 37 DEG C, then successively by front three
The chlorosilane of base one, AEO and polysiloxane-based levelling agent are added in No. 120 solvent naphthas, are stirred when adding
Mix, finally again add PPG, isocyanates and titanium dioxide, mix, with 350 mesh stainless steel mistakes after stirring
Strainer filtering, obtains waterproof finish paint.
The type power equipment is with the application method of the anti-oxidant insulated paint of waterproof：Protective primer is first sprayed, treats that lacquer painting is dried
Afterwards, then waterproof finish paint is sprayed.
Embodiment 4
A kind of power equipment anti-oxidant insulated paint of waterproof, including protective primer and waterproof finish paint, the composition of protective primer
It is by mass fraction：32 parts of dimethylbenzene, 33 parts of alkyd resin, 14 parts of aluminium powder slurry, 11 parts of china clay, 4 parts of talcum powder, tin dilaurate
2 parts of dibutyl tin, silica 1 part, 21 parts of glycol ether,
The composition of waterproof finish paint is by mass fraction：50 parts of PPG, 35 parts of isocyanates, 27 parts of titanium dioxide, three
12 parts of one chlorosilane of methyl, 3 parts of AEO, polysiloxane-based 2 parts of levelling agent, No. 120 45 parts of solvent naphthas.
The preparation method of protective primer is：Alkyd resin, aluminium powder slurry, china clay, silica and talcum powder are mixed equal
It is even, put into and fineness≤45 μm are ground in three-roller, be then dissolved into xylene solvent, after being mixed evenly, then add
Enter dibutyl tin laurate and glycol ether, compound is continued to stir, required protective primer is obtained.
The preparation method of waterproof finish paint is：By No. 120 solvent naphtha heating and thermal insulations, temperature is 45 DEG C, then successively by front three
The chlorosilane of base one, AEO and polysiloxane-based levelling agent are added in No. 120 solvent naphthas, are stirred when adding
Mix, finally again add PPG, isocyanates and titanium dioxide, mix, with 400 mesh stainless steel mistakes after stirring
Strainer filtering, obtains waterproof finish paint.
The type power equipment is with the application method of the anti-oxidant insulated paint of waterproof：Protective primer is first sprayed, treats that lacquer painting is dried
Afterwards, then waterproof finish paint is sprayed.
Performance test
According to GBT 1771-2007《The measure of the resistance to neutral salt spray performance of paint and varnish》、GBT 5210-2006《Colored paint
Method adhesion test is pulled open with varnish》、GBT 1733-1993《Paint and varnish water resistance testing method》To the resistance to of the present embodiment
Burn into adhesive force and water resistance are tested, and obtain following result：
Table 1：The present embodiment
Data above shows, a kind of anti-oxidant insulated paint of power equipment waterproof that the present invention is provided, with good resistance to
Corrosion and fire resistance characteristic, adhesive force are very strong, and property indices can reach the regulation of concerned countries standard.
The specific embodiment of the present invention is described above.It is to be appreciated that the invention is not limited in above-mentioned
Particular implementation, those skilled in the art can make various deformations or amendments within the scope of the claims, this not shadow
Ring the substantive content of the present invention.
Claims (9)
1. a kind of power equipment anti-oxidant insulated paint of waterproof, including protective primer and waterproof finish paint, it is characterised in that：It is described anti-
The composition of river bottom protection paint is by mass fraction：30-40 parts of dimethylbenzene, 30-35 parts of alkyd resin, 10-15 parts of aluminium powder slurry, china clay
10-15 parts, 3-8 parts of talcum powder, 2-3 parts of plasticizer, -2 parts of silica 1,15-25 parts of glycol ether；
The composition of the waterproof finish paint is by mass fraction：40-55 parts of PPG, 30-40 parts of isocyanates, titanium dioxide
25-30 parts, 11-15 parts of tri-methyl-chlorosilane, 3-4 parts of AEO, 2-3 parts of levelling agent, cosolvent 40-50
Part.
2. a kind of power equipment anti-oxidant insulated paint of waterproof according to claim 1, it is characterised in that the protective primer
Composition be by mass fraction：35 parts of dimethylbenzene, 33 parts of alkyd resin, 13 parts of aluminium powder slurry, 12 parts of china clay, 5 parts of talcum powder increases
Mould 2 parts of agent, silica 1 part, 20 parts of glycol ether.
3. a kind of power equipment anti-oxidant insulated paint of waterproof according to claim 1, it is characterised in that the waterproof finish paint
Composition be by mass fraction：50 parts of PPG, 35 parts of isocyanates, 27 parts of titanium dioxide, 13 parts of tri-methyl-chlorosilane,
4 parts of AEO, 3 parts of levelling agent, 45 parts of cosolvent.
4. a kind of power equipment anti-oxidant insulated paint of waterproof according to claim 1, it is characterised in that：The plasticizer is
Dibutyl tin laurate.
5. a kind of power equipment anti-oxidant insulated paint of waterproof according to claim 1, it is characterised in that：Levelling agent is poly- silicon
Oxygen alkanes levelling agent.
6. a kind of power equipment anti-oxidant insulated paint of waterproof according to claim 1, it is characterised in that：The cosolvent is
No. 120 solvent naphthas.
7. a kind of power equipment anti-oxidant insulated paint of waterproof according to claim 1, it is characterised in that the system of the priming paint
Preparation Method is：Alkyd resin, aluminium powder slurry, china clay, silica and talcum powder are well mixed, puts into three-roller and grinds
To fineness≤45 μm, then it is dissolved into xylene solvent, after being mixed evenly, adds plasticizer and glycol ether, will
Compound continues to stir, and obtains required protective primer.
8. a kind of power equipment anti-oxidant insulated paint of waterproof according to claim 1, it is characterised in that：The waterproof finish paint
Preparation method be：By cosolvent heating and thermal insulation, temperature is 35-50 DEG C, then successively by tri-methyl-chlorosilane, poly alkyl alcohol
Oxygen vinethene and levelling agent are added in cosolvent, are stirred while adding, finally again by PPG, isocyanates and titanium white
Powder is added, and is mixed, and is filtered after stirring with 300-400 mesh stainless steel filter screen, is obtained waterproof finish paint.
9. a kind of power equipment anti-oxidant insulated paint of waterproof according to claim 1, it is characterised in that the waterproof antioxygen
Change insulated paint application method be：Protective primer is first sprayed, after lacquer painting is dried, then waterproof finish paint is sprayed.