CN107188536A - A kind of use in toilet floor tile - Google Patents
A kind of use in toilet floor tile Download PDFInfo
- Publication number
- CN107188536A CN107188536A CN201710534022.XA CN201710534022A CN107188536A CN 107188536 A CN107188536 A CN 107188536A CN 201710534022 A CN201710534022 A CN 201710534022A CN 107188536 A CN107188536 A CN 107188536A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- floor tile
- raw material
- toilet floor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of floor tile, and in particular to a kind of use in toilet floor tile.A kind of use in toilet floor tile of the present invention, is made up, 10~30 parts of feldspar in powder, 20~25 parts of tourmaline, 20~30 parts of diatom ooze, 30~35 parts of waste old ceramics, 8~10 parts of silicon powder, 2~5 parts of zeolite with carrying silver, 2~5 parts of zinc oxide of the raw material of following parts by weight.The use in toilet floor tile of the present invention, can adjust the effect of toilet humidity, deodorization, and sterilization antibacterial.
Description
Technical field
The present invention relates to a kind of floor tile, and in particular to a kind of use in toilet floor tile.
Background technology
Mould, bacterium and harmful chemical etc. easily are concealed in toilet, disease, influence household's health is easily caused.
In addition, toilet moisture is overweight, also easy mould growth.
In addition, ceramic tile often uses finishing material as toilet, the waterproof material filled in ceramic tile gap come off or aging with
And ceramic tile rupture, it is easily caused steam entrance, mould growth.
The present invention can adjust toilet humidity to solve this problem there is provided one kind, and antibiotic and sterilizing floor tile.
The content of the invention
The invention solves the problems that first technical problem be to provide a kind of use in toilet floor tile.
A kind of use in toilet floor tile, is made up of the raw material of following parts by weight, 10~30 parts of feldspar in powder, tourmaline 20~25
Part, 20~30 parts of diatom ooze, 30~35 parts of waste old ceramics, 8~10 parts of silicon powder, 2~5 parts of zeolite with carrying silver, 2~5 parts of zinc oxide.
It is preferred that, a kind of use in toilet floor tile is made up of the raw material of following parts by weight, 20 parts of feldspar in powder, tourmaline 23
Part, 23 parts of diatom ooze, 30 parts of waste old ceramics, 8 parts of silicon powder, 5 parts of zeolite with carrying silver, 2 parts of zinc oxide.
The invention solves the problems that second technical problem be to provide a kind of preparation method of use in toilet floor tile.
A kind of preparation method of use in toilet floor tile, is prepared from according to the following steps, first raw material is weighed in proportion, by ball
Mill, is made raw material powder of the specification below 350 mesh, add water obtained mud, then powder is made by spray drying；By powder pressing
Into blank, it is fired, floor tile is made；The addition of its reclaimed water is the 45~55% of raw material gross weight.
It is preferred that, powder is pressed into blank under 84~86MPa.
It is preferred that, firing temperature is 1200~1250 DEG C.
Beneficial effects of the present invention：The use in toilet floor tile of the present invention, can adjust toilet humidity, deodorization, and kill
The effect of bacterium antibacterial.
Embodiment
The invention solves the problems that first technical problem be to provide a kind of use in toilet floor tile.
A kind of use in toilet floor tile, is made up of the raw material of following parts by weight, 10~30 parts of feldspar in powder, tourmaline 20~25
Part, 20~30 parts of diatom ooze, 30~35 parts of waste old ceramics, 8~10 parts of silicon powder, 2~5 parts of zeolite with carrying silver, 2~5 parts of zinc oxide.
It is preferred that, a kind of use in toilet floor tile is made up of the raw material of following parts by weight, 20 parts of feldspar in powder, tourmaline 23
Part, 23 parts of diatom ooze, 30 parts of waste old ceramics, 8 parts of silicon powder, 5 parts of zeolite with carrying silver, 2 parts of zinc oxide.
Use waste old ceramics can be with cost-effective.
Zeolite with carrying silver has very strong bactericidal property；And zinc oxide price is inexpensively, while also having bactericidal property, two
Person's compounding can reach preferable bactericidal effect.Other zeolite with carrying silver has hygroscopic effect, can reduce the humidity in bathroom, prevent
Bacteria breed.Zeolite with carrying silver can also remove the smell of toilet.
The invention solves the problems that second technical problem be to provide a kind of preparation method of use in toilet floor tile.
A kind of preparation method of use in toilet floor tile, is prepared from according to the following steps, first raw material is weighed in proportion, by ball
Mill, is made raw material powder of the specification below 350 mesh, add water obtained mud, then powder is made by spray drying；By powder pressing
Into blank, it is fired, floor tile is made；The addition of its reclaimed water is the 45~55% of raw material gross weight.
It is preferred that, powder is pressed into blank under 84~86MPa.
It is preferred that, firing temperature is 1200~1250 DEG C.
The embodiment of the present invention is further described with reference to embodiment, not therefore by present invention limit
System is among described scope of embodiments.
Embodiment 1
20 parts of feldspar in powder is weighed, 23 parts of tourmaline, 23 parts of diatom ooze, 30 parts of waste old ceramics, 8 parts of silicon powder carries silver boiling
5 parts of stone, 2 parts of zinc oxide.
Above-mentioned raw materials are passed through into ball milling, 350 mesh sieves are crossed, raw material powder is made, is added water into raw material powder, the addition of water is original
Expect the 45~55% of gross weight, mud is made, then powder is made by spray drying；By powder pressing into blank, it is fired,
Floor tile is made.
Embodiment 2
25 parts of feldspar in powder is weighed, 25 parts of tourmaline, 20 parts of diatom ooze, 30 parts of waste old ceramics, 8 parts of silicon powder carries silver boiling
5 parts of stone, 5 parts of zinc oxide.
Above-mentioned raw materials are passed through into ball milling, 350 mesh sieves are crossed, raw material powder is made, is added water into raw material powder, the addition of water is original
Expect the 45~55% of gross weight, mud is made, then powder is made by spray drying；By powder pressing into blank, it is fired,
Floor tile is made.
Claims (5)
1. a kind of use in toilet floor tile, it is characterised in that be made up of the raw material of following parts by weight, 10~30 parts of feldspar in powder, electricity
20~25 parts of gas stone, 20~30 parts of diatom ooze, 30~35 parts of waste old ceramics, 8~10 parts of silicon powder, 2~5 parts of zeolite with carrying silver, oxygen
Change 2~5 parts of zinc.
2. a kind of use in toilet floor tile according to claim 1, it is characterised in that be made up of the raw material of following parts by weight,
20 parts of feldspar in powder, 23 parts of tourmaline, 23 parts of diatom ooze, 30 parts of waste old ceramics, 8 parts of silicon powder, 5 parts of zeolite with carrying silver, zinc oxide 2
Part.
3. the preparation method of a kind of use in toilet floor tile described in claim 1 or 2, it is characterised in that prepare according to the following steps
Form, raw material is weighed in proportion, by ball milling, raw material powder of the specification below 350 mesh is made, add water obtained mud, then passes through
Powder is made in spray drying；By powder pressing into blank, it is fired, floor tile is made；The addition of its reclaimed water is raw material gross weight
The 45~55% of amount.
4. a kind of preparation method of use in toilet floor tile according to claim 3, it is characterised in that powder 84~
Blank is pressed under 86MPa.
5. the preparation method of a kind of use in toilet floor tile according to claim 3, it is characterised in that firing temperature is 1200
~1250 DEG C.