CN107097582A - A kind of color spot sweep-out method of old modeling rattan - Google Patents
A kind of color spot sweep-out method of old modeling rattan Download PDFInfo
- Publication number
- CN107097582A CN107097582A CN201710325249.3A CN201710325249A CN107097582A CN 107097582 A CN107097582 A CN 107097582A CN 201710325249 A CN201710325249 A CN 201710325249A CN 107097582 A CN107097582 A CN 107097582A
- Authority
- CN
- China
- Prior art keywords
- parts
- rattan
- modeling
- modeling rattan
- old
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of color spot sweep-out method of old modeling rattan, specifically includes following steps：By the old modeling rattan drawing of recovery, drawing terminates to be soaked with soak again；Pull modeling rattan out and soaked with concentration for 4.1% potassium hydroxide solution；Pull modeling rattan out and be washed with deionized water net, then covered with alum powder and be placed in depositing in the environment that temperature is 25 30 DEG C, relative humidity is 50% 60%, cleaned after one month with purified water by rattan is moulded, then again with clearing bath immersion modeling rattan 24 hours；Pull modeling rattan out and mould rattan surface with honey spread, dried 35 days after modeling rattan is placed under sunlight after honey drying, then modeling rattan is placed in middle liquid medicine and decocted 2 hours, modeling rattan is pulled out and cleans, dries.The inventive method can remove the corrosion scar on modeling rattan surface, while the blackspot inside removing modeling rattan that can be deep, will not produce burn, and can greatly improve the pliability of modeling rattan so that modeling rattan antioxygenic property and anti-ultraviolet property are greatly improved to modeling rattan.
Description
Technical field
The present invention relates to modeling rattan processing technology field, and in particular to a kind of color spot sweep-out method of old modeling rattan.
Background technology
Rattan plaited typically by beat rattan (pruning the knot on rattan), pick rattan, wash rattan, shine rattan, stubborn rattan, draw rattan (digging rattan), cut rattan,
More than ten procedures such as bleach, dye, weaving, painting.Rattan plaited is main using rattan branch, rattan core or bamboo as skeleton, then with rattan peel or
Tender rattan core braiding is formed, the characteristics of giving full play to rattan softness, be not easily broken.
On color, mostly using the light yellow of former rattan, or processing, bleaching are white, ivory white, it appears soft elegance,
Some are then equipped with coffee color, brown etc..Rattan furniture is using thick rattan as skeleton, through following closely frame, then with rattan peel, the braiding of rattan core
Into finally painting or paint.
Rattan-weaved products is increasingly liked because of its elegant, simple outward appearance by masses.It is to utilize plastic extrusion to mould rattan
The plastic products for the similar Rattan-shaped being made.Due to natural rattan plaited material, supply falls short of demand, so many products are using modeling now
The rattan imitating of rattan etc carries out being compiled into rattan woven ware imitation product to meet the market demand.But modeling rattan article use time it is long it is rear just
Can be oxidized, its surface occurs that color spot and corrosion spot seem very unsightly, thus many consumers used in modeling rattan it is long
Just directly throw away and be recovered afterwards.The old modeling rattan reclaimed at present is mostly directly taken as waste plastics and melted to mould again, so drops
The utilizing status of low modeling rattan, and extrusion molding increases production cost again.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of color spot sweep-out method of old modeling rattan.
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of color spot sweep-out method of old modeling rattan, specifically includes following steps：
(1) the old modeling rattan of recovery is subjected to drawing to improve the crimpness of modeling rattan, drawing terminates to soak 4- with soak again
10 hours, then pull modeling rattan out and be placed in exposure 1 day under the sun, then soaked 4-10 hours with soak, immersion is direct after terminating
Hot blow is carried out 10 minutes to modeling rattan with 100-120 DEG C of overheated steam；
The soak is made up of following raw material：
1-2 parts of isohomoarbutin, 1-2 parts of guiol, 4-5 parts of sorbitan carboxylic esterses, psoralen 3.5-4.5
Part, 2.5-4.5 parts of isoquercitrin, 5-8 parts of Ovum Anas domestica yolk, 1-2 parts of salicoside, 200-260 parts of water, its preparation method is by each raw material
Then mixing stirs in mixer, and mixing speed is 2500r/mim, and whipping temp is 50-60 DEG C, 10 minutes time；
(2) pull modeling rattan out and soaked with concentration for 4.1% potassium hydroxide solution, added in 3 days backward potassium hydroxide solutions
Enter sulphur, added by every kg potassium hydroxide solutions on the basis of 0.01-0.04kg sulphur, added in one week backward potassium hydroxide solution
The tincture of iodine, is added on the basis of the 0.01-0.04kg tincture of iodine by every 1kg potassium hydroxide solutions；
(3) pull out modeling rattan and be washed with deionized water it is net, then with alum powder covering be placed in temperature be 25-30 DEG C, it is relative
Humidity is cleaned after one month to be deposited in 50%-60% environment with purified water by rattan is moulded, then again with clearing bath immersion modeling rattan
24 hours；
(4) pull modeling rattan out and mould rattan surface with honey spread, 3-5 is dried after modeling rattan is placed under sunlight after honey drying
My god, then modeling rattan is placed in middle liquid medicine and decocted 2 hours, modeling rattan is pulled out and cleans, dries.
The soak is made up of following raw material：1.5 parts of isohomoarbutin, 1.5 parts of guiol, sorbierite
4.5 parts of acid anhydride fatty acid ester, 4 parts of psoralen, 3.5 parts of isoquercitrin, 6 parts of Ovum Anas domestica yolk, 1.5 parts of salicoside, 230 parts of water.
The clearing bath is made up of following raw material：8-10 parts of saikoside-C, 6-8 parts of acetyl CoA carboxylase,
8-12 parts of invertase, 2-3 parts of 2,5- orcins, 1.5-4 parts of methyleugenol, 5-6 parts of apple vinegar, extract solution from aloe
12-15 parts, liquor-saturated ester 1-2 parts of cinnamic acid epoxy cassia bark, 320-340 parts of water, its preparation method is that each raw material is well mixed.
Sulphur addition in step (2) is 0.03kg, and tincture of iodine addition is 0.03kg.
Also include 0.001kg hydrofluoric acid, 0.001kg sodium chloride in every kg honey in step (4).
The beneficial effects of the invention are as follows：This method can remove the corrosion scar on modeling rattan surface, while removing modeling that can be deep
Blackspot inside rattan, will not produce burn, and can greatly improve the pliability of modeling rattan so that modeling rattan antioxygenic property to modeling rattan
Greatly improved with anti-ultraviolet property.
Embodiment
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below
Specific embodiment is closed, the present invention is expanded on further.
Embodiment 1
A kind of color spot sweep-out method of old modeling rattan, specifically includes following steps：
(1) the old modeling rattan of recovery is subjected to drawing to improve the crimpness of modeling rattan, drawing terminates to soak 4- with soak again
10 hours, then pull modeling rattan out and be placed in exposure 1 day under the sun, then soaked 4-10 hours with soak, immersion is direct after terminating
Hot blow is carried out 10 minutes to modeling rattan with 100-120 DEG C of overheated steam；
Soak is made up of following raw material：
It is 1.5 parts of isohomoarbutin, 1.5 parts of guiol, 4.5 parts of sorbitan carboxylic esterses, 4 parts of psoralen, different
3.5 parts of quercitin, 6 parts of Ovum Anas domestica yolk, 1.5 parts of salicoside, 230 parts of water, its preparation method are mixed each raw material and then in stirring
Stirred in machine, mixing speed is 2500r/mim, whipping temp is 50-60 DEG C, 10 minutes time；
(2) pull modeling rattan out and soaked with concentration for 4.1% potassium hydroxide solution, added in 3 days backward potassium hydroxide solutions
Enter sulphur, added by every kg potassium hydroxide solutions on the basis of 0.03kg sulphur, the tincture of iodine is added in one week backward potassium hydroxide solution,
Added by every 1kg potassium hydroxide solutions on the basis of the 0.03kg tincture of iodine；
(3) pull out modeling rattan and be washed with deionized water it is net, then with alum powder covering be placed in temperature be 25-30 DEG C, it is relative
Humidity is cleaned after one month to be deposited in 50%-60% environment with purified water by rattan is moulded, then again with clearing bath immersion modeling rattan
24 hours；
(4) pull modeling rattan out and mould rattan surface with honey spread, 3-5 is dried after modeling rattan is placed under sunlight after honey drying
My god, then modeling rattan is placed in middle liquid medicine and decocted 2 hours, modeling rattan is pulled out and cleans, dries.
Clearing bath is made up of following raw material：8-10 parts of saikoside-C, 6-8 parts of acetyl CoA carboxylase, sucrose
8-12 parts of enzyme, 2-3 parts of 2,5- orcins, 1.5-4 parts of methyleugenol, 5-6 parts of apple vinegar, extract solution from aloe 12-15
Part, liquor-saturated ester 1-2 parts of cinnamic acid epoxy cassia bark, 320-340 parts of water, its preparation method are that each raw material is well mixed.
Also include 0.001kg hydrofluoric acid, 0.001kg sodium chloride in every kg honey in step (4).
Embodiment 2
A kind of color spot sweep-out method of old modeling rattan, specifically includes following steps：
(1) the old modeling rattan of recovery is subjected to drawing to improve the crimpness of modeling rattan, drawing terminates to soak 4- with soak again
10 hours, then pull modeling rattan out and be placed in exposure 1 day under the sun, then soaked 4-10 hours with soak, immersion is direct after terminating
Hot blow is carried out 10 minutes to modeling rattan with 100-120 DEG C of overheated steam；
Soak is made up of following raw material：
1 part of isohomoarbutin, 1 part of guiol, 4 parts of sorbitan carboxylic esterses, 3.5 parts of psoralen, isoquercitrin
2.5 parts of glycosides, 5 parts of Ovum Anas domestica yolk, 1 part of salicoside, 200 parts of water, its preparation method are to mix each raw material and then stirred in mixer
Mix uniform, mixing speed is 2500r/mim, whipping temp is 50-60 DEG C, 10 minutes time；
(2) pull modeling rattan out and soaked with concentration for 4.1% potassium hydroxide solution, added in 3 days backward potassium hydroxide solutions
Enter sulphur, added by every kg potassium hydroxide solutions on the basis of 0.01kg sulphur, the tincture of iodine is added in one week backward potassium hydroxide solution,
Added by every 1kg potassium hydroxide solutions on the basis of the 0.01kg tincture of iodine；
(3) pull out modeling rattan and be washed with deionized water it is net, then with alum powder covering be placed in temperature be 25-30 DEG C, it is relative
Humidity is cleaned after one month to be deposited in 50%-60% environment with purified water by rattan is moulded, then again with clearing bath immersion modeling rattan
24 hours；
(4) pull modeling rattan out and mould rattan surface with honey spread, 3-5 is dried after modeling rattan is placed under sunlight after honey drying
My god, then modeling rattan is placed in middle liquid medicine and decocted 2 hours, modeling rattan is pulled out and cleans, dries.
Clearing bath is made up of following raw material：8-10 parts of saikoside-C, 6-8 parts of acetyl CoA carboxylase, sucrose
8-12 parts of enzyme, 2-3 parts of 2,5- orcins, 1.5-4 parts of methyleugenol, 5-6 parts of apple vinegar, extract solution from aloe 12-15
Part, liquor-saturated ester 1-2 parts of cinnamic acid epoxy cassia bark, 320-340 parts of water, its preparation method are that each raw material is well mixed.
Also include 0.001kg hydrofluoric acid, 0.001kg sodium chloride in every kg honey in step (4).
Embodiment 3
A kind of color spot sweep-out method of old modeling rattan, specifically includes following steps：
(1) the old modeling rattan of recovery is subjected to drawing to improve the crimpness of modeling rattan, drawing terminates to soak 4- with soak again
10 hours, then pull modeling rattan out and be placed in exposure 1 day under the sun, then soaked 4-10 hours with soak, immersion is direct after terminating
Hot blow is carried out 10 minutes to modeling rattan with 100-120 DEG C of overheated steam；
Soak is made up of following raw material：
2 parts of isohomoarbutin, 2 parts of guiol, 5 parts of sorbitan carboxylic esterses, 4.5 parts of psoralen, isoquercitrin
4.5 parts of glycosides, 8 parts of Ovum Anas domestica yolk, 2 parts of salicoside, 260 parts of water, its preparation method are to mix each raw material and then stirred in mixer
Mix uniform, mixing speed is 2500r/mim, whipping temp is 50-60 DEG C, 10 minutes time；
(2) pull modeling rattan out and soaked with concentration for 4.1% potassium hydroxide solution, added in 3 days backward potassium hydroxide solutions
Enter sulphur, added by every kg potassium hydroxide solutions on the basis of 0.04kg sulphur, the tincture of iodine is added in one week backward potassium hydroxide solution,
Added by every 1kg potassium hydroxide solutions on the basis of the 0.04kg tincture of iodine；
(3) pull out modeling rattan and be washed with deionized water it is net, then with alum powder covering be placed in temperature be 25-30 DEG C, it is relative
Humidity is cleaned after one month to be deposited in 50%-60% environment with purified water by rattan is moulded, then again with clearing bath immersion modeling rattan
24 hours；
(4) pull modeling rattan out and mould rattan surface with honey spread, 3-5 is dried after modeling rattan is placed under sunlight after honey drying
My god, then modeling rattan is placed in middle liquid medicine and decocted 2 hours, modeling rattan is pulled out and cleans, dries.
Clearing bath is made up of following raw material：10 parts of saikoside-C, 8 parts of acetyl CoA carboxylase, invertase 12
Part, 3 parts of 2,5- orcins, 4 parts of methyleugenol, 6 parts of apple vinegar, 15 parts of extract solution from aloe, cinnamic acid epoxy cassia bark
Liquor-saturated 2 parts of ester, 340 parts of water, its preparation method are that each raw material is well mixed.
Also include 0.001kg hydrofluoric acid, 0.001kg sodium chloride in every kg honey in step (4).
Experiment
The modeling rattan of the processing of embodiment 1,2,3 is tested, result of the test is as follows：
Experiment is proved：Processing method of the present invention causes the tensile strength and flexural strength of moulding rattan to greatly promote.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (5)
1. a kind of color spot sweep-out method of old modeling rattan, it is characterised in that specifically include following steps：
(1) the old modeling rattan of recovery is subjected to drawing to improve the crimpness of modeling rattan, drawing terminates again small with soak immersion 4-10
When, then pull modeling rattan out and be placed in exposure 1 day under the sun, then soaked 4-10 hours with soak, immersion is directly used after terminating
100-120 DEG C of overheated steam carries out hot blow 10 minutes to modeling rattan；
The soak is made up of following raw material：
1-2 parts of isohomoarbutin, 1-2 parts of guiol, 4-5 parts of sorbitan carboxylic esterses, 3.5-4.5 parts of psoralen,
2.5-4.5 parts of isoquercitrin, 5-8 parts of Ovum Anas domestica yolk, 1-2 parts of salicoside, 200-260 parts of water, its preparation method is to mix each raw material
Close and then stirred in mixer, mixing speed is 2500r/mim, whipping temp is 50-60 DEG C, 10 minutes time；
(2) pull modeling rattan out and soaked with concentration for 4.1% potassium hydroxide solution, sulphur is added in 3 days backward potassium hydroxide solutions
Sulphur, is added on the basis of 0.01-0.04kg sulphur by every kg potassium hydroxide solutions, iodine is added in one week backward potassium hydroxide solution
Wine, is added on the basis of the 0.01-0.04kg tincture of iodine by every 1kg potassium hydroxide solutions；
(3) pull modeling rattan out and be washed with deionized water only, it is 25-30 DEG C, relative humidity to be then placed in temperature with alum powder covering
To be deposited in 50%-60% environment, cleaned after one month with purified water by rattan is moulded, it is then small with clearing bath immersion modeling rattan 24 again
When；
(4) pull modeling rattan out and mould rattan surface with honey spread, after modeling rattan is placed in into drying 3-5 days under sunlight after honey drying, so
Modeling rattan is placed in middle liquid medicine afterwards and decocted 2 hours, modeling rattan is pulled out and cleans, dries.
2. the color spot sweep-out method of a kind of old modeling rattan according to claim 1, it is characterised in that the soak is by following
Raw material is made：1.5 parts of isohomoarbutin, 1.5 parts of guiol, 4.5 parts of sorbitan carboxylic esterses, psoralen
4 parts, 3.5 parts of isoquercitrin, 6 parts of Ovum Anas domestica yolk, 1.5 parts of salicoside, 230 parts of water.
3. the color spot sweep-out method of a kind of old modeling rattan according to claim 1, it is characterised in that the clearing bath is by following
Raw material is made：8-10 parts of saikoside-C, 6-8 parts of acetyl CoA carboxylase, 8-12 parts of invertase, 2,5- dihydroxy first
2-3 parts of benzene, 1.5-4 parts of methyleugenol, 5-6 parts of apple vinegar, 12-15 parts of extract solution from aloe, the liquor-saturated ester of cinnamic acid epoxy cassia bark
1-2 parts, 320-340 parts of water, its preparation method are that each raw material is well mixed.
4. a kind of color spot sweep-out method of old modeling rattan according to claim 1, it is characterised in that the sulphur in step (2)
Addition is 0.03kg, and tincture of iodine addition is 0.03kg.
5. a kind of color spot sweep-out method of old modeling rattan according to claim 1, it is characterised in that every kg in step (4)
Also include 0.001kg hydrofluoric acid, 0.001kg sodium chloride in honey.