CN107160513A - A kind of processing method of wicker plaiting article raw material false indigo - Google Patents

A kind of processing method of wicker plaiting article raw material false indigo Download PDF

Info

Publication number
CN107160513A
CN107160513A CN201710410455.4A CN201710410455A CN107160513A CN 107160513 A CN107160513 A CN 107160513A CN 201710410455 A CN201710410455 A CN 201710410455A CN 107160513 A CN107160513 A CN 107160513A
Authority
CN
China
Prior art keywords
parts
false indigo
oily liquid
limb
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710410455.4A
Other languages
Chinese (zh)
Inventor
程昭
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
FUNAN COUNTY HONGDA ARTS CRAFTS FACTORY
Original Assignee
FUNAN COUNTY HONGDA ARTS CRAFTS FACTORY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FUNAN COUNTY HONGDA ARTS CRAFTS FACTORY filed Critical FUNAN COUNTY HONGDA ARTS CRAFTS FACTORY
Priority to CN201710410455.4A priority Critical patent/CN107160513A/en
Publication of CN107160513A publication Critical patent/CN107160513A/en
Pending legal-status Critical Current

Abstract

The present invention relates to willow-plaited process product technical field, a kind of processing method of wicker plaiting article raw material false indigo is disclosed, is comprised the following steps：（1）False indigo epidermis is removed using the method for simple and fast, quick lime and water reaction generation aqua calcis, with lubrication, reaction releases largely lasting heat, can accelerate the separation of epidermis；（2）False indigo limb after drying is used into oily liquid A processing, the inorganic agent is by organic solvent and surfactant compound, limb flexibility and Physical Mechanical can be made to change, avoid caused by limb convection drying and mutually to be bonded between fiber dehydration, fiber, cause after drying that sheet is hard, not resistant to bending, the flexible problem of shortage；（3）One layer of oily liquid B of product surface film after braiding, can improve the water resistance of product, and be easier to make for surface applied decorative, be unlikely to deform under rewetting drying, and be easy to cleaning.

Description

A kind of processing method of wicker plaiting article raw material false indigo
Technical field
The invention belongs to willow-plaited process product technical field, and in particular to a kind of processing method of wicker plaiting article raw material false indigo.
Background technology
Wicker plaiting article is one of folks of china traditional handicraft product.People are intended only as common daily utility in ancient times, directly Decades just gradually rise after to 20th century, also the project exported goods and earned foreign currency as selected areas of China gradually.The whole nation has three big Wicker plaiting article production base：Shandong, Henan and Anhui.Wicker products is traditional national handicraft, many countries set up naturally, Pollution-free, quality-high and inexpensive perfectly matched layers, increasingly show economic value and social benefit.Willow-plaited process product is in my area's development Existing nearly 20 years history.It is once once exhibition in " Guangzhou Export Commodities Fair ", and obtain sizing article No. use till today always.With me State's market economic system continuous development of the reform, the wicker plaiting article industry in my area several times wind and rain, with its advantageous salix monogolica resource, high-quality Wicker and exquisite artisan craftsmanship attracted numerous China and foreign countries travelling traders.
Woven more than traditional wicker products using wicker, resource constraint is big, and willow easily damages by worms, parasitic worm's ovum Inside wicker, after processed finished products, the harm for handicraft is great, when seeking other raw materials instead of wicker, is found The excellent usability of false indigo, false indigo fast growth, fertility is strong, and branch is flexible elongated, does sliding uniform, is difficult life Worm, is the splendid substitute of wicker.
The content of the invention
The purpose of the present invention is there is provided a kind of processing method of wicker plaiting article raw material false indigo, by purple the problem of being directed to existing Favour Chinese scholartree is after treatment, it is easy to weave, and effect of painting is good, long lifespan.
The present invention is achieved by the following technical solutions：
A kind of processing method of wicker plaiting article raw material false indigo, comprises the following steps：
（1）The false indigo newly gathered in is removed into other branch and leaf, false indigo limb is obtained, is put into after shining 3-5 days processed in the sun In water vat, add water and flood false indigo limb, according still further to quick lime：Water is 1：300-320 ratio addition quick lime, stirring is to having The bubble that seethes with excitement occurs, and false indigo limb is taken out after 2-3 hours, is put into clear water, the bark that surface comes off in advance is removed, in 30- It is 20-30% to be dried at 40 DEG C to water content；
（2）False indigo limb after drying is dipped in oily liquid A, after soaking 20-30 minutes, taking-up is wrapped up using tinfoil, is put Enter in baking oven and dry 15-20 minutes, oven temperature is 80-90 DEG C, and oily liquid A is made up of following component in parts by weight：58 Spend 60-65 parts of palm oil, 13-16 parts of Lauxite, 10-15 parts of polyethyleneimine, disecoctylmaleate sodium sulfonate 7- 10 parts, 3.5-4.5 parts of APES, 2.5-3.0 parts of acetic acid, 0.5-0.8 parts of sodium chloride, 0.4-0.6 parts of sodium sulphate, 0.2-0.4 parts of calcium hydroxide, 0.1-0.2 parts of chitosan, 100-110 parts of water；
（3）Purple favour Chinese scholartree limb after being handled using oily liquid A passes through Temperature fall, removes surface tinfoil, further dries to matter Measure constant weight, you can woven, one layer of oily liquid B of product surface film after braiding, air-dried by 40-50 DEG C of hot blast Afterwards, you can carry out outward appearance coating modification, oily liquid B is made up of following component in parts by weight：40-50 parts of sulfonated oil, two 35-40 parts of methyl-silicone oil, 70-80 parts of acrylic emulsion, 15-18 parts of alkyl sulfamoyl sodium acetate, 12-15 parts of lanolin, chlorination stone 10-12 parts of wax, 7-10 parts of adipic acid, 20-25 parts of glycerine.
Further described as to such scheme, step（1）The reaction solution of middle quick lime and water can be used continuously, directly Less than 50 DEG C are reduced to temperature.
Further described as to such scheme, step（2）Described in oily liquid A be at 1200-1300 revs/min Under continuously stir obtained oily dispersant.
Further described as to such scheme, step（2）Described in oily liquid B relative air humidity be 40- 50% time progress film, coating thickness is 0.2-0.4 microns.
The present invention has advantages below compared with prior art：In order to find a kind of suitable wicker substitute, by purple favour Chinese scholartree After treatment, it is easy to weave, and effect of painting is good, long lifespan, the invention provides a kind of place of wicker plaiting article raw material false indigo Reason method, comprises the following steps：（1）False indigo epidermis is removed using the method for simple and fast, quick lime and water reaction generation Aqua calcis, with lubrication, reaction releases largely lasting heat, can accelerate the separation of epidermis；（2）After drying False indigo limb using oily liquid A processing, organic solvent and surfactant compound can be made limb flexibility by the inorganic agent Changed with Physical Mechanical, it is to avoid mutually bonded between fiber dehydration, fiber caused by limb convection drying, cause to do Dry rear sheet is hard, not resistant to bending, lack flexible problem；（3）One layer of oily liquid B of product surface film after braiding, The water resistance of product can be improved, and is easier to make for surface applied decorative, is unlikely to deform under rewetting drying, and just In cleaning.
Embodiment
With reference to specific embodiment, the present invention will be further described.
Embodiment 1
A kind of processing method of wicker plaiting article raw material false indigo, comprises the following steps：
（1）The false indigo newly gathered in is removed into other branch and leaf, false indigo limb is obtained, is put into after shining 3-5 days processed in the sun In water vat, add water and flood false indigo limb, according still further to quick lime：Water is 1：300 ratio addition quick lime, stirring is to there is boiling Bubble occurs, and false indigo limb is taken out after 2 hours, is put into clear water, the bark that surface comes off in advance is removed, and is dried at 30 DEG C It is 20% to water content；
（2）False indigo limb after drying is dipped in oily liquid A, after soaking 20 minutes, taking-up is wrapped up using tinfoil, is put into baking Dried 15 minutes in case, oven temperature is 80 DEG C, and oily liquid A is made up of following component in parts by weight：58 degree of palm oils 60 Part, 13 parts of Lauxite, 10 parts of polyethyleneimine, 7 parts of disecoctylmaleate sodium sulfonate, APES 3.5 parts, 2.5 parts of acetic acid, 0.5 part of sodium chloride, 0.4 part of sodium sulphate, 0.2 part of calcium hydroxide, 0.1 part of chitosan, 100 parts of water；
（3）Purple favour Chinese scholartree limb after being handled using oily liquid A passes through Temperature fall, removes surface tinfoil, further dries to matter Measure constant weight, you can woven, one layer of oily liquid B of product surface film after braiding, after 40 DEG C of hot blasts are air-dried, i.e., Outward appearance coating modification can be carried out, oily liquid B is made up of following component in parts by weight：40 parts of sulfonated oil, dimethicone 35 parts, 70 parts of acrylic emulsion, 15 parts of alkyl sulfamoyl sodium acetate, 12 parts of lanolin, 10 parts of chlorinated paraffin, 7 parts of adipic acid, the third three 20 parts of alcohol.
Further described as to such scheme, step（1）The reaction solution of middle quick lime and water can be used continuously, directly Less than 50 DEG C are reduced to temperature.
Further described as to such scheme, step（2）Described in oily liquid A be to connect under 1200 revs/min It is continuous to stir obtained oily dispersant.
Further described as to such scheme, step（2）Described in oily liquid B relative air humidity be 40- 50% time progress film, coating thickness is 0.2 micron.
Embodiment 2
A kind of processing method of wicker plaiting article raw material false indigo, comprises the following steps：
（1）The false indigo newly gathered in is removed into other branch and leaf, false indigo limb is obtained, system is shone in the sun and is put into water after 4 days In cylinder, add water and flood false indigo limb, according still further to quick lime：Water is 1：310 ratio addition quick lime, stirring is to there is boiling gas Bubble out now, false indigo limb is taken out after 2.5 hours, is put into clear water, the bark that surface comes off in advance is removed, dried at 35 DEG C It is 25% to water content；
（2）False indigo limb after drying is dipped in oily liquid A, after soaking 25 minutes, taking-up is wrapped up using tinfoil, is put into baking Dried 17 minutes in case, oven temperature is 85 DEG C, and oily liquid A is made up of following component in parts by weight：58 degree of palm oils 62 Part, 14 parts of Lauxite, 13 parts of polyethyleneimine, 8 parts of disecoctylmaleate sodium sulfonate, APES 4.0 parts, 2.7 parts of acetic acid, 0.6 part of sodium chloride, 0.5 part of sodium sulphate, 0.3 part of calcium hydroxide, 0.15 part of chitosan, 105 parts of water；
（3）Purple favour Chinese scholartree limb after being handled using oily liquid A passes through Temperature fall, removes surface tinfoil, further dries to matter Measure constant weight, you can woven, one layer of oily liquid B of product surface film after braiding, after 45 DEG C of hot blasts are air-dried, i.e., Outward appearance coating modification can be carried out, oily liquid B is made up of following component in parts by weight：45 parts of sulfonated oil, dimethicone 37 parts, 75 parts of acrylic emulsion, 16 parts of alkyl sulfamoyl sodium acetate, 13 parts of lanolin, 11 parts of chlorinated paraffin, 8 parts of adipic acid, the third three 22 parts of alcohol.
Further described as to such scheme, step（1）The reaction solution of middle quick lime and water can be used continuously, directly Less than 50 DEG C are reduced to temperature.
Further described as to such scheme, step（2）Described in oily liquid A be to connect under 1250 revs/min It is continuous to stir obtained oily dispersant.
Further described as to such scheme, step（2）Described in oily liquid B relative air humidity be 45% Lower carry out film, coating thickness is 0.3 micron.
Embodiment 3
A kind of processing method of wicker plaiting article raw material false indigo, comprises the following steps：
（1）The false indigo newly gathered in is removed into other branch and leaf, false indigo limb is obtained, system is shone in the sun and is put into water after 5 days In cylinder, add water and flood false indigo limb, according still further to quick lime：Water is 1：320 ratio addition quick lime, stirring is to there is boiling gas Bubble out existing, false indigo limb taken out after 3 hours, is put into clear water, the bark that surface comes off in advance is removed, dried at 40 DEG C to Water content is 30%；
（2）False indigo limb after drying is dipped in oily liquid A, after soaking 30 minutes, taking-up is wrapped up using tinfoil, is put into baking Dried 20 minutes in case, oven temperature is 90 DEG C, and oily liquid A is made up of following component in parts by weight：58 degree of palm oils 65 Part, 16 parts of Lauxite, 15 parts of polyethyleneimine, 10 parts of disecoctylmaleate sodium sulfonate, APES 4.5 parts, 3.0 parts of acetic acid, 0.8 part of sodium chloride, 0.6 part of sodium sulphate, 0.4 part of calcium hydroxide, 0.2 part of chitosan, 110 parts of water；
（3）Purple favour Chinese scholartree limb after being handled using oily liquid A passes through Temperature fall, removes surface tinfoil, further dries to matter Measure constant weight, you can woven, one layer of oily liquid B of product surface film after braiding, after 50 DEG C of hot blasts are air-dried, i.e., Outward appearance coating modification can be carried out, oily liquid B is made up of following component in parts by weight：50 parts of sulfonated oil, dimethicone 40 parts, 80 parts of acrylic emulsion, 18 parts of alkyl sulfamoyl sodium acetate, 15 parts of lanolin, 12 parts of chlorinated paraffin, 10 parts of adipic acid, third 25 parts of triol.
Further described as to such scheme, step（1）The reaction solution of middle quick lime and water can be used continuously, directly Less than 50 DEG C are reduced to temperature.
Further described as to such scheme, step（2）Described in oily liquid A be to connect under 1300 revs/min It is continuous to stir obtained oily dispersant.
Further described as to such scheme, step（2）Described in oily liquid B relative air humidity be 50% Lower carry out film, coating thickness is 0.4 micron.

Claims (4)

1. a kind of processing method of wicker plaiting article raw material false indigo, it is characterised in that comprise the following steps：
（1）The false indigo newly gathered in is removed into other branch and leaf, false indigo limb is obtained, is put into after shining 3-5 days processed in the sun In water vat, add water and flood false indigo limb, according still further to quick lime：Water is 1：300-320 ratio addition quick lime, stirring is to having The bubble that seethes with excitement occurs, and false indigo limb is taken out after 2-3 hours, is put into clear water, the bark that surface comes off in advance is removed, in 30- It is 20-30% to be dried at 40 DEG C to water content；
（2）False indigo limb after drying is dipped in oily liquid A, after soaking 20-30 minutes, taking-up is wrapped up using tinfoil, is put Enter in baking oven and dry 15-20 minutes, oven temperature is 80-90 DEG C, and oily liquid A is made up of following component in parts by weight：58 Spend 60-65 parts of palm oil, 13-16 parts of Lauxite, 10-15 parts of polyethyleneimine, disecoctylmaleate sodium sulfonate 7- 10 parts, 3.5-4.5 parts of APES, 2.5-3.0 parts of acetic acid, 0.5-0.8 parts of sodium chloride, 0.4-0.6 parts of sodium sulphate, 0.2-0.4 parts of calcium hydroxide, 0.1-0.2 parts of chitosan, 100-110 parts of water；
（3）Purple favour Chinese scholartree limb after being handled using oily liquid A passes through Temperature fall, removes surface tinfoil, further dries to matter Measure constant weight, you can woven, one layer of oily liquid B of product surface film after braiding, air-dried by 40-50 DEG C of hot blast Afterwards, you can carry out outward appearance coating modification, oily liquid B is made up of following component in parts by weight：40-50 parts of sulfonated oil, two 35-40 parts of methyl-silicone oil, 70-80 parts of acrylic emulsion, 15-18 parts of alkyl sulfamoyl sodium acetate, 12-15 parts of lanolin, chlorination stone 10-12 parts of wax, 7-10 parts of adipic acid, 20-25 parts of glycerine.
2. a kind of processing method of wicker plaiting article raw material false indigo as claimed in claim 1, it is characterised in that step（1）Middle quick lime Can continuously it be used with the reaction solution of water, until temperature is reduced to less than 50 DEG C.
3. a kind of processing method of wicker plaiting article raw material false indigo as claimed in claim 1, it is characterised in that step（2）Described in Oily liquid A is that obtained oily dispersant is continuously stirred under 1200-1300 revs/min.
4. a kind of processing method of wicker plaiting article raw material false indigo as claimed in claim 1, it is characterised in that step（2）Described in Oily liquid B carries out film in the case where relative air humidity is 40-50%, and coating thickness is 0.2-0.4 microns.
CN201710410455.4A 2017-06-03 2017-06-03 A kind of processing method of wicker plaiting article raw material false indigo Pending CN107160513A (en)