CN107178002A - A kind of wear-resisting colored overlay paper production technology - Google Patents
A kind of wear-resisting colored overlay paper production technology Download PDFInfo
- Publication number
- CN107178002A CN107178002A CN201710479250.1A CN201710479250A CN107178002A CN 107178002 A CN107178002 A CN 107178002A CN 201710479250 A CN201710479250 A CN 201710479250A CN 107178002 A CN107178002 A CN 107178002A
- Authority
- CN
- China
- Prior art keywords
- glue
- overlay paper
- steeping
- colored overlay
- paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the wear-resisting colored overlay paper production technology of one kind, first, body paper uncoiling；Second, background color of printing and dyeing；3rd, printing and dyeing are colored；4th, single-steeping, in the third step the back side of obtained colored overlay paper infiltrated with glue, when waiting the glue at the back side to completely penetrate front, colored overlay paper is completely immersed in glue, colored overlay paper rolled by rolling device；5th, the colored overlay paper after dipping is put into baking in 80 DEG C ~ 200 DEG C of baking oven and obtains wear-resisting colored overlay paper in 1 ~ 5 minute by first drying；6th, double-steeping；7th, secondary drying；8th, cool, volatile content is reduced to 2.5% ~ 15% in colored overlay paper after dipping, and colored overlay paper is reduced into room temperature；Long, winding storage, the wear-resisting colored overlay paper winding processed is packed, and stacking enters warehouse.
Description
Technical field
The present invention relates to building lifting management method field, particularly a kind of wear-resisting colored overlay paper production technology.
Background technology
The mid-90 in last century, reinforced composite floorboard, i.e. impregnated-paper laminated wood floor initially enter China market.Arrive
At present, Chinese consolidated floor production technology and marketing model are very ripe, grown up numerous mighty brands and surging enterprise,
Because consolidated floor surface physicochemical property is better than solid wooden floor board, easy scale is produced, yield has accounted for the half of the country of Flooring.
With wear-resisting colored overlay paper as a kind of main raw material(s) in reinforced composite floorboard production process, mainly pass through
Cross its press-paste technique to be pasted together with base material and eventually become the surface layer on floor, so the quality of dipping paper is to reinforced composite floorboard
Quality and some main performances play conclusive effect.
The wear-resisting colored overlay paper of traditional band has two kinds of technology paths：1）Traditional reinforced composite floorboard is with one layer of leaching
Stain abrasion-proof paper adds one layer of dipping decorative paper to mat formation in the wood-based plate substrate surface such as high density fiberboard, particieboard, and the back side adds balance
Paper, the floor being molded through hot pressing, mortise, but such processing mode inefficiency, the difficulty subsequently impregnate, overlayed is big；2）
Another traditional route is omitted the abrasion-proof paper on top layer, but facing paper has sprayed high-abrasive material in dipping process, but
It is that spraying is a very complicated technology in dipping process, defect rate is very high；And because domestic manufacturer's starting point is low,
Production equipment and development tool fall behind, so as to be difficult to the technological requirement for meeting high-grade dipping paper, all the time in small-scale, low and middle-grade
It is secondary to fluctuate, it is impossible to meet the demand in client and market.
The content of the invention
The present invention solves the technical problem of a kind of wear-resisting colored overlay paper production technology is provided, can effectively it carry
The quality of high abrasion colour overlay paper.
In order to solve the above technical problems, one aspect of the present invention is：A kind of wear-resisting colored overlay paper is provided
Production technology, its step includes：
First, web-like printing is mounted on uncoiler by body paper uncoiling with body paper；
Second, background color of printing and dyeing, one layer of background color of being printed and dyed on body paper, the color of background color and body paper is differed；
3rd, printing and dyeing are colored, add print colored on background color layer：Print the first color → color of drying → print second → color of drying → print the 3rd
→ dry →... ... → print N colors → drying；
4th, single-steeping, the in the third step back side of obtained colored overlay paper single-steeping glue infiltration waits the glue at the back side
When water completely penetrates front, colored overlay paper is completely immersed in glue, colored overlay paper carried out by rolling device
Rolling；
5th, the colored overlay paper after dipping is put into baking 30 ~ 50 seconds in 80 DEG C ~ 200 DEG C of baking oven by first drying；
6th, double-steeping, 5% is down to when the volatile content in the single-steeping glue in color table layer paper in the 5th step~
20%, double-steeping is carried out, double-steeping glue is coated in the front of impregnated carrier during double-steeping, then secondary leaching is applied in reverse side
Stain glue balances the positive and negative glue amount of impregnated carrier；
7th, secondary drying dries the baking oven for entering 80 DEG C~200 DEG C by the impregnated carrier of double-steeping 60~180 seconds, leaching
Glue in stain carrier, which is oven-dried, is solidified into glued membrane；
8th, cool, volatile content is reduced to 2.5% ~ 15% in colored overlay paper after dipping, and colored overlay paper is reduced
To room temperature；
9th, winding storage, the wear-resisting colored overlay paper winding processed is packed, and stacking enters warehouse.
Preferably, in the step of bottom four glue of dipping be at least containing melamine resin adehsive, urea-formaldehyde resin adhesive,
Two kinds of mixed solution in phenolic resin glue, isocyanate resin glue.
Preferably, the cooling method in the 6th step is by natural wind natural cooling.
The beneficial effects of the invention are as follows：A kind of wear-resisting colored overlay paper production technology is provided, the difficulty subsequently overlayed is reduced
Degree, fundamentally changes the traditional reinforced composite floorboard low side manufacture of China and the situation manufactured in a rough and slipshod way, is vast consumption
Person provides stable performance, visual appearance and the first-class product of quality, and also the sustained and rapid development for national economy, which is made, to have
Contribution.
Embodiment
Presently preferred embodiments of the present invention is described in detail below so that advantages and features of the invention can be easier to by
It will be appreciated by those skilled in the art that apparent clearly being defined so as to be made to protection scope of the present invention.
The embodiment of the present invention 1 includes：A kind of wear-resisting colored overlay paper production technology, its step includes：
First, web-like printing is mounted on uncoiler by body paper uncoiling with body paper；
Second, background color of printing and dyeing, one layer of background color of being printed and dyed on body paper, the color of background color and body paper is differed；
3rd, printing and dyeing are colored, add print colored on background color layer：Print the first color → color of drying → print second → color of drying → print the 3rd
→ dry →... ... → print N colors → drying；
4th, single-steeping, the in the third step back side of obtained colored overlay paper single-steeping glue infiltration waits the glue at the back side
When water completely penetrates front, colored overlay paper is completely immersed in glue, colored overlay paper carried out by rolling device
Rolling；Wherein, the concocting method of single-steeping glue：0.1 ‰~the 9 ‰ of addition glue weight in the glue of solid content 20%
It is sufficiently stirred for after 0.1 ‰~9 ‰ curing agent of bleeding agent, 0.1 ‰~9 ‰ releasing agents of glue weight and glue weight.
5th, the colored overlay paper after dipping is put into 80 DEG C of baking oven and toasted 30 seconds by first drying；
6th, double-steeping, when the volatile content in the single-steeping glue in color table layer paper in the 5th step is down to 5%, progress
Double-steeping glue, is coated in the front of impregnated carrier by double-steeping during double-steeping, then applying double-steeping glue in reverse side makes leaching
The positive and negative glue amount balance of stain carrier；The concocting method of double-steeping glue is to add diluent in single-steeping glue to stir
Obtain；
7th, secondary drying dries the baking oven for entering 80 DEG C by the impregnated carrier of double-steeping 60 seconds, the glue in impregnated carrier
Water, which is oven-dried, is solidified into glued membrane；
8th, cool, volatile content is reduced to 2.5% in colored overlay paper after dipping, and colored overlay paper is reduced into room
Temperature；
9th, winding storage, the wear-resisting colored overlay paper winding processed is packed, and stacking enters warehouse.
The embodiment of the present invention 2 includes：A kind of wear-resisting colored overlay paper production technology, its step includes：
First, web-like printing is mounted on uncoiler by body paper uncoiling with body paper；
Second, background color of printing and dyeing, one layer of background color of being printed and dyed on body paper, the color of background color and body paper is differed；
3rd, printing and dyeing are colored, add print colored on background color layer：Print the first color → color of drying → print second → color of drying → print the 3rd
→ dry →... ... → print N colors → drying；
4th, single-steeping, the in the third step back side of obtained colored overlay paper single-steeping glue infiltration waits the glue at the back side
When water completely penetrates front, colored overlay paper is completely immersed in glue, colored overlay paper carried out by rolling device
Rolling；Wherein, the concocting method of single-steeping glue：0.1 ‰~the 9 ‰ of addition glue weight in the glue of solid content 40%
It is sufficiently stirred for after 0.1 ‰~9 ‰ curing agent of bleeding agent, 0.1 ‰~9 ‰ releasing agents of glue weight and glue weight.
5th, the colored overlay paper after dipping is put into 140 DEG C of baking oven and toasted 40 seconds by first drying；
6th, double-steeping, when the volatile content in the single-steeping glue in color table layer paper in the 5th step is down to 13%, enters
Double-steeping glue, is coated in the front of impregnated carrier by row double-steeping during double-steeping, then applying double-steeping glue in reverse side makes
The positive and negative glue amount balance of impregnated carrier；The concocting method of double-steeping glue is that diluent stirring is added in single-steeping glue
It is even to obtain；
7th, secondary drying dries the baking oven for entering 150 DEG C by the impregnated carrier of double-steeping 120 seconds, in impregnated carrier
Glue, which is oven-dried, is solidified into glued membrane；
8th, cool, volatile content is reduced to 10% in colored overlay paper after dipping, and colored overlay paper is reduced into room
Temperature；
9th, winding storage, the wear-resisting colored overlay paper winding processed is packed, and stacking enters warehouse.
The embodiment of the present invention 3 includes：A kind of wear-resisting colored overlay paper production technology, its step includes：
First, web-like printing is mounted on uncoiler by body paper uncoiling with body paper；
Second, background color of printing and dyeing, one layer of background color of being printed and dyed on body paper, the color of background color and body paper is differed；
3rd, printing and dyeing are colored, add print colored on background color layer：Print the first color → color of drying → print second → color of drying → print the 3rd
→ dry →... ... → print N colors → drying；
4th, single-steeping, the in the third step back side of obtained colored overlay paper single-steeping glue infiltration waits the back side
When glue completely penetrates front, colored overlay paper is completely immersed in glue, colored overlay paper entered by rolling device
Row rolling；
5th, the colored overlay paper after dipping is put into 200 DEG C of baking oven and toasted 50 seconds by first drying；
6th, double-steeping, when the single-steeping glue volatile content in color table layer paper in the 5th step is down to 20%, carries out two
Double-steeping glue, is coated in the front of impregnated carrier by secondary dipping during double-steeping, then applying double-steeping glue in reverse side makes dipping
The positive and negative glue amount balance of carrier；
7th, secondary drying dries the baking oven for entering 200 DEG C by the impregnated carrier of double-steeping 180 seconds, in impregnated carrier
Glue, which is oven-dried, is solidified into glued membrane；
8th, cool, volatile content is reduced to 15% in colored overlay paper after dipping, and colored overlay paper is reduced into room
Temperature；
9th, winding storage, the wear-resisting colored overlay paper winding processed is packed, and stacking enters warehouse.
According to above-mentioned processing step, the embodiment 4 ~ 9 of specific process parameter is as shown in the table：
| Sequence number | Glue Water Gu Contain Amount （%） | Infiltration Agent is accounted for Glue Weight ‰ | Curing agent Account for glue Weight ‰ | Once Baking Temperature （℃） | Once dry The dry time （Minute） | Single-steeping Glue volatile matter Content（%） | It is secondary Baking Temperature （℃） | It is secondary to dry The dry time （Minute） | Double-steeping Glue volatile matter Content（%） |
| Embodiment 4 | 20 | 0.1 | 0.1 | 80 | 5 | 2.5 | 80 | 5 | 3.0 |
| Embodiment 5 | 20 | 0.1 | 0.1 | 100 | 3 | 3.0 | 100 | 3 | 5.0 |
| Embodiment 6 | 20 | 0.1 | 0.1 | 120 | 2 | 4.0 | 120 | 2 | 4.5 |
| Embodiment 7 | 20 | 0.1 | 0.1 | 100 | 3 | 8.5 | 100 | 3 | 8.0 |
| Embodiment 8 | 20 | 0.1 | 0.1 | 80 | 5 | 15 | 80 | 5 | 10.0 |
| Embodiment 9 | 20 | 0.1 | 0.1 | 200 | 1 | 12 | 200 | 1 | 11.5 |
If having ink to be not easy to grow dim in impregnated carrier when product impregnates, the glued membrane effect made is good；Product surface is arranged
The depth of parallelism is good, and color effect is obvious, glossiness is good.The wear-resisting colored overlay paper production technology of the present invention program, rationally, simply,
It is workable.
The above embodiments merely illustrate the technical concept and features of the present invention, and its object is to allow person skilled in the art
Scholar can understand present disclosure and be carried out, and it is not intended to limit the scope of the present invention, all according to the present invention
The equivalent change or modification that Spirit Essence is made, should all cover within the scope of the present invention.
Claims (3)
1. a kind of wear-resisting colored overlay paper production technology, it is characterised in that：Its step includes：
First, web-like printing is mounted on uncoiler by body paper uncoiling with body paper；
Second, background color of printing and dyeing, one layer of background color of being printed and dyed on body paper, the color of background color and body paper is differed；
3rd, printing and dyeing are colored, add print colored on background color layer：Print the first color → color of drying → print second → color of drying → print the 3rd
→ dry →... ... → print N colors → drying；
4th, single-steeping, the in the third step back side of obtained colored overlay paper single-steeping glue infiltration waits the glue at the back side
When water completely penetrates front, colored overlay paper is completely immersed in glue, colored overlay paper carried out by rolling device
Rolling；
5th, the colored overlay paper after dipping is put into baking 30 ~ 50 seconds in 80 DEG C ~ 200 DEG C of baking oven by first drying；
6th, double-steeping, 5% is down to when the volatile content in the single-steeping glue in color table layer paper in the 5th step~
20%, double-steeping is carried out, double-steeping glue is coated in the front of impregnated carrier during double-steeping, then secondary leaching is applied in reverse side
Stain glue balances the positive and negative glue amount of impregnated carrier；
7th, secondary drying dries the baking oven for entering 80 DEG C~200 DEG C by the impregnated carrier of double-steeping 60~180 seconds, leaching
Glue in stain carrier, which is oven-dried, is solidified into glued membrane；
8th, cool, volatile content is reduced to 2.5% ~ 15% in colored overlay paper after dipping, and colored overlay paper is reduced
To room temperature；
9th, winding storage, the wear-resisting colored overlay paper winding processed is packed, and stacking enters warehouse.
2. the wear-resisting colored overlay paper production technology of one kind according to claim 1, it is characterised in that：Soaked in the step of bottom four
The glue of stain is at least containing two kinds in melamine resin adehsive, urea-formaldehyde resin adhesive, phenolic resin glue, isocyanate resin glue
Mixed solution.
3. the wear-resisting colored overlay paper production technology of one kind according to claim 1, it is characterised in that：In 6th step
Cooling method is by natural wind natural cooling.