CN107142791A - 一种防涂鸦聚氯乙烯墙纸及其制备方法 - Google Patents

一种防涂鸦聚氯乙烯墙纸及其制备方法 Download PDF

Info

Publication number
CN107142791A
CN107142791A CN201710314551.9A CN201710314551A CN107142791A CN 107142791 A CN107142791 A CN 107142791A CN 201710314551 A CN201710314551 A CN 201710314551A CN 107142791 A CN107142791 A CN 107142791A
Authority
CN
China
Prior art keywords
polyvinyl chloride
graffiti
parts
wallpaper
functional layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710314551.9A
Other languages
English (en)
Inventor
舒峰
李琨
姚艳芳
马勇
张宇运
舒玉法
刘学辉
王祖林
胡克文
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI YUFA PLASTIC INDUSTRY Co Ltd
Original Assignee
ANHUI YUFA PLASTIC INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI YUFA PLASTIC INDUSTRY Co Ltd filed Critical ANHUI YUFA PLASTIC INDUSTRY Co Ltd
Priority to CN201710314551.9A priority Critical patent/CN107142791A/zh
Publication of CN107142791A publication Critical patent/CN107142791A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种防涂鸦聚氯乙烯墙纸及其制备方法，其中所述防涂鸦聚氯乙烯墙纸包括基层和功能层，所述功能层包括：聚氯乙烯树脂100‑120份、丙烯酸树脂100‑150份、丙烯酸固化剂20‑30份、钛白粉10‑20份、助剂2‑8份。本发明的聚氯乙烯墙纸具备良好的防涂鸦性能，其易擦除的特性使得所述墙纸可反复涂鸦，且不影响室内美观效果。

Description

一种防涂鸦聚氯乙烯墙纸及其制备方法
技术领域
本发明涉及墙纸壁纸技术领域，尤其涉及一种防涂鸦聚氯乙烯墙纸及其制备方法。
背景技术
墙纸作为一种普遍使用的室内装饰材料，具有提升居室整体美观效果的特点。然而，在实际生活中，粘贴好的壁纸上总会被有意或无意的弄上污渍、油迹等，特别是家中有小孩的家庭，墙纸更是被随时涂鸦上各种笔迹，而且这种涂鸦很难彻底清除干净，使得原本整洁美观的墙纸显得脏乱不堪，降低居室舒心度。因此，研发一种具有防涂鸦功能的墙纸，使其具备良好的擦除功能具有重要的实际意义。
发明内容
本发明要解决的技术问题是克服现有的墙纸不具备防涂鸦性能的缺陷，提出一种防涂鸦聚氯乙烯墙纸及其制备方法，本发明采用的技术方案是：
一种防涂鸦聚氯乙烯墙纸，包括基层和功能层，所述功能层包括：
聚氯乙烯树脂100-120份、丙烯酸树脂100-150份、丙烯酸固化剂20-30份、钛白粉10-20份、助剂2-8份。
优选的，所述丙烯酸树脂为缩水甘油基丙烯酸树脂。
优选的，所述的丙烯酸固化剂为饱和脂肪族二酸。
优选的，所述助剂为流平剂或消泡剂。
优选的，所述基层为墙纸原纸、无纺纸、无纺布、平织布中的任意一种。
一种防涂鸦聚氯乙烯墙纸的制备方法，该方法包括以下步骤：
(1)将所述丙烯酸树脂、丙烯酸固化剂、钛白粉以及助剂按一定比例混合均匀并搅碎得防涂鸦填料；
(2)在上述防涂鸦填料中加入聚氯乙烯，升高温度为80-100℃，并保温搅拌10-20min，得改性聚氯乙烯材料；
(3)将上述改性聚氯乙烯材料在双螺杆挤出机中挤出，并经冷却、造粒得功能层材料；
(4)在准备好的基层上通过涂刮或涂布或覆合的方式覆盖所述功能层材料。
本发明的优点是：
本发明的墙纸具备良好的擦除功能，可防反复涂鸦；且其耐酸碱腐蚀性较强，可防多种油渍污渍。
本发明的墙纸实用性高、制备工艺简单，具备广阔的市场空间和巨大的经济效益。
具体实施方式
实施例1
一种防涂鸦聚氯乙烯墙纸，包括基层和功能层，所述功能层包括：
聚氯乙烯树脂100份、缩水甘油基丙烯酸树脂100份、饱和脂肪族二酸20份、钛白粉10份、流平剂2份；所述基层为墙纸原纸。
一种防涂鸦聚氯乙烯墙纸的制备方法，该方法包括以下步骤：
(1)将缩水甘油基丙烯酸树脂100份、饱和脂肪族二酸20份、钛白粉10份、流平剂2份混合均匀并搅碎10min，得防涂鸦填料；
(2)在上述防涂鸦填料中加入聚氯乙烯树脂100份，升高温度为80℃，并保温搅拌10min，得改性聚氯乙烯材料；
(3)将上述改性聚氯乙烯材料在双螺杆挤出机中挤出，挤出温度为100℃，并经冷却、造粒得功能层材料；
(4)在准备好的墙纸原纸上通过涂刮的方式覆盖所述功能层材料。
实施例2
一种防涂鸦聚氯乙烯墙纸，包括基层和功能层，所述功能层包括：
聚氯乙烯树脂120份、缩水甘油基丙烯酸树脂150份、饱和脂肪族二酸30份、钛白粉20份、消泡剂8份；所述基层为无纺布。
一种防涂鸦聚氯乙烯墙纸的制备方法，该方法包括以下步骤：
(1)将缩水甘油基丙烯酸树脂150份、饱和脂肪族二酸30份、钛白粉20份、消泡剂8份混合均匀并搅碎10min，得防涂鸦填料；
(2)在上述防涂鸦填料中加入聚氯乙烯树脂120份，升高温度为100℃，并保温搅拌20min，得改性聚氯乙烯材料；
(3)将上述改性聚氯乙烯材料在双螺杆挤出机中挤出，挤出温度为100℃，并经冷却、造粒得功能层材料；
(4)在准备好的基层上通过涂布的方式覆盖所述功能层材料。
实施例3
一种防涂鸦聚氯乙烯墙纸，包括基层和功能层，所述功能层包括：
聚氯乙烯树脂110份、缩水甘油基丙烯酸树脂120份、饱和脂肪族二酸25份、钛白粉15份、流平剂5份；所述基层为平织布。
一种防涂鸦聚氯乙烯墙纸的制备方法，该方法包括以下步骤：
(1)将所述缩水甘油基丙烯酸树脂120份、饱和脂肪族二酸25份、钛白粉15份、流平剂5份混合均匀并搅碎10min，得防涂鸦填料；
(2)在上述防涂鸦填料中加入聚氯乙烯110份，升高温度为90℃，并保温搅拌15min，得改性聚氯乙烯材料；
(3)将上述改性聚氯乙烯材料在双螺杆挤出机中挤出，挤出温度为100℃，并经冷却、造粒得功能层材料；
(4)在准备好的基层上通过覆合的方式覆盖所述功能层材料。
本发明的聚氯乙烯墙纸具备良好的防涂鸦性能，其易擦除的特性使得所述墙纸可反复涂鸦，且不影响室内美观效果，同时本发明还具备较强的耐酸碱腐蚀性，可防多种油渍污渍。其实用性强，市场开发价值大，经济效益显著。

Claims (6)

1.一种防涂鸦聚氯乙烯墙纸，包括基层和功能层，其特征在于，所述功能层包括：
聚氯乙烯树脂100-120份、丙烯酸树脂100-150份、丙烯酸固化剂20-30份、钛白粉10-20份、助剂2-8份。
2.如权利要求1所述的一种防涂鸦聚氯乙烯墙纸，其特征在于，所述丙烯酸树脂为缩水甘油基丙烯酸树脂。
3.如权利要求2所述的一种防涂鸦聚氯乙烯墙纸，其特征在于，所述丙烯酸固化剂为饱和脂肪族二酸。
4.如权利要求3所述的一种防涂鸦聚氯乙烯墙纸，其特征在于，所述助剂为流平剂或消泡剂。
5.如权利要求4所述的一种防涂鸦聚氯乙烯墙纸，其特征在于，所述基层为墙纸原纸、无纺纸、无纺布、平织布中的任意一种。
6.一种如权利要求1-5任一项所述的防涂鸦聚氯乙烯墙纸的制备方法，其特征在于，该方法包括以下步骤：
(1)将所述丙烯酸树脂、丙烯酸固化剂、钛白粉以及助剂按一定比例混合均匀并搅碎得防涂鸦填料；
(2)在上述防涂鸦填料中加入聚氯乙烯，升高温度为80-100℃，并保温搅拌10-20min，得改性聚氯乙烯材料；
(3)将上述改性聚氯乙烯材料在双螺杆挤出机中挤出，并经冷却、造粒得功能层材料；
(4)在准备好的基层上通过涂刮或涂布或覆合的方式覆盖所述功能层材料。
CN201710314551.9A 2017-05-06 2017-05-06 一种防涂鸦聚氯乙烯墙纸及其制备方法 Pending CN107142791A (zh)