CN107029756A - 一种固相制备硫化锌‑硫化银异质结复合材料的方法 - Google Patents
一种固相制备硫化锌‑硫化银异质结复合材料的方法 Download PDFInfo
- Publication number
- CN107029756A CN107029756A CN201710404681.1A CN201710404681A CN107029756A CN 107029756 A CN107029756 A CN 107029756A CN 201710404681 A CN201710404681 A CN 201710404681A CN 107029756 A CN107029756 A CN 107029756A
- Authority
- CN
- China
- Prior art keywords
- zinc sulphide
- silver sulfide
- solid phase
- heterojunction composite
- sulfide heterojunction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种固相制备硫化锌‑硫化银异质结复合材料的方法，属于纳米材料制备领域。该方法是将金属锌盐、十二烷基硫酸钠、硫代乙酰胺和醋酸银在室温条件下依次混合研磨反应，实现了硫化锌‑硫化银异质结复合材料的低热固相合成。本发明制备硫化锌‑硫化银异质结复合材料的低热固相化学法具有操作简单、不使用溶剂、高产率、成本低、合成工艺简单等特点；且本发明制备的硫化锌‑硫化银异质结复合材料具有大的比表面积和高的反应活性，将在太阳能电池、光催化等领域具有广阔的应用前景。
Description
技术领域
本发明涉及一种固相制备硫化锌-硫化银异质结复合材料的方法，属于纳米材料制备领域。
背景技术
近年来，纳米材料由于其本身所具有的独特的物理化学特性而受到了科研工作者的广泛关注。硫化锌作为一种十分重要的半导体纳米材料，因其具有特异的光、电、热、磁等性质，而在半导体发光器件、化工、国防、光催化等领域表现出巨大的应用前景。然而，硫化锌的禁带较宽，对可见光吸收弱成为制约其实际应用的重要因素。因而，对硫化锌光催化材料进行改性研究是非常重要的研究领域。研究发现，利用异质结构可有效改善其性能。硫化银纳米材料因产生较大的比表面以及量子尺寸效应，在光吸收、传感、催化等方面有重要的潜在应用，为此将硫化锌与硫化银复合可有效地改善其性能。
目前，制备硫化锌-硫化银异质结复合材料的方法包括水热法和微波法等，然而这些方法涉及到实验条件苛刻、能耗高等不足，因而开发一种简单、高产、环境友好的合成方法仍然十分迫切。低热固相化学法具有操作简单、成本低、产量高和环境友好等优点，已经成为合成纳米材料的一种有效方法。
发明内容
本发明的目的在于提供一种固相制备硫化锌-硫化银异质结复合材料的方法，是以十二烷基硫酸钠为表面活性剂，采用低热固相化学反应来制备硫化锌-硫化银异质结复合材料。该方法克服了硫化锌纳米材料在制备过程中发生严重团聚现象，并实现了硫化锌与硫化银的复合。
本发明公开了一种固相制备硫化锌-硫化银异质结复合材料的方法。本发明的方法是用金属锌盐、十二烷基硫酸钠、硫代乙酰胺和醋酸银依次混合研磨发生反应进而实现硫化锌-硫化银异质结复合材料的低热固相化学制备。
本发明以十二烷基硫酸钠为表面活性剂固相制备硫化锌-硫化银异质结复合材料的方法操作简单、不使用溶剂、高产率、成本低，为硫化锌基复合材料的制备提供了一种新的思路。
附图说明
图1为固相制备硫化锌-硫化银异质结复合材料的透射电镜图。
具体实施方式
固相制备硫化锌-硫化银异质结复合材料的方法，按以下步骤进行：
具体实施方式1：准确称取0.009摩尔的醋酸锌置于玛瑙研钵中，将其充分研细后加入0.005摩尔十二烷基硫酸钠，研磨60分钟后加入0.01摩尔硫代乙酰胺，研磨60分钟混合均匀后加入0.002摩尔醋酸银，再将其充分研磨60分钟并放置3小时以确保固相反应完全。用去离子水和无水乙醇将其洗涤、抽滤，于干燥箱中60度干燥2小时即得硫化锌-硫化银异质结复合材料。
具体实施方式2：准确称取0.009摩尔的氯酸锌置于玛瑙研钵中，将其充分研细后加入0.005摩尔十二烷基硫酸钠，研磨60分钟后加入0.01摩尔硫代乙酰胺，研磨60分钟混合均匀后加入0.002摩尔醋酸银，再将其充分研磨60分钟并放置3小时以确保固相反应完全。用去离子水和无水乙醇将其洗涤、抽滤，于干燥箱中60度干燥2小时即得硫化锌-硫化银异质结复合材料。
具体实施方式3：准确称取0.009摩尔的硫酸锌置于玛瑙研钵中，将其充分研细后加入0.005摩尔十二烷基硫酸钠，研磨60分钟后加入0.01摩尔硫代乙酰胺，研磨60分钟混合均匀后加入0.002摩尔醋酸银，再将其充分研磨60分钟并放置3小时以确保固相反应完全。用去离子水和无水乙醇将其洗涤、抽滤，于干燥箱中60度干燥2小时即得硫化锌-硫化银异质结复合材料。
具体实施方式4：准确称取0.009摩尔的硝酸锌置于玛瑙研钵中，将其充分研细后加入0.005摩尔十二烷基硫酸钠，研磨60分钟后加入0.01摩尔硫代乙酰胺，研磨60分钟混合均匀后加入0.002摩尔醋酸银，再将其充分研磨60分钟并放置3小时以确保固相反应完全。用去离子水和无水乙醇将其洗涤、抽滤，于干燥箱中60度干燥2小时即得硫化锌-硫化银异质结复合材料。
Claims (1)
1.一种固相法制备硫化锌-硫化银异质结纳米片的方法，其特征是将适量金属锌盐置于玛瑙研钵中，研细后加入十二烷基硫酸钠，研磨后加入硫代乙酰胺，研磨后加入适量醋酸银，再充分研磨并放置完成固相反应，用去离子水和无水乙醇洗涤，抽滤，在干燥箱中60度干燥2小时制得硫化锌-硫化银异质结复合材料。