CN106832927A - Prepare compound material of carbon fiber fishing rod and preparation method thereof - Google Patents
Prepare compound material of carbon fiber fishing rod and preparation method thereof Download PDFInfo
- Publication number
- CN106832927A CN106832927A CN201710053432.2A CN201710053432A CN106832927A CN 106832927 A CN106832927 A CN 106832927A CN 201710053432 A CN201710053432 A CN 201710053432A CN 106832927 A CN106832927 A CN 106832927A
- Authority
- CN
- China
- Prior art keywords
- parts
- carbon fiber
- fishing rod
- composite
- polyimides
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of composite for preparing carbon fiber fishing rod, is related to fishing gear technical field, is prepared from by the component of following mass fraction meter:Polyimides, carbon fiber, polyethylene fibre, titanium alloy wire, aramid fiber, Teflon, magnesium carbonate, calcium stearate, diphenyl silanediol, coumarone indeneresin, rosin.The Recipe of raw material of the present invention is novel, and cost of material is low, using the fishing rod good toughness of raw material making, light weight, with preferable antioxygenic property and antistatic property.
Description
Technical field:
The present invention relates to fishing gear technical field, and in particular to a kind of composite for preparing carbon fiber fishing rod and its preparation side
Method.
Background technology:
With the continuous improvement of people's living standard, fish and have become a kind of important amusement of people, stress-relieving activity, it is competing
Skill fishing frequent development also like a raging fire, fishing rod in the market is mostly carbon fiber fishing rod, is used without shuttle
Spin carbon fiber longitudinal direction cloth tubulation, solidify through resin pickup and manufacture, for fishing rod production in terms of carbon fiber content how much, directly
Determine fishing rod value and grade, general phosphorus content be 30%, 90% or so, the fishing rod manufactured with carbon fiber have it is light, solid,
The characteristics of tensile strength is high, existing manufacture fishing rod material although already have excellent tensile strength, yield strength and
The mechanical performances such as elongation, but its antistatic property, toughness and ageing-resistant performance be not high, in use or with limit
Many restrictions processed.
The content of the invention:
The technical problems to be solved by the invention are to provide a kind of composite for preparing carbon fiber fishing rod, the raw material
Recipe is novel, and cost of material is low, using the fishing rod good toughness of raw material making, light weight, with preferable inoxidizability
Energy and antistatic property.
The technical problems to be solved by the invention are realized using following technical scheme:
A kind of composite for preparing carbon fiber fishing rod, is prepared from by the component of following mass fraction meter:Polyimides
50~70 parts, 20~30 parts of carbon fiber, 15~30 parts of polyethylene fibre, 10~20 parts of titanium alloy wire, 2~8 parts of aramid fiber is special
5~13 parts of fluorine dragon, 5~8 parts of magnesium carbonate, 4~10 parts of calcium stearate, 3~5 parts of diphenyl silanediol, coumarone indeneresin 5~8
Part, 5~10 parts of rosin;
The preparation method of above-mentioned composite is:
1) by polyimides, carbon fiber, polyethylene fibre, titanium alloy wire, aramid fiber, Teflon, input mixer in,
Rotating speed be 500r/min, temperature be 40~60 DEG C at be well mixed;
2) by the 10~15min of raw material ultrasound in above-mentioned steps;
3) and then put it into magnesium carbonate, calcium stearate, diphenyl silanediol, coumarone indene tree are added in reactor
Fat, rosin are reacted, with 300~400 DEG C of thermotonus 30~45 minutes;
3) by reacted mixed material in double screw extruder extruding pelletization, obtain final product manufacture fishing rod composite wood
Material, wherein extrusion temperature are 280 DEG C, and screw speed is 250r/min;
The beneficial effects of the invention are as follows:The Recipe of raw material is novel, and cost of material is low, the fishing rod made using the raw material
Good toughness, light weight, with preferable antioxygenic property and antistatic property.
Specific embodiment:
In order that technological means, creation characteristic, reached purpose and effect that the present invention is realized are easy to understand, tie below
Specific example is closed, the present invention is expanded on further.
Embodiment 1:A kind of composite for preparing carbon fiber fishing rod, is prepared from by the component of following mass fraction meter:
50 parts of polyimides, 20 parts of carbon fiber, 15 parts of polyethylene fibre, 10 parts of titanium alloy wire, 2 parts of aramid fiber, 13 parts of Teflon, carbon
8 parts of sour magnesium, 10 parts of calcium stearate, 5 parts of diphenyl silanediol, 8 parts of coumarone indeneresin, 5 parts of rosin;
The preparation method for preparing the composite of carbon fiber fishing rod is:
1) by polyimides, carbon fiber, polyethylene fibre, titanium alloy wire, aramid fiber, Teflon, input mixer in,
Rotating speed be 500r/min, temperature be 40 DEG C at be well mixed;
2) by the raw material ultrasound 15min in above-mentioned steps;
3) and then put it into magnesium carbonate, calcium stearate, diphenyl silanediol, coumarone indene tree are added in reactor
Fat, rosin are reacted, with 300 DEG C of thermotonus 45 minutes;
3) by reacted mixed material in double screw extruder extruding pelletization, obtain final product manufacture fishing rod composite wood
Material, wherein extrusion temperature are 280 DEG C, and screw speed is 250r/min.
Embodiment 2:
A kind of composite for preparing carbon fiber fishing rod, is prepared from by the component of following mass fraction meter:Polyimides
60 parts, 25 parts of carbon fiber, 20 parts of polyethylene fibre, 15 parts of titanium alloy wire, 4 parts of aramid fiber, 8 parts of Teflon, 6 parts of magnesium carbonate,
7 parts of calcium stearate, 4 parts of diphenyl silanediol, 6 parts of coumarone indeneresin, 8 parts of rosin;
The preparation method of above-mentioned composite is:
1) by polyimides, carbon fiber, polyethylene fibre, titanium alloy wire, aramid fiber, Teflon, input mixer in,
Rotating speed be 500r/min, temperature be 48 DEG C at be well mixed;
2) by the raw material ultrasound 12min in above-mentioned steps;
3) and then put it into magnesium carbonate, calcium stearate, diphenyl silanediol, coumarone indene tree are added in reactor
Fat, rosin are reacted, with 350 DEG C of thermotonus 38 minutes;
3) by reacted mixed material in double screw extruder extruding pelletization, obtain final product manufacture fishing rod composite wood
Material, wherein extrusion temperature are 280 DEG C, and screw speed is 250r/min.
Embodiment 3:
A kind of composite for preparing carbon fiber fishing rod, is prepared from by the component of following mass fraction meter:Polyimides
70 parts, 30 parts of carbon fiber, 30 parts of polyethylene fibre, 20 parts of titanium alloy wire, 8 parts of aramid fiber, 13 parts of Teflon, 8 parts of magnesium carbonate,
4 parts of calcium stearate, 3 parts of diphenyl silanediol, 5 parts of coumarone indeneresin, 5 parts of rosin;
The preparation method of above-mentioned composite is:
1) by polyimides, carbon fiber, polyethylene fibre, titanium alloy wire, aramid fiber, Teflon, input mixer in,
Rotating speed be 500r/min, temperature be 60 DEG C at be well mixed;
2) by the raw material ultrasound 10min in above-mentioned steps;
3) and then put it into magnesium carbonate, calcium stearate, diphenyl silanediol, coumarone indene tree are added in reactor
Fat, rosin are reacted, with 300 DEG C of thermotonus 45 minutes;
3) by reacted mixed material in double screw extruder extruding pelletization, obtain final product manufacture fishing rod composite wood
Material, wherein extrusion temperature are 280 DEG C, and screw speed is 250r/min;
4) by step 3) in the composite organic solvent for preparing be configured to the glue that solid content is 50%, then by glass
In fiber, carbon nano-fiber, carbon fiber and titanium alloy wire immersion glue, drying obtains prepreg cloth after taking-up, then by prepreg cloth
Cut out according to design size, pipe crimping, tape wrap are fastened, be heating and curing, pole embryo is obtained after the demoulding, last pole embryo through polishing, application and
Fishing rod is made after assembling.
General principle of the invention and principal character and advantages of the present invention has been shown and described above.The technology of the industry
Personnel it should be appreciated that the present invention is not limited to the above embodiments, simply explanation described in above-described embodiment and specification this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appending claims and its
Equivalent thereof.
Claims (4)
1. a kind of composite for preparing carbon fiber fishing rod, it is characterised in that:It is prepared from by the component of following mass fraction meter:
50~70 parts of polyimides, 20~30 parts of carbon fiber, 15~30 parts of polyethylene fibre, 10~20 parts of titanium alloy wire, aramid fiber 2
~8 parts, 5~13 parts of Teflon, 5~8 parts of magnesium carbonate, 4~10 parts of calcium stearate, 3~5 parts of diphenyl silanediol, coumarone indene
5~8 parts of resin, 5~10 parts of rosin.
2. a kind of preparation method of the composite for preparing carbon fiber fishing rod, it is characterised in that:
1) by polyimides, carbon fiber, polyethylene fibre, titanium alloy wire, aramid fiber, Teflon, input mixer, turning
Speed is 500r/min, temperature is well mixed at 40~60 DEG C;
2) by the 10~15min of raw material ultrasound in above-mentioned steps;
3) and then put it into magnesium carbonate, calcium stearate, diphenyl silanediol, coumarone indeneresin, pine are added in reactor
Perfume (or spice) is reacted, with 300~400 DEG C of thermotonus 30~45 minutes;
4) by reacted mixed material in double screw extruder extruding pelletization, obtain final product manufacture fishing rod composite, its
Middle extrusion temperature is 280 DEG C, and screw speed is 250r/min.
3. the composite for preparing carbon fiber fishing rod according to claim 1, it is characterised in that:By following mass fraction meter
Component be prepared from:50 parts of polyimides, 20 parts of carbon fiber, 15 parts of polyethylene fibre, 10 parts of titanium alloy wire, aramid fiber 2
Part, 13 parts of Teflon, 8 parts of magnesium carbonate, 10 parts of calcium stearate, 5 parts of diphenyl silanediol, 8 parts of coumarone indeneresin, 5 parts of rosin.
4. the composite for preparing carbon fiber fishing rod according to claim 1, it is characterised in that:By following mass fraction meter
Component be prepared from:60 parts of polyimides, 25 parts of carbon fiber, 20 parts of polyethylene fibre, 15 parts of titanium alloy wire, aramid fiber 4
Part, 8 parts of Teflon, 6 parts of magnesium carbonate, 7 parts of calcium stearate, 4 parts of diphenyl silanediol, 6 parts of coumarone indeneresin, 8 parts of rosin.