CN107022897A - A kind of processing technology of anti-chiseling down silk quilt - Google Patents
A kind of processing technology of anti-chiseling down silk quilt Download PDFInfo
- Publication number
- CN107022897A CN107022897A CN201610068540.2A CN201610068540A CN107022897A CN 107022897 A CN107022897 A CN 107022897A CN 201610068540 A CN201610068540 A CN 201610068540A CN 107022897 A CN107022897 A CN 107022897A
- Authority
- CN
- China
- Prior art keywords
- silk
- processing
- quilt
- fabric
- silk quilt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of processing technology of anti-chiseling down silk quilt, processing technology includes the procedure of processing of silk：From doupion silk and upper silk, its mass ratio is 60-55:40-45；In refining pond, the aqueous solution that pH value is the electric point ± 0.5 of silk, bath raio 1 are configured with sulfuric acid:5-15 weighs silk, is immersed in 30-70min in sulfuric acid solution；In refining pond, with bath raio 1:5-15 configuration concentrations are the aqueous solution of 0.02%-2% epoxypropyl tri alkyl quaternary ammonium salts, and aqueous temperature is controlled at 60-120 DEG C, and adjustment pH value of water solution is 5.5-8.5, and the silk that wettability treatment is crossed is added thereto into immersion 60-90 minutes, is then dehydrated；Using hydrophilic silicon oil Goon1260, consumption is 2-5%o.w.f, and bath raio is 1:5-15, it is 30-50 DEG C to arrange temperature, and the time is 15-30 minutes；Warp thread, the weft yarn of silk quilt fabric use 60S tencels, and processing is combined to silk and fabric finally by silk quilt processing machine, and silk quilt is made in processing.Silk quilt antistatic behaviour produced by the present invention is high, will not bore suede.
Description
Technical field
The present invention relates to a kind of processing technology of silk quilt, more particularly to a kind of processing work of anti-chiseling down silk quilt
Skill.
Background technology
Silk is that secreted silk liquid is concretionary continuous " long fibre " when matured silkworm cocoons, be in nature most
Can easily it be restored to the original state after soft most thin natural fiber, revocation external force, it is not caking for doing core, do not send out
It is vexed, do not shrink, homogeneous soft, can use for a long time.Contain the necessary amino acid of a variety of human bodies, tool in silk
Have functions that it is windproof, dehumidify, calm the nerves, nourishing and balanced human's skin.In addition, compliance and the guarantor of silk
Warm property is splendid, and has effects that the sweat gas that the body of absorption and dialysis people are produced in deep sleep, with silkworm
Silk as the silk quilt of filling have more the advantageous quality such as soft, personal, warming, Breathable healthcare and
Advantage, it is very welcomed by the people.But it is due to silk silk thinner than common fiberfill fibers and natural
Due to friction, drawn in use, the influence of the factor such as heated-air drying is easy to produce electrostatic, leads
Cause silk quilt to be easy to bore suede, greatly reduce the comfortableness that silk quilt is used.Zhou Jidong have studied《It is a kind of
The preparation method of antistatic silk fabric》, silk fabric is arranged using polyoxyethylene alkyl amine, greatly
The big antistatic property for improving silk fabric, but the method employs adhesive progress gluing, to silk fabric
Feel have very macrolesion, applied to silk quilt silk arrange it is infeasible.
The content of the invention
It is high the technical problem to be solved in the present invention is to provide a kind of antistatic behaviour, the anti-chiseling down silk of suede will not be bored
The processing technology of quilt.
To reach above-mentioned purpose, technical scheme is as follows：
A kind of processing technology of anti-chiseling down silk quilt, the processing technology includes processing and the silk quilt cover of silk
The processing of material；
The processing of the silk comprises the following steps：
(1) selection of silk, from doupion silk and upper silk, its mass ratio is 60-55:40-45；
(2) antistatic treatment on silk surface；
(2.1) silk wettability treatment, in refining pond, it is silk isoelectric point ± 0.5 to configure pH value with sulfuric acid
The aqueous solution, bath raio 1:5-15 weighs silk, is immersed in 30-70min in sulfuric acid solution；
(2.2) silk antistatic treatment, in refining pond, with bath raio 1:5-15 configuration concentrations are 0.02%-2%
The aqueous solution of epoxypropyl tri alkyl quaternary ammonium salt, aqueous temperature is controlled at 60-120 DEG C, adjusts the aqueous solution
PH value is 5.5-8.5, and the silk that wettability treatment is crossed is added thereto into immersion 60-90 minutes, is then dehydrated；
(2.3) the hydrophilic soft treatment of silk, using hydrophilic silicon oil Goon1260, consumption is 2-5%o.w.f,
Bath raio is 1:5-15, it is 30-50 DEG C to arrange temperature, and the time is 15-30 minutes；
The processing of silk quilt fabric comprises the following steps：
(1) warp thread, weft yarn use 60S tencels, and density is 120 × 100/10cm, using weaving cotton cloth
Machine is processed, the fabric processed be 2 on/1 under institutional framework；
Processing is combined to silk and fabric finally by silk quilt processing machine, silk quilt is made in processing.
In one embodiment of the invention, also need to carry out at windproof softness the silk quilt fabric processed
Manage, specific method is：Using the special aliphatic high-molecular compound emulsion King-tech containing organosilicon
TK-803 and hydrophilic silicon oil Goon1260 combination solutions, it is TK-803 that it, which is matched,：Goon1260：Water
For：6-10%:3-5%：85-91%, then pads silk quilt fabric in combination solution, and pick-up is 70%,
Then drying and processing is carried out, drying temperature is 100-120 DEG C, and the time is 40-60s.
In one embodiment of the invention, obtained silk quilt tire compressive recovery rate≤95%.
In one embodiment of the invention, the resistivity on the silk surface after antistatic treatment is 1.0
×1010-1.0×1013Between.
In one embodiment of the invention, brill suede amount≤30 of the fabric Jing Guo windproof soft treatment
Root/cm2。
By above-mentioned technical proposal, the beneficial effects of the invention are as follows：
The present invention selects the silk of high-quality, and carries out antistatic treatment and hydrophilic soft treatment to silk,
Windproof soft treatment is carried out from highdensity fabric, and to fabric；It causes the silk quilt processed to have
Have the advantages that antistatic property is strong, anti-chiseling down is good, flexibility is good.
Embodiment
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand,
The present invention is further elucidated below.
Embodiment 1
A kind of processing technology of anti-chiseling down silk quilt, the processing technology includes processing and the silk quilt fabric of silk
Processing；
The processing of the silk comprises the following steps：
(1) selection of silk, from doupion silk and upper silk, its mass ratio is 60:40；Doupion silk and upper
Silk has more preferable antistatic property compared to common silk；
(2) antistatic treatment on silk surface；
(2.1) silk wettability treatment, is the electric point ± 0.5 of silk with sulfuric acid configuration pH value in refining pond
The aqueous solution, bath raio 1:5 weigh silk, are immersed in 30min in sulfuric acid solution；
(2.2) silk antistatic treatment, in refining pond, with bath raio 1:5 configuration concentrations are 0.02% epoxy radicals
The aqueous solution of propyl group tri alkyl quaternary ammonium salt, aqueous temperature is controlled at 60 DEG C, and adjustment pH value of water solution is 5.5,
The silk that wettability treatment is crossed is added thereto immersion 60 minutes, is then dehydrated；After antistatic treatment
The resistivity on silk surface is 1.0 × 1010-1.0×1013Between.
(2.3) the hydrophilic soft treatment of silk, using hydrophilic silicon oil Goon1260, consumption is 2%o.w.f,
Bath raio is 1:5, it is 30 DEG C to arrange temperature, and the time is 15 minutes.
The processing of silk quilt fabric comprises the following steps：
(1) warp thread, weft yarn use 60S tencels, and density is 120 × 100/10cm, using weaving cotton cloth
Machine is processed, the fabric processed be 2 on/1 under institutional framework.
(2) windproof soft treatment, using the special aliphatic high-molecular compound emulsion containing organosilicon
King-tech TK-803 and hydrophilic silicon oil Goon1260 combination solutions, it is TK-803 that it, which is matched,：
Goon1260：Water is：6%:3%：91%, then silk quilt fabric is padded in combination solution, pick-up
For 70%, drying and processing is then carried out, drying temperature is 100- DEG C, and the time is 40s；By windproof softness
Brill suede amount≤30 piece/cm2 of the fabric of processing；Fabric is using 60S tencels as raw material, and it has high density
Property, and windproof soft treatment is carried out, it not only increases the anti-chiseling down effect of fabric, while ensure that face
The flexibility of material.
Processing is combined to silk and fabric finally by silk quilt processing machine, silk quilt is made in processing, and
Obtained silk quilt tire compressive recovery rate≤95%.
Embodiment 2
A kind of processing technology of anti-chiseling down silk quilt, the processing technology includes processing and the silk quilt fabric of silk
Processing；
The processing of the silk comprises the following steps：
(1) selection of silk, from doupion silk and upper silk, its mass ratio is 58:42；Doupion silk and
Upper silk has more preferable antistatic property compared to common silk；
(2) antistatic treatment on silk surface；
(2.1) silk wettability treatment, is the electric point ± 0.5 of silk with sulfuric acid configuration pH value in refining pond
The aqueous solution, bath raio 1:10 weigh silk, are immersed in 50min in sulfuric acid solution；
(2.2) silk antistatic treatment, in refining pond, with bath raio 1:10 configuration concentrations are 1% epoxy radicals third
The aqueous solution of base tri alkyl quaternary ammonium salt, aqueous temperature is controlled at 90 DEG C, and adjustment pH value of water solution is 7,
The silk that wettability treatment is crossed is added thereto immersion 80 minutes, is then dehydrated；After antistatic treatment
The resistivity on silk surface is 1.0 × 1010-1.0×1013Between.
(2.3) the hydrophilic soft treatment of silk, using hydrophilic silicon oil Goon1260, consumption is 3%o.w.f,
Bath raio is 1:10, it is 40 DEG C to arrange temperature, and the time is 20 minutes.
The processing of silk quilt fabric comprises the following steps：
(1) warp thread, weft yarn use 60S tencels, and density is 120 × 100/10cm, using weaving cotton cloth
Machine is processed, the fabric processed be 2 on/1 under institutional framework.
(2) windproof soft treatment, using the special aliphatic high-molecular compound emulsion containing organosilicon
King-tech TK-803 and hydrophilic silicon oil Goon1260 combination solutions, it is TK-803 that it, which is matched,：
Goon1260：Water is：8%:4%：88%, then silk quilt fabric is padded in combination solution, pick-up
For 70%, drying and processing is then carried out, drying temperature is 110 DEG C, and the time is 50s；By windproof softness
Brill suede amount≤30 piece/cm2 of the fabric of processing；Fabric is using 60S tencels as raw material, and it has high density
Property, and windproof soft treatment is carried out, it not only increases the anti-chiseling down effect of fabric, while ensure that face
The flexibility of material.
Processing is combined to silk and fabric finally by silk quilt processing machine, silk quilt is made in processing, and
Obtained silk quilt tire compressive recovery rate≤95%.
Embodiment 3
A kind of processing technology of anti-chiseling down silk quilt, the processing technology includes processing and the silk quilt fabric of silk
Processing；
The processing of the silk comprises the following steps：
(1) selection of silk, from doupion silk and upper silk, its mass ratio is 55:45；Doupion silk and
Upper silk has more preferable antistatic property compared to common silk；
(2) antistatic treatment on silk surface；
(2.1) silk wettability treatment, is the electric point ± 0.5 of silk with sulfuric acid configuration pH value in refining pond
The aqueous solution, bath raio 1:15 weigh silk, are immersed in 70min in sulfuric acid solution；
(2.2) silk antistatic treatment, in refining pond, with bath raio 1:15 configuration concentrations are 2% epoxy radicals
The aqueous solution of propyl group tri alkyl quaternary ammonium salt, aqueous temperature is controlled at 120 DEG C, and adjustment pH value of water solution is
8.5, the silk that wettability treatment is crossed is added thereto immersion 90 minutes, is then dehydrated；By antistatic treatment
The resistivity on silk surface afterwards is 1.0 × 1010-1.0×1013Between.
(2.3) the hydrophilic soft treatment of silk, using hydrophilic silicon oil Goon1260, consumption is 5%o.w.f,
Bath raio is 1:15, it is 50 DEG C to arrange temperature, and the time is 30 minutes.
The processing of silk quilt fabric comprises the following steps：
(1) warp thread, weft yarn use 60S tencels, and density is 120 × 100/10cm, using weaving cotton cloth
Machine is processed, the fabric processed be 2 on/1 under institutional framework.
(2) windproof soft treatment, using the special aliphatic high-molecular compound emulsion containing organosilicon
King-tech TK-803 and hydrophilic silicon oil Goon1260 combination solutions, it is TK-803 that it, which is matched,：
Goon1260：Water is：10%:5%：85%, then silk quilt fabric is padded in combination solution, rolls remaining
Rate is 70%, then carries out drying and processing, and drying temperature is 120 DEG C, and the time is 60s；By windproof soft
Brill suede amount≤30 piece/cm2 of the fabric of supple-settlement；Fabric is using 60S tencels as raw material, and it has highly dense
Degree property, and windproof soft treatment is carried out, it not only increases the anti-chiseling down effect of fabric, ensure that simultaneously
The flexibility of fabric.
Processing is combined to silk and fabric finally by silk quilt processing machine, silk quilt is made in processing, and
Obtained silk quilt tire compressive recovery rate≤95%.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The industry
Technical staff it should be appreciated that the present invention is not limited to the above embodiments, in above-described embodiment and specification
Merely illustrating the principles of the invention for description, it is without departing from the spirit and scope of the present invention, of the invention
Various changes and modifications are also had, these changes and improvements all fall within the protetion scope of the claimed invention.This
The claimed scope of invention is by appended claims and its equivalent thereof.
Claims (5)
1. a kind of processing technology of anti-chiseling down silk quilt, it is characterised in that the processing technology includes silk
Processing and silk quilt fabric processing；
The processing of the silk comprises the following steps：
(1) selection of silk, from doupion silk and upper silk, its mass ratio is 60-55:40-45；
(2) antistatic treatment on silk surface；
(2.1) silk wettability treatment, in refining pond, it is silk isoelectric point ± 0.5 to configure pH value with sulfuric acid
The aqueous solution, bath raio 1:5-15 weighs silk, is immersed in 30-70min in sulfuric acid solution；
(2.2) silk antistatic treatment, in refining pond, with bath raio 1:5-15 configuration concentrations are 0.02%-2%
The aqueous solution of epoxypropyl tri alkyl quaternary ammonium salt, aqueous temperature is controlled at 60-120 DEG C, adjusts the aqueous solution
PH value is 5.5-8.5, and the silk that wettability treatment is crossed is added thereto into immersion 60-90 minutes, is then dehydrated；
(2.3) the hydrophilic soft treatment of silk, using hydrophilic silicon oil Goon1260, consumption is 2-5%o.w.f,
Bath raio is 1:5-15, it is 30-50 DEG C to arrange temperature, and the time is 15-30 minutes；
The processing of silk quilt fabric comprises the following steps：
(1) warp thread, weft yarn use 60S tencels, and density is 120 × 100/10cm, using weaving cotton cloth
Machine is processed, the fabric processed be 2 on/1 under institutional framework；
Processing is combined to silk and fabric finally by silk quilt processing machine, silk quilt is made in processing.
2. a kind of processing technology of anti-chiseling down silk quilt according to claim 1, it is characterised in that
Also need to carry out windproof soft treatment to the silk quilt fabric processed, specific method is：Using containing organosilicon
Special aliphatic high-molecular compound emulsion King-tech TK-803 and hydrophilic silicon oil Goon1260
Combination solution, it is TK-803 that it, which is matched,：Goon1260：Water is 6-10%:3-5%：85-91%, then will
Silk quilt fabric is padded in combination solution, and pick-up is 70%, then carries out drying and processing, drying temperature
For 100-120 DEG C, the time is 40-60s.
3. a kind of processing technology of anti-chiseling down silk quilt according to claim 1, it is characterised in that
Obtained silk quilt tire compressive recovery rate≤95%.
4. a kind of processing technology of anti-chiseling down silk quilt according to claim 1, it is characterised in that
The resistivity on the silk surface after antistatic treatment is 1.0 × 1010-1.0×1013Between.
5. a kind of processing technology of anti-chiseling down silk quilt according to claim 2, it is characterised in that
Brill suede amount≤30 piece/cm of the fabric Jing Guo windproof soft treatment2。