CN107057325A - The method for preparing the raw material of carbon fiber fishing rod and fishing rod being prepared using the raw material - Google Patents
The method for preparing the raw material of carbon fiber fishing rod and fishing rod being prepared using the raw material Download PDFInfo
- Publication number
- CN107057325A CN107057325A CN201710053399.3A CN201710053399A CN107057325A CN 107057325 A CN107057325 A CN 107057325A CN 201710053399 A CN201710053399 A CN 201710053399A CN 107057325 A CN107057325 A CN 107057325A
- Authority
- CN
- China
- Prior art keywords
- fishing rod
- raw material
- carbon fiber
- prepared
- reaction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of raw material for making carbon fiber fishing rod, is related to fishing gear technical field, is prepared from the following components：Glass fibre, nanometer boron fibre, carbon fiber, titanium alloy wire, polyurethane, epoxy resin, expoxy propane, linear polypropylene, Brazil wax, dibutyl ester, oxidized starch, epoxy hardener and organic solvent.The Recipe of raw material of the present invention is novel, and cost of material is low, using the fishing rod good toughness of raw material making, light weight, with certain insulating properties.
Description
Technical field：
The present invention relates to fishing gear technical field, and in particular to a kind of raw material for preparing carbon fiber fishing rod and utilize the raw material system
The method of standby fishing rod.
Background technology：
A kind of important amusement of people, stress-relieving activity are had become with the continuous improvement of people's living standards, fishing, it is competing
Skill fishing also frequent development like a raging fire, fishing rod in the market is mostly carbon fiber fishing rod, is used without shuttle
Spin the longitudinal cloth tubulation of carbon fiber, solidify through resin pickup and manufacture, for fishing rod production in terms of carbon fiber content how much, directly
Determine fishing rod value and grade, general phosphorus content be 30%, 90% or so, the fishing rod manufactured with carbon fiber have it is light, solid,
The characteristics of tensile strength is high, existing manufacture fishing rod material although already have excellent tensile strength, yield strength and
The mechanical performances such as elongation, but its antistatic property, toughness and ageing-resistant performance be not high, in use or with limit
Many restrictions processed.
The content of the invention：
The technical problems to be solved by the invention are to provide a kind of raw material for preparing carbon fiber fishing rod, the formula of the raw material
New technology, cost of material is low, using the fishing rod good toughness of raw material making, light weight, with certain insulating properties.
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of raw material for making carbon fiber fishing rod, is prepared from the following components：
Glass fibre, nanometer boron fibre, carbon fiber, titanium alloy wire, polyurethane, epoxy resin, expoxy propane, linear poly- third
Alkene, Brazil wax, dibutyl ester, oxidized starch, epoxy hardener and organic solvent；
The method that fishing rod is prepared using above-mentioned raw materials, is comprised the following steps：
1) in proportion successively by polyurethane, epoxy resin, expoxy propane, linear polypropylene, Brazil wax, dibutyl ester and
Oxidized starch adds reactor, by mixture temperature reaction after being sufficiently mixed uniformly, and reaction is filtrated to get mixture after terminating；
2) by step 1) prepare mixture add reactor, obtain composite wood after then adding epoxy hardener, mixing
Material；
3) by step 2) in composite be put into microwave 15 minutes under microwave environment, microwave frequency is：800MHz-
900MHz；
4) by step 3) in the composite for preparing the glue that solid content is 50% is configured to organic solvent, then by glass
In fiber, nanometer boron fibre, carbon fiber and titanium alloy wire immersion glue, drying obtains prepreg cloth after taking-up, then by prepreg cloth
Cut out according to design size, pipe crimping, tape wrap are fastened, are heating and curing, be stripped after obtain pole embryo, last pole embryo through polishing, application and
Fishing rod is made after assembling.
The step 1) in reactor reaction temperature be 130-150 DEG C, the reaction time is 1-2h.
The step 4) in organic solvent be one in the low boiling point solvent such as ketone, esters, ether alcohol class or chlorinated hydrocarbon
Plant or several combinations；
The beneficial effects of the invention are as follows：The Recipe of raw material is novel, and cost of material is low, the fishing rod made using the raw material
Good toughness, light weight, with certain insulating properties, material is tieed up using carbon and is fabricated by existing product character hair compared with the market
Give birth to more superior than pure carbon fishing rod in some changes, performance, quality is lighter, and intensity is bigger, prevented disconnected pole, broken string；Simultaneously can
Avoid recreational fishing thunderbolt, electric shock accidents from occurring, effectively reduce the unexpected rate in thundery sky outdoor fishing.
Embodiment：
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below
Specific example is closed, the present invention is expanded on further.
Embodiment 1：A kind of raw material for making carbon fiber fishing rod, is prepared from the following components：
Glass fibre, nanometer boron fibre, carbon fiber, titanium alloy wire, polyurethane, epoxy resin, expoxy propane, linear poly- third
Alkene, Brazil wax, dibutyl ester, oxidized starch, epoxy hardener and organic solvent；
Then：
1) in proportion successively by polyurethane, epoxy resin, expoxy propane, linear polypropylene, Brazil wax, dibutyl ester and
Oxidized starch adds reactor, by mixture temperature reaction after being sufficiently mixed uniformly, and reaction is filtrated to get mixture after terminating；
2) by step 1) prepare mixture add reactor, obtain composite wood after then adding epoxy hardener, mixing
Material, reaction temperature is 150 DEG C, and the reaction time is 1h；
3) by step 2) in composite be put into microwave 15 minutes under microwave environment, microwave frequency is：800MHz；
4) by step 3) in the composite for preparing the glue that solid content is 50% is configured to organic solvent, then by glass
In fiber, nanometer boron fibre, carbon fiber and titanium alloy wire immersion glue, drying obtains prepreg cloth after taking-up, then by prepreg cloth
Cut out according to design size, pipe crimping, tape wrap are fastened, are heating and curing, be stripped after obtain pole embryo, last pole embryo through polishing, application and
Fishing rod is made after assembling.
Embodiment 2：
A kind of raw material for making carbon fiber fishing rod, is prepared from the following components：
Glass fibre, nanometer boron fibre, carbon fiber, titanium alloy wire, polyurethane, epoxy resin, expoxy propane, linear poly- third
Alkene, Brazil wax, dibutyl ester, oxidized starch, epoxy hardener and organic solvent；
Then：
1) in proportion successively by polyurethane, epoxy resin, expoxy propane, linear polypropylene, Brazil wax, dibutyl ester and
Oxidized starch adds reactor, by mixture temperature reaction after being sufficiently mixed uniformly, and reaction is filtrated to get mixture after terminating；
2) by step 1) prepare mixture add reactor, obtain composite wood after then adding epoxy hardener, mixing
Material, reaction temperature is 130 DEG C, and the reaction time is 2h；
3) by step 2) in composite be put into microwave 15 minutes under microwave environment, microwave frequency is：900MHz；
4) by step 3) in the composite for preparing the glue that solid content is 50% is configured to organic solvent, then by glass
In fiber, nanometer boron fibre, carbon fiber and titanium alloy wire immersion glue, drying obtains prepreg cloth after taking-up, then by prepreg cloth
Cut out according to design size, pipe crimping, tape wrap are fastened, are heating and curing, be stripped after obtain pole embryo, last pole embryo through polishing, application and
Fishing rod is made after assembling.
Embodiment 3：
A kind of raw material for making carbon fiber fishing rod, is prepared from the following components：
Glass fibre, nanometer boron fibre, carbon fiber, titanium alloy wire, polyurethane, epoxy resin, expoxy propane, linear poly- third
Alkene, Brazil wax, dibutyl ester, oxidized starch, epoxy hardener and organic solvent；
Then：
1) in proportion successively by polyurethane, epoxy resin, expoxy propane, linear polypropylene, Brazil wax, dibutyl ester and
Oxidized starch adds reactor, by mixture temperature reaction after being sufficiently mixed uniformly, and reaction is filtrated to get mixture after terminating；
2) by step 1) prepare mixture add reactor, obtain composite wood after then adding epoxy hardener, mixing
Material, reaction temperature is 140 DEG C, and the reaction time is 1.5h；
3) by step 2) in composite be put into microwave 15 minutes under microwave environment, microwave frequency is：
850MHzMHz；
4) by step 3) in the composite for preparing the glue that solid content is 50% is configured to organic solvent, then by glass
In fiber, nanometer boron fibre, carbon fiber and titanium alloy wire immersion glue, drying obtains prepreg cloth after taking-up, then by prepreg cloth
Cut out according to design size, pipe crimping, tape wrap are fastened, are heating and curing, be stripped after obtain pole embryo, last pole embryo through polishing, application and
Fishing rod is made after assembling.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (3)
1. a kind of raw material for making carbon fiber fishing rod, it is characterised in that：It is prepared from the following components：
Glass fibre, nanometer boron fibre, carbon fiber, titanium alloy wire, polyurethane, epoxy resin, expoxy propane, linear polypropylene,
Brazil wax, dibutyl ester, oxidized starch, epoxy hardener and organic solvent.
2. the method for fishing rod is prepared using the raw material described in claim 1, it is characterised in that：Comprise the following steps：1) in proportion
Polyurethane, epoxy resin, expoxy propane, linear polypropylene, Brazil wax, dibutyl ester and oxidized starch are added successively and reacted
Kettle, by mixture temperature reaction after being sufficiently mixed uniformly, reaction is filtrated to get mixture after terminating；
2) by step 1) prepare mixture add reactor, obtain composite after then adding epoxy hardener, mixing；
3) by step 2) in composite be put into microwave 15 minutes under microwave environment, microwave frequency is：800MHz-
900MHz；
4) by step 3) in the composite for preparing the glue that solid content is 50% is configured to organic solvent, then by glass fibers
In dimension, nanometer boron fibre, carbon fiber and titanium alloy wire immersion glue, drying obtains prepreg cloth after taking-up, then presses prepreg cloth
Cut out according to design size, pipe crimping, tape wrap are fastened, are heating and curing, be stripped after obtain pole embryo, last pole embryo is through polishing, application and dress
Fishing rod is made after matching somebody with somebody.
3. the preparation method of fishing rod according to claim 2, it is characterised in that：Step 1) in the reaction temperature of reactor be
130-150 DEG C, the reaction time is 1-2h.