CN108908577A - A kind of high-quality peeling method of wicker plaiting article raw material - Google Patents
A kind of high-quality peeling method of wicker plaiting article raw material Download PDFInfo
- Publication number
- CN108908577A CN108908577A CN201810883345.4A CN201810883345A CN108908577A CN 108908577 A CN108908577 A CN 108908577A CN 201810883345 A CN201810883345 A CN 201810883345A CN 108908577 A CN108908577 A CN 108908577A
- Authority
- CN
- China
- Prior art keywords
- raw material
- plaiting article
- wicker plaiting
- article raw
- processing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high-quality peeling methods of wicker plaiting article raw material, include the following steps：（1）Dipping by lye processing,（2）Freezing processing,（3）Ultrasonication.The peeling walnut hulling rate of the method for the present invention reaches 99.5% or more, and the efficiency of processing improves 40% or more, and peeling is complete, not damaged rate, residue are small, the great market competitiveness and application value.
Description
Technical field
The invention belongs to wicker plaiting article working process technical fields, and in particular to a kind of high-quality peeling method of wicker plaiting article raw material.
Background technique
Wicker plaiting article is one of folks of china traditional handicraft product.People are intended only as common daily utility in ancient times, directly
Decades just gradually rise after to 20th century, also the project for becoming selected areas of China foreign exchange earning gradually.The whole nation has three big
Wicker plaiting article production base：Shandong, Henan and Anhui.Wicker products are traditional national handicrafts, many countries set up it is natural,
Pollution-free, quality-high and inexpensive perfectly matched layers, increasingly show economic value and social benefit.Willow-plaited process product develops in my area
Has nearly 20 years history.It is once once exhibition in " Guangzhou Export Commodities Fair ", and obtain sizing article No. and use till today always.With me
State's market economic system continuous development of the reform, the wicker plaiting article industry in my area several times wind and rain, with its advantageous salix monogolica resource, high-quality
Wicker and exquisite artisan craftsmanship attracted numerous China and foreign countries travelling traders.
On the make, the peeling to braided material is relatively complicated step to willow-plaited process product, needs to consume a large amount of
Time and labour, it is artificial time-consuming big, but obtain that the effect is unsatisfactory, in order to improve efficiency, corresponding peeling machine meet the tendency of and
It is raw, but due to that can not can only identify the thickness and concavity and convexity of wicker plaiting article material surface, easily formation cut mark, cracking, weak spot,
It does over again serious, cost is larger, and peeling machine effect is not also ideal.
Summary of the invention
The purpose of the present invention is being directed to existing problem, a kind of high-quality peeling method of wicker plaiting article raw material is provided.
The present invention is achieved by the following technical solutions：
A kind of high-quality peeling method of wicker plaiting article raw material, includes the following steps：
（1）Dipping by lye processing：
It after the bundled binding of wicker plaiting article raw material, then puts into pond, then puts into water gross mass 0.1 ~ 0.3% into pond again
Quick lime, bundled wicker plaiting article raw material is pulled out after 15 ~ 20min of stir process spare；
（2）Freezing processing：
By step（1）Treated, and bundled wicker plaiting article raw material is put into progress freezing processing in freezing chamber, takes out after 6 ~ 8h spare；
（3）Ultrasonication：
To step（2）Treated, and wicker plaiting article raw material carries out ultrasonication, carries out peeling processing to wicker plaiting article raw material after 2 ~ 3h.
Further, step（1）Described in stir process when speed of agitator be 100 ~ 150 revs/min.
Further, step（2）Described in the indoor temperature of freezing processing time control fine frozen be -8 ~ -10 DEG C.
Further, step（3）Described in ultrasonication when ultrasonic wave frequency be 400 ~ 450kHz.
The present invention has the following advantages that compared with prior art：
The present invention provides a kind of special peeling methods, wherein first being carried out at immersion with lime water solution to wicker plaiting article raw material
Reason, the lye and heat of formation corrode wicker plaiting article raw material, bast can be made to be detached from forming layer well, and lye has
There is certain lubricating action, joint part can be made without damage, bone skin separative efficiency is high, has then put it into freezing chamber
Interior carry out freezing processing has further promoted the disengaging of bast, has finally carried out using expanding with heat and contract with cold and the principle of the big temperature difference
Ultrasonication bast and forms interlayer and forms a large amount of small ice crystal when freezing, and ice crystal concussion is to this when ultrasonic treatment
Between tissue worn, cut, preferably promote the separation of two tissues, improve the efficiency and effect of peeling.The present invention
The peeling walnut hulling rate of method reaches 99.5% or more, and the efficiency of processing improves 40% or more, and peeling is complete, not damaged rate, residual
Excess is small, the great market competitiveness and application value.
Specific embodiment
Embodiment 1
A kind of high-quality peeling method of wicker plaiting article raw material, includes the following steps：
（1）Dipping by lye processing：
It after the bundled binding of wicker plaiting article raw material, then puts into pond, then puts into the life of water gross mass 0.1% into pond again
Lime is pulled bundled wicker plaiting article raw material out after stir process 15min spare；
（2）Freezing processing：
By step（1）Treated, and bundled wicker plaiting article raw material is put into progress freezing processing in freezing chamber, takes out after 6h spare；
（3）Ultrasonication：
To step（2）Treated, and wicker plaiting article raw material carries out ultrasonication, carries out peeling processing to wicker plaiting article raw material after 2h.
Further, step（1）Described in stir process when speed of agitator be 100 revs/min.
Further, step（2）Described in the indoor temperature of freezing processing time control fine frozen be -8 DEG C.
Further, step（3）Described in ultrasonication when ultrasonic wave frequency be 400kHz.
Embodiment 2
A kind of high-quality peeling method of wicker plaiting article raw material, includes the following steps：
（1）Dipping by lye processing：
It after the bundled binding of wicker plaiting article raw material, then puts into pond, then puts into the life of water gross mass 0.2% into pond again
Lime is pulled bundled wicker plaiting article raw material out after stir process 18min spare；
（2）Freezing processing：
By step（1）Treated, and bundled wicker plaiting article raw material is put into progress freezing processing in freezing chamber, takes out after 7h spare；
（3）Ultrasonication：
To step（2）Treated, and wicker plaiting article raw material carries out ultrasonication, carries out peeling processing to wicker plaiting article raw material after 2.5h.
Further, step（1）Described in stir process when speed of agitator be 130 revs/min.
Further, step（2）Described in the indoor temperature of freezing processing time control fine frozen be -9 DEG C.
Further, step（3）Described in ultrasonication when ultrasonic wave frequency be 420kHz.
Embodiment 3
A kind of high-quality peeling method of wicker plaiting article raw material, includes the following steps：
（1）Dipping by lye processing：
It after the bundled binding of wicker plaiting article raw material, then puts into pond, then puts into the life of water gross mass 0.3% into pond again
Lime is pulled bundled wicker plaiting article raw material out after stir process 20min spare；
（2）Freezing processing：
By step（1）Treated, and bundled wicker plaiting article raw material is put into progress freezing processing in freezing chamber, takes out after 8h spare；
（3）Ultrasonication：
To step（2）Treated, and wicker plaiting article raw material carries out ultrasonication, carries out peeling processing to wicker plaiting article raw material after 3h.
Further, step（1）Described in stir process when speed of agitator be 150 revs/min.
Further, step（2）Described in the indoor temperature of freezing processing time control fine frozen be -10 DEG C.
Further, step（3）Described in ultrasonication when ultrasonic wave frequency be 450kHz.
The peeling walnut hulling rate of the method for the present invention reaches 99.5% or more, and the efficiency of processing improves 40% or more, and peeling is complete
Whole, not damaged rate, residue are small, the great market competitiveness and application value.
Claims (4)
1. a kind of high-quality peeling method of wicker plaiting article raw material, which is characterized in that include the following steps：
（1）Dipping by lye processing：
It after the bundled binding of wicker plaiting article raw material, then puts into pond, then puts into water gross mass 0.1 ~ 0.3% into pond again
Quick lime, bundled wicker plaiting article raw material is pulled out after 15 ~ 20min of stir process spare；
（2）Freezing processing：
By step（1）Treated, and bundled wicker plaiting article raw material is put into progress freezing processing in freezing chamber, takes out after 6 ~ 8h spare；
（3）Ultrasonication：
To step（2）Treated, and wicker plaiting article raw material carries out ultrasonication, carries out peeling processing to wicker plaiting article raw material after 2 ~ 3h.
2. a kind of high-quality peeling method of wicker plaiting article raw material according to claim 1, which is characterized in that step（1）Middle institute
The speed of agitator when stir process stated is 100 ~ 150 revs/min.
3. a kind of high-quality peeling method of wicker plaiting article raw material according to claim 1, which is characterized in that step（2）Middle institute
The indoor temperature of freezing processing time control fine frozen stated is -8 ~ -10 DEG C.
4. a kind of high-quality peeling method of wicker plaiting article raw material according to claim 1, which is characterized in that step（3）Middle institute
The frequency of ultrasonic wave is 400 ~ 450kHz when the ultrasonication stated.