CN107057523A - A kind of LED heat radiation coating - Google Patents
A kind of LED heat radiation coating Download PDFInfo
- Publication number
- CN107057523A CN107057523A CN201710313586.0A CN201710313586A CN107057523A CN 107057523 A CN107057523 A CN 107057523A CN 201710313586 A CN201710313586 A CN 201710313586A CN 107057523 A CN107057523 A CN 107057523A
- Authority
- CN
- China
- Prior art keywords
- parts
- heat radiation
- led heat
- radiation coating
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of LED heat radiation coating, constituted according to the parts by weight of following raw material:10 30 parts modified of 30 50 parts of epoxy resin solution, 20 30 parts of acrylic resin, 30 40 parts of silicone acrylic emulsion, 15 parts of aluminium nitride, 12 parts of sulfonated graphene, 15 parts of superfine iron powder, 1 10 parts of oleic acid and auxiliary agent.The LED heat radiation coating of the present invention has high temperature resistant, ageing-resistant, high adhesion force, the advantages of good heat dissipation effect.
Description
Technical field
The present invention relates to a kind of LED heat radiation coating.
Background technology
As LED lamps use the rapid expansion of scope, extension LED lamps service life also turns into is badly in need of asking for solution
Topic.LED lamp heat dissipation problems are solved using heat-conducting glue at present, but its used material has heatproof to be compared with ageing-resistant
Difference, the technical problem that, radiating effect small to base material cohesive force be not good and construction is inconvenient, it is difficult to meet people and radiated to LED
Requirement.
The content of the invention
The purpose of the present invention is that provides a kind of high temperature resistant to solve the above problems, ageing-resistant, there is high attachment
Power, the LED heat radiation coating of good heat dissipation effect.
To achieve these goals, the present invention is achieved by the following technical solutions:A kind of LED heat radiation coating,
Constituted according to the parts by weight of following raw material:Modified 30-50 parts of epoxy resin solution, 20-30 parts of acrylic resin, the breast of silicon third
30-40 parts of liquid, 1-5 parts of aluminium nitride, 1-2 parts of sulfonated graphene, 1-5 parts of superfine iron powder, 1-10 parts of oleic acid, 1-5 parts of pigment and
10-30 parts of auxiliary agent.
Further, a kind of LED heat radiation coating, is constituted according to the parts by weight of following raw material:Modified asphalt mixtures modified by epoxy resin
35-40 parts of lipoprotein solution, 25-28 parts of acrylic resin, 25-27 parts of silicone acrylic emulsion, 2-4 parts of aluminium nitride, 1-2 parts of sulfonated graphene,
15-20 parts of 2-3 parts of superfine iron powder, 4-8 parts of oleic acid, 3 parts of pigment 1- and auxiliary agent.
Further, a kind of LED heat radiation coating, is constituted according to the parts by weight of following raw material:Modified epoxy
38 parts of resin solution, 26 parts of acrylic resin, 27 parts of silicone acrylic emulsion, 3 parts of aluminium nitride, 2 parts of sulfonated graphene, 3 parts of superfine iron powder,
18 parts of 6 parts of oleic acid, 2 parts of pigment and auxiliary agent.
Further, the auxiliary agent is constituted according to the parts by weight of following raw material:5-10 parts of anti-settling agent, dispersant 3-4
Part, 1-5 parts of levelling agent, 1-2 parts of wetting agent and 10-50 parts of mixed solvent.
Particularly, the mixed solvent is by DAA, isophorone, ethyl acetate mixing composition.
In summary the invention has the advantages that:The LED heat radiation coating of the present invention has high temperature resistant, resistance to old
The advantages of change, high adhesion force, good heat dissipation effect.
Embodiment
Specific embodiment 1:A kind of LED heat radiation coating, is constituted according to the parts by weight of following raw material:Modified epoxy
30 parts of resin solution, 20 parts of acrylic resin, 30 parts of silicone acrylic emulsion, 1 part of aluminium nitride, 1 part of sulfonated graphene, 1 part of superfine iron powder,
10 parts of 1 part of oleic acid, 1 part of pigment and auxiliary agent.
Above-mentioned auxiliary agent is constituted according to the parts by weight of following raw material:5 parts of anti-settling agent, 3 parts of dispersant, 1 part of levelling agent, wetting
10 parts of 1 part of agent and mixed solvent;The mixed solvent is by DAA, isophorone, ethyl acetate mixing composition.
Specific embodiment 2:A kind of LED heat radiation coating, is constituted according to the parts by weight of following raw material:Modified epoxy
38 parts of resin solution, 26 parts of acrylic resin, 27 parts of silicone acrylic emulsion, 3 parts of aluminium nitride, 2 parts of sulfonated graphene, 3 parts of superfine iron powder,
18 parts of 6 parts of oleic acid, 2 parts of pigment and auxiliary agent.
Above-mentioned auxiliary agent is constituted according to the parts by weight of following raw material:7 parts of anti-settling agent, 3 parts of dispersant, 3 parts of levelling agent, wetting
30 parts of 2 parts of agent and mixed solvent;The mixed solvent is by DAA, isophorone, ethyl acetate mixing composition.
Specific embodiment 3:A kind of LED heat radiation coating, is constituted according to the parts by weight of following raw material:Modified epoxy
50 parts of resin solution, 30 parts of acrylic resin, 40 parts of silicone acrylic emulsion, 5 parts of aluminium nitride, 2 parts of sulfonated graphene, 5 parts of superfine iron powder,
30 parts of 10 parts of oleic acid, 5 parts of pigment and auxiliary agent.
Above-mentioned auxiliary agent is constituted according to the parts by weight of following raw material:10 parts of anti-settling agent, 4 parts of dispersant, 5 parts of levelling agent, profit
50 parts of 2 parts of humectant and mixed solvent;The mixed solvent is by DAA, isophorone, ethyl acetate mixing composition.
Embodiment provided above is the better embodiment of the present invention, only illustrates the present invention for convenient, not to this hair
It is bright to make any formal limitation, any those of ordinary skill in the art, if putting forward skill not departing from the present invention
In the range of art feature, using the equivalent embodiment for locally changing or modifying made by disclosed technology contents, and
Without departing from the technical characteristic content of the present invention, in the range of still falling within the technology of the present invention feature.
Claims (5)
1. a kind of LED heat radiation coating, it is characterised in that:Constituted according to the parts by weight of following raw material:Modified asphalt mixtures modified by epoxy resin
30-50 parts of lipoprotein solution, 20-30 parts of acrylic resin, 30-40 parts of silicone acrylic emulsion, 1-5 parts of aluminium nitride, 1-2 parts of sulfonated graphene,
10-30 parts of 1-5 parts of superfine iron powder, 1-10 parts of oleic acid, 1-5 parts of pigment and auxiliary agent.
2. a kind of LED heat radiation coating according to claim 1, it is characterised in that:According to the parts by weight of following raw material
Array into:Modified 35-40 parts of epoxy resin solution, 25-28 parts of acrylic resin, 25-27 parts of silicone acrylic emulsion, aluminium nitride 2-4
Part, 1-2 parts of sulfonated graphene, 2-3 parts of superfine iron powder, 4-8 parts of oleic acid, 3 parts of pigment 1- and 15-20 parts of auxiliary agent.
3. a kind of LED heat radiation coating according to claim 1, it is characterised in that:According to the parts by weight of following raw material
Array into:Modified 38 parts of epoxy resin solution, 26 parts of acrylic resin, 27 parts of silicone acrylic emulsion, 3 parts of aluminium nitride, sulfonated graphite
18 parts of 2 parts of alkene, 3 parts of superfine iron powder, 6 parts of oleic acid, 2 parts of pigment and auxiliary agent.
4. according to a kind of any described LED heat radiation coatings of claim 1-3, it is characterised in that:The auxiliary agent according to
The parts by weight composition of lower raw material:5-10 parts of anti-settling agent, 3-4 parts of dispersant, 1-5 parts of levelling agent, 1-2 parts of wetting agent and mixing
10-50 parts of solvent.
5. according to a kind of any described LED heat radiation coating of claim 4, it is characterised in that:The mixed solvent be by
DAA, isophorone, ethyl acetate mixing composition.