CN107059418B - 防静电耐油污耐腐蚀的环保过滤材料及其制备方法 - Google Patents

防静电耐油污耐腐蚀的环保过滤材料及其制备方法 Download PDF

Info

Publication number
CN107059418B
CN107059418B CN201710385092.3A CN201710385092A CN107059418B CN 107059418 B CN107059418 B CN 107059418B CN 201710385092 A CN201710385092 A CN 201710385092A CN 107059418 B CN107059418 B CN 107059418B
Authority
CN
China
Prior art keywords
parts
silk
fibre silk
resistance
environmentally friendly
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201710385092.3A
Other languages
English (en)
Other versions
CN107059418A (zh
Inventor
单素梅
朱彦加
朱靓靓
吴健健
张瑜
李素英
付译鋆
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Lvdi Environmental Protection Filter Co Ltd
Original Assignee
Jiangsu Lvdi Environmental Protection Filter Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Lvdi Environmental Protection Filter Co Ltd filed Critical Jiangsu Lvdi Environmental Protection Filter Co Ltd
Priority to CN201710385092.3A priority Critical patent/CN107059418B/zh
Publication of CN107059418A publication Critical patent/CN107059418A/zh
Application granted granted Critical
Publication of CN107059418B publication Critical patent/CN107059418B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种防静电耐油污耐腐蚀的环保过滤材料及其制备方法，它包括由聚苯硫醚纤维丝、聚亚酰胺纤维丝、芳香族聚砜酰胺纤维丝和玻璃纤维丝混纺得到的纺织布，针刺在纺织布上下表面的氟美斯针刺毡，覆在氟美斯针刺毡表面的化学薄膜；芳香族聚砜酰胺纤维丝和玻璃纤维丝表面经过聚氨酯溶液浸渍处理；聚苯硫醚纤维丝和聚亚酰胺纤维丝表面经过聚四氟乙烯溶液浸渍处理。本发明结构设计合理，过滤性能好，具有优异的防静电、耐油污、耐腐蚀、耐高温和抗拉力性强等综合性能，使用寿命长。本发明提供的防静电耐油污耐腐蚀的环保过滤材料的制备方法，工艺设计合理，可操作性强，能耗低，环保性强，且生产工作效率高，可实现工业化生产。

Description

防静电耐油污耐腐蚀的环保过滤材料及其制备方法
技术领域
本发明涉及一种环保滤材，具体涉及一种环保性强，过滤性能好，耐腐蚀，耐高温，抗拉力性强的防静电耐油污耐腐蚀的环保过滤材料及其制备方法，属于环保技术领域。
背景技术
在钢铁、水泥、石油化工、液床锅炉、燃煤锅炉、电石厂和精密仪器加工等生产行业，生产过程中需要对粉尘或烟雾过滤除尘处理，但是现有技术的过滤材料防静电、耐油污和耐腐蚀性能弱，过滤效果差，且使用寿命较短，耐用性能差。
另外现有技术中单种纤维的纺织布性能并不全面，如在保持良好抗拉力和耐磨性同时，弹性模量较低，防静电拒油性等方面不足。因此，如何创造出具有防静电、耐腐蚀、防油污、耐酸碱、抗拉力性好等综合性能全面的过滤纺织布具有重要意义。
发明内容
发明目的：本发明的目的是为了解决现有技术的不足，提供一种结构设计合理，过滤性能好，具有防静电、耐腐蚀、防油污、耐酸碱、抗拉力力学性能优，使用寿命长，应用范围广泛的环保过滤材料；本发明另外一个目的是提供该环保过滤材料的制备方法。
技术方案：为了实现以上目的，本发明采取的技术方案为：
一种防静电耐油污耐腐蚀的环保过滤材料，它包括由聚苯硫醚纤维丝、聚亚酰胺纤维丝、芳香族聚砜酰胺纤维丝和玻璃纤维丝混纺得到的纺织布，针刺在纺织布上下表面的氟美斯针刺毡，覆在氟美斯针刺毡表面的化学薄膜；
所述的芳香族聚砜酰胺纤维丝和玻璃纤维丝表面经过聚氨酯溶液浸渍处理；
所述的聚苯硫醚纤维丝和聚亚酰胺纤维丝表面经过聚四氟乙烯溶液浸渍处理；
所述的聚苯硫醚纤维丝、聚亚酰胺纤维丝、芳香族聚砜酰胺纤维丝和玻璃纤维丝的体积比为2～6:1～3:4～8:1～3。
作为优选方案，以上所述的防静电耐油污耐腐蚀的环保过滤材料，所述的环保过滤材料的厚度为2～8毫米，每平方米的重量为700～1200克。
作为优选方案，以上所述的防静电耐油污耐腐蚀的环保过滤材料，所述的聚苯硫醚纤维丝、聚亚酰胺纤维丝、芳香族聚砜酰胺纤维丝和玻璃纤维丝均选择纳米级的纤维丝。
本发明所述的防静电耐油污耐腐蚀的环保过滤材料的制备方法，包括以下步骤：
(1)首先将芳香族聚砜酰胺纤维丝和玻璃纤维丝分别经过梳理、分沙后浸入含有聚氨酯的胶槽中进行浸胶处理，然后在卷纱机牵引下穿过导纱孔板，然后在微波加热箱内固化成型，分别得到表面均匀浸渍有聚氨酯薄膜层的芳香族聚砜酰胺纤维丝和玻璃纤维丝；
(2)然后将聚苯硫醚纤维丝和聚亚酰胺纤维丝经过梳理、分沙后浸入含有聚四氟乙烯溶液的胶槽中进行浸胶处理，然后在卷纱机牵引下穿过导纱孔板，然后在微波加热箱内固化成型，得到表面均匀浸渍有聚四氟乙烯薄膜层的聚苯硫醚纤维丝和聚亚酰胺纤维丝；
(3)将表面均匀浸渍有聚氨酯薄膜层的芳香族聚砜酰胺纤维丝和玻璃纤维丝与表面均匀浸渍有聚四氟乙烯薄膜层的聚苯硫醚纤维丝和聚亚酰胺纤维丝通过织布机纺织得到的纺织布或者通过针刺的方式得到针刺纺织布；
(4)取步骤(3)的纺织布浸入储有防静电耐油污化学处理液的浸渍槽中浸轧，出槽后再进行1～2次轧辊挤压，然后输送到微波加热箱中进行加热固化成型；
(5)将步骤(4)加热固化成型的环保过滤材料通过成卷机打卷，并用聚氯乙烯薄膜包裹。
作为优选方案，以上所述的防静电耐油污耐腐蚀的环保过滤材料的制备方法，所述的防静电耐油污化学处理液由下列重量份数的原料组成：
有机硅树脂10～40份、酚醛环氧树脂5～25份、羟基聚酯树脂5～25份、聚氨酯树脂4～16份、热固性氟碳树脂3～12份、三元醇15～30份、正硅酸乙酯5～15份、苯酐3～6份、醋酸丁酯3～6份、异氰酸酯2～6份、二甲基乙醇胺3～9份、去离子水20～60份。
作为优选方案，以上所述的防静电耐油污耐腐蚀的环保过滤材料的制备方法，所述的耐腐蚀耐高温化学处理液由下列重量份数的原料组成：
有机硅树脂20～40份、酚醛环氧树脂15～25份、羟基聚酯树脂15～25份、聚氨酯树脂8～16份、热固性氟碳树脂6～12份、三元醇15～30份、正硅酸乙酯5～15份、苯酐3～6份、醋酸丁酯3～6份、异氰酸酯4～6份、二甲基乙醇胺6～9份、去离子水40～60份。
作为优选方案，以上所述的防静电耐油污耐腐蚀的环保过滤材料的制备方法，所述三元醇为甘油、三羟甲基丙烷或三羟甲基乙烷中的一种或它们的混合物。
作为优选方案，以上所述的防静电耐油污耐腐蚀的环保过滤材料的制备方法，步骤(1)和步骤(2)微波加热箱内微波加热功率为1KW，加热时间为10～30秒。
作为优选方案，以上所述的防静电耐油污耐腐蚀的环保过滤材料的制备方法，步骤(4)微波加热箱中，先在1KW微波源功率下加热10～30秒，然后在5KW微波源功率下加热10～30秒。
作为优选方案，以上所述的防静电耐油污耐腐蚀的环保过滤材料的制备方法，步骤(3)纺织或针刺时所述的聚苯硫醚纤维丝、聚亚酰胺纤维丝、芳香族聚砜酰胺纤维丝和玻璃纤维丝的体积比为2～6:1～3:4～8:1～3。
本发明通过大量实验筛选，引进绿色环保的微波加热装置，打破现有技术依靠烘箱烘干的方式，现有的加热炉烘箱烘干，需要非常高的能耗，成本高，环保性低，且加热烘干温度需要阶梯升温烘干，操作复杂，生产效率低，且树脂浸入到空间极其细小的纤维纺织布内层，依靠烘箱外部烘干的方式，很难将其加热固化透，从而影响过滤材料的性能和成膜效果。本发明创造性的采用微波加热固化成膜的方式，微波可由内之外加热固化树脂，从而可以使树脂快速固化成膜，防止过滤纤维材料内部不能够彻底固化成膜的不足。并且采用微波加热，需要的功率低，加热固化时间短(一般只需要1到2分钟，而传统烘箱加热需要10～30分钟)，生产效率非常高，并且能耗非常低，加热成本是现有烘箱加热的十分之一，并且取得了非常好的技术效果。当然在选择微波加热功率和加热时间非常关键，过高的功率和过长的微波加热时间对纤维和薄膜具有一定的损伤，本发明通过大量实验选，先对单个纤维丝表面薄膜进行低功率1KW，5～30秒加热时间进行处理，先在单个纤维表面处理得到聚氨酯薄膜或有机硅树脂薄膜，这种处理方式可以最大程度的提高单个纤维的综合表面性能，相比现有技术先纺织得到织物再进行表面化学处理具有更加优越的理化性能，取得了非常好的技术效果。
纺织布在化学处理液浸胶后，本发明再经过优选的微波加热功率和加热时间，采用二个梯度进行微波辐射加热固化成膜，首先采用低功率1KW微波源功率下加热10～30秒，然后在高功率5KW微波源功率下加热10～30秒。这种分阶段、分功率的加热方式，可以使纺织布表面的形成附着力牢固的化学膜。本发明通过实验筛选，如果直接采用高功率的微波源加热，由于加热固化速度过快，成膜后附着力和致密性较差，耐用性较差。
作为优选方案，以上所述的纳米聚苯硫醚丝、纳米玄武岩纤维丝、纳米碳纤维丝和纳米芳纶纤维丝的体积比为1～3:2～6:3～9:1～4；
并且本发明通过大量实验筛选，在纺织布上、下表面针刺有氟美斯针刺毡(氟美斯针刺毡以100％无碱玻璃纤维为原料，采用高支数玻璃纤维丝分丝成绒针刺而成，具有良好的耐热，阻燃，防腐效果、气体过滤阻力小、除尘效率超过机织滤料)，并且在有氟美斯针刺毡表面浸渍处理得到薄膜，可以在保证优异的机械力学性能的同时，最大程度的提高过滤性能。
有益效果：本发明提供的防静电耐油污耐腐蚀的环保过滤材料及其制备方法和现有技术相比具有以下优点:
本发明提供的防静电耐油污耐腐蚀的环保过滤材料，通过大量实验筛选得到最佳的纤维材料，制备得到的环保滤材结构设计合理，过滤性能好，并且具有优异的防静电、耐油污、耐腐蚀、耐高温和抗拉力性强等综合性能，并且使用寿命长，可广泛应用于钢铁、水泥、石油化工、精密仪器制造、电石厂等不同的生产行业，是一种新型的过滤材料，应用前景广泛。
本发明提供的防静电耐油污耐腐蚀的环保过滤材料的制备方法，工艺设计合理，可操作性强，能耗低，环保性强，且生产工作效率高，可实现工业化生产。
具体实施方式
下面结合具体实施例，进一步阐明本发明，应理解这些实施例仅用于说明本发明而不用于限制本发明的范围，在阅读了本发明之后，本领域技术人员对本发明的各种等价形式的修改均落于本申请所附权利要求所限定的范围。
实施例1
一种防静电耐油污耐腐蚀的环保过滤材料，它包括由聚苯硫醚纤维丝、聚亚酰胺纤维丝、芳香族聚砜酰胺纤维丝和玻璃纤维丝混纺得到的纺织布，针刺在纺织布上下表面的氟美斯针刺毡，覆在氟美斯针刺毡表面的化学薄膜；
所述的芳香族聚砜酰胺纤维丝和玻璃纤维丝表面经过聚氨酯溶液浸渍处理；
所述的聚苯硫醚纤维丝和聚亚酰胺纤维丝表面经过聚四氟乙烯溶液浸渍处理；
所述的聚苯硫醚纤维丝、聚亚酰胺纤维丝、芳香族聚砜酰胺纤维丝和玻璃纤维丝的体积比为4:2:6:3。
以上所述的防静电耐油污耐腐蚀的环保过滤材料，所述的环保过滤材料的厚度为2～8毫米，每平方米的重量为700～1200克。
2、本发明所述的防静电耐油污耐腐蚀的环保过滤材料的制备方法，包括以下步骤：
(1)首先将芳香族聚砜酰胺纤维丝和玻璃纤维丝分别经过梳理、分沙后浸入含有聚氨酯的胶槽中进行浸胶处理，然后在卷纱机牵引下穿过导纱孔板(为孔径约大于纱线直径的带多孔的导纱板)，然后在微波加热箱内固化成型，分别得到表面均匀浸渍有聚氨酯薄膜层的芳香族聚砜酰胺纤维丝和玻璃纤维丝；
(2)然后将聚苯硫醚纤维丝和聚亚酰胺纤维丝经过梳理、分沙后浸入含有聚四氟乙烯溶液的胶槽中进行浸胶处理，然后在卷纱机牵引下穿过导纱孔板，然后在微波加热箱内固化成型，得到表面均匀浸渍有聚四氟乙烯薄膜层的聚苯硫醚纤维丝和聚亚酰胺纤维丝；
(3)将表面均匀浸渍有聚氨酯薄膜层的芳香族聚砜酰胺纤维丝和玻璃纤维丝与表面均匀浸渍有聚四氟乙烯薄膜层的聚苯硫醚纤维丝和聚亚酰胺纤维丝按体积比为4:2:6:3通过织布机纺织得到的纺织布或者通过针刺的方式得到针刺纺织布；
(4)取步骤(3)的纺织布浸入储有防静电耐油污化学处理液的浸渍槽中浸轧，出槽后再进行2次轧辊挤压，然后输送到微波加热箱中进行加热固化成型；
(5)将步骤(4)加热固化成型的环保过滤材料通过成卷机打卷，并用聚氯乙烯薄膜包裹。
以上所述的防静电耐油污耐腐蚀的环保过滤材料的制备方法，所述的防静电耐油污化学处理液由下列重量份数的原料组成：
有机硅树脂40份、酚醛环氧树脂20份、羟基聚酯树脂20份、聚氨酯树脂10份、热固性氟碳树脂8份、甘油30份、正硅酸乙酯10份、苯酐6份、醋酸丁酯6份、异氰酸酯6份、二甲基乙醇胺6份、去离子水60份。
以上所述的防静电耐油污耐腐蚀的环保过滤材料的制备方法，步骤(1)和步骤(2)微波加热箱内微波加热功率为1KW，加热时间为20秒。步骤(4)微波加热箱中，先在1KW微波源功率下加热15秒，然后在5KW微波源功率下加热20秒。
3、性能检测
取上述防静电耐油污耐腐蚀的环保过滤材料进行基本力学和化学性能检测，检测结果如下：
由以上检测结果表明，本发明提供的防静电耐油污耐腐蚀的环保过滤材料具有优异的过滤性能，并且具有优异的防静电耐油污耐腐蚀性能，是一种新型环保过滤材料，应用范围非常广泛。
实施例2
一种防静电耐油污耐腐蚀的环保过滤材料，它包括由纳米聚苯硫醚纤维丝、纳米聚亚酰胺纤维丝、纳米芳香族聚砜酰胺纤维丝和纳米玻璃纤维丝混纺得到的纺织布，针刺在纺织布上下表面的氟美斯针刺毡，覆在氟美斯针刺毡表面的化学薄膜；
所述的纳米芳香族聚砜酰胺纤维丝和纳米玻璃纤维丝表面经过聚氨酯溶液浸渍处理；
所述的纳米聚苯硫醚纤维丝和纳米聚亚酰胺纤维丝表面经过聚四氟乙烯溶液浸渍处理；
所述的纳米聚苯硫醚纤维丝、纳米聚亚酰胺纤维丝、纳米芳香族聚砜酰胺纤维丝和纳米玻璃纤维丝的体积比为1:2:3:1。
以上所述的防静电耐油污耐腐蚀的环保过滤材料，所述的环保过滤材料的厚度为2～8毫米，每平方米的重量为700～1100克。
2、本发明所述的防静电耐油污耐腐蚀的环保过滤材料的制备方法，包括以下步骤：
(1)首先将纳米芳香族聚砜酰胺纤维丝和纳米玻璃纤维丝分别经过梳理、分沙后浸入含有聚氨酯的胶槽中进行浸胶处理，然后在卷纱机牵引下穿过导纱孔板(为孔径约大于纱线直径的带多孔的导纱板)，然后在微波加热箱内固化成型，分别得到表面均匀浸渍有聚氨酯薄膜层的芳香族聚砜酰胺纤维丝和玻璃纤维丝；
(2)然后将纳米聚苯硫醚纤维丝和纳米聚亚酰胺纤维丝经过梳理、分沙后浸入含有聚四氟乙烯溶液的胶槽中进行浸胶处理，然后在卷纱机牵引下穿过导纱孔板(为孔径约大于纱线直径的带多孔的导纱板)，然后在微波加热箱内固化成型，得到表面均匀浸渍有聚四氟乙烯薄膜层的纳米聚苯硫醚纤维丝和纳米聚亚酰胺纤维丝；
(3)将表面均匀浸渍有聚氨酯薄膜层的纳米芳香族聚砜酰胺纤维丝和纳米玻璃纤维丝与表面均匀浸渍有聚四氟乙烯薄膜层的纳米聚苯硫醚纤维丝和纳米聚亚酰胺纤维丝按体积比为1:2:3:1通过织布机纺织得到的纺织布或者通过针刺的方式得到针刺纺织布；
(4)取步骤(3)的纺织布浸入储有防静电耐油污化学处理液的浸渍槽中浸轧，出槽后再进行2次轧辊挤压，然后输送到微波加热箱中进行加热固化成型；
(5)将步骤(4)加热固化成型的环保过滤材料通过成卷机打卷，并用聚氯乙烯薄膜包裹。
以上所述的防静电耐油污耐腐蚀的环保过滤材料的制备方法，所述的防静电耐油污化学处理液由下列重量份数的原料组成：
有机硅树脂20份、酚醛环氧树脂15份、羟基聚酯树脂15份、聚氨酯树脂8份、热固性氟碳树脂6份、甘油15份、正硅酸乙酯5份、苯酐3份、醋酸丁酯3份、异氰酸酯4份、二甲基乙醇胺6份、去离子水50份。
以上所述的防静电耐油污耐腐蚀的环保过滤材料的制备方法，步骤(1)和步骤(2)微波加热箱内微波加热功率为1KW，加热时间为20秒。步骤(4)微波加热箱中，先在1KW微波源功率下加热15秒，然后在5KW微波源功率下加热30秒。
3、性能检测
取上述防静电耐油污耐腐蚀的环保过滤材料进行基本力学和化学性能检测，检测结果如下：
由以上检测结果表明，本发明提供的防静电耐油污耐腐蚀的环保过滤材料具有优异的过滤性能，并且具有优异的防静电耐油污耐腐蚀性能，是一种新型环保过滤材料，应用范围非常广泛。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (9)

1.一种防静电耐油污耐腐蚀的环保过滤材料，其特征在于：它包括由聚苯硫醚纤维丝、聚亚酰胺纤维丝、芳香族聚砜酰胺纤维丝和玻璃纤维丝混纺得到的纺织布，针刺在纺织布上下表面的氟美斯针刺毡，覆在氟美斯针刺毡表面的化学薄膜；
所述的芳香族聚砜酰胺纤维丝和玻璃纤维丝表面经过聚氨酯溶液浸渍处理；
所述的聚苯硫醚纤维丝和聚亚酰胺纤维丝表面经过聚四氟乙烯溶液浸渍处理；
所述的聚苯硫醚纤维丝、聚亚酰胺纤维丝、芳香族聚砜酰胺纤维丝和玻璃纤维丝的体积比为2～6:1～3:4～8:1～3；
所述的防静电耐油污耐腐蚀的环保过滤材料的制备方法，包括以下步骤：
(1)首先将芳香族聚砜酰胺纤维丝和玻璃纤维丝分别经过梳理、分纱后浸入含有聚氨酯的胶槽中进行浸胶处理，然后在卷纱机牵引下穿过导纱孔板，然后在微波加热箱内固化成型，分别得到表面均匀浸渍有聚氨酯薄膜层的芳香族聚砜酰胺纤维丝和玻璃纤维丝；
(2)然后将聚苯硫醚纤维丝和聚亚酰胺纤维丝经过梳理、分纱后浸入含有聚四氟乙烯溶液的胶槽中进行浸胶处理，然后在卷纱机牵引下穿过导纱孔板，然后在微波加热箱内固化成型，得到表面均匀浸渍有聚四氟乙烯薄膜层的聚苯硫醚纤维丝和聚亚酰胺纤维丝；
(3)将表面均匀浸渍有聚氨酯薄膜层的芳香族聚砜酰胺纤维丝和玻璃纤维丝与表面均匀浸渍有聚四氟乙烯薄膜层的聚苯硫醚纤维丝和聚亚酰胺纤维丝通过织布机纺织得到的纺织布或者通过针刺的方式得到针刺纺织布；
(4)取步骤(3)的纺织布浸入储有防静电耐油污化学处理液的浸渍槽中浸轧，出槽后再进行1～2次轧辊挤压，然后输送到微波加热箱中进行加热固化成型；
(5)将步骤(4)加热固化成型的环保过滤材料通过成卷机打卷，并用聚氯乙烯薄膜包裹；
步骤(4)所述的防静电耐油污化学处理液由下列重量份数的原料组成：
有机硅树脂10～40份、酚醛环氧树脂5～25份、羟基聚酯树脂5～25份、聚氨酯树脂4～16份、热固性氟碳树脂3～12份、三元醇15～30份、正硅酸乙酯5～15份、苯酐3～6份、醋酸丁酯3～6份、异氰酸酯2～6份、二甲基乙醇胺3～9份、去离子水20～60份。
2.根据权利要求1所述的防静电耐油污耐腐蚀的环保过滤材料，其特征在于：所述的环保过滤材料的厚度为2～8毫米，每平方米的重量为700～1200克。
3.权利要求1或2所述的防静电耐油污耐腐蚀的环保过滤材料的制备方法，其特征在于：包括以下步骤：
(1)首先将芳香族聚砜酰胺纤维丝和玻璃纤维丝分别经过梳理、分纱后浸入含有聚氨酯的胶槽中进行浸胶处理，然后在卷纱机牵引下穿过导纱孔板，然后在微波加热箱内固化成型，分别得到表面均匀浸渍有聚氨酯薄膜层的芳香族聚砜酰胺纤维丝和玻璃纤维丝；
(2)然后将聚苯硫醚纤维丝和聚亚酰胺纤维丝经过梳理、分纱后浸入含有聚四氟乙烯溶液的胶槽中进行浸胶处理，然后在卷纱机牵引下穿过导纱孔板，然后在微波加热箱内固化成型，得到表面均匀浸渍有聚四氟乙烯薄膜层的聚苯硫醚纤维丝和聚亚酰胺纤维丝；
(3)将表面均匀浸渍有聚氨酯薄膜层的芳香族聚砜酰胺纤维丝和玻璃纤维丝与表面均匀浸渍有聚四氟乙烯薄膜层的聚苯硫醚纤维丝和聚亚酰胺纤维丝通过织布机纺织得到的纺织布或者通过针刺的方式得到针刺纺织布；
(4)取步骤(3)的纺织布浸入储有防静电耐油污化学处理液的浸渍槽中浸轧，出槽后再进行1～2次轧辊挤压，然后输送到微波加热箱中进行加热固化成型；
(5)将步骤(4)加热固化成型的环保过滤材料通过成卷机打卷，并用聚氯乙烯薄膜包裹。
4.根据权利要求3所述的防静电耐油污耐腐蚀的环保过滤材料的制备方法，其特征在于：所述的防静电耐油污化学处理液由下列重量份数的原料组成：
有机硅树脂10～40份、酚醛环氧树脂5～25份、羟基聚酯树脂5～25份、聚氨酯树脂4～16份、热固性氟碳树脂3～12份、三元醇15～30份、正硅酸乙酯5～15份、苯酐3～6份、醋酸丁酯3～6份、异氰酸酯2～6份、二甲基乙醇胺3～9份、去离子水20～60份。
5.根据权利要求4所述的防静电耐油污耐腐蚀的环保过滤材料的制备方法，其特征在于：所述的防静电耐油污化学处理液由下列重量份数的原料组成：
有机硅树脂20～40份、酚醛环氧树脂15～25份、羟基聚酯树脂15～25份、聚氨酯树脂8～16份、热固性氟碳树脂6～12份、三元醇15～30份、正硅酸乙酯5～15份、苯酐3～6份、醋酸丁酯3～6份、异氰酸酯4～6份、二甲基乙醇胺6～9份、去离子水40～60份。
6.根据权利要求4或5所述的防静电耐油污耐腐蚀的环保过滤材料的制备方法，其特征在于：所述三元醇为甘油、三羟甲基丙烷或三羟甲基乙烷中的一种或它们的混合物。
7.根据权利要求4所述的防静电耐油污耐腐蚀的环保过滤材料的制备方法，其特征在于：步骤(1)和步骤(2)微波加热箱内微波加热功率为1KW，加热时间为10～30秒。
8.根据权利要求4所述的防静电耐油污耐腐蚀的环保过滤材料的制备方法，其特征在于：步骤(4)微波加热箱中，先在1KW微波源功率下加热10～30秒，然后在5KW微波源功率下加热10～30秒。
9.根据权利要求4所述的防静电耐油污耐腐蚀的环保过滤材料的制备方法，其特征在于：步骤(3)纺织或针刺时所述的聚苯硫醚纤维丝、聚亚酰胺纤维丝、芳香族聚砜酰胺纤维丝和玻璃纤维丝的体积比为2～6:1～3:4～8:1～3。
CN201710385092.3A 2017-05-26 2017-05-26 防静电耐油污耐腐蚀的环保过滤材料及其制备方法 Active CN107059418B (zh)