CN107139294A - A kind of renovation method of outmoded modeling rattan cradle - Google Patents
A kind of renovation method of outmoded modeling rattan cradle Download PDFInfo
- Publication number
- CN107139294A CN107139294A CN201710325779.8A CN201710325779A CN107139294A CN 107139294 A CN107139294 A CN 107139294A CN 201710325779 A CN201710325779 A CN 201710325779A CN 107139294 A CN107139294 A CN 107139294A
- Authority
- CN
- China
- Prior art keywords
- cradle
- parts
- rattan
- outmoded
- minutes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of renovation method of outmoded modeling rattan cradle, specifically includes following steps：Cradle wavelength that is well-worn but not damaging will be made to be irradiated 10 minutes for 320 360nm ultraviolets, cradle is then placed in immersion treatment 4 20 hours in modified soak；It is again that 220 280nm ultraviolets irradiate 10 minutes with wavelength to pull cradle out, and then cradle is immersed in ethanol solution again；Take out cradle and be irradiated with infrared ray, cradle is then subjected to immersion 24 hours with old agent is removed；Cradle is cleaned with purified water, and cradle purged with clean air；It is placed in after cradle is dried in 80 90 DEG C of greenhouses, oxygen is blasted into greenhouse within each 10 minutes.The inventive method can be recovered to mould rattan toughness, greatly enhance its pulling force, and can take off the aging layer on modeling rattan surface but not interfere with the effect of modeling rattan, and cradle need not be dismantled during processing, technique is greatly simplified, the cradle bright color after processing, cradle surface adhesion force is low.
Description
Technical field
The present invention relates to the processing technology field of modeling rattan article, and in particular to a kind of renovation method of outmoded modeling rattan cradle.
Background technology
Rattan plaited typically by beat rattan (pruning the knot on rattan), pick rattan, wash rattan, shine rattan, stubborn rattan, draw rattan (digging rattan), cut rattan,
More than ten procedures such as bleach, dye, weaving, painting.Rattan plaited is main using rattan branch, rattan core or bamboo as skeleton, then with rattan peel or
Tender rattan core braiding is formed, the characteristics of giving full play to rattan softness, be not easily broken.
On color, mostly using the light yellow of former rattan, or processing, bleaching are white, ivory white, it appears soft elegance,
Some are then equipped with coffee color, brown etc..Rattan furniture is using thick rattan as skeleton, through following closely frame, then with rattan peel, the braiding of rattan core
Into finally painting or paint.
Rattan-weaved products is increasingly liked because of its elegant, simple outward appearance by masses.It is to utilize plastic extrusion to mould rattan
The plastic products for the similar Rattan-shaped being made.Due to natural rattan plaited material, supply falls short of demand, so many products are using modeling now
The rattan imitating of rattan etc carries out being compiled into rattan woven ware imitation product to meet the market demand.But modeling rattan article use time it is long it is rear just
It can be oxidized, its color and intensity are substantially reduced.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of renovation method of outmoded modeling rattan cradle.
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of renovation method of outmoded modeling rattan cradle, mainly handles the cradle for moulding rattan plaited, is shaken without handling
The irony support frame of basket, specifically includes following steps：
(1) will make the well-worn but cradle that does not damage is that 320-360nm ultraviolets irradiate 10 minutes with wavelength, so
Cradle is placed in modified soak immersion treatment 4-20 hours afterwards；
The modified soak is made up of following raw material：
5-10 parts of guar gum ether, 5-10 parts of L-arabinose, 5-10 parts of d- corydalines, 8-9.5 parts of golden larch furans acid, go
3.5-3.8 parts of methyl hyoscyamine, 1-2 parts of sodium chloride, 1-2 parts of DDAO, 150-180 parts of water, it is prepared
Method is to mix each raw material and then stirred in mixer, and mixing speed is 2500r/mim, and whipping temp is 50-60
DEG C, 10 minutes time；
(2) it is again that 220-280nm ultraviolets irradiate 10 minutes with wavelength to pull cradle out, and cradle then is immersed in into ethanol again
In solution, calcium hydroxide is added in one week backward ethanol solution, is added by every 1kg ethanol on the basis of 0.01-0.02kg calcium hydroxides, then
Cross one week backward ethanol solution and add glacial acetic acid, added by every 1kg ethanol on the basis of 0.01-0.02kg glacial acetic acid；
(3) take out cradle and be irradiated with infrared ray, cradle is then subjected to immersion 24 hours with old agent is removed；
(4) cradle is cleaned with purified water, and cradle purged with clean air；
(5) it is placed in after cradle is dried in 80-90 DEG C of greenhouse, oxygen is blasted into greenhouse within each 10 minutes, according to temperature
Room area, every 1 cubic meter volume blasts 0.01 cubic metre of oxygen.
The modified soak is made up of following raw material：8 parts of guar gum ether, 8 parts of L-arabinose, d- corydalines
8 parts, golden larch furans acid 9 parts, 3.6 parts of Norhyoscyamine, 1.5 parts of sodium chloride, 1.5 parts of DDAO,
165 parts of water.
It is described except old agent is made up of following raw material：15-16 parts of butyl butyrate, 6-8 parts of acetyl CoA carboxylase, ten
Eight 6-8 parts of alcohol, 0.5-3.5 parts of coptisine, 1-2 parts of paraffin, 1-2 parts of lithium bromide, 5-10 parts of tea-seed oil, methyl glycol fatty acid ester 3-
7 parts, 300-350 parts of water, its preparation method are that each raw material is well mixed.
It is described to remove old agent temperature in use for 42-48 DEG C.
Calcium hydroxide addition in step (2) is 0.015kg, and glacial acetic acid addition is 0.015kg.
Also include 0.003kg sodium chloride in every kg ethanol solutions in step (2).
The beneficial effects of the invention are as follows：This method can be recovered to mould rattan toughness, greatly enhance its pulling force, and can take off modeling rattan
Surface aging layer but do not interfere with modeling rattan effect, cradle need not be dismantled during processing, technique is greatly simplified, shaking after processing
Basket bright color, cradle surface adhesion force is low.
Embodiment
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below
Specific embodiment is closed, the present invention is expanded on further.
Embodiment 1
A kind of renovation method of outmoded modeling rattan cradle, mainly handles the cradle for moulding rattan plaited, is shaken without handling
The irony support frame of basket, specifically includes following steps：
(1) will make the well-worn but cradle that does not damage is that 320-360nm ultraviolets irradiate 10 minutes with wavelength, so
Cradle is placed in modified soak immersion treatment 4-20 hours afterwards；
The modified soak is made up of following raw material：
8 parts of guar gum ether, 8 parts of L-arabinose, 8 parts of d- corydalines, golden larch furans sour 9 parts, Norhyoscyamine 3.6
Part, 1.5 parts of sodium chloride, 1.5 parts of DDAO, 165 parts of water, its preparation method are to mix each raw material then
Stirred in mixer, mixing speed is 2500r/mim, whipping temp is 50-60 DEG C, 10 minutes time；
(2) it is again that 220-280nm ultraviolets irradiate 10 minutes with wavelength to pull cradle out, and cradle then is immersed in into ethanol again
In solution, calcium hydroxide is added in one week backward ethanol solution, is added by every 1kg ethanol on the basis of 0.015kg calcium hydroxides, Zai Guoyi
Zhou Houxiang ethanol solutions add glacial acetic acid, are added by every 1kg ethanol on the basis of 0.015kg glacial acetic acid；
(3) take out cradle and be irradiated with infrared ray, cradle is then subjected to immersion 24 hours with old agent is removed；
(4) cradle is cleaned with purified water, and cradle purged with clean air；
(5) it is placed in after cradle is dried in 80-90 DEG C of greenhouse, oxygen is blasted into greenhouse within each 10 minutes, according to temperature
Room area, every 1 cubic meter volume blasts 0.01 cubic metre of oxygen.
Except old agent is made up of following raw material：15.5 parts of butyl butyrate, 7 parts of acetyl CoA carboxylase, 7 parts of octadecyl alcolol,
2 parts of coptisine, 1.5 parts of paraffin, 1.5 parts of lithium bromide, 8 parts of tea-seed oil, 5 parts of methyl glycol fatty acid ester, 320 parts of water, its preparation side
Method is that each raw material is well mixed, except old agent temperature in use is 42-48 DEG C.
Also include 0.003kg sodium chloride in every kg ethanol solutions in step (2).
Embodiment 2
A kind of renovation method of outmoded modeling rattan cradle, mainly handles the cradle for moulding rattan plaited, is shaken without handling
The irony support frame of basket, specifically includes following steps：
(1) will make the well-worn but cradle that does not damage is that 320-360nm ultraviolets irradiate 10 minutes with wavelength, so
Cradle is placed in modified soak immersion treatment 4-20 hours afterwards；
Modified soak is made up of following raw material：
5 parts of guar gum ether, 5 parts of L-arabinose, 5 parts of d- corydalines, golden larch furans sour 8 parts, Norhyoscyamine 3.5
Part, 1 part of sodium chloride, 1 part of DDAO, 150 parts of water, its preparation method are that each raw material is mixed and then stirred
Mix in machine and stir, mixing speed is 2500r/mim, whipping temp is 50-60 DEG C, 10 minutes time；
(2) it is again that 220-280nm ultraviolets irradiate 10 minutes with wavelength to pull cradle out, and cradle then is immersed in into ethanol again
In solution, calcium hydroxide is added in one week backward ethanol solution, is added by every 1kg ethanol on the basis of 0.01kg calcium hydroxides, Zai Guoyi
Zhou Houxiang ethanol solutions add glacial acetic acid, are added by every 1kg ethanol on the basis of 0.01kg glacial acetic acid；
(3) take out cradle and be irradiated with infrared ray, cradle is then subjected to immersion 24 hours with old agent is removed；
(4) cradle is cleaned with purified water, and cradle purged with clean air；
(5) it is placed in after cradle is dried in 80-90 DEG C of greenhouse, oxygen is blasted into greenhouse within each 10 minutes, according to temperature
Room area, every 1 cubic meter volume blasts 0.01 cubic metre of oxygen.
Except old agent is made up of following raw material：15 parts of butyl butyrate, 6 parts of acetyl CoA carboxylase, 6 parts of octadecyl alcolol, Huang
Connect 0.5 part of alkali, 1 part of paraffin, 1 part of lithium bromide, 5 parts of tea-seed oil, 3 parts of methyl glycol fatty acid ester, 300 parts of water, its preparation method is
Each raw material is well mixed, except old agent temperature in use is 42-48 DEG C.
Also include 0.003kg sodium chloride in every kg ethanol solutions in step (2).
Embodiment 3
A kind of renovation method of outmoded modeling rattan cradle, mainly handles the cradle for moulding rattan plaited, is shaken without handling
The irony support frame of basket, specifically includes following steps：
(1) will make the well-worn but cradle that does not damage is that 320-360nm ultraviolets irradiate 10 minutes with wavelength, so
Cradle is placed in modified soak immersion treatment 4-20 hours afterwards；
The modified soak is made up of following raw material：
10 parts of guar gum ether, 10 parts of L-arabinose, 10 parts of d- corydalines, golden larch furans sour 9.5 parts, demethyl henbane
3.8 parts of alkali, 2 parts of sodium chloride, 2 parts of DDAO, 180 parts of water, its preparation method are that each raw material is mixed into right
Stirred afterwards in mixer, mixing speed is 2500r/mim, whipping temp is 50-60 DEG C, 10 minutes time；
(2) it is again that 220-280nm ultraviolets irradiate 10 minutes with wavelength to pull cradle out, and cradle then is immersed in into ethanol again
In solution, calcium hydroxide is added in one week backward ethanol solution, is added by every 1kg ethanol on the basis of 0.02kg calcium hydroxides, Zai Guoyi
Zhou Houxiang ethanol solutions add glacial acetic acid, are added by every 1kg ethanol on the basis of 0.02kg glacial acetic acid；
(3) take out cradle and be irradiated with infrared ray, cradle is then subjected to immersion 24 hours with old agent is removed；
(4) cradle is cleaned with purified water, and cradle purged with clean air；
(5) it is placed in after cradle is dried in 80-90 DEG C of greenhouse, oxygen is blasted into greenhouse within each 10 minutes, according to temperature
Room area, every 1 cubic meter volume blasts 0.01 cubic metre of oxygen.
Except old agent is made up of following raw material：16 parts of butyl butyrate, 8 parts of acetyl CoA carboxylase, 8 parts of octadecyl alcolol, Huang
Connect 3.5 parts of alkali, 2 parts of paraffin, 2 parts of lithium bromide, 10 parts of tea-seed oil, 7 parts of methyl glycol fatty acid ester, 350 parts of water, its preparation method is
Each raw material is well mixed, and age resistor temperature in use is 42-48 DEG C.
Also include 0.003kg sodium chloride in every kg ethanol solutions in step (2).
Experiment
The cradle that embodiment 1,2,3 is renovated is tested, and result of the test is as follows：
Experiment is proved：Renovation method of the present invention not only can fully take off modeling rattan surface aging skin, and can also further carry
The tensile capacity of high-plastic rattan.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (6)
1. a kind of renovation method of outmoded modeling rattan cradle, it is characterised in that mainly handle the cradle for moulding rattan plaited, and
The irony support frame of cradle is not handled, specifically includes following steps：
(1) will make the well-worn but cradle that does not damage is that 320-360nm ultraviolets irradiate 10 minutes with wavelength, then will
Cradle is placed in modified soak immersion treatment 4-20 hours；
The modified soak is made up of following raw material：
5-10 parts of guar gum ether, 5-10 parts of L-arabinose, 5-10 parts of d- corydalines, 8-9.5 parts of golden larch furans acid, demethyl
3.5-3.8 parts of hyoscyamine, 1-2 parts of sodium chloride, 1-2 parts of DDAO, 150-180 parts of water, its preparation method
It is that each raw material is mixed and then stirred in mixer, mixing speed is 2500r/mim, whipping temp is 50-60 DEG C, when
Between 10 minutes；
(2) it is again that 220-280nm ultraviolets irradiate 10 minutes with wavelength to pull cradle out, and cradle then is immersed in into ethanol solution again
In, calcium hydroxide is added in one week backward ethanol solution, is added by every 1kg ethanol on the basis of 0.01-0.02kg calcium hydroxides, Zai Guoyi
Zhou Houxiang ethanol solutions add glacial acetic acid, are added by every 1kg ethanol on the basis of 0.01-0.02kg glacial acetic acid；
(3) take out cradle and be irradiated with infrared ray, cradle is then subjected to immersion 24 hours with old agent is removed；
(4) cradle is cleaned with purified water, and cradle purged with clean air；
(5) it is placed in after cradle is dried in 80-90 DEG C of greenhouse, oxygen is blasted into greenhouse within each 10 minutes, according to greenhouse face
Product, every 1 cubic meter volume blasts 0.01 cubic metre of oxygen.
2. a kind of renovation method of outmoded modeling rattan cradle according to claim 1, it is characterised in that the modified soak
It is made up of following raw material：8 parts of guar gum ether, 8 parts of L-arabinose, 8 parts of d- corydalines, golden larch furans are sour 9 parts, go
3.6 parts of methyl hyoscyamine, 1.5 parts of sodium chloride, 1.5 parts of DDAO, 165 parts of water.
3. it is according to claim 1 it is a kind of it is outmoded modeling rattan cradle renovation method, it is characterised in that it is described except old agent by with
Lower raw material is made：15-16 parts of butyl butyrate, 6-8 parts of acetyl CoA carboxylase, 6-8 parts of octadecyl alcolol, coptisine 0.5-3.5
Part, 1-2 parts of paraffin, 1-2 parts of lithium bromide, 5-10 parts of tea-seed oil, 3-7 parts of methyl glycol fatty acid ester, 300-350 parts of water, it is prepared
Method is that each raw material is well mixed.
4. the renovation method of a kind of outmoded modeling rattan cradle according to claim 3, it is characterised in that described except old agent is used
Temperature is 42-48 DEG C.
5. a kind of renovation method of outmoded modeling rattan cradle according to claim 1, it is characterised in that disappearing in step (2)
Lime adding amount is 0.015kg, and glacial acetic acid addition is 0.015kg.
6. according to claim 1 or 5 it is a kind of it is outmoded modeling rattan cradle renovation method, it is characterised in that in step (2)
Also include 0.003kg sodium chloride in per kg ethanol solutions.