CN107089827A - 无机宽波远红外复合环保材料 - Google Patents

无机宽波远红外复合环保材料 Download PDF

Info

Publication number
CN107089827A
CN107089827A CN201710245397.4A CN201710245397A CN107089827A CN 107089827 A CN107089827 A CN 107089827A CN 201710245397 A CN201710245397 A CN 201710245397A CN 107089827 A CN107089827 A CN 107089827A
Authority
CN
China
Prior art keywords
far infrared
weight
tourmaline
parts
machine width
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710245397.4A
Other languages
English (en)
Inventor
刘华文
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201710245397.4A priority Critical patent/CN107089827A/zh
Publication of CN107089827A publication Critical patent/CN107089827A/zh
Pending legal-status Critical Current

Abstract

本发明属于远红外复合材料,具体地是一种无机宽波远红外复合环保材料。现有的远红外材料的缺点是：材料单一、远红外波段狭窄，功能局限性大；有的复合材料配方不合理，含有对人体有害成分。本发明由和田玉25重量份、泗水砭石25重量份、磁石25重量份、托玛琳25重量份组成。制备步骤为：将各原料分别粉碎至6000目，混合、加适量水搅拌均匀；压制成型；常温晾干；高温1000℃煅烧24小时；常温冷却。压制的型状为粉状、粒状、片状、圆柱状。本发明优点是：选用的材料全部为中药材，无毒；远红外波段宽、功能多、应用广泛；能持久发射宽波远红外线；一次使用，长期受益，使用成本低。

Description

无机宽波远红外复合环保材料
技术领域
本发明属于远红外复合材料,具体地是一种无机宽波远红外复合环保材料。
背景技术
远红外线有较强的渗透力和辐射力，具有显著的温控效应和共振效应，易被物体吸收并转化为物体的内能。现有远红外线技术广泛应用于环境保护、农业、交通、机械、电器、电子、制衣纺织、建筑材料、医学、人民生活等技术领域。远红外线被人体吸收后，可使体内水分子产生共振，使水分子活化，增强其分子间的结合力，从而活化蛋白质等生物大分子，使生物体细胞处于最高振动能级。可将远红外热能传递到人体皮下较深的部分，产生的温热由内向外散发，使毛细血管扩张，促进血液循环，强化各组织之间的新陈代谢，增加组织的再生能力，提高机体的免疫能力，调节精神状态，从而起到医疗保健的作用。
产生远红外线的主要方法是选择热交换能力强、能放射特定波长远红外线的材料。现有发生远红外线的材料有：生物炭、碳纤维制品、电气石、远红外陶瓷、玉石、金属氧化物及碳化硅等等。
现有的远红外材料的缺点是：1.材料单一、远红外波段狭窄，功能局限性大；2.有的复合材料配方不合理，含有对人体有害成分，长期使用对人造成伤害。本发明选用多种纯天然无毒材料，利用对撞超细粉加工技术，制成无机宽波远红外复合环保材料。本发明利用多种天然材料的互补作用，克服了单一材料的局限性，激发了材料的内在能量，获得远红外波段宽、功能多、应用广泛、性能优良、能持久发射宽波远红外的复合环保材料。本发明复合环保材料具有一次使用，长期受益的效果。
本发明选用的材料全部为中药材，传统中医将和田玉、泗水砭石、磁石、托玛琳等作为矿物质药材治疗人体疾病。本发明复合环保材料根据中医理论和方法，除了应用于人体医学之外，首次将上述四种中药材经过粉碎、混合、煅烧处理后用于水、土壤、空气的处理；应用于工业、农业、环境保护、交通等领域，具有保护环境、改良土壤、提高农作物产量和品质、节约能源等效果。
经广泛查阅专利文献和国内外公开出版物，均未见有与本发明相同的技术方案，未见有与本发明原料和配方相同的远红外复合材料；本发明具有新颖性、创造性；本发明广泛应用于工业、农业、环境保护、医学等领域，具有广泛的实用性。
发明内容
本发明的目的是：提供一种远红外波段宽、功能多、适用范围广、性能优良持久的无机宽波远红外复合环保材料。
本发明的目的是这样实现的：
一种无机宽波远红外复合环保材料，由下列重量比物质组成：
一种无机宽波远红外复合环保材料，制备步骤如下：
(1)准确称取和田玉、泗水砭石、磁石、托玛琳各25重量份；
(2)将和田玉、泗水砭石、磁石、托玛琳分别粉碎至6000目；
(3)将粉碎后的和田玉、泗水砭石、磁石、托玛琳粉混合、加适量水搅拌均匀；
(4)将步骤(3)产物压制成型；
(5)将步骤(4)产物常温晾干；
(6)将步骤(5)产物高温1000℃煅烧24小时；
(7)将步骤(6)产物常温冷却。
步骤(4)压制的型状为粒状、片状、圆柱状。
本发明的要点是：
1.和田玉、泗水砭石、磁石、托玛琳四种原料全部为中药材，人体医学使用安全。
2.和田玉、泗水砭石、磁石、托玛琳四种原料同等重量，混合后产生特性互补，互相激发，各自独特的功能得到充分的发挥，产生了出人意料的效果。
3.将四种原料分别粉碎、然后混合均匀、压制成型、煅烧，冷却制成粉状、粒状、片状、圆柱状等不同形状，可广泛应用于多种不同技术领域。
本发明无机宽波远红外复合环保材料的原料具有如下特点：
和田玉无毒、具有热容量大、辐射散热好的物理特性，可减少血液耗氧量，使血液中的酶分子不变性而保持大活性，加强代谢提高各种生理机能。和田玉的特殊分子结构能发射人体吸收的远红外电磁波，波长8—15微米，与人体共振吸收。和田玉同时含有多种对人体有益的微量元素，粉碎后会产生对人体有益的光电效应。和田玉受热后反应程度强烈，负离子释放速度快，负离子数量增多。
泗水砭石是一种微晶灰岩矿物质，无毒，是一种可治病的石头。砭石无放射性；有奇异的能量场，作用于人体可产生红外热像并可循经而行；砭石接触人体表皮，在“微循环检测仪”监视器的屏幕上，可清楚看到小血管和毛细血管中的血液加快流动的状态；砭石含有锶、氧化钙、氧化硅、氧化钠、铬、锰等三十几种对人体有益的微量元素，其中锶的含量甚高；砭石可产生极远红外辐射，频带宽，远红外频率可达范围为7—20微米。砭石摩擦后，可以发出2-200万赫兹的超声波脉冲，产生超声波脉冲次数达3708次，频率范围可达2—40万赫兹，是所有材质之首。砭石摩擦后，反应强烈，电磁波增强，负氧离子增多，尤其适用于在风扇叶片上使用,清洁空气效果好，对人体健康有促进作用。
磁石辛、咸、平、无毒，是地球内部磁场产生的天然铁磁性矿物，密度5.16--5.18g/cm3，具强磁性，性脆，无臭，无味。磁石能产生电子运动，围绕原子核运动的电子产生电流，电流产生磁场，磁场中原子自动的排列有序，在其电子电流和磁场运动的作用下，大大激发其它材料的内在能量，使其它材料的远红外、负离子、电磁波、超声波等功能得到极大的放大，产生奇特的效应。磁石能引起人体内水分子共振，使水分子活性化，变成独立水分子。磁化后的水具有抗疲劳、抗幅射、抗衰老、提高人体免疫力的作用，达到调理和保健的功效。饮用磁性水可以提高人体细胞含氧量、恢复活力、抗疲劳、抗幅射；舒筋活血，延缓衰老；促进人体微循环系统、促进新陈代谢；润肤美容；减轻颈椎痛；预防因尿酸过高而引起的骨络关节痛等作用。
托玛琳又称碧玺、电气石，无毒，为硅酸盐类-硼硅酸盐物质，呈全透明、半透明状。化学式为Na(Mg,Fe,Mn,Li,Al)3Al6[Si6O18][BO3]3(OH,F)4，具有压电效应。托玛琳含有多种人类必须的微量元素，是极佳的矿物质来源。托玛琳具有永电性，能产生大量负氧离子，其远红外波长4—14微米，发射力高达88％，可永久产生微弱电流，释放大量负离子，起到调节人体离子平衡作用。托玛琳受热后特征体现更为强烈，负离子释放速度快，负离子数量增多。
本发明与现有同类产品相比，具有如下实质性不同：
1.四种原料全部为中药材；
2.四种原料重量比相等；
3.原料特性互补，如和田玉、托玛琳受热后反应程度强烈，负离子释放速度快，负离子数量增多；砭石摩擦后，电磁波增强，负氧离子增多。特性互补的结果，使本发明复合材料应用广泛。
本发明四种原料重量比相等，经对撞超细粉加工成粉后混合，各自独特的功能得到充分的发挥，同时产生特性互补，互相激发，产生了出人意料的效果。经检测每立方厘米含有400个负离子；远红外波段4—16微米，达到了人体最适宜的生命之光6—14的波段。经多年在多领域应用，均取得良好的效果。
本发明也可根据需要,在和田玉、泗水砭石、磁石、托玛琳四种材料的基础上,增加同等重量份的高岭土,使压制成型更方便。高岭土又名瓷土，成分为:SiO246.51％，Al2O339.54％，H2O 13.95％,熔点：1780℃。大部分带有白色丝绢状的光泽，是陶瓷的主要原料。瓷土颗粒表面具有微细孔隙，有吸附性。本发明中瓷土主要起粘结和填充料的作用，将材料粘结成型，并且增大材料的表面积。
本发明根据需要，也可制成粉状，其方法是将煅烧过的产品再次粉碎至6000目。
本发明的优点是：
1.选用的材料全部为中药材，无毒。
2.远红外波段宽、功能多、应用广泛。
3.本发明复合材料能持久发射宽波远红外线。
4.一次使用，长期受益，使用成本低。
具体实施方式
本发明已经多年在不同领域应用，效果显著。下面通过具体实施例对本发明做进一步说明。
实施例一：
取和田玉、泗水砭石、磁石、托玛琳、各100公斤，分别用对撞机粉碎至6000目，然后将其混合、加入适量水搅拌均匀，压制成直径0.5厘米的圆球，1000℃煅烧24小时，常温冷却后，放入水中。2小时后检测Ph值7.8，氯为0，矿物质含量提高10％。
实施例二：
和田玉、泗水砭石、磁石、托玛琳各5公斤，分别用对撞机粉碎至6000目，然后将其混合、1000度煅烧24小时；再次粉碎至6000目后，加入医用脱敏胶搅拌均匀，喷敷在立式风扇的叶片两面。夏天风扇工作，室内空气每立方厘米负氧离子1000个，空气清新。
实施例三：
和田玉、泗水砭石、磁石、托玛琳各50公斤，分别用对撞机粉碎至6000目，然后将其混合、加入适量水搅拌均匀，压制成直径0.5厘米、高度0.5厘米的圆柱，1000℃煅烧24小时，常温冷却后。均匀撒入菜地中，三个月后土壤农药残留物和铅、镉、汞、砷为零，土壤恢复原生态，蔬菜产量提高15％。
上述实施例仅为本发明的优选例，并不用来限制本发明，凡在本发明的原则之内，所做的任何修改和变化，均在本发明的保护范围之内。

Claims (3)

1.一种无机宽波远红外复合环保材料，由下列重量比物质组成：
。
2.一种无机宽波远红外复合环保材料，制备步骤如下：
(1)准确称取和田玉、泗水砭石、磁石、托玛琳各25重量份；
(2)将和田玉、泗水砭石、磁石、托玛琳分别粉碎至6000目；
(3)将粉碎后的和田玉、泗水砭石、磁石、托玛琳粉混合、加适量水搅拌均匀；
(4)将步骤(3)产物压制成型；
(5)将步骤(4)产物常温晾干；
(6)将步骤(5)产物高温1000℃煅烧24小时；
(7)将步骤(6)产物常温冷却。
3.根据权利要求2所述的无机宽波远红外复合环保材料，其特征在于：步骤(4)压制的型状为粉状、粒状、片状、圆柱状。
CN201710245397.4A 2017-04-14 2017-04-14 无机宽波远红外复合环保材料 Pending CN107089827A (zh)