CN107057577A - It is a kind of for water colour paint of Wood-bar pencil and preparation method thereof - Google Patents
It is a kind of for water colour paint of Wood-bar pencil and preparation method thereof Download PDFInfo
- Publication number
- CN107057577A CN107057577A CN201710283200.6A CN201710283200A CN107057577A CN 107057577 A CN107057577 A CN 107057577A CN 201710283200 A CN201710283200 A CN 201710283200A CN 107057577 A CN107057577 A CN 107057577A
- Authority
- CN
- China
- Prior art keywords
- wood
- parts
- coalescents
- water colour
- minutes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to water paint field, and in particular to a kind of for water colour paint of Wood-bar pencil and preparation method thereof, wherein colored paint is made up of the component of following parts by weight：Aqueous 80 100 parts of anionic emulsion resin, 4 10 parts of coalescents；13 parts of wetting agent；15 parts of dispersant；0.2 1.5 parts of defoamer；14 parts of fatting agent；15 25 parts of talcum powder；10 20 parts of kaolin；10 15 parts of coarse whiting；5 10 parts of mill base；48 parts of thickener.Using the colored paint obtained by the preparation method of the water colour paint for Wood-bar pencil of the present invention, dry quickly, adhesive force is strong, strong coloring force, strong covering power, smoothness is high.
Description
Technical field
The invention belongs to water paint field, and in particular to a kind of water colour paint and its preparation side for Wood-bar pencil
Method.
Background technology
Pencil is important writing implement in modern people's culture life, and the most traditional Wood-bar pencil is special due to its writing
Point, is still main instrument in fields such as sketch, drawing, examination, color make-ups, there is the status do not replaced.In order to rod lead
Pen is protected and is not had pipe, it is necessary to carries out application, and to reach preferable painting effect, first has to priming, i.e., in rod
The priming paint of topical oil paint machine coating white, is then coated colored paint, is then coated with surface layer finishing varnish.It is coated with the mesh of white primer
Be cover the lines on rod surface and the primary colors of timber, improve the flatness on surface, be easy to pigmented top coat to reach due
Smoothness, glossiness and color, surface layer finishing varnish are free of color, for glazing.
Traditional solvent-borne type pencil lacquer, the overwhelming majority is nitrate paint, there is substantial amounts of organic solvent, these compounds are in life
Our natural environment and healthy can be seriously endangered during production and use；Organic solvent feature the most obvious is exactly to have
There is strong impulse smell, these penetrating odors can seriously stimulate eye mucosa, schneiderian membrane, respiratory mucosa and cause skin
Allergy；A certain amount of plasticizer, severe jamming endocrine can be added in nitro pencil lacquer；The usual solid content of nitro pencil lacquer is inclined
It is low, it must reach that certain viscosity needs to construct several times and relatively low solid content is while also result in paint film richness during construction
It is low to cause to influence hardness；Humidity requirement when nitro pencil lacquer is to construction is higher, and the moisture content of coating surface have to be lower than 12%,
The weather of higher levels of humidity is also unfavorable for construction during production, and the slurry configured can not be exposed to the air of high humidity for a long time
In, its solidification that easily absorbs water is not reusable and causes slurry to waste；When humidity is high, the steam in air or on base material will applied
Dew is condensed on film, so as to produce whiting, yield rate is substantially reduced；Film forming matter in nitrate paint is nitrocellulose cellulose, nitre
It is that cotton fiber is formed through strong acid degreasing to change gossypin, therefore nitrocellulose cellulose can introduce free acid in nitrate paint, trip
It can cause the decomposition of celluosic resin from acid, further result in loss of gloss, discoloration, efflorescence or even the cracking of paint film, cause nitrate paint
Finished product is low；Meanwhile, the storage and transportation conditions of nitrate paint is extremely harsh, it is impossible to drench with rain, and making moist, it is rotten to solidify；It is unable to sunlight
It is exposed to the sun, it is impossible to collide, easily triggers organic solvent blast；High corrosion-resistant packaging material is selected, is stored at shady and cool ventilation, is completely cut off
Burning things which may cause a fire disaster, away from thermal source.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of for water colour paint of Wood-bar pencil and preparation method thereof, with
Solve the above problems.
A kind of water colour paint for Wood-bar pencil of the present invention, is made up of the component of following parts by weight：
Preferably, coalescents include coalescents A and coalescents B, and coalescents A is Tao Shi dipropylene glycol propyl ethers
(DPNP), coalescents B is Tao Shi dipropylene glycol methyl ethers (DPM), and coalescents A components by weight percent is 2-6 parts, coalescents B
Components by weight percent be 2-4 parts.
Preferably, thickener is association type polyurethanes thickener.
Preferably, wetting agent is polyethers trisiloxanes (8030).
Preferably, dispersant is block copolymer and moist type organosilicon (7117).
Preferably, defoamer is polyether siloxane copolymer emulsion (902).
Preferably, fatting agent is Modified Fish Oil.
Preferably, when allocating black paint, the number of mill base occupies the 10-15% of all components number summation in formula；Adjust
During with color paint, the number of mill base occupies the 15-20% of all components number summation in formula.
A kind of preparation method of water colour paint for Wood-bar pencil of the present invention, comprises the following steps：
S10, the aqueous anionic emulsion resin of precise, disposably puts into dispersion machine；
S20, after first coalescents A is uniformly mixed in advance with coalescents B, in dispersion machine 1200-1500r/min point
Coalescents A and coalescents B are slowly added dropwise under bulk state, it is scattered 15-20 minutes at a high speed；
Wetting agent is slowly added dropwise in S30, dispersion machine 800-1000r/min, dispersion process, middling speed is scattered 10-15 minutes；
Dispersant is slowly added dropwise in S40, dispersion machine 800-1000r/min, dispersion process, middling speed is scattered 10-15 minutes；
Defoamer is slowly added dropwise in S50, dispersion machine 800-1000r/min, dispersion process, middling speed is scattered 10-15 minutes；
Disposable input talcum powder and fatting agent in S60, dispersion machine 800-1000r/min, dispersion process, middling speed are disperseed
10-15 minutes；
Disposable input coarse whiting and kaolin, disperse 10-15 points in S70, dispersion machine 800-1000r/min, dispersion process
Filtered after clock；
S80, dispersion machine 800-1000r/min, put into mill base, after filtering, add thickener, disperse 20-30 minutes, obtain
Water colour paint for Wood-bar pencil.
Preferably, after for the water colour paint lacquering of Wood-bar pencil, observation whether there is obvious bubble, if any then standing 10-14
Hour；The viscosity of water colour paint is in 60000CPS-65000CPS.
There is following beneficial effect using the present invention：
1st, the water colour paint for Wood-bar pencil of the invention, without adding curing agent or plasticizer；There is no excitant gas
Taste, will not cause allergic, environmental protection, excellent performance, and work progress is not wanted to air humidity and substrate moisture rate
Ask；Transport and storage link have security and convenience；Paint film is fine and smooth..
2nd, the water colour paint for Wood-bar pencil of the invention, is dried quickly, adhesive force is strong, strong coloring force, strong covering power,
Smoothness is high.
Brief description of the drawings
Fig. 1 is a kind of flow chart for the water colour paint of Wood-bar pencil and preparation method thereof of the embodiment of the present invention.
Embodiment
Below in conjunction with the accompanying drawing in the embodiment of the present invention, the technical scheme in the embodiment of the present invention is carried out clear, complete
Site preparation is described, it is clear that described embodiment is a part of embodiment of the invention, rather than whole embodiments.Based on this hair
Embodiment in bright, the every other implementation that those of ordinary skill in the art are obtained under the premise of creative work is not made
Example, belongs to the scope of protection of the invention.
Embodiment 1
As shown in figure 1, the aqueous anionic emulsion resin of 80 parts of precise, disposably puts into dispersion machine, with deionized water
Make solvent；After 2 parts of coalescents A and 2 parts of coalescents B are pre-mixed, dispersity of the control dispersion machine in 1200r/min
Under be slowly added dropwise coalescents and coalescents B, scattered 20 minutes at a high speed, coalescents A is Tao Shi dipropylene glycol propyl ethers
(DPNP), coalescents B is Tao Shi dipropylene glycol methyl ethers (DPM)；Control dispersion machine in 800r/min, 3 parts of wettings are slowly added dropwise
Agent, middling speed is scattered 10 minutes, and wetting agent is polyethers trisiloxanes；5 parts of dispersants are slowly added dropwise again, disperse 10 minutes, dispersant
For block copolymer and moist type organosilicon；0.2 part of defoamer is slowly added dropwise again, disperses 10 minutes, defoamer is ether siloxanes
Copolymer emulsion；Property puts into 25 parts of talcum powder and 4 parts of fatting agents again, disperses 10 minutes, fatting agent is Modified Fish Oil；Further
Secondary property puts into 15 parts of coarse whitings and 13 parts of kaolin, disperses 10 minutes；Mill base is finally put into, 5 parts of thickeners are put into after filtering, is disperseed
20 minutes, thickener was association type polyurethanes thickener；The water colour paint for Wood-bar pencil is made, its viscosity exists
After 60000CPS-65000CPS, lacquering, observation whether there is obvious bubble, if any then standing 10 hours.
Wherein, when allocating black paint, the number of mill base occupies the 10-15% of all components number summation in formula；At this
In embodiment, the number of mill base is 17.13 parts, occupies the 10% of all components number summation.
Embodiment 2
As shown in figure 1, the aqueous anionic emulsion resin of 100 parts of precise, disposably puts into dispersion machine, with deionized water
Make solvent；After 6 parts of coalescents A and 4 parts of coalescents B are pre-mixed, dispersity of the control dispersion machine in 1300r/min
Under be slowly added dropwise coalescents and coalescents B, scattered 15 minutes at a high speed, coalescents A is Tao Shi dipropylene glycol propyl ethers
(DPNP), coalescents B is Tao Shi dipropylene glycol methyl ethers (DPM)；Control dispersion machine in 900r/min, 1 part of wetting is slowly added dropwise
Agent, middling speed is scattered 15 minutes, and wetting agent is polyethers trisiloxanes；4 parts of dispersants are slowly added dropwise again, disperse 15 minutes, dispersant
For block copolymer and moist type organosilicon；0.6 part of defoamer is slowly added dropwise again, disperses 15 minutes, defoamer is ether siloxanes
Copolymer emulsion；Property puts into 20 parts of talcum powder and 1 part of fatting agent again, disperses 15 minutes, fatting agent is Modified Fish Oil；Further
Secondary property puts into 14 parts of coarse whitings and 16 parts of kaolin, disperses 15 minutes；Mill base is finally put into, 4 parts of thickeners are put into after filtering, is disperseed
30 minutes, thickener was association type polyurethanes thickener；The water colour paint for Wood-bar pencil is made, its viscosity exists
After 60000CPS-65000CPS, lacquering, observation whether there is obvious bubble, if any then standing 14 hours.
Wherein, when allocating black paint, the number of mill base occupies the 10-15% of all components number summation in formula；At this
In embodiment, the number of the mill base of corresponding color is 30.10 parts, occupies the 15% of all components number summation.
Embodiment 3
As shown in figure 1, the aqueous anionic emulsion resin of 90 parts of precise, disposably puts into dispersion machine, with deionized water
Make solvent；After 4 parts of coalescents A and 3 parts of coalescents B are pre-mixed, dispersity of the control dispersion machine in 1500r/min
Under be slowly added dropwise coalescents and coalescents B, scattered 18 minutes at a high speed, coalescents A is Tao Shi dipropylene glycol propyl ethers
(DPNP), coalescents B is Tao Shi dipropylene glycol methyl ethers (DPM)；Control dispersion machine in 1000r/min, 2 parts of wettings are slowly added dropwise
Agent, middling speed is scattered 13 minutes, and wetting agent is polyethers trisiloxanes；1 part of dispersant is slowly added dropwise again, disperses 13 minutes, dispersant
For block copolymer and moist type organosilicon；1.5 parts of defoamers are slowly added dropwise again, disperse 13 minutes, defoamer is ether siloxanes
Copolymer emulsion；Property puts into 15 parts of talcum powder and 2 parts of fatting agents again, disperses 13 minutes, fatting agent is Modified Fish Oil；Further
Secondary property puts into 10 parts of coarse whitings and 10 parts of kaolin, disperses 13 minutes；Mill base is finally put into, 8 parts of thickeners are put into after filtering, is disperseed
25 minutes, thickener was association type polyurethanes thickener；The water colour paint for Wood-bar pencil is made, its viscosity exists
After 60000CPS-65000CPS, lacquering, observation whether there is obvious bubble, if any then standing 12 hours.
When allocating color paint, the number of mill base occupies the 15-20% of all components number summation in formula.In the present embodiment
In, the number of mill base is 25.8 parts, occupies the 15% of all components number summation, and color paint includes red colour system, yellow class, royal purple
Colour system etc..
Embodiment 4
As shown in figure 1, the aqueous anionic emulsion resin of 95 parts of precise, disposably puts into dispersion machine, with deionized water
Make solvent；After 5 parts of coalescents A and 2.5 parts of coalescents B are pre-mixed, dispersed of the control dispersion machine in 1400r/min
Coalescents and coalescents B are slowly added dropwise under state, scattered 16 minutes at a high speed, coalescents A is Tao Shi dipropylene glycol propyl ethers
(DPNP), coalescents B is Tao Shi dipropylene glycol methyl ethers (DPM)；Control dispersion machine in 850r/min, 3 parts of wettings are slowly added dropwise
Agent, middling speed is scattered 12 minutes, and wetting agent is polyethers trisiloxanes；3 parts of dispersants are slowly added dropwise again, disperse 12 minutes, dispersant
For block copolymer and moist type organosilicon；1.1 parts of defoamers are slowly added dropwise again, disperse 12 minutes, defoamer is ether siloxanes
Copolymer emulsion；Property puts into 20 parts of talcum powder and 3 parts of fatting agents again, disperses 12 minutes, fatting agent is Modified Fish Oil；Further
Secondary property puts into 12 parts of coarse whitings and 20 parts of kaolin, disperses 12 minutes；Mill base is finally put into, 6 parts of thickeners are put into after filtering, is disperseed
27 minutes, thickener was association type polyurethanes thickener；The water colour paint for Wood-bar pencil is made, its viscosity exists
After 60000CPS-65000CPS, lacquering, observation whether there is obvious bubble, if any then standing 13 hours.
When allocating color paint, the number of mill base occupies the 15-20% of all components number summation in formula.In the present embodiment
In, the number of the mill base of corresponding color is 43.15 parts, occupies the 20% of all components number summation, color paint include red colour system,
Yellow class, royal purple colour system etc..
Film performance of the product painting obtained by above-described embodiment on pencil and after spontaneous curing is as follows：
First, the adhesive force of the coating layer after detection coating：
Comparative example：(Shanghai Gu Leima Hua Qing Co., Ltds, cereal horse board is black for the existing ripe solvent based product in market
Color).
Experiment equipment：50mm adhesive tapes
Experimental procedure：50mm adhesive tapes are tightly sticked on the surface with sounding lead penholder, with 45° angle at the uniform velocity pull-up, observation
The dropping situations of pencil coating：
| Sample | As a result |
| Comparative example | Coating slightly comes off (qualified) |
| Embodiment 1 | Coating is not fallen off (qualified) |
| Embodiment 2 | Coating is not fallen off (qualified) |
| Embodiment 3 | Coating is not fallen off (qualified) |
| Embodiment 4 | Coating is not fallen off (qualified) |
Conclusion：It can be seen that from above-mentioned application result, use the water for Wood-bar pencil prepared by embodiment 1-4 method
Property colored paint, compared with comparative example, adhesive force is significantly improved.
2nd, the tack after the friction of detection sweat
Experimental method：In 20 degree or so of room temperature, 4 layers of the folding that synthetic perspiration is soaked, 500g power, apart from 6cm, is wiped back and forth
Tested paint film is wiped, one is calculated as 1 circulation, 60 cycles per minutes back and forth, and friction testing must meet 500 circulations, be observed after 500 circulations
Whether paint film has bubble, corrugation, fracture phenomena, if having substantially heterochromatic.
Testing result：
| Sample | As a result |
| Embodiment 1 | It is without exception |
| Embodiment 2 | It is without exception |
| Embodiment 3 | It is without exception |
| Embodiment 4 | It is without exception |
Conclusion：It can be seen that from above-mentioned application result, use the water for Wood-bar pencil prepared by embodiment 1-4 method
Property colored paint, sweat friction after adhesive force meet the requirements.
3rd, the covering power of the coating after detection coating
Comparative example：The existing ripe solvent based product in market.(Shanghai Gu Leima Qing Hua Co., Ltds, Gu Leima boards are black
Color)
Experimental method：According to GB1726-79 spread coating.Covering power numerical value is calculated, numerical value is smaller, illustrate to cover
Power is better.
Computational methods and accuracy：
Covering power g/m2(X) it is calculated as follows：
X=(W1-W2)/S×104=50 (W1-W2)
In formula：The cup of paint and the gross weight of painting brush, g are filled before W1-do not brush；
The cup of remaining paint and the gross weight of painting brush, g are filled after W2-brushing；
The area of S-black and white panel japanning, cm2
Twice, difference as a result is not more than the 5% of average value, then takes its average value, otherwise must test again for parallel determination,
Result of calculation：
| Sample | Covering power |
| Comparative example | 116 |
| Embodiment 1 | 107 |
| Embodiment 2 | 108 |
| Embodiment 3 | 102 |
| Embodiment 4 | 105 |
Conclusion：It can be seen that from above-mentioned application result, use the water for Wood-bar pencil prepared by embodiment 1-4 method
Property colored paint, compared with comparative example, covering power is significantly improved.
It should be appreciated that exemplary embodiment as described herein is illustrative and be not restrictive.Although being retouched with reference to accompanying drawing
One or more embodiments of the invention is stated, it should be understood by one skilled in the art that without departing from appended right
It is required that in the case of the spirit and scope of the present invention limited, the change of various forms and details can be made.
Claims (10)
1. a kind of water colour paint for Wood-bar pencil, it is characterised in that be made up of the component of following parts by weight：
2. the water colour paint according to claim 1 for Wood-bar pencil, it is characterised in that coalescents are helped including film forming
Agent A and coalescents B, the coalescents A are Tao Shi dipropylene glycol propyl ethers (DPNP), and the coalescents B is Tao Shi dipropyls
Glycol methyl ether (DPM), the components by weight percent of the coalescents A is 2-6 parts, and the components by weight percent of the coalescents B is 2-4 parts.
3. the water colour paint according to claim 1 or 2 for Wood-bar pencil, it is characterised in that the thickener is to form
Mould assembly polyurethanes thickener.
4. the water colour paint according to claim 1 or 2 for Wood-bar pencil, it is characterised in that the wetting agent is poly-
Ether trisiloxanes (8030).
5. the water colour paint according to claim 1 or 2 for Wood-bar pencil, it is characterised in that the dispersant is embedding
Section copolymer and moist type organosilicon (7117).
6. the water colour paint according to claim 1 or 2 for Wood-bar pencil, it is characterised in that the defoamer is poly-
Ether silicone copolymer emulsion (902).
7. the water colour paint according to claim 1 or 2 for Wood-bar pencil, it is characterised in that the fatting agent is to change
Property fish oil.
8. the water colour paint according to claim 1 or 2 for Wood-bar pencil, it is characterised in that during allotment black paint, color
The number of slurry occupies the 10-15% of all components number summation in formula；When allocating color paint, the number of mill base is occupied in formula
The 15-20% of all components number summation.
9. according to the preparation method of any described water colour paints for Wood-bar pencil of claim 2-8, it is characterised in that bag
Include following steps：
S10, the aqueous anionic emulsion resin of precise, disposably puts into dispersion machine；
S20, after first coalescents A is uniformly mixed in advance with coalescents B, in dispersion machine 1200-1500r/min dispersed
Coalescents A and coalescents B are slowly added dropwise under state, it is scattered 15-20 minutes at a high speed；
Wetting agent is slowly added dropwise in S30, dispersion machine 800-1000r/min, dispersion process, middling speed is scattered 10-15 minutes；
Dispersant is slowly added dropwise in S40, dispersion machine 800-1000r/min, dispersion process, middling speed is scattered 10-15 minutes；
Defoamer is slowly added dropwise in S50, dispersion machine 800-1000r/min, dispersion process, middling speed is scattered 10-15 minutes；
Disposable input talcum powder and fatting agent in S60, dispersion machine 800-1000r/min, dispersion process, middling speed disperse 10-15
Minute；
Disposable input coarse whiting and kaolin in S70, dispersion machine 800-1000r/min, dispersion process, after disperseing 10-15 minutes
Filtering；
S80, dispersion machine 800-1000r/min, put into mill base, after filtering, add thickener, disperse 20-30 minutes, are used for
The water colour paint of Wood-bar pencil.
10. the preparation method of the water colour paint according to claim 9 for Wood-bar pencil, it is characterised in that for wood
After the water colour paint lacquering of rod pencil, observation whether there is obvious bubble, if any then standing 10-14 hours；Water colour paint it is viscous
Degree is in 60000CPS-65000CPS.