CN105239372A - Novel light warm-keeping multi-functional baby sleeping bag fabric and preparation method thereof - Google Patents
Novel light warm-keeping multi-functional baby sleeping bag fabric and preparation method thereof Download PDFInfo
- Publication number
- CN105239372A CN105239372A CN201510681576.3A CN201510681576A CN105239372A CN 105239372 A CN105239372 A CN 105239372A CN 201510681576 A CN201510681576 A CN 201510681576A CN 105239372 A CN105239372 A CN 105239372A
- Authority
- CN
- China
- Prior art keywords
- fibre
- bag fabric
- lightweight thermal
- layer
- wool
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides novel light warm-keeping multi-functional baby sleeping bag fabric and preparation method thereof. The preparation method comprise the specific steps of immersing pre-treated natural colored cotton fibers in a solution containing medical zinc oxide and titanium dioxide, and obtaining anti-ultraviolet natural colored cotton fibers; making wool with impurities removed be subjected to low temperature air plasma treatment, then immersing the wool in a protease treatment solution, and obtaining shrinkproof antistatic wool; interweaving the anti-ultraviolet natural colored cotton fibers and antistatic wool fibers for forming an outer layer; interweaving ceramic fibers and bamboo carbon fibers for forming a non-woven fabric layer, laying silk fiber layers on the upper surface and the lower surface of the non-woven fabric layer, conducting needling and sealing, and forming a filling layer; immersing pre-treated 100% combed cotton fibers in liquefied ammonia, removing ammonia through microwaves, and then immersing the pre-treated 100% combed cotton fibers in an antibacterial treatment solution, conducting weaving, and forming an inner layer; sewing and compositing the outer layer, the filling layer and the inner layer in sequence, and forming the light warm-keeping multi-functional baby sleeping bag fabric.
Description
Technical field:
The invention belongs to textile material technical field, Multifunctional baby sleep bag fabric being specifically related to a kind of lightweight thermal and preparation method thereof.
Background technology:
Baby expires month children to an one full year of life after referring to birth, the body development of the baby in this period is incomplete, and bone is soft, and bear a pretty, delicate skin sensitivity, resistance is poor, behavioral activity can not be autonomous, and nervous system development is perfect not enough, and brain is easily tired, sleep occupies its most of the time of growing up, and the less length of one's sleep at age is longer, therefore baby sleep quality is very important, and the selection of baby bunting material also needs very prudent.
The multinomial aspects such as gas permeability, poisture-penetrability, security, surface property and appearance style mainly considered by the material of baby bunting.Moisture-penetrable ventilated is the important sanitary index of textile garment fabric, and baby due to metabolism fast, easy perspiration, bowel movement function is unsound, temperature reacts slow feature to external world, therefore baby bunting needs to possess excellent hygroscopicity, gas permeability and warmth retention property, to help baby's regulate body temperature, and acclimatization environment.Secondly sleeping bag needs soft so flexible, increases the sense of security in baby's sense of touch and the freedom in activity, also needs in addition to ensure security, prevents chemical noxious material from remaining and preventing electrostatic from producing.
The internal layer that baby bunting is generally divided into three layers: 100% combed cotton to prepare, skin prepared by packed layer, wool or pure cotton cloth prepared by chemical fibre cotton, cotton or silk, baby bunting material require accomplishes lightweight thermal, soft comfortable, safety and environmental protection, the health of the overweight big city baby of mistake increases pressure, the breathing of obstruction baby and blood circulation etc.The disclosed a kind of lightweight thermal baby bunting of Chinese patent CN102973070B (publication date 2013.3.20), comprise cotton skin and heating intermediate layer, wherein launch in intermediate layer containing bamboo-carbon fibre and titanium dioxide, the compound far infrared powder of zinc oxide, the method is by being shown in that day far infrared powder makes the weight of baby bunting reduce 30-50%, the temperature on sleeping bag surface is than infant temperature height 3-6 DEG C, warming effect is better than common baby bunting, but directly should contact with baby containing the bamboo-carbon fibre of far infrared powder, be easy to infiltrate through the tender and lovely skin of baby, cause allergic reaction, be not conducive to growing of baby.Chinese patent CN104687913A (publication date 2015.6.10) disclosed one Sleeping bag for children in summer, comprise textile flower, mulberry silk and mung bean shell, prepare Sleeping bag for children and there is good hygroscopicity and flexibility, cooling ventilating, smell is pure and fresh, the sleep of children can be promoted, be applicable to using summer.
From prior art, sleeping bag material at present for infant is still in relatively more conservative traditional field, sleeping bag functional single of preparation, lightweight thermal comfort property is limited, be unfavorable for the exquisite sleep quality ensureing infant, especially in comparatively cold autumn and winter season, more difficult balance warming and comfortable between relation, the Multifunctional baby sleep bag fabric therefore preparing a lightweight thermal seems particularly important.
Summary of the invention:
The technical problem to be solved in the present invention Multifunctional baby sleep bag fabric being to provide a kind of lightweight thermal and preparation method thereof, the Multifunctional baby sleep bag fabric of this lightweight thermal comprises skin, packed layer and internal layer, skin is uvioresistant natural color cotton and shrinkproof anlistatig wool, packed layer is silk, bamboo-carbon fibre and ceramic fibre, internal layer is 100% antibacterial combed cotton, and three is compounded to form the Multifunctional baby sleep bag fabric of lightweight thermal.The grammes per square metre that the present invention prepares the Multifunctional baby sleep bag fabric of lightweight thermal is light, and warmth retention property is good, and sense of touch is soft, soft comfortable, green safety, and also possessing uvioresistant, the function such as shrinkproof, antistatic, antibacterial, is a Multifunctional baby sleep bag fabric.
For solving the problems of the technologies described above, technical scheme of the present invention is:
A kind of Multifunctional baby sleep bag fabric of lightweight thermal, it is characterized in that, the Multifunctional baby sleep bag fabric of described lightweight thermal comprises skin, packed layer and internal layer, described skin is uvioresistant natural color cotton and shrinkproof anlistatig wool, described packed layer is silk, bamboo-carbon fibre and ceramic fibre, and described internal layer is 100% antibacterial combed cotton.
Preferably, the grammes per square metre of the Multifunctional baby sleep bag fabric of described lightweight thermal is 98-132g/ ㎡.
The present invention also provides a kind of preparation method of Multifunctional baby sleep bag fabric of lightweight thermal, it is characterized in that: comprise the following steps:
(1) impregnated in the ammonium oxalate solution of 5-6g/L by natural colorful cotton fibre and 100% combed cotton with bath raio 1:50,50-60 DEG C of constant temperature oscillation, take out, washing is dried, and obtains pretreated natural colorful cotton fibre and 100% combed cotton;
(2) pretreated natural colorful cotton fibre step (1) prepared impregnated in containing in medical zinc oxide and titania solution with bath raio 1:30, takes out, and dries washing oven dry and obtains uvioresistant natural colorful cotton fibre;
(3) by removing the wool of impurity after low temperature atomsphere plasma process, impregnated in the Protease Treatment liquid of 0.5-1g/L, taking out washing and drying, obtaining shrinkproof anlistatig wool;
(4) anlistatig wool fibre prepared by uvioresistant natural colorful cotton fibre step (2) prepared and step (3) carries out intertexture and forms skin;
(5) ceramic fibre and bamboo-carbon fibre are interweaved make nonwoven layer, lay silk fiber layer, the closely sealed formation packed layer of acupuncture in the upper and lower surface of nonwoven layer;
(6) impregnated in liquefied ammonia by 100% combing cotton fibre prepared by step (1), microwave is except after ammonia, and in the antimicrobial treatment solution that impregnated in 1-2g/L, dewatered drying, through weaving formation internal layer;
(7) packed layer prepared by skin step (4) prepared successively, step (5) and internal layer prepared by step (6) carry out seam and to spread out compound, form the Multifunctional baby sleep bag fabric of lightweight thermal.
Preferred as technique scheme, in described step (2), the content containing zinc oxide medical in medical zinc oxide and titania solution and titanium dioxide is 2-5g/L, and wherein the amount ratio of medical zinc oxide and titanium dioxide is 1:1.
Preferred as technique scheme, in described step (3), Protease Treatment liquid is cutinase and keratinase treatment fluid.
Preferred as technique scheme, in described step (4), in skin, the consumption of natural colorful cotton fibre and wool is 2-4:1.
Preferred as technique scheme, in described step (5), in packed layer, the mass ratio of ceramic fibre, bamboo-carbon fibre and silk is 0.2-0.5:1:3-5.
Preferred as technique scheme, in described step (5), the thickness of packed layer is 0.5-1cm, and grammes per square metre is 78-94g/ ㎡.
Preferred as technique scheme, in described step (6), antimicrobial treatment solution is the solution containing aloe elite.
Preferred as technique scheme, in described step (7), the content of formaldehyde of the Multifunctional baby sleep bag fabric of lightweight thermal is lower than 5mg/kg.
Compared with prior art, the present invention has following beneficial effect:
(1) skin of the Multifunctional baby sleep bag fabric of lightweight thermal that prepared by the present invention is uvioresistant natural color cotton and shrinkproof anlistatig wool, select the wool fibre of thermal property the best and the good cotton fiber of sucting wet air permeability as raw material, and by wool fibre through shrinkproof antistatic treatment, cotton fiber is through uvioresistant process, the outer shell fabric of preparation is made to ensure on excellent warming, moisture absorption, ventilative basis, unnecessary ultraviolet can be kept out, prevent the generation of electrostatic, and good stability of the dimension.
(2) packed layer of the Multifunctional baby sleep bag fabric of lightweight thermal that prepared by the present invention is silk, bamboo-carbon fibre and ceramic fibre, first using bamboo-carbon fibre and the ceramic fibre internal layer as packed layer, the internal layer of packed layer is made to have excellent antibacterial and heat insulation effect, select insulation again, the silk of moisture absorption pro-skin is again as the skin of packed layer, the skin of infant is played to the effect of nourishing care, and whole packed layer all selects fibrous material as raw material, avoid using pulvis, prevent pulvis in the process used and clean from leaking or hardening, affect the comfortable and safe performance of fabric.
(3) internal layer of the Multifunctional baby sleep bag fabric of lightweight thermal that prepared by the present invention is 100% antibacterial combed cotton, 100% combed cotton is the material that generally acknowledged softness is solid again, pro-skin performance is good again, directly can contact the skin of baby, the present invention adopts aloe elite to process the top layer of combed cotton and inside, makes combed cotton have excellent antibacterial moisturizing effect.
(4) method for sorting of the plurality of raw materials of the employing of the Multifunctional baby sleep bag fabric of lightweight thermal that prepared by the present invention is all the process gimmick of environmental protection, while imparting material function, the material green natural no side effects ensured, is suitable for infant and uses.
Detailed description of the invention:
Describe the present invention in detail below in conjunction with specific embodiment, be used for explaining the present invention in this illustrative examples of the present invention and explanation, but not as a limitation of the invention.
Embodiment 1:
(1) impregnated in the ammonium oxalate solution of 5g/L by natural colorful cotton fibre and 100% combed cotton with bath raio 1:50,50 DEG C of constant temperature oscillations, take out, washing is dried, and obtains pretreated natural colorful cotton fibre and 100% combed cotton.
(2) by pretreated natural colorful cotton fibre with bath raio 1:30 impregnated in 2g/L containing in medical zinc oxide and titania solution, wherein the amount ratio of medical zinc oxide and titanium dioxide is 1:1, take out, dry washing oven dry and obtain uvioresistant natural colorful cotton fibre.
(3) by removing the wool of impurity after low temperature atomsphere plasma process, impregnated in cutinase and the keratinase treatment fluid of 0.5g/L, taking out washing and drying, obtaining shrinkproof anlistatig wool.
(4) be that the uvioresistant natural colorful cotton fibre of 2:1 and anlistatig wool fibre carry out intertexture and form skin by amount ratio.
(5) by weight, interweaved by the bamboo-carbon fibre of the ceramic fibre of 0.2 part and 1 part and make nonwoven layer, lay the silk fiber layer of 3 parts in the upper and lower surface of nonwoven layer, the closely sealed formation thickness of acupuncture is 0.5cm, and grammes per square metre is the packed layer of 78g/ ㎡.
(6) 100% combing cotton fibre be impregnated in liquefied ammonia, microwave except after ammonia, impregnated in 1g/L containing in the antimicrobial treatment solution of aloe elite, dewatered drying, through weaving formation internal layer.
(7) successively skin, packed layer and internal layer are carried out seam to spread out compound, form the Multifunctional baby sleep bag fabric of lightweight thermal.
Embodiment 2:
(1) impregnated in the ammonium oxalate solution of 6g/L by natural colorful cotton fibre and 100% combed cotton with bath raio 1:50,60 DEG C of constant temperature oscillations, take out, washing is dried, and obtains pretreated natural colorful cotton fibre and 100% combed cotton.
(2) by pretreated natural colorful cotton fibre with bath raio 1:30 impregnated in 5g/L containing in medical zinc oxide and titania solution, wherein the amount ratio of medical zinc oxide and titanium dioxide is 1:1, take out, dry washing oven dry and obtain uvioresistant natural colorful cotton fibre.
(3) by removing the wool of impurity after low temperature atomsphere plasma process, impregnated in cutinase and the keratinase treatment fluid of 1g/L, taking out washing and drying, obtaining shrinkproof anlistatig wool.
(4) be that the uvioresistant natural colorful cotton fibre of 4:1 and anlistatig wool fibre carry out intertexture and form skin by amount ratio.
(5) by weight, interweaved by the bamboo-carbon fibre of the ceramic fibre of 0.5 part and 1 part and make nonwoven layer, lay the silk fiber layer of 5 parts in the upper and lower surface of nonwoven layer, the closely sealed formation thickness of acupuncture is 1cm, and grammes per square metre is the packed layer of 94g/ ㎡.
(6) 100% combing cotton fibre be impregnated in liquefied ammonia, microwave except after ammonia, impregnated in 2g/L containing in the antimicrobial treatment solution of aloe elite, dewatered drying, through weaving formation internal layer.
(7) successively skin, packed layer and internal layer are carried out seam to spread out compound, form the Multifunctional baby sleep bag fabric of lightweight thermal.
Embodiment 3:
(1) impregnated in the ammonium oxalate solution of 5.2g/L by natural colorful cotton fibre and 100% combed cotton with bath raio 1:50,55 DEG C of constant temperature oscillations, take out, washing is dried, and obtains pretreated natural colorful cotton fibre and 100% combed cotton.
(2) by pretreated natural colorful cotton fibre with bath raio 1:30 impregnated in 3g/L containing in medical zinc oxide and titania solution, wherein the amount ratio of medical zinc oxide and titanium dioxide is 1:1, take out, dry washing oven dry and obtain uvioresistant natural colorful cotton fibre.
(3) by removing the wool of impurity after low temperature atomsphere plasma process, impregnated in cutinase and the keratinase treatment fluid of 0.6g/L, taking out washing and drying, obtaining shrinkproof anlistatig wool.
(4) be that the uvioresistant natural colorful cotton fibre of 3:1 and anlistatig wool fibre carry out intertexture and form skin by amount ratio.
(5) by weight, interweaved by the bamboo-carbon fibre of the ceramic fibre of 0.3 part and 1 part and make nonwoven layer, lay the silk fiber layer of 3-5 part in the upper and lower surface of nonwoven layer, the closely sealed formation thickness of acupuncture is 0.8cm, and grammes per square metre is the packed layer of 82g/ ㎡.
(6) 100% combing cotton fibre be impregnated in liquefied ammonia, microwave except after ammonia, impregnated in 1.5g/L containing in the antimicrobial treatment solution of aloe elite, dewatered drying, through weaving formation internal layer.
(7) successively skin, packed layer and internal layer are carried out seam to spread out compound, form the Multifunctional baby sleep bag fabric of lightweight thermal.
Embodiment 4:
(1) impregnated in the ammonium oxalate solution of 5.6g/L by natural colorful cotton fibre and 100% combed cotton with bath raio 1:50,53 DEG C of constant temperature oscillations, take out, washing is dried, and obtains pretreated natural colorful cotton fibre and 100% combed cotton.
(2) by pretreated natural colorful cotton fibre with bath raio 1:30 impregnated in 4g/L containing in medical zinc oxide and titania solution, wherein the amount ratio of medical zinc oxide and titanium dioxide is 1:1, take out, dry washing oven dry and obtain uvioresistant natural colorful cotton fibre.
(3) by removing the wool of impurity after low temperature atomsphere plasma process, impregnated in cutinase and the keratinase treatment fluid of 0.7g/L, taking out washing and drying, obtaining shrinkproof anlistatig wool.
(4) be that the uvioresistant natural colorful cotton fibre of 2:1 and anlistatig wool fibre carry out intertexture and form skin by amount ratio.
(5) by weight, interweaved by the bamboo-carbon fibre of the ceramic fibre of 0.4 part and 1 part and make nonwoven layer, lay the silk fiber layer of 4 parts in the upper and lower surface of nonwoven layer, the closely sealed formation thickness of acupuncture is 0.7cm, and grammes per square metre is the packed layer of 82g/ ㎡.
(6) 100% combing cotton fibre be impregnated in liquefied ammonia, microwave except after ammonia, impregnated in 1.4g/L containing in the antimicrobial treatment solution of aloe elite, dewatered drying, through weaving formation internal layer.
(7) successively skin, packed layer and internal layer are carried out seam to spread out compound, form the Multifunctional baby sleep bag fabric of lightweight thermal.
Embodiment 5:
(1) impregnated in the ammonium oxalate solution of 5.7g/L by natural colorful cotton fibre and 100% combed cotton with bath raio 1:50,60 DEG C of constant temperature oscillations, take out, washing is dried, and obtains pretreated natural colorful cotton fibre and 100% combed cotton.
(2) by pretreated natural colorful cotton fibre with bath raio 1:30 impregnated in 3.5g/L containing in medical zinc oxide and titania solution, wherein the amount ratio of medical zinc oxide and titanium dioxide is 1:1, take out, dry washing oven dry and obtain uvioresistant natural colorful cotton fibre.
(3) by removing the wool of impurity after low temperature atomsphere plasma process, impregnated in cutinase and the keratinase treatment fluid of 0.8g/L, taking out washing and drying, obtaining shrinkproof anlistatig wool.
(4) be that the uvioresistant natural colorful cotton fibre of 2-4:1 and anlistatig wool fibre carry out intertexture and form skin by amount ratio.
(5) by weight, interweaved by the bamboo-carbon fibre of the ceramic fibre of 0.4 part and 1 part and make nonwoven layer, lay the silk fiber layer of 3-5 part in the upper and lower surface of nonwoven layer, the closely sealed formation thickness of acupuncture is 0.9cm, and grammes per square metre is the packed layer of 90g/ ㎡.
(6) 100% combing cotton fibre be impregnated in liquefied ammonia, microwave except after ammonia, impregnated in 1.7g/L containing in the antimicrobial treatment solution of aloe elite, dewatered drying, through weaving formation internal layer.
(7) successively skin, packed layer and internal layer are carried out seam to spread out compound, form the Multifunctional baby sleep bag fabric of lightweight thermal.
Embodiment 6:
(1) impregnated in the ammonium oxalate solution of 5.4g/L by natural colorful cotton fibre and 100% combed cotton with bath raio 1:50,50 DEG C of constant temperature oscillations, take out, washing is dried, and obtains pretreated natural colorful cotton fibre and 100% combed cotton.
(2) by pretreated natural colorful cotton fibre with bath raio 1:30 impregnated in 4g/L containing in medical zinc oxide and titania solution, wherein the amount ratio of medical zinc oxide and titanium dioxide is 1:1, take out, dry washing oven dry and obtain uvioresistant natural colorful cotton fibre.
(3) by removing the wool of impurity after low temperature atomsphere plasma process, impregnated in cutinase and the keratinase treatment fluid of 1g/L, taking out washing and drying, obtaining shrinkproof anlistatig wool.
(4) be that the uvioresistant natural colorful cotton fibre of 4:1 and anlistatig wool fibre carry out intertexture and form skin by amount ratio.
(5) by weight, interweaved by the bamboo-carbon fibre of the ceramic fibre of 0.5 part and 1 part and make nonwoven layer, lay the silk fiber layer of 3 parts in the upper and lower surface of nonwoven layer, the closely sealed formation thickness of acupuncture is 0.8cm, and grammes per square metre is the packed layer of 89g/ ㎡.
(6) 100% combing cotton fibre be impregnated in liquefied ammonia, microwave except after ammonia, impregnated in 1.3g/L containing in the antimicrobial treatment solution of aloe elite, dewatered drying, through weaving formation internal layer.
(7) successively skin, packed layer and internal layer are carried out seam to spread out compound, form the Multifunctional baby sleep bag fabric of lightweight thermal.
After testing, the result of the grammes per square metre of the Multifunctional baby sleep bag fabric of lightweight thermal prepared of embodiment 1-6, warmth retention property, poisture-penetrability, gas permeability, ultraviolet-resistent property, DIMENSIONAL STABILITY, security and antibiotic property is as follows:
As seen from the above table, the Multifunctional baby sleep bag fabric quality of lightweight thermal prepared by the present invention is light, and warming coefficient is good, and moisture absorption is breathed freely, and dimensionally stable, can prevent some ultra violet rays and bacterium, is suitable for infant and uses.
Above-described embodiment is illustrative principle of the present invention and effect thereof only, but not for limiting the present invention.Any person skilled in the art scholar all without prejudice under spirit of the present invention and category, can modify above-described embodiment or changes.Therefore, such as have in art usually know the knowledgeable do not depart from complete under disclosed spirit and technological thought all equivalence modify or change, must be contained by claim of the present invention.
Claims (10)
1. the Multifunction baby bunting fabric of a lightweight thermal, it is characterized in that, the Multifunctional baby sleep bag fabric of described lightweight thermal comprises skin, packed layer and internal layer, described skin is uvioresistant natural color cotton and shrinkproof anlistatig wool, described packed layer is silk, bamboo-carbon fibre and ceramic fibre, and described internal layer is 100% antibacterial combed cotton.
2. the Multifunctional baby sleep bag fabric of a kind of lightweight thermal according to claim 1, is characterized in that, the grammes per square metre of the Multifunctional baby sleep bag fabric of described lightweight thermal is 98-132g/ ㎡.
3. a preparation method for the Multifunction baby bunting fabric of lightweight thermal, is characterized in that: comprise the following steps:
(1) impregnated in the ammonium oxalate solution of 5-6g/L by natural colorful cotton fibre and 100% combed cotton with bath raio 1:50,50-60 DEG C of constant temperature oscillation, take out, washing is dried, and obtains pretreated natural colorful cotton fibre and 100% combed cotton;
(2) pretreated natural colorful cotton fibre step (1) prepared impregnated in containing in medical zinc oxide and titania solution with bath raio 1:30, takes out, and dries washing oven dry and obtains uvioresistant natural colorful cotton fibre;
(3) by removing the wool of impurity after low temperature atomsphere plasma process, impregnated in the Protease Treatment liquid of 0.5-1g/L, taking out washing and drying, obtaining shrinkproof anlistatig wool;
(4) anlistatig wool fibre prepared by uvioresistant natural colorful cotton fibre step (2) prepared and step (3) carries out intertexture and forms skin;
(5) ceramic fibre and bamboo-carbon fibre are interweaved make nonwoven layer, lay silk fiber layer, the closely sealed formation packed layer of acupuncture in the upper and lower surface of nonwoven layer;
(6) impregnated in liquefied ammonia by 100% combing cotton fibre prepared by step (1), microwave is except after ammonia, and in the antimicrobial treatment solution that impregnated in 1-2g/L, dewatered drying, through weaving formation internal layer;
(7) packed layer prepared by skin step (4) prepared successively, step (5) and internal layer prepared by step (6) carry out seam and to spread out compound, form the Multifunctional baby sleep bag fabric of lightweight thermal.
4. the preparation method of the Multifunctional baby sleep bag fabric of a kind of lightweight thermal according to claim 3, it is characterized in that: in described step (2), content containing zinc oxide medical in medical zinc oxide and titania solution and titanium dioxide is 2-5g/L, and wherein the amount ratio of medical zinc oxide and titanium dioxide is 1:1.
5. the preparation method of the Multifunctional baby sleep bag fabric of a kind of lightweight thermal according to claim 3, is characterized in that: in described step (3), and Protease Treatment liquid is cutinase and keratinase treatment fluid.
6. the preparation method of the Multifunctional baby sleep bag fabric of a kind of lightweight thermal according to claim 3, is characterized in that: in described step (4), and in skin, the consumption of natural colorful cotton fibre and wool is 2-4:1.
7. the preparation method of the Multifunctional baby sleep bag fabric of a kind of lightweight thermal according to claim 3, is characterized in that: in described step (5), and in packed layer, the mass ratio of ceramic fibre, bamboo-carbon fibre and silk is 0.2-0.5:1:3-5.
8. the preparation method of the Multifunctional baby sleep bag fabric of a kind of lightweight thermal according to claim 3, is characterized in that: in described step (5), and the thickness of packed layer is 0.5-1cm, and grammes per square metre is 78-94g/ ㎡.
9. the preparation method of the Multifunctional baby sleep bag fabric of a kind of lightweight thermal according to claim 3, is characterized in that: in described step (6), and antimicrobial treatment solution is the solution containing aloe elite.
10. the preparation method of the Multifunctional baby sleep bag fabric of a kind of lightweight thermal according to claim 3, is characterized in that: in described step (7), and the content of formaldehyde of the Multifunctional baby sleep bag fabric of lightweight thermal is lower than 5mg/kg.